CN106957565A - Antibacterial high stability solid wooden compound floor edge sealing agent and application method - Google Patents
Antibacterial high stability solid wooden compound floor edge sealing agent and application method Download PDFInfo
- Publication number
- CN106957565A CN106957565A CN201710192446.2A CN201710192446A CN106957565A CN 106957565 A CN106957565 A CN 106957565A CN 201710192446 A CN201710192446 A CN 201710192446A CN 106957565 A CN106957565 A CN 106957565A
- Authority
- CN
- China
- Prior art keywords
- edge sealing
- sealing agent
- compound floor
- solid wooden
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to antibacterial high stability solid wooden compound floor edge sealing agent and application method, the edge sealing agent is formed by the Raw material processing of following parts by weight：80 120 parts of polyethylene, 10 20 parts of bee glue powder, 5 10 parts of organobentonite.The edge sealing agent of the present invention, using the good chemical stability of polyethylene, is aided with bee glue powder and organobentonite, edge sealing agent product is not influenceed by epidemic disaster, and waterproof effect persistently, while also having antibacterial, wear-resisting, stain resistance, is easy to the advantage of cleaning.
Description
Technical field
The present invention relates to antibacterial high stability solid wooden compound floor edge sealing agent and application method, belong to solid wooden compound floor and add
Work technical field.
Background technology
Floor as interior decoration product throughout huge numbers of families, but in the market on floor cracking, buckling deformation etc.
Complain of common occurrence, most problems are caused by because of floor, moisture content is uneven during preparation and use.For upper
Quality problems are stated, manufacturer generally uses following four mode to handle floor to reach certain waterproof effect：
（1）Edge sealing：As described in application number CN200520060045.4, one layer of stone of spraying covering on the groove and tenon of floor side
Wax protective layer, paraffin waterproof effect is good, adhesive force is high, and this method is also widely adopted, but paraffin is on the high side, stability
Difference, easily solidification, plate face is easily polluted in spraying process, is difficult to clean off, so as to influence floor surface attractive in appearance.Therefore, some enterprises
Research and development new water repellent is to substitute the paraffin of costliness, a kind of consolidated floor envelope as disclosed in application number CN201010219782.X
Side agent, is mainly mixed with by beeswax, resin, esters solvent and alkane solvents and formed, and in CN201310125807.3
Disclosed a kind of non-degradable Corn Starch Glue etc., the waterproofing agent species of enterprise development is various, and excellent to cheap, water resistance
Different, environmental protection research direction development, but its term of validity is unstable, is easy to run off or fails.In addition, also Some Enterprises are being applied
Adorn in technique and floor side is directly subjected to envelope paint processing, though certain waterproof action can be played temporarily, paint film fragility is big, one
Denier cracking, come off, not only influence product attractive in appearance, and end face will lose waterproof effect, floor can still make moist deformation.
（2）Add waterproof interlayer：A kind of waterproof Sound insulation flooringses as described in CN201320511513.X, by substrate
One layer of waterproof beeswax layer is laid in lower section, and this adhesive property to adhesive requires higher, and production cost is higher.
（3）Assembly structure：A kind of five-layered thick core wood compound floor board manufacturer as described in CN200610086625.X
Method, it is during assembly that the direction of wooden fibers of dash board is consistent with backboard direction, it is vertical with core plate direction, because the glue molding of slab is
By the blanket glued veneer layer between table, plate and sandwich layer, it can eliminate using caused dash board stress deformation during single flaggy, maintain ground
Board size stability.But when slab is integrally pressed, end layer adhesive first solidifies, and end layer hydrone can be moved to intermediate layer, be caused
Slab intermediate layer moisture content is higher than end layer, thus the easy bubbling deformation during ground heating of floor intermediate layer.
（4）Veneer impregnation process：A kind of full poplar multilayer engineered solid wood flooring as described in CN201110245727.2
Manufacture method, board using poplar board is handled by vacuum pressed impregnated melamine formaldehyde resin method, can be significantly improved
Single plate intensity, dimensional stability and water proofing property.But hard fragility is big after the viscosity, solidification due to resin, dry and glued mistake
Moisture evaporation in journey, can cause slab craze and transfiguration.
（5）Mortice opening：Such as：Lock, flat button, back of the body groove etc., are influenceed to produce after mating formation except that can avoid floor by humiture
Warpage, the problems such as arch upward, and lock, flat button design are also convenient for mating formation.Such as application number CN201210205108.5,
CN201110183883.0 etc. of all kinds, baroque shackle designs, are proved according to production practices, and lock is more complicated,
Cost can also increase, and tensile strength diminishes, and still can cause the problems such as excessive occlusion gap, dropout, lock are damaged.
