CN106957497A - Manufacture the material compositions of sport pad body and the manufacture method of the sport pad body - Google Patents
Manufacture the material compositions of sport pad body and the manufacture method of the sport pad body Download PDFInfo
- Publication number
- CN106957497A CN106957497A CN201610012299.1A CN201610012299A CN106957497A CN 106957497 A CN106957497 A CN 106957497A CN 201610012299 A CN201610012299 A CN 201610012299A CN 106957497 A CN106957497 A CN 106957497A
- Authority
- CN
- China
- Prior art keywords
- pad body
- content
- plant fiber
- body according
- sport pad
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of manufacture method for the material compositions and the sport pad body for manufacturing sport pad body, the manufacture method is comprised the steps of:Composite material of plant fiber and content expanded material between 40~85% between of the content between 15~60% based on overall weight is mixed, addition foaming agent carries out foaming and molding, and then shapes a pad;Wherein the composite material of plant fiber includes plant fiber material, starch adjuvant and biopolymer additive, and the biopolymer additive includes plant hormone, ferment, biological vinegar and lactate;Wherein the expanded material is selected from one kind in polyvinyl chloride (PVC) and natural rubber (NR).
Description
Technical field
The present invention it is relevant with the material and manufacture method of sport pad body, particularly relate to it is environmentally friendly, low it is smelly,
The manufacture of the material compositions and the sport pad body of a kind of manufacture sport pad body of resource reutilization effect
Method.
Background technology
China's TW I367234 patents (with respect to the B2 patents of U.S. case US 8,389,110), disclose one
Plant the constituent for composite material of plant fiber.It mainly provides a kind of nontoxic, harmless, high resource profit
With the few regenerated resources material of rate, pollutant yield.The patented technology can avoid sensitive paper palpus from using trees,
Therefore it can need not chop at a tree, and can use the current less plant waste being utilized, such as withered bar,
The things such as bagasse, corncob, cocoanut shell, cereal shell, peanut shell, leaf, the leaf of bamboo, wood chip, bamboo scraps
Matter is come as raw material.Therefore, there is environmentally friendly, resource reclaim and nontoxic.
However, aforementioned component thing, the application examples in sport pad body is not applied, and whether can answer at present
Also turn into query used in sport pad body.
The content of the invention
It is a primary object of the present invention to provide a kind of material compositions for manufacturing sport pad body and the motion
With the manufacture method of pad, composite material of plant fiber can be used to be combined with expanded material for it, and produce fortune
Pad is employed, the sport pad body produced has the advantages that environmentally friendly, low smelly, resource reutilization.
Then, to achieve these goals, the invention provides a kind of combination of materials for manufacturing sport pad body
Thing, includes:Composite material of plant fiber of the content between 15~60% based on overall weight
And expanded material of the content between 40~85%;Wherein the composite material of plant fiber is fine comprising plant
Raw material, starch adjuvant and biopolymer additive are tieed up, the biopolymer additive includes plant
Hormone, ferment, biological vinegar and lactate;Wherein the expanded material is selected from polyvinyl chloride (PVC) and day
One kind in right rubber (NR).
It is preferred that the plant fiber material is selected from the group being made up of following material:Withered bar, bagasse,
Corncob, cocoanut shell, cereal shell, peanut shell, leaf, the leaf of bamboo, wood chip, bamboo scraps and aforementioned substances
Combination.
It is preferred that the starch adjuvant is selected from the group being made up of following material:Sweet potato flour, Ma Ling
The combination of potato powder, cornstarch and aforementioned substances.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 15%, the foaming
The content of material is 85%.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 30%, the foaming
The content of material is 70%.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 45%, the foaming
The content of material is 55%.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 60%, the foaming
The content of material is 40%.
It is preferred that in the composite material of plant fiber, the plant fiber material, starch adjuvant and life
The weight ratio of thing polymeric additive is 6:1:3.
It is preferred that in the composite material of plant fiber, the plant fiber material, starch adjuvant and life
Weight ratio between thing polymeric additive is 7:1:2.
It is preferred that the biopolymer additive be by weight ratio be 10:5:2:3 plant hormone,
What ferment, biological vinegar and lactate were constituted.
