CN106956483A - Decorating film and its manufacture method with refractive power effect - Google Patents
Decorating film and its manufacture method with refractive power effect Download PDFInfo
- Publication number
- CN106956483A CN106956483A CN201710198158.8A CN201710198158A CN106956483A CN 106956483 A CN106956483 A CN 106956483A CN 201710198158 A CN201710198158 A CN 201710198158A CN 106956483 A CN106956483 A CN 106956483A
- Authority
- CN
- China
- Prior art keywords
- refractive power
- layer
- coating
- decorating film
- face mask
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention relates to a kind of decorating film and its manufacture method, especially a kind of decorating film with refractive power effect and its manufacture method belong to decoration technical field of membrane.A kind of decorating film with refractive power effect, including refractive power embossed layer, adhesive layer and bottom membrane, it is characterised in that：The refractive power embossed layer is that, using UV materials and by the concavo-convex surface layer of molding sizing, the refractive power embossed layer, adhesive layer, bottom membrane are overlapped successively, and refractive power embossed layer and bottom membrane are adhesively fixed by adhesive layer, the bottom membrane support embossed layer and adhesive layer.Production cost is low, the characteristics of technique is simple.
Description
Technical field
The present invention relates to a kind of decorating film and its manufacture method, especially a kind of decorating film with refractive power effect and
Its manufacture method, belongs to decoration technical field of membrane.
Background technology
The refractive power grain effect of current decorating film generally uses high temperature calendering process：In the case of a high temperature, film is softened, led to
Cross dandy roll and mould is gone out texture, so that there is refractive power effect, but the texture that profit is made in this way, because film has necessarily
The contraction of amount, texture is not sharp keen, while also having the following disadvantages：1st, the material of film is restricted, general heat posted machine operating temperature
160-180 DEG C, it is adaptable to which hot pressing grain material has an OPP, PVC, the material such as PVC, if material that will be higher to softening temperature is carried out
Embossing, can only the higher equipment of selection work temperature, the increase of one side energy consumption；Secondly at high operating temperatures, the shaping of product, heat
Setting requires higher, and product is not fine.2nd, part membrane material, ink, pigment are unstable at high temperature in decorating film, occur discoloration color
Poor phenomenon.3rd, the high material of transparency is much not suitable for hot pressing line.4th, when material softening press grain forming afterboarding effect is by material
Shrinkage factor influence is big, and cooling meat substantially, influences stereoeffect after the thermoforming such as similar PE, causes material not to be suitable for embossing work
Skill.5th, after the hot Cheng Wen of material, original material hardness only can be kept, so hardness is not high.Total scolds, similar this kind of materials of PET,
General hot embossing process can not be used to realize embossing, but PET has transparency height in itself, and chemical resistance is good, and cost performance is high
The features such as, it is widely used on decorating film.
For this reason, it may be necessary to design a kind of decorating film with refractive power effect and its manufacture method, with manufacturing process it is simple,
The characteristics of low cost.
The content of the invention
The purpose of the present invention, be in order to which the refractive power connection with production of structures for solving decorating film of the prior art is difficult, film
Autogenous shrinkage can weaken refractive power texture third dimension, and need high-temperature heating, therefore used material in manufacturing process
Material is limited；Higher heating-up temperature is needed if needing to use other materials, now manufacturing equipment requires higher, causes manufacturing cost
High the problem of.A kind of decorating film with refractive power effect and its manufacture method are provided, had
The press back information on molding die is transferred on UV films using UV coating, UV films surface forms male and fomale(M＆F), so as to realize
The effect of refractive power, production cost is low, the characteristics of technique is simple.
The purpose of the present invention can be reached by taking following technical scheme：
A kind of decorating film with refractive power effect, including refractive power embossed layer, adhesive layer and bottom membrane, it is structurally characterized in that：It is described
Refractive power embossed layer is using UV materials and by the concavo-convex surface layer of molding sizing, the refractive power embossed layer, adhesive layer, counterdie
Layer is overlapped successively, and refractive power embossed layer and bottom membrane are adhesively fixed by adhesive layer, the bottom membrane support refractive power embossed layer and gluing
Layer.