The content of the invention
The purpose of the present invention be for above-mentioned processing method exist defect there is provided antibacterial high stability solid wooden compound floor
Edge sealing agent and application method.
The technical solution adopted for the present invention to solve the technical problems is：
Antibacterial high stability solid wooden compound floor edge sealing agent, the edge sealing agent is formed by the Raw material processing of following parts by weight：Poly- second
80-120 parts of alkene, 10-20 parts of bee glue powder, 5-10 parts of organobentonite, 0-8 parts of insect-proof agent, 0-5 parts of Nano Silver, the insect-proof agent
For any one or a few the composition in cypermethrin, Permethrin, Biphenthrin and cyphenothrin.
Propolis is the viscous secretion that honeybee gathers from tree bud or bark, and research finds that propolis has the chemical group of complexity
Into planting fragrant fat, more than 30 kinds of flavonoids, more than ten including more than 30 and plant aromatic acids etc., propolis is described as " natural
Small Drug Storage ", be precious natural wide spectrum antibiotics, have to various bacteria, fungi, germ etc. and significantly suppress and kill work
With the appropriate bee glue powder of addition, using its natural broad-spectrum antiseptic bactericidal property, is realized the anti-microbial property of edge sealing agent of the present invention, kept away
Exempt from floorboard side go mouldy, it is infested etc., greatly prolong the service life of solid wooden compound floor.
Bentonite addition is also the great discovery of present inventor, and organobentonite has good thixotroping
Added in property, suspension stability, high-temperature stability, chemical stability, edge sealing agent prescription after appropriate organobentonite stirs,
Stable dispersion can be formed, that is, realize the stable homogeneous of edge sealing agent, also significantly improve edge sealing agent film forming homogeneity,
Ageing resistace and peeling resistance.
It is preferred that, the edge sealing agent is formed by the Raw material processing of following parts by weight：100 parts of polyethylene, 15 parts of bee glue powder, has
8 parts of machine bentonite, 5 parts of insect-proof agent, 3 parts of Nano Silver.
The application method of the antibacterial high stability solid wooden compound floor edge sealing agent of the present invention, for manufacturing the compound ground of solid wood
Plate, the manufacture method comprises the following steps：
（1）It is prepared by base material：Wooden veneer from moisture content 6 ~ 12%, is obtained after sequentially passing through cloth glue, assembly, cold pressing, hot pressing
Base material；
（2）Surface is posted；
（3）Mortice opening；
（4）Top finishing；
（5）Edge sealing processing, concrete operations are as follows：Edge sealing agent first heats melting, and it is 100 ~ 115 DEG C to maintain temperature, passes through high pressure
Pumping is at the uniform velocity sprayed on step into nozzle（4）Obtained floorboard side, quantity for spray is 20 ~ 40g/m2。
It is preferred that, the assembly uses " odd-even symmetry structure " mode；Specially odd-level uses the wood of key element all same
Matter veneer, even level uses the Wooden veneer of key element all same；The key element includes moisture content, texture, seeds and thickness.
It is preferred that, the number of plies of the solid wooden compound floor is more than four layers, step（1）Middle hot pressing is using " layering forging and stamping "
Mode, be specially first assembly suppress at least two layers middle Wooden veneer base and upper and lower both sides each at least one layer it is wooden
Veneer base, assembly is hot-forming again after repairing respectively.
It is preferred that, step（2）Surface is posted specially：Natural precious wood skin or recombinant decorative list are posted in substrate upper surface
Plate, balance layer veneer is posted in base material lower surface.
It is preferred that, step（3）Slotted in the way of " the flat button in horizontal lock-longitudinal direction ", " laterally lock " tool
Body is that male and female tapered end and lock match on solid wooden compound floor width, in the center line of male locked groove and female locked groove
Heart line aligns, and " the flat button in longitudinal direction " is specially that male and female tapered end and locked groove match on solid wooden compound floor length direction.
It is preferred that, during the male and female locked groove in " laterally lock " is trapezoidal, triangle or circular arc, " the flat button in longitudinal direction "
Locked groove be circular arc.
It is preferred that, step（4）Middle upper and lower surface covers with paint, lacquer, colour wash, etc. UV paints, PU paints, vegetable oil or any two kinds of compound.
It is preferred that, the seeds of the Wooden veneer are the one or more in poplar, Eucalyptus, birch, pine, described
Balance layer veneer is birch veneer.
