CN106946505A - A kind of construction wall refractory material and preparation method thereof - Google Patents
A kind of construction wall refractory material and preparation method thereof Download PDFInfo
- Publication number
- CN106946505A CN106946505A CN201710072840.2A CN201710072840A CN106946505A CN 106946505 A CN106946505 A CN 106946505A CN 201710072840 A CN201710072840 A CN 201710072840A CN 106946505 A CN106946505 A CN 106946505A
- Authority
- CN
- China
- Prior art keywords
- parts
- construction wall
- cellulose ether
- hydrophober
- wall refractory
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of construction wall refractory material and preparation method thereof, by weight, it is prepared from the following components：6 10 parts of cement, 36 parts of quick lime, 14 parts of silica white, 38 parts of coal ash powder, 26 parts of cellulose ether, 14 parts of hydrophober, 15 parts of chopped strand, 18 35 parts of water, preparation method is：According to above-mentioned parts by weight, cement, quick lime, silica white, coal ash powder are added in mixer, stirring mixing 68 minutes, obtain compound, then cellulose ether, hydrophober, chopped strand are added into compound, stir after 48 minutes, add water, be stirred for after 15 35 minutes can be used.The present invention has the advantages that good toughness, excellent fire retarding performance.
Description
Technical field
The present invention relates to building thermal insulation material field, specifically a kind of construction wall refractory material and its preparation side
Method.
Background technology
Construction material can be divided into structural material, ornament materials and some proprietary materials, structural material include timber, bamboo wood,
Stone material, cement, concrete, metal, brick and tile, ceramics, glass, engineering plastics, composite etc., ornament materials include various apply
Material, paint, coating, veneer, assorted ceramic tile, glass with special-effect etc.；Proprietary material refer to for waterproof, protection against the tide, anti-corrosion,
Fire prevention, fire-retardant, sound insulation, heat-insulated, insulation, sealing etc..
With the continuous progressive and development of society, the scientific and technological strength of China also constantly strengthens, wherein, the insulation of construction material
Performance etc. is gradually improved, but existing construction material still has wilful poor, the not high defect of fire resistance, once
Generation fire, consequence is hardly imaginable, work out a good toughness, fire resistance it is high go high carry material, it has also become current weight
Want one of problem.
The content of the invention
The invention aims to solve construction material of the prior art in the presence of wilful poor, fire resistance is bad to lack
Fall into and solved the above problems there is provided a kind of construction wall refractory material and preparation method thereof.
To achieve these goals, technical scheme is as follows：The invention discloses a kind of construction wall fire proofed wood
Material, by weight, is prepared from the following components：6-10 parts of cement, 3-6 parts of quick lime, 1-4 parts of silica white, coal ash powder 3-8
Part, 2-6 parts of cellulose ether, 1-4 parts of hydrophober, 1-5 parts of chopped strand, 18-35 parts of water.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：It is 7-9 parts of cement, 4-5 parts of quick lime, 2-3 parts of silica white, 4-7 parts of coal ash powder, 3-5 parts of cellulose ether, 2-3 parts of hydrophober, short
Cut 2-4 parts of fiber, 19-32 parts of water.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：8 parts of cement, 4 parts of quick lime, 3 parts of silica white, 5 parts of coal ash powder, 4 parts of cellulose ether, 2 parts of hydrophober, 3 parts of chopped strand, water
25 parts.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：6 parts of cement, 3 parts of quick lime, 4 parts of silica white, 8 parts of coal ash powder, 2 parts of cellulose ether, 4 parts of hydrophober, 1 part of chopped strand, water
35 parts.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：10 parts of cement, 6 parts of quick lime, 1 part of silica white, 3 parts of coal ash powder, 2 parts of cellulose ether, 1 part of hydrophober, 5 parts of chopped strand,
18 parts of water.
Preferably, described cellulose ether uses one kind in methyl cellulose ether, hydroxypropylcelluloether ether.