The purpose of the present invention can also be reached by taking following technical scheme：
Further, also including light barrier layer, the light barrier layer is brought into close contact below refractive power embossed layer, light barrier
Layer is metal ink coating or plating chromatograph.
Further, also including face mask layer, the face mask layer is PET material, and face mask layer is brought into close contact in refractive power embossed layer
On.
Further, also there is printing layer, the printing layer is printing-ink between the face mask layer and refractive power embossed layer
Coating, printing layer is coated on face mask layer.
Further, also it is brought into close contact the second refractive power embossed layer above the face mask layer.
Further, the UV materials that the refractive power embossed layer is used are main by polymerizing prepolymer, photo-sensitive monomer, light
Initiator, auxiliary agent, polymerization inhibitor composition.
As a kind of preferred embodiment, the UV materials that the refractive power embossed layer is used are main by pure acrylate, amine modification
Acrylate, urethane acrylate, adhesion promoter, combination of stabilizers, photoinitiator system, adjuvant system, cured, gas phase
Silica is constituted.
Further, the UV materials are by pure acrylate 45%, amine modification acrylate 5%, urethane acrylate
20%th, adhesion promoter 20%, combination of stabilizers 1%, photoinitiator system 5%, adjuvant system 1%, cured 1%, gas phase two
Silica 2% is constituted.
A kind of manufacture method of the decorating film with refractive power effect, its method characteristic is：
Step 1) UV coating is molded using molding die, the male and fomale(M＆F) of the molding die designed is stamped in UV coating
On, then the UV coating progress setting solidification on molding die, ultimately form refractive power embossed layer；
Step 2) refractive power embossed layer is bonding with bottom membrane by adhesive layer, form decorating film.
Further, also including step 3) in refractive power embossing layer surface laminating, face mask layer is set.
Further, also including step 4) the second refractive power embossed layer of laminating setting on face mask layer.
Further, be additionally included in step 3) before add step a) added between face mask layer and refractive power embossed layer by printing
The printing layer that ink is made, printing layer is coated on face mask layer bottom.
Further, it is additionally included in step 1) step b) is added afterwards adds and be coated with by metal ink below refractive power embossed layer
Light barrier layer.
Preferably, the step 1) application UV method can with spraying or curtain coating or rolling method or comma rubbing method
Or nick rubbing method or slot coated method, wherein coating weight 10-100g/m2。
Preferably, the step 1) molding die can be dandy roll or photoetching roller or moulding film or Erodent Algorithm.
The present invention has beneficial effect prominent as follows：
By coating UV coating on molding die, the male and fomale(M＆F) information on molding die is set to go to UV layers by impressing mode
On, after setting process, form refractive power embossed layer.Refractive power embossed layer fits into decorating film with bottom membrane by adhesive layer, decoration
The stereoscopic visual effect that film is observed due to the male and fomale(M＆F) formation user of refractive power embossed layer.Light barrier layer applies for metal ink
Layer or plating chromatograph, refractive power embossed layer complexed metal ink or electroplating tinting, can represent sharp keen metal refractive power effect.The UV
Material is main by pure acrylate 45%, amine modification acrylate 5%, urethane acrylate 20%, adhesion promoter
20%th, combination of stabilizers 1%, photoinitiator system 5%, adjuvant system 1%, cured 1%, aerosil 2% are constituted.Pass through
Its solidifying and setting effect of the UV materials of component formation is good, compliance is high, adhesive force good, heat endurance is strong, polymerization is notable,
Solidification effect is good, easy to manufacture.UV materials do not have adhesive force to molding die, and have good adhesion to stock, work as flowing
The coating mould that is molded is squeezed into after line, is solidified by UV, and the texture pressed is shaped to form refractive power embossed layer, technique letter completely
It is single.