The invention has the advantages that：The present invention edge sealing agent, using the good chemical stability of polyethylene, be aided with bee glue powder and
Organobentonite, edge sealing agent product is not influenceed by epidemic disaster, and waterproof effect is lasting, while also having antibacterial, wear-resisting, resistant
Metachromia, is easy to the advantage of cleaning.In addition, in the edge sealing agent application method of the present invention, odd-even symmetry structure assembly：Strict control base
Material correspondence material moisture content, texture, seeds, thickness four elementses, eliminate stress deformation, maintain the stabilization of substrate sizes and structure；
Using the second pressing technique of " three layers of forging and stamping "：Mechanical stability based on three-decker, will be contained by being layered hot pressing in slab
Water rate is adjusted to uniform and stable, is substantially discharged the formaldehyde in slab, product is reached requirement；Simultaneously as positive and negative is all
By sufficiently repairing, veneer internal stress is fully discharged, and mechanical property is more stablized；Flat shackle designs：According to actual raw
Production situation, technique is simple, can not only reduce the phenomenons such as termination crack, maintains floor panel structure stable, can also be by product volume recovery
Improve 4 ~ 6%.
In summary, the high stable type solid wooden compound floor Form aldehyde release manufactured using edge sealing agent of the present invention and application method
The low, moisture content of amount is uniform, good stability of the dimension, and antibacterial, water resistance be excellent and effect stability, can effectively solve floor drying shrinkage wet
The problem on deformation such as swollen.
Brief description of the drawings
Fig. 1 is the horizontal buckle structure schematic diagram in the present invention;
Fig. 2 is the flat structural representation detained in longitudinal direction in the present invention.
Embodiment
Below by specific embodiment, and with reference to accompanying drawing, technical scheme is described in further detail.
Embodiment 1：
Antibacterial high stability solid wooden compound floor edge sealing agent, the edge sealing agent is formed by the Raw material processing of following parts by weight：Poly- second
80 parts of alkene, 10 parts of bee glue powder, 5 parts of organobentonite；
The application method of the antibacterial high stability solid wooden compound floor edge sealing agent, for manufacturing solid wooden compound floor, including such as
Lower step：
（1）It is prepared by base material：Wooden veneer from moisture content 6%, base is obtained after sequentially passing through cloth glue, assembly, cold pressing, hot pressing
Material, the seeds of the Wooden veneer are poplar；
The assembly uses " odd-even symmetry structure " mode；Specially odd-level uses the Wooden veneer of key element all same, even number
Layer uses the Wooden veneer of key element all same；The key element includes moisture content, texture, seeds and thickness；
The number of plies of the solid wooden compound floor is four layers, and hot pressing is specially that first assembly is suppressed by the way of " layering forging and stamping "
Two layers of middle Wooden veneer base and each one layer of Wooden veneer base of upper and lower both sides, the assembly hot pressing again after repairing respectively
Shaping；
（2）Surface is posted：Natural precious wood skin is posted in substrate upper surface, balance layer veneer is posted in base material lower surface, it is described
Balance layer veneer is birch veneer
（3）Mortice opening：As illustrated in fig. 1 and 2, slotted in the way of " the flat button in horizontal lock-longitudinal direction ", it is described " laterally to lock
Button " is specially that on solid wooden compound floor width, male tapered end, female tapered end and lock match, the center line of public locked groove with
The center line alignment of female locked groove, " the flat button in longitudinal direction " is specially male and female tapered end and lock on solid wooden compound floor length direction
Groove matches, and the male and female locked groove in " the laterally lock " is trapezoidal, and the locked groove in " the flat button in longitudinal direction " is circular arc；
（4）Top finishing, upper and lower surface covers with paint, lacquer, colour wash, etc. UV paints；
（5）Edge sealing processing, edge sealing agent, which is first heated, is melt into stable dispersion, and it is 100 DEG C to maintain temperature, passes through high-pressure pump
It is evacuated in nozzle and is at the uniform velocity sprayed on step（4）Obtained floorboard side, quantity for spray is 20g/m2。
Embodiment 2：
Antibacterial high stability solid wooden compound floor edge sealing agent, the edge sealing agent is formed by the Raw material processing of following parts by weight：Poly- second
120 parts of alkene, 20 parts of bee glue powder, 10 parts of organobentonite, 8 parts of insect-proof agent, 5 parts of Nano Silver, the insect-proof agent is cypermethrin；
The application method of the antibacterial high stability solid wooden compound floor edge sealing agent, for manufacturing solid wooden compound floor, including such as
Lower step：
（1）It is prepared by base material：Wooden veneer from moisture content 12%, base is obtained after sequentially passing through cloth glue, assembly, cold pressing, hot pressing
Material, the seeds of the Wooden veneer are Eucalyptus；
The assembly uses " odd-even symmetry structure " mode；Specially odd-level uses the Wooden veneer of key element all same, even number
Layer uses the Wooden veneer of key element all same；The key element includes moisture content, texture, seeds and thickness；
The number of plies of the solid wooden compound floor is seven layers, and first assembly suppresses three layers of middle Wooden veneer base and upper and lower two
The Wooden veneer base of each two layers of side, assembly is hot-forming again after repairing respectively；
（2）Surface is posted：Recombinant decorative veneer is posted in substrate upper surface, balance layer, the balance are posted in base material lower surface
Layer veneer is birch veneer；
（3）Mortice opening；Slotted in the way of " the flat button in horizontal lock-longitudinal direction ", " the laterally lock " is specially in reality
On wood composite floor width, male and female tapered end and lock match, the center line pair of the center line of male locked groove and female locked groove
Together, described " the flat button in longitudinal direction " is specially that male and female tapered end and locked groove match on solid wooden compound floor length direction；It is described " horizontal
To lock " in male and female locked groove to be trapezoidal, the locked groove in " the flat button in longitudinal direction " is circular arc.
