CN106938278A - A kind of Rolling compund method of stainless steel clad plate - Google Patents
A kind of Rolling compund method of stainless steel clad plate Download PDFInfo
- Publication number
- CN106938278A CN106938278A CN201710262682.7A CN201710262682A CN106938278A CN 106938278 A CN106938278 A CN 106938278A CN 201710262682 A CN201710262682 A CN 201710262682A CN 106938278 A CN106938278 A CN 106938278A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- composite
- clad plate
- steel clad
- rolling compund
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of Rolling compund method of stainless steel clad plate, the composite surface of female base is surface-treated by it, then docking relative with the composite surface of stainless steel billet, then two blank materials are welded as a whole, composite billet is constituted, composite plate blanks are finally rolled into described composite plate.When being rolled using this method, composite bed is directly contacted with milling train, stress(Inwardly, roll-force transfer capability is poor for the general surface stainless steel of symmetrical sandwich), therefore composite surface performance will get well, and realize the production for the steel plate that more than width 3000mm and/or shear strength more than 350Mpa special dimension is used.More than the shear strength 350Mpa of stainless steel clad plate obtained by this method, composite bed flaw detection can close I grades of forging, excellent combination property;Available for fields such as nuclear power, pipeline, production platform, elevated temperature vessel steel plates.
Description
Technical field
The present invention relates to a kind of production method of composite plate, the Rolling compund method of especially a kind of stainless steel clad plate.
Background technology
Clad steel plate as a kind of new economical material, it is low in steel market in the case of, will increasingly by
People are to attention, and its application also will more and more extensively, and the market demand also will be in rising trend.China's clad steel plate sale class
It is mainly stainless steel clad plate in type, accounts for more than the 80% of total amount, it is widely used in its people's warp such as oil, chemical industry, salt manufacturing alkaline
In Ji and all trades and professions.
The mode of country's stainless steel clad plate production has three kinds at present, roll-bonding method, explosion composite method and " blast+
Rolling " composite algorithm.Explosive clad plate when producing can environment pollute, production cost is high, low production efficiency and rolling composite plate
Because production technology and production equipment require high, it is desirable to have large-scale steel mill does support and could produced, so manufacturer is less, rolls
The advantage of composite plate processed is that speed of production is fast, the most long 13000mm of the production most wide 2500mm of plate width.Answer for most notable 3 in the world
Plywood Chang Doushi rolling composite plates factory, as the JFE of Japan, there be the VAI of Austria the Bethlehem in the U.S..
In the process aspect of Rolling Production stainless steel clad plate, domestic manufacturer is much using the method system of symmetry rolling
Base, this is due to that single base is combined that base is very high to equipment requirement, complex process is caused.Symmetrical blank-making method is fairly simple, still
Rolled products performance is not high, and steel plate width is mainly used in the product for civilian use in below 2800mm, it is impossible to be used in production nuclear power, oil recovery
The high-end fields such as platform, wind-powered electricity generation plate, these high-end fields are to composite surface Percentage bound requirement 100%, and shear strength index exists
More than 350Mpa.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of Rolling compund side of the high stainless steel clad plate of shear strength
Method.
In order to solve the above technical problems, the technical solution used in the present invention is:The composite surface of female base is carried out at surface
Reason, then docking relative with the composite surface of stainless steel billet, then two blank materials are welded as a whole, constitutes composite billet, finally will be compound
Slab is rolled into described composite plate.
The composite surface surface treated of female base of the present invention is to roughness in 2~5um.
The butt seam of two composite surface of the present invention is at 20 and following.
The solder joint that four edge points weldering length of two blank material of the present invention is 200mm, solder joint layer depth is not less than 35mm.Institute
2 weldings are used when stating welding;First time, weld heat input was in 86~110KJ/cm3, speed of welding is 250~300mm/s;
Second of welding energy is in 135~160KJ/cm3, speed of welding is 150~200mm/s.
Hot rolling of the present invention is:Composite plate blanks are heated to 1200~1240 DEG C, are incubated 3~6 hours, then roll.