Brief description of the drawings：
Fig. 1 is the layer structure figure of specific embodiment 1 in the present invention；
Fig. 2 is the refractive power embossed layer schematic diagram of specific embodiment 1 or 2 in the present invention；
Embodiment：
Specific embodiment 1
The present invention is specifically described with reference to the present embodiment and accompanying drawing 1 to 2：
In the present embodiment, including refractive power embossed layer 1.4, adhesive layer 1.6 and bottom membrane 1.7, it is characterised in that：The refractive power embossing
Layer 1.4 be using UV materials and by molding sizing concavo-convex surface layer, the refractive power embossed layer 1.4, adhesive layer (1.6),
Bottom membrane 1.7 is overlapped successively, and refractive power embossed layer 1.4 and bottom membrane 1.7 are adhesively fixed by adhesive layer 1.6, and the bottom membrane 1.7 is held
Hold in the palm refractive power embossed layer and 1.4 adhesion coatings 1.6.
In the present embodiment, also including light barrier layer 1.5, the light barrier layer 1.5 is brought into close contact in refractive power embossed layer
1.4 lower sections, light barrier layer 1.5 is plating chromatograph.
In the present embodiment, also including face mask layer 1.2, the face mask layer 1.2 be PET material, face mask layer 1.2 be brought into close contact in
In refractive power embossed layer 1.4.
In the present embodiment, also there is printing layer 1.3, the printing layer between the face mask layer 1.2 and refractive power embossed layer 1.4
1.3 be the coating of printing-ink, and printing layer 1.3 is coated on face mask layer 1.2.
In the present embodiment, the top of face mask layer 1.2 is also brought into close contact the second refractive power embossed layer 1.1.
In the present embodiment, the UV materials are by pure acrylate 45%, amine modification acrylate 5%, polyurethane acroleic acid
Ester 20%, adhesion promoter 20%, combination of stabilizers 1%, photoinitiator system 5%, adjuvant system 1%, cured 1%, gas phase
Silica 2% is constituted.
The present embodiment principle：
UV materials in the present embodiment-as shown in Table 1
| Resinous type | Name of product | Typical amounts | Characteristic |
| Pure acrylate | Eb745 | 45% | Adhesive force |
| Amine modification acrylate | Eb7100 | 5% | Reactivity-surface cure |
| Urethane acrylate | Eb264 | 20% | Compliance |
| Adhesion promoter | Eb303 | 20% | Adhesive force |
| Combination of stabilizers | 1% | Stability | |
| Photoinitiator system | Cocktail | 5% | Trigger polymerization |
| Adjuvant system | 1% | Froth breaking-levelling | |
| It is cured | 1% | Scratch resistance | |
| Aerosil (Aerosil 380) | 2% | Thixotropy is provided |
Table one
According to the intrinsic property of material, its composition possesses the physics and chemical property of material included in it.UV materials refer to
By the polymerizing prepolymers such as polyurethane acroleic acid, photo-sensitive monomer, light trigger, auxiliary agent, the UV dope layers of polymerization inhibitor composition.Its
In, it is due to that selected component makes UV materials not have adhesive force to molding die integrally that molding die, which is stamped on UV materials, and right
Stock is that counterdie or face mask layer have good adhesion, when flow coating be molded mould be squeezed into line after, it is solid by UV
Chemical industry skill, the texture pressed is shaped completely, and information line is transferred.