In addition, to achieve the above object, present invention also offers a kind of manufacture method of sport pad body, bag
Contain the following steps:String of the content between 15~60% based on overall weight is mixed to answer
The expanded material of condensation material and content between 40~85%, addition foaming agent carries out foaming and molding, enters
And shape a pad;Wherein the composite material of plant fiber includes plant fiber material, starch adjuvant
And biopolymer additive, the biopolymer additive includes plant hormone, ferment, biological vinegar
And lactate;Wherein the expanded material is selected from one kind in polyvinyl chloride (PVC) and natural rubber (NR).
It is preferred that the plant fiber material is selected from the group being made up of following material:Withered bar, bagasse,
Corncob, cocoanut shell, cereal shell, peanut shell, leaf, the leaf of bamboo, wood chip, bamboo scraps and aforementioned substances
Combination.
It is preferred that the starch adjuvant is selected from the group being made up of following material:Sweet potato flour, Ma Ling
The combination of potato powder, cornstarch and aforementioned substances.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 15%, the foaming
The content of material is 85%.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 30%, the foaming
The content of material is 70%.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 45%, the foaming
The content of material is 55%.
It is preferred that based on overall weight, the content of the composite material of plant fiber is 60%, the foaming
The content of material is 40%.
It is preferred that in the composite material of plant fiber, the plant fiber material, starch adjuvant and life
The weight ratio of thing polymeric additive is 6:1:3.
It is preferred that in the composite material of plant fiber, the plant fiber material, starch adjuvant and life
Weight ratio between thing polymeric additive is 7:1:2.
It is preferred that the biopolymer additive be by weight ratio be 10:5:2:3 plant hormone,
What ferment, biological vinegar and lactate were constituted.
Whereby, the usable composite material of plant fiber of the present invention is combined with expanded material, and produces motion use
Pad, and then there is environmentally friendly, low smelly, resource reutilization.
Embodiment
In order to describe the technical characterstic of the present invention in detail, preferred embodiments below is now lifted, wherein:
A kind of manufacture method for sport pad body that a preferred embodiment of the present invention is provided, includes following step
Suddenly:
Mix composite material of plant fiber between 15~60% of content based on overall weight and
Expanded material of the content between 40~85%, adds appropriate foaming agent, and carry out in a design temperature
Foaming and molding, foam pattern can be the mode of continuous foamed, shooting foaming or foam-in-mould, and then shape
Go out a pad.Wherein the composite material of plant fiber includes plant fiber material, starch adjuvant and life
Thing polymeric additive, the biopolymer additive includes plant hormone, ferment, biological vinegar and breast
Acid esters;Wherein the expanded material is selected from one kind in polyvinyl chloride (PVC) and natural rubber (NR);Wherein should
Foaming agent is selected from known foaming agent, such as ACDA (azodicarbonamide, also known as AC foaming agents) or
OBSH (disulfonyl hydrazide diphenyl ether), and the design temperature is also traditional blowing temperature, such as expanded material
During for PVC, then design temperature is 180 degree Celsius or so;And the expanded material be NR when, then set
Temperature is about at 150 degree Celsius or so.
In above-mentioned manufacture method, plant of the content between 15~60% based on overall weight
The expanded material of fibrous composite and content between 40~85%, as manufactures sport pad body
Material compositions.Wherein the composite material of plant fiber comprising plant fiber material, starch adjuvant and
Biopolymer additive, the biopolymer additive comprising plant hormone, ferment, biological vinegar and
Lactate;Wherein the expanded material is selected from one kind in polyvinyl chloride (PVC) and natural rubber (NR).