（4）Top finishing, upper and lower surface covers with paint, lacquer, colour wash, etc. PU paints；
（5）Edge sealing processing, edge sealing agent first heats melting, and it is 115 DEG C to maintain temperature, is evacuated in nozzle and at the uniform velocity sprayed by high-pressure pump
It is coated in step（4）Obtained floorboard side, quantity for spray is 40g/m2。
Embodiment 3：
Antibacterial high stability solid wooden compound floor edge sealing agent, the edge sealing agent is formed by the Raw material processing of following parts by weight：Poly- second
100 parts of alkene, 15 parts of bee glue powder, 8 parts of organobentonite, 5 parts of insect-proof agent, 3 parts of Nano Silver, the insect-proof agent is cypermethrin and chlorine
The equal proportion mixture of chrysanthemum ester；
The application method of the antibacterial high stability solid wooden compound floor edge sealing agent, for manufacturing solid wooden compound floor, including such as
Lower step：
（1）It is prepared by base material：Wooden veneer from moisture content 8%, base is obtained after sequentially passing through cloth glue, assembly, cold pressing, hot pressing
Material, the seeds of the Wooden veneer are birch,
The assembly uses " odd-even symmetry structure " mode；Specially odd-level uses the Wooden veneer of key element all same, even number
Layer uses the Wooden veneer of key element all same；The key element includes moisture content, texture, seeds and thickness；
The number of plies of the solid wooden compound floor is seven layers, and first assembly suppresses three layers of middle Wooden veneer base and upper and lower two
The Wooden veneer base of each two layers of side, assembly is hot-forming again after repairing respectively；
（2）Surface is posted, and posts natural precious wood skin in substrate upper surface, balance layer veneer is posted in base material lower surface, described
Balance layer veneer is birch veneer；
（3）Mortice opening；Slotted in the way of " the flat button in horizontal lock-longitudinal direction ", " the laterally lock " is specially in reality
On wood composite floor width, male and female tapered end and lock match, the center line pair of the center line of male locked groove and female locked groove
Together, described " the flat button in longitudinal direction " is specially that male and female tapered end and locked groove match on solid wooden compound floor length direction, described " horizontal
To lock " in male and female locked groove to be trapezoidal, the locked groove in " the flat button in longitudinal direction " is circular arc.
（4）Top finishing, upper and lower surface covers with paint, lacquer, colour wash, etc. the compound of UV paints and vegetable oil；
（5）Edge sealing processing, concrete operations are as follows：Edge sealing agent first heats melting, and it is 110 DEG C to maintain temperature, passes through high pressure pumping
Step is at the uniform velocity sprayed on into nozzle（4）Obtained floorboard side, quantity for spray is 30g/m2。
The advantage of embodiment 1-3 edge sealing agent is as follows：Using the good chemical stability of polyethylene, it is aided with bee glue powder and has
Machine bentonite, edge sealing agent product is not influenceed by epidemic disaster, and waterproof effect is lasting, while also having antibacterial, wear-resisting, anti-pollution
Property, it is easy to the advantage of cleaning.