Following table two, is that reference picture 1 is had a guide look of to the component of layers of material
| Composition | Composition | Thickness | Effect |
| 1.1 second refractive power embossed layers | UV resins | 1-10 microns | UV layers in light refractive structures layer |
| 1.2 face mask layers | PET film | 12-280 microns | Bearing bed in light refractive structures layer |
| 1.3 printing layers | Printing-ink | 1-5 microns | PET printing-inks |
| 1.4 refractive power embossed layers | UV resins | 1-20 microns | UV layers in light refractive structures layer |
| 1.5 light barrier layers | Aluminium, metal ink | Aluminize<1 micron or 5 microns of metal ink | Metal effect, bridging effect |
| 1.6 adhesive layers | Polyurethane adhesive | 3-50 microns | DIC adhesive, 10 microns of coating |
| 1.7 bottom membranes | PVC, macromolecule, color film | 30-200 microns | Counterdie masking, laminating |
Table two
Reference picture 2, refractive power effect is due to that UV materials are squeezed cured rear formation Z-Correct bump mapping Z-correct, and observer sees under different angles
To effect caused by vision difference, the technique can be as needed, produces minute surface, radium-shine, opal, the Water Cube, geometry line, song
The abundant lines such as line prism, cylindrical grating, lenticule, manufacture is flexible, wide using scope.
In the present embodiment, refractive power embossed layer and the second refractive power embossed layer are all light refractive structures layers, and it can be used simultaneously, phase
Mutually overlapping is used may also differentiate between and used.
Face mask layer main component is PET material, and it is printed as the important carrier of decorating film, ink formation printing layer
To the surface of face mask layer, to carry out step process.
Light barrier layer, metal effect and bridging effect are realized by vacuum electric coating or type metal ink layer, by
Line can be filled out by other transparent layers in refractive power embossed layer and the second refractive power embossed layer, so when one layer of light barrier layer of loading is in folding
Below optical pressure lamina, fully reflection light mirror-like silver effect can be even realized, strengthen third dimension.
As shown in table three, table four：
Table three
Wherein, ink with mirror effect formula:
| Composition | Classification | Content |
| 9117 resins | PU resins | 12% |
| N-propyl | Solvent | 78% |
| SX710 silver pastes | Silver paste | 10% |
Table four
Adhesive layer, adhesive layer is, using coating, combination process, to be combined with each other whole decorative layer thereon and deielectric-coating.
Bottom membrane plays the functions such as covering and heat pressure adhesive, and this structure sheaf can use ink, PVC, macromolecule etc.
Material specific embodiment 2
In the present embodiment, a kind of manufacture method of the decorating film with refractive power effect, it is characterised in that：
Step 1) UV coating is molded using molding die, the male and fomale(M＆F) of the molding die designed is stamped in UV coating
On, then the UV coating progress setting solidification on molding die, refractive power embossed layer 1.4 is ultimately formed, the setting of UV coating is logical
Cross and give UV light sources or electron beam realizes UV coating to shape and reach solidification；
Step 2) refractive power embossed layer 1.4 is bonding by adhesive layer 1.6 and bottom membrane 1.7, form decorating film.
In the present embodiment, also including step 3) on the surface of refractive power embossed layer 1.4, laminating sets face mask layer 1.2.
In the present embodiment, also including step 4) the second refractive power embossed layer 1.1 of laminating setting on face mask layer 1.2.
In the present embodiment, be additionally included in step 3) before add step a) added between face mask layer and refractive power embossed layer by printing
The printing layer 1.3 that brush ink is made, printing layer 1.3 is coated on the bottom of face mask layer 1.2.
In the present embodiment, be additionally included in step 1) afterwards add step b) added below refractive power embossed layer 1.4 by metal oil
The light barrier layer 1.5 of ink coating.
In the present embodiment, the step 1) application UV method can apply with spraying or curtain coating or rolling method or comma
Cloth method or nick rubbing method or slot coated method, wherein coating weight 10-100g/m2。
In the present embodiment, the step 1) setting of UV coating is to realize UV coating by giving UV light sources or electron beam
Shape and reach solidification, wherein UV light sources use pumping lamp source UV light sources and/or LED UV light sources and/or electron beam, and UV light sources refer to
Wavelength 210-420nm scopes light source, LED UV light sources use 365nm and/or 385nm and/or 395nm and/or 405nm tetra-
The light source of individual wavelength；After UV coating contacts UV light sources, crosslinking curing, solid is become by the liquid flowed originally immediately, and it is fixed to reach
Shape purpose, while also reaching solidification purpose.