In the present embodiment, the plant fiber material is selected from the group being made up of following material:Withered bar,
Bagasse, corncob, cocoanut shell, cereal shell, peanut shell, leaf, the leaf of bamboo, wood chip, bamboo scraps and preceding
State the combination of material.In addition, the starch adjuvant is selected from the group being made up of following material:Sweet potato
Powder, dehydrated potato powder, the combination of cornstarch and aforementioned substances.Wherein, in the composite material of plant fiber,
The weight ratio of the plant fiber material, starch adjuvant and biopolymer additive is 6:1:3,
Or 7:1:2, the two ratios are disclosed in TW I367234 patents, public due to having belonged to
Know the application emphasis of technology and non-invention, appearance is not repeated.In addition, the biopolymer additive is by weight
Amount is than being 10:5:2:3 plant hormone, ferment, biological vinegar and lactate is constituted, this ratio
Also it is disclosed in TW I367234 patents, appearance is not repeated.
In the present embodiment, based on overall weight, the content of the composite material of plant fiber is 15%,
The content of the expanded material is 85%.
In the present embodiment, ratio is alternatively:Based on overall weight, the composite material of plant fiber
Content is 30%, and the content of the expanded material is 70%.
In the present embodiment, ratio is alternatively:Based on overall weight, the composite material of plant fiber
Content is 45%, and the content of the expanded material is 55%.
In the present embodiment, ratio is alternatively:Based on overall weight, the composite material of plant fiber
Content is 60%, and the content of the expanded material is 40%.
The above-mentioned composite material of plant fiber and the expanded material according to above-mentioned preparation method according to above-mentioned different proportion system
Into after sport pad body, corresponding confficient of static friction and the coefficient of kinetic friction are simultaneously differed.Table 1 below is listed
The expanded material confficient of static friction and the coefficient of kinetic friction corresponding under different proportion when being polyvinyl chloride.Its
In, confficient of static friction and the coefficient of kinetic friction are measured according to ASTM D1894-11 methods, and test environment is:Temperature
23 ± 2 DEG C of degree, humidity 50 ± 2%, speed 150mm/min, strength 221.83g, contact surface are wooden.
Table 1
Its confficient of static friction of sport pad body made under different proportion is understood by above-mentioned table 1 and dynamic is rubbed
The change of coefficient is wiped, therefore produces the sport pad body of anti-slip effect when can be as motion to ground.
Table 2 below static friction system corresponding under different proportion when listing the expanded material for natural rubber
Number and the coefficient of kinetic friction.
Table 2
Its confficient of static friction of sport pad body made under different proportion is understood by above-mentioned table 2 and dynamic is rubbed
The change of coefficient is wiped, therefore produces the sport pad body of anti-slip effect when can be as motion to ground.
In addition, the composite material of plant fiber is mixed after sport pad body with the expanded material, it can produce
To the effect of the taste deodorization of expanded material in itself.It is known that the stink of natural rubber is larger, typically make
It is that it is natural components that the reason for user can receive natural rubber products, which is, and other expanded materials are also or more
Or few all some stinks.Therefore, sport pad body provided by the present invention, can be gone to the part of stink
Remove, significantly solve and use upper undesirable bad-smell problem.And the ratio of the composite material of plant fiber
Example is higher, then the effect for removing stink is naturally expectablely can be more preferable.
To sum up, sport pad body provided by the present invention, can be used composite material of plant fiber and expanded material
After combination, it is made up of foaming and molding.In addition, the present invention is due to having used composite material of plant fiber,
Therefore there is environmentally friendly, low smelly, resource reutilization.
Certainly, the present invention can also have other various embodiments, in the feelings without departing substantially from spirit of the invention and its essence
Under condition, those of ordinary skill in the art can make various corresponding changes and deformation, but this according to the present invention
A little corresponding changes and deformation should all belong to the protection domain of the claims in the present invention.
Claims (22)
1. a kind of material compositions for manufacturing sport pad body, it is characterised in that include:
Composite material of plant fiber and content of the content between 15~60% based on overall weight
Expanded material between 40~85%;Wherein the composite material of plant fiber comprising plant fiber material,
Starch adjuvant and biopolymer additive, the biopolymer additive comprising plant hormone,
Ferment, biological vinegar and lactate;The wherein one kind of the expanded material in polyvinyl chloride and natural rubber.
2. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
The plant fiber material is selected from the group being made up of following material:Withered bar, bagasse, corncob, coconut palm
Sub- shell, cereal shell, peanut shell, leaf, the leaf of bamboo, wood chip, the combination of bamboo scraps and aforementioned substances.
