CN106947993A - A kind of noninductive light anodic process - Google Patents
A kind of noninductive light anodic process Download PDFInfo
- Publication number
- CN106947993A CN106947993A CN201710189569.0A CN201710189569A CN106947993A CN 106947993 A CN106947993 A CN 106947993A CN 201710189569 A CN201710189569 A CN 201710189569A CN 106947993 A CN106947993 A CN 106947993A
- Authority
- CN
- China
- Prior art keywords
- washing
- ink
- oxidation
- move back
- oiling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of noninductive light anodic process, including raw material polishing, once oxidation, printing-ink covers, move back oxide scale film, sandblasting, secondary oxidation, de-oiling ink and finished product inspection, anode material is carried out raw material polishing by the noninductive light anodic process, the subsequent downstream step of the raw material polishing is once oxidation, the subsequent downstream step of the once oxidation is covered for printing-ink, the subsequent downstream step of the printing-ink masking is to move back oxide-film, the subsequent downstream step for moving back oxide-film is sandblasting, the subsequent downstream step of the sandblasting is secondary oxidation, the subsequent downstream step of the secondary oxidation is de-oiling ink, the subsequent downstream step of the de-oiling ink is finished product inspection, this is noninductive, and light anodic process is polished using raw material, once oxidation, printing-ink covers, move back oxide scale film, sandblasting, secondary oxidation, de-oiling ink and finished product inspection step cooperative cooperating, obtain the good corrosion resistant high light of the good property of pleochroism and the aluminium alloy of no concave-convex sense.
Description
Technical field
The present invention relates to field of metal surface treatment technology, and in particular to a kind of noninductive light anodic process.
Background technology
Aluminium and its alloy have intensity high, heat conduction and conduct electricity very well, color and luster is attractive in appearance, nonmagnetic, decay resistance and
Plasticity and processability is good, advantage without black brittleness, is a kind of nonferrous materials with premium properties, current aluminium and its
Alloy is widely used in Aero-Space, building, automobile, mechanical performance and civilian art metal part;But some performances of aluminium are also not
It is too preferable, such as surface property of hardness, wearability and corrosion resistance;To overcome the shortcoming of aluminum alloy surface aspect of performance, it is also
It is the most frequently used salvo to improve the anodic oxidation in protective, ornamental and feature, the sufacing of aluminium.
The anodic oxidation of aluminium and aluminium alloy is that aluminium and aluminium alloy are placed in the process handled in electrolyte as anode,
After anodic oxidation, aluminium surface can generate the oxide-film that thickness is several microns and hundreds of microns, and its surface is entered so as to reach
The effect of row protection, general traditional anode oxidation coloration can only obtain single coloring effect, and in order that outer after anodic oxidation
Sight surface is good-looking, and at present, the expression way of aluminum alloy surface LOGO patterns includes the side of laser carving, punching press, printing or OEM
Formula represents, but laser carving mode has Shamian Island on LOGO patterns, and color and luster is dim, and two kinds of only dull colors;Punching press
Mode can have raised or recessed on the surface, and appearance color is single, unsightly;Printing has the marking of ink and easily comes off
Color, reduction shelf life of products, OEM mode rat, outward appearance is more simple and easily comes off, reduction product quality and class.
Existing anodizing technology is general to do anodic oxidation to realize to aluminium table using 5 series and 6 series alloys
The protection in face, but have the following disadvantages:
1st, 5 be with 6 line aluminium alloy compositions due to, 5 be relatively low with the 6 line aluminium alloy strengths of materials, in structure design by
To many limitations;
2nd, the high strength alumin ium alloy intensity of 7 series is high, still, in the prior art, and the high strength alumin ium alloy of 7 series is typically using electrophoresis etc.
Others surface treatment, such as carries out anodic oxidation, its surface easily generates material line, outer light performance to the high strength alumin ium alloy of 7 series
Power is not strong.
Therefore, a kind of new technology for aluminum alloy surface anodic oxidation is needed badly, carrying out quasi-complement, product is not in the market
Foot.
The content of the invention
In view of this, in view of the existing deficiencies of the prior art, its main purpose is to provide that a kind of color is various, hold to the present invention
Long property is good, good corrosion resistance, high light, the noninductive bright anodizing technique of aluminium alloy of no concave-convex sense.