In the present embodiment, the step 1) molding die can be dandy roll or photoetching roller or moulding film or corrosion mode
Plate.
The present embodiment principle：
By coating UV coating on molding die, the male and fomale(M＆F) information on molding die is set to go to UV layers by impressing mode
On, after setting process, form refractive power embossed layer.
Face mask layer, as the important carrier of decorating film, ink is printed to its surface, to carry out step process.
Face mask layer main component is PET, and coating PET techniques divide the processes, the printing of PET film such as sided corona treatment, immersion coating processing
More than 48 dynes of processing degree are typically wanted in face, just ensure ink adhesion, general to use sided corona treatment method.And immersion coating technique
It is also beneficial to ink attachment.It is low pole material additionally, due to PET, UV resin's crosslinkages are high, and wetability is poor, immersion coating processing
PET, the adhesive force of UV resins will be greatly improved.Preferably pet layer selects sided corona treatment, immersion coating processing or both simultaneously
The polyester film used.
Printing layer is directly printed on a pet film using printing-ink, and other method, example can also be used in the prior art
Such as formed and PET film is bonded in after ink layer, to represent abundant pattern, printing layer is typically completed by multiple chromatograph double exposures, color oil
Ink includes color ink and metal color ink, and the typography of printing layer has gravure, anilox printing, cylinder printing, flexographic printing etc., schemes
By color separation, engraving roller is made, then ink is transferred on PET film by roller ink cell in case.
Light barrier layer, metal effect and bridging effect are realized by vacuum plating or type metal ink, refractive power line by
In that can fill out line by other transparent materials, so one layer of light-shielding barrier material must be loaded, vacuum plating is that aluminium atom is plated
Onto material, mirror-like silver effect is realized.It can in advance be printed before plating and wash aluminium lamination, can be by washing aluminium work after the completion of plating
Skill washes away the reverted image of pattern, finally realizes parcel plating effect.Gravure, reticulate pattern roll marks can be used by washing aluminium pre-treatment printing layer
The techniques such as brush, cylinder printing realize printing.
Light barrier layer can also be used metal ink to realize, the printing of ink can be printed by gravure, anilox roll coating, cylinder
Brush etc. realizes that, to produce fine definition refractive power effect, metal ink preferably can use ink with mirror effect to express, and its performance is special
Point is to reduce because resin thickness fills and leads up refractive power texture, such as table 3, and wherein grey parts are refractive power texture layer, and black portions are gold
Belong to layer.
Adhesive used in adhesive layer is general is PU class adhesive, is cured by 12 hours, be up to highest peel off, with
Water-fast function.Solvent-based adhesive, solventless adhesive, aqueous adhesive etc., the work of coating binder can be used in adhesive
Skill includes net roller coat cloth, scraper for coating, multiple roll coating, extrusion coated etc..
The present embodiment holds printed book hair due to multiple technique chromatographs being completed on the intensive printing production line to specialty
It is bright typically to take effective air cleaning technique, it is more favourable to environmental protection.
The products application of the present patent application adds in transfer film, transfer film, aluminium-plastic panel, metal in ornament materials, aluminum, film
Work, door and window shaping.
More than, it is only the present invention preferably specific embodiment, but protection scope of the present invention is not limited thereto, and it is any ripe
Those skilled in the art are known in the technique according to the invention scheme the invention discloses in the range of and its design to be subject to
With replacing or changing, protection scope of the present invention is belonged to.
Claims (9)
1. a kind of decorating film with refractive power effect, including refractive power embossed layer (1.4), adhesive layer (1.6) and bottom membrane (1.7),
It is characterized in that：The refractive power embossed layer (1.4) is using UV materials and by the concavo-convex surface layer of molding sizing, the folding
Optical pressure lamina (1.4), adhesive layer (1.6), bottom membrane (1.7) are overlapped successively, adhesive layer (1.6) by refractive power embossed layer (1.4) and
Bottom membrane (1.7) is adhesively fixed, bottom membrane (1.7) the support refractive power embossed layer and (1.4) adhesion coating (1.6).