Preferably, described chopped strand uses basalt chopped fiber.
Preferably, the length of described chopped strand is 4-8 ㎜, the filament diameter of described chopped strand is 6-12 μ
m。
Preferably, described hydrophober uses organosilicon moisture repellent.
Preferably, the invention also discloses a kind of preparation method of above-mentioned construction wall refractory material, specific steps are such as
Under：According to above-mentioned parts by weight, cement, quick lime, silica white, coal ash powder are added in mixer, 6-8 points of stirring mixing
Clock, obtains compound, and cellulose ether, hydrophober, chopped strand are then added into compound, after stirring 4-8 minutes, adds
Water, is stirred for after 15-35 minutes can be used.
The present invention has advantages below compared with prior art：
Construction wall refractory material of the present invention, by adding hydrophober, can make material one layer of permanent waterproof layer of formation
For waterproof, good water-proof effect；
After being dissolved in water by adding the cellulose ether in cellulose ether, material, materials for wall system can be made more stable；
By adding basalt fibre, basalt fibre, be basalt building stones after 1450 DEG C of -1500 DEG C of meltings, pass through platinum rhodium
The continuous fiber of alloy bushing high speed pulling, similar to glass fibre, its performance between high intensity S glass fibres and
Between alkali-free E glass fibres, the color of pure natural basalt fibre is generally brown, and some are like golden.Basalt fibre is one
Emerging novel inorganic environment-friendly and green high performance fibre material is planted, it is by silica, aluminum oxide, calcium oxide, iron oxide
Basalt building stones with the oxide such as titanium dioxide composition pass through bushing Defect, basalt after high-temperature fusion
Continuous fiber not only good stability, but also there are a variety of excellent properties such as electrical insulating property, anticorrosive, flame resistant, high temperature resistant, because
This is by adding basalt fibre, and the construction material prepared has good toughness and fire resistance；
In summary, construction wall refractory material of the invention, not only toughness is preferable, and excellent fire retarding performance, is suitable for pushing away
Wide application.
Embodiment
Embodiments of the invention are elaborated below, the present embodiment is carried out lower premised on technical solution of the present invention
Implement, give detailed embodiment and specific operating process, but protection scope of the present invention is not limited to following implementations
Example.
The invention discloses a kind of construction wall refractory material, by weight, it is prepared from the following components：Cement 6-
10 parts, 3-6 parts of quick lime, 1-4 parts of silica white, 3-8 parts of coal ash powder, 2-6 parts of cellulose ether, 1-4 parts of hydrophober, chopped strand 1-
5 parts, 18-35 parts of water.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：It is 7-9 parts of cement, 4-5 parts of quick lime, 2-3 parts of silica white, 4-7 parts of coal ash powder, 3-5 parts of cellulose ether, 2-3 parts of hydrophober, short
Cut 2-4 parts of fiber, 19-32 parts of water.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：8 parts of cement, 4 parts of quick lime, 3 parts of silica white, 5 parts of coal ash powder, 4 parts of cellulose ether, 2 parts of hydrophober, 3 parts of chopped strand, water
25 parts.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：6 parts of cement, 3 parts of quick lime, 4 parts of silica white, 8 parts of coal ash powder, 2 parts of cellulose ether, 4 parts of hydrophober, 1 part of chopped strand, water
35 parts.
Preferably, the invention discloses a kind of construction wall refractory material, by weight, by following components preparation
Into：10 parts of cement, 6 parts of quick lime, 1 part of silica white, 3 parts of coal ash powder, 2 parts of cellulose ether, 1 part of hydrophober, 5 parts of chopped strand,
18 parts of water.
Preferably, described cellulose ether uses one kind in methyl cellulose ether, hydroxypropylcelluloether ether.
Preferably, described chopped strand uses basalt chopped fiber.
Preferably, the length of described chopped strand is 4-8 ㎜, the filament diameter of described chopped strand is 6-12 μ
m。
Preferably, described hydrophober uses organosilicon moisture repellent.