To achieve the above object, the present invention is using following technical scheme:A kind of noninductive light anode oxidation process, including
Following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 5 ~ 20 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjust ink -- frame web plate -- debugging position -- 25 ~ 60 minutes temperature 60 of printing-ink -- inspections -- baking ~
100°;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:3 ~ 5, oxidization time is moved back for 20 ~ 30 seconds;
5)Sandblasting:Put tool -- adjusting sand-blasting gun -- sandblasting;The sand-blasting gun spray angle is 45 ~ 60 °, and pressure is 1.5 ~ 4KG, spray
The distance of sand rifle and product is 10 ~ 30cm, 80 ~ 150# of model steel sands or glass sand;
6)Secondary oxidation:Degreasing bath cleans -- washing -- 5 ~ 30S of alkali cleaning, 90 ~ 110 ° of temperature, and -- washing --- neutralizes -- washing -- acid
Washing 5 ~ 30S, 90 ~ 110 ° of temperature, -- washing -- neutralizes and -- washes and -- aoxidize 5 ~ 20 minutes and -- wash -- washing -- and dye 1 ~ 40 point
-- -- --- sealing of hole -- washing -- is toasted clock for washing for washing;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;
8)Check.
The step 3)The ink includes:
Acrylic resin: 17-27%;
Urethane: 18-24%;
Isopropyl acetone: 13-19%;
Cyclohexanone: 10-18%;
Acids solvent: 5-11% ;
Ethyl benzene solvent: 13-18%.
The step 7)The black agent of de-oiling used includes phosphoric acid, nitric acid, citric acid, nitric acid hydrogen sodium, water, and its proportioning is
Phosphoric acid:Nitric acid:Citric acid:Nitric acid hydrogen sodium:Water=13:32:9:7:30~60.
The acids solvent is acetate solvate.
The present invention has clear advantage and beneficial effect compared with prior art:Through repetition test, this programme technology is adopted
With corresponding printing-ink and under the process conditions of this project, aluminum alloy surface strong bonded that can be with oxidized mistake,
Can not occur any physical reactions with the follow-up oxide scale film solution that moves back simultaneously, and be removed by the de- printing ink solvent of correspondence configuration
Printing-ink, and the oxide-film in secondary oxidation is not influenceed, so that noninductive light pattern is made.
Meanwhile, the technological parameter obtained by blasting craft is after repetition test in technical solution of the present invention can be carried effectively
The effect of high product secondary oxidation, while influence of the reduction to masking ink layer, obtains the noninductive pattern of surface-brightening.
Embodiment
Embodiment 1
A kind of noninductive light anode oxidation process, comprises the following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 20 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjusting ink, -- -- -- printing-ink -- inspection -- toasts 25 minutes 100 ° of temperature to frame web plate for debugging position;
The ink includes:Acrylic resin 17%, urethane 18%, isopropyl acetone 19%, cyclohexanone 18%, acetate solvate 10%, ethyl benzene solvent
18%;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:3, oxidization time is moved back for 20 seconds;
5)Sandblasting:Put tool -- adjusting sand-blasting gun -- sandblasting;The sand-blasting gun spray angle is 60 °, and pressure is 1.5KG, sand-blasting gun
Distance with product is 10cm, 80 ~ 150# of model steel sands or glass sand;
6)Secondary oxidation:Degreasing bath cleans -- washing -- alkali cleaning(5S, 110 ° of temperature)-- washing --- neutralizes -- washing -- pickling
-- washing -- neutralizes -- washing -- -- washing -- washing -- 40 minutes -- washing -- water of dyeing of oxidation 20 minutes by 5S, 110 ° of temperature
Wash --- sealing of hole -- washing -- baking;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;Its de-oiling used ink agent include phosphoric acid, nitric acid, citric acid,
Nitric acid hydrogen sodium, water, it is phosphoric acid that it, which is matched,:Nitric acid:Citric acid:Nitric acid hydrogen sodium:Water=13:32:9:7:30;
8)Check.
Embodiment 2
A kind of noninductive light anode oxidation process, comprises the following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 5 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjusting ink, -- -- -- printing-ink -- inspection -- toasts 60 minutes 60 ° of temperature to frame web plate for debugging position;Should
Ink includes:Acrylic resin 27%, urethane 24%, isopropyl acetone 13%, cyclohexanone 18%, acetate solvate 5%, ethyl benzene solvent 13%;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:5, oxidization time is moved back for 30 seconds;
5)Sandblasting:Put tool -- adjusting sand-blasting gun -- sandblasting;The sand-blasting gun spray angle is 50 °, and pressure is 3KG, sand-blasting gun with
The distance of product is 20cm, 80 ~ 150# of model steel sands or glass sand;
6)Secondary oxidation:Degreasing bath cleaning -- washing -- alkali cleaning 30S, 90 ° of temperature -- washing --- -- washing -- pickling 30S is neutralized,
-- washing -- neutralizes -- washing -- -- washing -- washing -- -- washing -- washing --- envelope of dyeing 1 minute of oxidation 5 minutes to 90 ° of temperature
Toast in hole -- washing --;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;The black agent of the de-oiling that is used include phosphoric acid, nitric acid, citric acid,
Nitric acid hydrogen sodium, water, it is phosphoric acid that it, which is matched,:Nitric acid:Citric acid:Nitric acid hydrogen sodium:Water=13:32:9:7: 60;
8)Check.