2. the decorating film according to claim 1 with refractive power effect, it is characterised in that：Also include light barrier layer
(1.5), the light barrier layer (1.5) is brought into close contact below refractive power embossed layer (1.4), and light barrier layer (1.5) is metal
Ink coating or plating chromatograph.
3. the decorating film according to claim 1 with refractive power effect, it is characterised in that：Also include face mask layer (1.2), institute
Face mask layer (1.2) is stated for PET material, face mask layer (1.2) is brought into close contact in refractive power embossed layer (1.4).
4. the decorating film according to claim 3 with refractive power effect, it is characterised in that：The face mask layer (1.2) and folding
Also there is printing layer (1.3), the printing layer (1.3) is the coating of printing-ink, printing layer between optical pressure lamina (1.4)
(1.3) it is coated on face mask layer (1.2).
5. the decorating film according to claim 3 with refractive power effect, it is characterised in that：Above the face mask layer (1.2)
Also it is brought into close contact the second refractive power embossed layer (1.1).
6. the decorating film according to claim 1 with refractive power effect, it is characterised in that：The refractive power embossed layer (1.4)
The UV materials used are mainly made up of polymerizing prepolymer, photo-sensitive monomer, light trigger, auxiliary agent, polymerization inhibitor.
7. the decorating film according to claim 1 with refractive power effect, it is characterised in that：The refractive power embossed layer (1.4)
The UV materials that are used it is main by pure acrylate, it is amine modification acrylate, urethane acrylate, adhesion promoter, steady
Determine agent combination, photoinitiator system, adjuvant system, cured, aerosil composition.
8. the decorating film according to claim 7 with refractive power effect, it is characterised in that：The UV materials are by pure acrylic acid
Ester 45%, amine modification acrylate 5%, urethane acrylate 20%, adhesion promoter 20%, combination of stabilizers 1%, light
Initiator system 5%, adjuvant system 1%, cured 1%, aerosil 2% are constituted.
9. a kind of manufacture method of the decorating film with refractive power effect, it is characterised in that：
Step 1) UV coating is molded using molding die, the male and fomale(M＆F) of the molding die designed is stamped in UV coating
On, then the UV coating progress setting solidification on molding die, ultimately form refractive power embossed layer (1.4)；
Step 2) refractive power embossed layer (1.4) is bonding by adhesive layer 1.6 and bottom membrane (1.7), form decorating film；
Step 3) on refractive power embossed layer (1.4) surface, laminating sets face mask layer (1.2)；
Step 4) the second refractive power embossed layer (1.1) of laminating setting on face mask layer (1.2)；
In step 3) before add step a) printing layer being made up of printing-ink is added between face mask layer and refractive power embossed layer
(1.3), printing layer (1.3) is coated on face mask layer (1.2) bottom；
In step 1) step b) the light barrier layers that addition is coated with by metal ink below refractive power embossed layer (1.4) are added afterwards
(1.5)；
The step 1) application UV method can be coated with spraying or curtain coating or rolling method or comma rubbing method or nick
Method or slot coated method, wherein coating weight 10-100g/m2；
The step 1) molding die can be dandy roll or photoetching roller or moulding film or Erodent Algorithm；
The step 1) UV coating setting be by giving UV light sources or electron beam realizes UV coating to shape and reach solidification,
Wherein UV light sources use pumping lamp source UV light sources and/or LED UV light sources and/or electron beam, and UV light sources refer to wavelength in 210-420nm
The light source of scope, LED UV light sources use the light source of tetra- wavelength of 365nm and/or 385nm and/or 395nm and/or 405nm；UV
After coating contacts UV light sources, crosslinking curing, solid is become by the liquid flowed originally immediately, reaches setting purpose, while also reaching
To solidification purpose.