The application method of embodiment 1-3 edge sealing agents has the following advantages that：
In method of the edge sealing agent of the present invention using manufacture solid wooden compound floor, odd-even symmetry structure assembly：Strict control base material
Correspondence material moisture content, texture, seeds, thickness four elementses, eliminate stress deformation, maintain the stabilization of substrate sizes and structure；Adopt
With the second pressing technique of " three layers of forging and stamping "：
Mechanical stability based on three-decker, moisture content in slab is adjusted to uniform and stable, maximize by being layered hot pressing
Formaldehyde in ground release slab, makes product reach requirement；Simultaneously as positive and negative is all by sufficiently repairing, veneer internal stress
Fully discharged, mechanical property is more stablized；
Flat shackle designs：According to practical condition, technique is simple, can not only reduce the phenomenons such as termination crack, maintains floor
Stability Analysis of Structures, can also improve 4 ~ 6% by product volume recovery.
Embodiment described above is a kind of preferably scheme of the present invention, not makees any formal to the present invention
Limitation, also has other variants and remodeling on the premise of without departing from the technical scheme described in claim.
Claims (10)
1. antibacterial high stability solid wooden compound floor edge sealing agent, it is characterised in that：The edge sealing agent by following parts by weight raw material
Process：80-120 parts of polyethylene, 10-20 parts of bee glue powder, 5-10 parts of organobentonite, 0-8 parts of insect-proof agent, Nano Silver 0-5
Part, the insect-proof agent is any one or a few the composition in cypermethrin, Permethrin, Biphenthrin and cyphenothrin.
2. antibacterial high stability solid wooden compound floor edge sealing agent according to claim 1, it is characterised in that：The edge sealing agent
Formed by the Raw material processing of following parts by weight：100 parts of polyethylene, 15 parts of bee glue powder, 8 parts of organobentonite, 5 parts of insect-proof agent is received
3 parts of rice silver.
3. the application method of the antibacterial high stability solid wooden compound floor edge sealing agent described in a kind of claim 1 or 2, for manufacturing
Solid wooden compound floor, it is characterised in that：The manufacture method comprises the following steps：
（1）It is prepared by base material：Wooden veneer from moisture content 6 ~ 12%, is obtained after sequentially passing through cloth glue, group embryo, cold pressing, hot pressing
Base material；
（2）Surface is posted；
（3）Mortice opening；
（4）Top finishing；
（5）Edge sealing processing, concrete operations are as follows：Edge sealing agent first heats melting, and it is 100 ~ 115 DEG C to maintain temperature, passes through high pressure
Pumping is at the uniform velocity sprayed on step into nozzle（4）Obtained floorboard side, quantity for spray is 20 ~ 40g/m2。
4. the application method of antibacterial high stability solid wooden compound floor edge sealing agent according to claim 3, it is characterised in that：
Described group of embryo uses " odd-even symmetry structure " mode；Specially odd-level uses the Wooden veneer of key element all same, and even level is adopted
With the Wooden veneer of key element all same；The key element includes moisture content, texture, seeds and thickness.
5. the application method of antibacterial high stability solid wooden compound floor edge sealing agent according to claim 3, it is characterised in that：
The number of plies of the solid wooden compound floor is more than four layers, step（1）Middle hot pressing is specially first group by the way of " layering forging and stamping "
Embryo suppresses at least two layers of middle Wooden veneer base and each at least one layer of Wooden veneer base of upper and lower both sides, through repairing respectively
Embryo is organized after benefit again hot-forming.
6. antibacterial high stability solid wooden compound floor edge sealing agent according to claim 3, it is characterised in that：Step（2）Table
Face is posted specially：Natural precious wood skin or recombinant decorative veneer are posted in substrate upper surface, balance is posted in base material lower surface
Layer veneer.
7. antibacterial high stability solid wooden compound floor edge sealing agent according to claim 3, it is characterised in that：Step（3）Press
Mode according to " the flat button in horizontal lock-longitudinal direction " is slotted, and " the laterally lock " is specially in solid wooden compound floor width side
Upwards, male and female tapered end and lock match, and the center line of male locked groove aligns with the center line of female locked groove, " the flat button in longitudinal direction "
Specially on solid wooden compound floor length direction, male and female tapered end and locked groove match.
8. antibacterial high stability solid wooden compound floor edge sealing agent according to claim 7, it is characterised in that：It is described " horizontal
Male and female locked groove in lock " is that the locked groove in trapezoidal, triangle or circular arc, " the flat button in longitudinal direction " is circular arc.
9. antibacterial high stability solid wooden compound floor edge sealing agent according to claim 3, it is characterised in that：Step（4）In
Upper and lower surface covers with paint, lacquer, colour wash, etc. UV paints, PU paints, vegetable oil or any two kinds of compound.
10. antibacterial high stability solid wooden compound floor edge sealing agent according to claim 6, it is characterised in that：It is described wooden
The seeds of veneer are the one or more in poplar, Eucalyptus, birch, pine, and the balance layer veneer is birch veneer.