Embodiment 3
A kind of noninductive light anode oxidation process, comprises the following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 10 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjusting ink, -- -- -- printing-ink -- inspection -- toasts 30 minutes 70 ° of temperature to frame web plate for debugging position;Should
Ink includes:Acrylic resin 19%, urethane 20%, isopropyl acetone 16%, cyclohexanone 15%, acetate solvate 12%, ethyl benzene solvent
18%;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:4, oxidization time is moved back for 25 seconds;
5)Sandblasting:Put tool -- adjusting sand-blasting gun -- sandblasting;The sand-blasting gun spray angle is 60 °, and pressure is 4KG, sand-blasting gun with
The distance of product is 30cm, 80 ~ 150# of model steel sands or glass sand;
6)Secondary oxidation:Degreasing bath cleans -- washing -- alkali cleaning 10S, 100 ° of temperature, and -- washing --- neutralizes -- washing -- pickling
-- washing -- neutralizes -- washing -- -- washing -- washing -- 20 minutes -- washing -- water of dyeing of oxidation 10 minutes by 10S, 110 ° of temperature
Wash --- sealing of hole -- washing -- baking;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;The black agent of the de-oiling that is used include phosphoric acid, nitric acid, citric acid,
Nitric acid hydrogen sodium, water, it is phosphoric acid that it, which is matched,:Nitric acid:Citric acid:Nitric acid hydrogen sodium:Water=13:32:9:7:40;
8)Check.
Embodiment 4
A kind of noninductive light anode oxidation process, comprises the following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 14 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjusting ink, -- -- -- printing-ink -- inspection -- toasts 25 ~ 60 minutes temperature to frame web plate for debugging position
90°;The ink includes:Acrylic resin 23%, urethane 22%, isopropyl acetone 15%, cyclohexanone 15%, acetate solvate 9%, ethylbenzene are molten
Agent 16%;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:3.5, oxidization time is moved back for 25 seconds;
5)Sandblasting:Put tool -- adjusting sand-blasting gun -- sandblasting;The sand-blasting gun spray angle is 55 °, and pressure is 2KG, sand-blasting gun with
The distance of product is 25cm, 80 ~ 150# of model steel sands or glass sand;
6)Secondary oxidation:Degreasing bath cleans -- washing -- alkali cleaning 20S, 110 ° of temperature, and -- washing --- neutralizes -- washing -- pickling
-- washing -- neutralizes -- washing -- -- washing -- washing -- 31 minutes -- washing -- water of dyeing of oxidation 12 minutes by 20S, 110 ° of temperature
Wash --- sealing of hole -- washing -- baking;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;The black agent of the de-oiling that is used include phosphoric acid, nitric acid, citric acid,
Nitric acid hydrogen sodium, water, it is phosphoric acid that it, which is matched,:Nitric acid:Citric acid:Nitric acid hydrogen sodium:Water=13:32:9:7:30~60;
8)Check.
Embodiment 5
A kind of noninductive light anode oxidation process, comprises the following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 10 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjusting ink, -- -- -- printing-ink -- inspection -- toasts 25 ~ 60 minutes temperature to frame web plate for debugging position
60°;The ink includes:Acrylic resin 18%, urethane 24%, isopropyl acetone 19%, cyclohexanone 10%, acetate solvate 11%, ethylbenzene
Solvent 18%;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:5, oxidization time is moved back for 20 seconds;
5)Sandblasting:Put tool -- adjusting sand-blasting gun -- sandblasting;The sand-blasting gun spray angle is 45 °, and pressure is 2.5KG, sand-blasting gun
Distance with product is 20cm, 80 ~ 150# of model steel sands or glass sand;
6)Secondary oxidation:Degreasing bath cleaning -- washing -- alkali cleaning 10S, 98 ° of temperature -- washing --- -- washing -- pickling 10S is neutralized,
-- washing -- neutralizes -- washing -- -- washing -- the washing -- -- washing -- washing --- of dyeing 30 minutes of oxidation 18 minutes to 98 ° of temperature
Sealing of hole -- washing -- is toasted;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;The black agent of the de-oiling that is used include phosphoric acid, nitric acid, citric acid,
Nitric acid hydrogen sodium, water, it is phosphoric acid that it, which is matched,:Nitric acid:Citric acid:Nitric acid hydrogen sodium:Water=13:32:9:7:45;
8)Check.