Preferably, the invention also discloses a kind of preparation method of above-mentioned construction wall refractory material, specific steps are such as
Under：According to above-mentioned parts by weight, cement, quick lime, silica white, coal ash powder are added in mixer, 6-8 points of stirring mixing
Clock, obtains compound, and cellulose ether, hydrophober, chopped strand are then added into compound, after stirring 4-8 minutes, adds
Water, is stirred for after 15-35 minutes can be used.
Embodiment 1
The invention discloses a kind of construction wall refractory material, by weight, it is prepared from the following components：8 parts of cement, life
4 parts of lime, 3 parts of silica white, 5 parts of coal ash powder, 4 parts of cellulose ether, 2 parts of hydrophober, 3 parts of chopped strand, 25 parts of water.
Described cellulose ether uses methyl cellulose ether.
Described chopped strand uses basalt chopped fiber.
The length of described chopped strand is 6 ㎜, and the filament diameter of described chopped strand is 10 μm.
Described hydrophober uses organosilicon moisture repellent.
The invention also discloses a kind of preparation method of above-mentioned construction wall refractory material, comprise the following steps that：According to upper
Parts by weight are stated, cement, quick lime, silica white, coal ash powder are added in mixer, stirring mixing 7 minutes is mixed
Material, then adds cellulose ether, hydrophober, chopped strand into compound, after stirring 6 minutes, adds water, is stirred for 20 minutes
It can be used afterwards.
Embodiment 2
The invention discloses a kind of construction wall refractory material, by weight, it is prepared from the following components：6 parts of cement, life
3 parts of lime, 4 parts of silica white, 8 parts of coal ash powder, 2 parts of cellulose ether, 4 parts of hydrophober, 1 part of chopped strand, 35 parts of water.
Described cellulose ether uses hydroxypropylcelluloether ether.
Described chopped strand uses basalt chopped fiber.
The length of described chopped strand is 4 ㎜, and the filament diameter of described chopped strand is 12 μm.
Described hydrophober uses organosilicon moisture repellent.
The invention also discloses a kind of preparation method of above-mentioned construction wall refractory material, comprise the following steps that：According to upper
Parts by weight are stated, cement, quick lime, silica white, coal ash powder are added in mixer, stirring mixing 6 minutes is mixed
Material, then adds cellulose ether, hydrophober, chopped strand into compound, after stirring 8 minutes, adds water, is stirred for 15 minutes
It can be used afterwards.
Embodiment 3
The invention discloses a kind of construction wall refractory material, by weight, it is prepared from the following components：10 parts of cement,
6 parts of quick lime, 1 part of silica white, 3 parts of coal ash powder, 2 parts of cellulose ether, 1 part of hydrophober, 5 parts of chopped strand, 18 parts of water.
Described cellulose ether uses methyl cellulose ether.
Described chopped strand uses basalt chopped fiber.
The length of described chopped strand is 8 ㎜, and the filament diameter of described chopped strand is 12 μm.
Described hydrophober uses organosilicon moisture repellent.
The invention also discloses a kind of preparation method of above-mentioned construction wall refractory material, comprise the following steps that：According to upper
Parts by weight are stated, cement, quick lime, silica white, coal ash powder are added in mixer, stirring mixing 8 minutes is mixed
Material, then adds cellulose ether, hydrophober, chopped strand into compound, after stirring minute, adds water, is stirred for 35 minutes
It can be used afterwards.
Embodiment 4
The invention discloses a kind of construction wall refractory material, by weight, it is prepared from the following components：7 parts of cement, life
5 parts of lime, 3 parts of silica white, 4 parts of coal ash powder, 3 parts of cellulose ether, 2 parts of hydrophober, 2 parts of chopped strand, 19 parts of water.
Described cellulose ether uses one kind in methyl cellulose ether, hydroxypropylcelluloether ether.