3. the material compositions of manufacture sport pad body according to claim 2, it is characterised in that
The starch adjuvant is selected from the group being made up of following material:Sweet potato flour, dehydrated potato powder, corn form sediment
The combination of powder and aforementioned substances.
4. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
The starch adjuvant is selected from the group being made up of following material:Sweet potato flour, dehydrated potato powder, corn form sediment
The combination of powder and aforementioned substances.
5. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
Based on overall weight, the content of the composite material of plant fiber is 15%, and the content of the expanded material is
85%.
6. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
Based on overall weight, the content of the composite material of plant fiber is 30%, and the content of the expanded material is
70%.
7. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
Based on overall weight, the content of the composite material of plant fiber is 45%, and the content of the expanded material is
55%.
8. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
Based on overall weight, the content of the composite material of plant fiber is 60%, and the content of the expanded material is
40%.
9. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
In the composite material of plant fiber, the plant fiber material, starch adjuvant and biopolymer addition
The weight ratio of agent is 6:1:3.
10. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
In the composite material of plant fiber, the plant fiber material, starch adjuvant and biopolymer addition
Weight ratio between agent is 7:1:2.
11. the material compositions of manufacture sport pad body according to claim 1, it is characterised in that
The biopolymer additive be by weight ratio be 10:5:2:3 plant hormone, ferment, biological vinegar
And lactate is constituted.
12. a kind of manufacture method of sport pad body, it is characterised in that include the following steps:
Mix composite material of plant fiber between 15~60% of content based on overall weight and
Expanded material of the content between 40~85%, addition foaming agent carries out foaming and molding, and then shapes one
Pad;Wherein the composite material of plant fiber is poly- comprising plant fiber material, starch adjuvant and biology
Compound additive, the biopolymer additive includes plant hormone, ferment, biological vinegar and lactate;
The wherein one kind of the expanded material in polyvinyl chloride and natural rubber.
13. the manufacture method of sport pad body according to claim 12, it is characterised in that the plant
Fibres raw material is selected from the group being made up of following material:Withered bar, bagasse, corncob, cocoanut shell,
Cereal shell, peanut shell, leaf, the leaf of bamboo, wood chip, the combination of bamboo scraps and aforementioned substances.
14. the manufacture method of sport pad body according to claim 13, it is characterised in that the shallow lake
Powder class adjuvant is selected from the group being made up of following material:Sweet potato flour, dehydrated potato powder, cornstarch and
The combination of aforementioned substances.
15. the manufacture method of sport pad body according to claim 12, it is characterised in that the shallow lake
Powder class adjuvant is selected from the group being made up of following material:Sweet potato flour, dehydrated potato powder, cornstarch and
The combination of aforementioned substances.
16. the manufacture method of sport pad body according to claim 12, it is characterised in that with whole
Based on body weight, the content of the composite material of plant fiber is 15%, and the content of the expanded material is 85%.
17. the manufacture method of sport pad body according to claim 12, it is characterised in that with whole
Based on body weight, the content of the composite material of plant fiber is 30%, and the content of the expanded material is 70%.
18. the manufacture method of sport pad body according to claim 12, it is characterised in that with whole
Based on body weight, the content of the composite material of plant fiber is 45%, and the content of the expanded material is 55%.
19. the manufacture method of sport pad body according to claim 12, it is characterised in that with whole
Based on body weight, the content of the composite material of plant fiber is 60%, and the content of the expanded material is 40%.
20. the manufacture method of sport pad body according to claim 12, it is characterised in that the plant
In fibres composite, the plant fiber material, starch adjuvant and biopolymer additive
Weight ratio is 6:1:3.
21. the manufacture method of sport pad body according to claim 12, it is characterised in that the plant
In fibres composite, the plant fiber material, starch adjuvant and biopolymer additive it
Between weight ratio be 7:1:2.
22. the manufacture method of sport pad body according to claim 12, it is characterised in that the life
Thing polymeric additive be by weight ratio be 10:5:2:3 plant hormone, ferment, biological vinegar and
What lactate was constituted.