Embodiment 6
A kind of noninductive light anode oxidation process, comprises the following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 15 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjusting ink, -- -- -- printing-ink -- inspection -- toasts 25 ~ 60 minutes temperature to frame web plate for debugging position
75°;The ink includes:Acrylic resin 25%, urethane 19%, isopropyl acetone 19%, cyclohexanone 18%, acetate solvate 6%, ethylbenzene are molten
Agent 13%;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:3, oxidization time is moved back for 30 seconds;
5)Sandblasting:Put tool -- adjusting sand-blasting gun -- sandblasting;The sand-blasting gun spray angle is 60 °, and pressure is 2.5KG, sand-blasting gun
Distance with product is 20cm, 80 ~ 150# of model steel sands or glass sand;
6)Secondary oxidation:Degreasing bath cleans -- washing -- alkali cleaning 25S, 110 ° of temperature, and -- washing --- neutralizes -- washing -- pickling
-- washing -- neutralizes -- washing -- -- washing -- washing -- 32 minutes -- washing -- water of dyeing of oxidation 15 minutes by 25S, 110 ° of temperature
Wash --- sealing of hole -- washing -- baking;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;The black agent of the de-oiling that is used include phosphoric acid, nitric acid, citric acid,
Nitric acid hydrogen sodium, water, it is phosphoric acid that it, which is matched,:Nitric acid:Citric acid:Nitric acid hydrogen sodium:Water=13:32:9:7:45;
8)Check.
Use properties of product test made from technique as follows through the present embodiment 1 ~ 6:
The above, is only presently preferred embodiments of the present invention, and not the technical scope of the present invention is imposed any restrictions, therefore all
It is, to any trickle amendment made for any of the above embodiments, equivalent variations and modification, to still fall within according to technical spirit of the invention
In the range of technical solution of the present invention.
Claims (4)
1. a kind of noninductive light anode oxidation process, it is characterised in that:Comprise the following steps:
1)Raw material aluminium sheet is polished:Scar, sisal polishing, cotton dolly is gone to receive light using 180# ~ 400# emery cloths silk;
2)Once oxidation:Aluminium sheet after polishing is aoxidized 5 ~ 20 points in degreasing bath in washing-oxidation trough in cleaning-rinsing bowl
--- sealing of hole in sealing of hole groove -- is washed in clock-rinse bath to dry in washing-baking box in rinse bath;
3)Ink covers:Adjust ink -- frame web plate -- debugging position -- 25 ~ 60 minutes temperature 60 of printing-ink -- inspections -- baking ~
100°;
4)Move back oxidation:Move back oxide scale film --- washing --- baking;It is described move back oxide scale film with move back oxidation solution include NaOH,
Sodium nitrate and water, its mol ratio are NaOH:Sodium nitrate:Water=0.01:1:3 ~ 5, oxidization time is moved back for 20 ~ 30 seconds;
6)Secondary oxidation:Degreasing bath cleans -- washing -- 5 ~ 30S of alkali cleaning, 90 ~ 110 ° of temperature, and -- washing --- neutralizes -- washing -- acid
Washing 5 ~ 30S, 90 ~ 110 ° of temperature, -- washing -- neutralizes and -- washes and -- aoxidize 5 ~ 20 minutes and -- wash -- washing -- and dye 1 ~ 40 point
-- -- --- sealing of hole -- washing -- is toasted clock for washing for washing;
7)De-oiling ink:-- washing -- drying -- is checked de-oiling ink;
8)Check.
2. a kind of noninductive light anode oxidation process according to claim 1, it is characterised in that:The step 3)The ink
Include:
Acrylic resin: 17-27%;
Urethane: 18-24%;
Isopropyl acetone: 13-19%;
Cyclohexanone: 10-18%;
Acids solvent: 5-11% ;
Ethyl benzene solvent: 13-18%.
3. a kind of noninductive light anode oxidation process according to claim 1, it is characterised in that:The step 7)Used
De-oiling ink agent includes phosphoric acid, nitric acid, citric acid, nitric acid hydrogen sodium, water, and it is phosphoric acid that it, which is matched,:Nitric acid:Citric acid:Nitric acid hydrogen sodium:
Water=13:32:9:7:30~60.
4. a kind of noninductive light anode oxidation process according to claim 2, it is characterised in that:The acids solvent is acetic acid
Solvent.