Described chopped strand uses basalt chopped fiber.
The length of described chopped strand is 7 ㎜, and the filament diameter of described chopped strand is 11 μm.
Described hydrophober uses organosilicon moisture repellent.
The invention also discloses a kind of preparation method of above-mentioned construction wall refractory material, comprise the following steps that：According to upper
Parts by weight are stated, cement, quick lime, silica white, coal ash powder are added in mixer, stirring mixing 8 minutes is mixed
Material, then adds cellulose ether, hydrophober, chopped strand into compound, after stirring 7 minutes, adds water, is stirred for 22 minutes
It can be used afterwards.
General principle, principal character and the advantages of the present invention of the present invention has been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and that described in above-described embodiment and specification is the present invention
Principle, various changes and modifications of the present invention are possible without departing from the spirit and scope of the present invention, these change and
Improvement is both fallen within the range of claimed invention.The protection domain of application claims by appending claims and its
Equivalent is defined.
Claims (10)
1. a kind of construction wall refractory material, it is characterised in that：By weight, it is prepared from the following components：Cement 6-10
Part, 3-6 parts of quick lime, 1-4 parts of silica white, 3-8 parts of coal ash powder, 2-6 parts of cellulose ether, 1-4 parts of hydrophober, chopped strand 1-5
Part, 18-35 parts of water.
2. a kind of construction wall refractory material according to claim 1, it is characterised in that：By weight, by with the following group
Divide and be prepared from：7-9 parts of cement, 4-5 parts of quick lime, 2-3 parts of silica white, 4-7 parts of coal ash powder, 3-5 parts of cellulose ether, hydrophober
2-3 parts, 2-4 parts of chopped strand, 19-32 parts of water.
3. a kind of construction wall refractory material according to claim 1, it is characterised in that：By weight, by with the following group
Divide and be prepared from：8 parts of cement, 4 parts of quick lime, 3 parts of silica white, 5 parts of coal ash powder, 4 parts of cellulose ether, 2 parts of hydrophober, chopped fibre
Tie up 3 parts, 25 parts of water.
4. a kind of construction wall refractory material according to claim 1, it is characterised in that：By weight, by with the following group
Divide and be prepared from：6 parts of cement, 3 parts of quick lime, 4 parts of silica white, 8 parts of coal ash powder, 2 parts of cellulose ether, 4 parts of hydrophober, chopped fibre
Tie up 1 part, 35 parts of water.
5. a kind of construction wall refractory material according to claim 1, it is characterised in that：By weight, by with the following group
Divide and be prepared from：10 parts of cement, 6 parts of quick lime, 1 part of silica white, 3 parts of coal ash powder, 2 parts of cellulose ether, 1 part of hydrophober, be chopped
5 parts of fiber, 18 parts of water.
6. a kind of construction wall refractory material according to claim 1, it is characterised in that：Described cellulose ether uses first
One kind in base cellulose ether, hydroxypropylcelluloether ether.
7. according to a kind of any described construction wall refractory materials of claim 1-6, it is characterised in that：Described chopped strand
Using basalt chopped fiber.
8. according to a kind of any described construction wall refractory materials of claim 1-6, it is characterised in that：Described chopped strand
Length be 4-8 ㎜, the filament diameter of described chopped strand is 6-12 μm.
9. according to a kind of any described construction wall refractory materials of claim 1-6, it is characterised in that：Described hydrophober is adopted
Use organosilicon moisture repellent.
10. according to a kind of preparation method of any described construction wall refractory materials of claim 1-6, it is characterised in that：Tool
Body step is as follows：According to above-mentioned parts by weight, cement, quick lime, silica white, coal ash powder are added in mixer, stirring is mixed
Close 6-8 minutes, obtain compound, cellulose ether, hydrophober, chopped strand are then added into compound, stir 4-8 minutes
Afterwards, water is added, is stirred for after 15-35 minutes can be used.