It is using the beneficial effect produced by above-mentioned technical proposal:During using present invention rolling, composite bed is directly with rolling
Machine contact, stress(Inwardly, roll-force transfer capability is poor for the general surface stainless steel of symmetrical sandwich), therefore composite surface performance will get well,
Realize the production for the steel plate that more than width 3000mm and/or shear strength more than 350Mpa special dimension is used.The present invention
More than the shear strength 350Mpa of gained stainless steel clad plate, composite bed flaw detection can close I grades of forging, excellent combination property;It can use
In fields such as nuclear power, pipeline, production platform, elevated temperature vessel steel plates.
Embodiment
With reference to specific embodiment, the present invention is further detailed explanation.
Embodiment 1:The Rolling compund method of this stainless steel clad plate uses following concrete technologies.
Female base is Q345B, and stainless steel billet is 316, and it is thick, 3200 wide that specification is 20+2mm;After surface treated, female base is answered
The roughness in conjunction face is in 5um.The handling whole process of stainless steel billet uses vacuum magnetic disc suspending, and the butt seam of stainless steel billet and female base exists
20.After stainless steel billet is docked with two composite surfaces of female base, spot welding, assembly are carried out using artificial.During spot welding, four edge points of blank material
Weldering length is 200mm solder joints, to realize fixation.Using 2 weldings, first time weld heat input 86KJ/cm during welding3, weldering
Speed is connect for 300mm/s;Second of weld heat input 135KJ/cm3, speed of welding is 200mm/s;Solder joint depth 35mm layer by layer.
1220 DEG C of composite billet maximum heating temperature, is incubated 4 hours, is rolled using big pressure, you can obtain described stainless steel clad plate.
Result of implementation:Forging is closed in the shear strength 400Mpa of stainless steel clad plate, composite bed Percentage bound 100%, composite bed flaw detection
I grades of part.
Embodiment 2:The Rolling compund method of this stainless steel clad plate uses following concrete technologies.
Female base is Q345R, and stainless steel billet is 316L, and it is thick, 3500 wide that specification is 16+2mm;After surface treated, female base
The roughness of composite surface is in 3um.The handling whole process of stainless steel billet uses vacuum magnetic disc suspending, the butt seam of stainless steel billet and female base
At 15.After stainless steel billet is docked with two composite surfaces of female base, spot welding, assembly are carried out using artificial.During spot welding, four sides of blank material
Spot welding length is 200mm solder joints, to realize fixation.Using 2 weldings, first time weld heat input 100KJ/cm during welding3,
Speed of welding is 250mm/s;Second of weld heat input 140KJ/cm3, speed of welding is 180mm/s;Solder joint depth layer by layer
50mm.1240 DEG C of composite billet maximum heating temperature, is incubated 4 hours, is rolled using big pressure, you can obtain described stainless steel double
Plywood.
Result of implementation:Forging is closed in the shear strength 380Mpa of stainless steel clad plate, composite bed Percentage bound 100%, composite bed flaw detection
I grades of part.
Embodiment 3:The Rolling compund method of this stainless steel clad plate uses following concrete technologies.
Female base is X52, and stainless steel billet is 316L, and it is thick that specification is 12+2mm;After surface treated, female base composite surface it is thick
Rugosity is in 2um.The butt seam of the handling whole process use vacuum magnetic disc suspending of stainless steel billet, stainless steel billet and female base is at 10.No
After rust steel billet is docked with two composite surfaces of female base, spot welding, assembly are carried out using artificial.During spot welding, four edge point weldering length of blank material
For 200mm solder joints, to realize fixation.Using 2 weldings, first time weld heat input 100KJ/cm during welding3, speed of welding
For 300mm/s;Second of weld heat input 140KJ/cm3, speed of welding is 150mm/s;Solder joint depth 50mm layer by layer.Composite billet
1220 DEG C of maximum heating temperature, is incubated 4 hours, is rolled using big pressure, you can obtain described stainless steel clad plate.
Result of implementation:Forging is closed in the shear strength 420Mpa of stainless steel clad plate, composite bed Percentage bound 100%, composite bed flaw detection
I grades of part.
Embodiment 4:The Rolling compund method of this stainless steel clad plate uses following concrete technologies.
Female base is 14CrMo1R, and stainless steel billet is 410S, and it is thick that specification is 50+3mm;After surface treated, female base is combined
The roughness in face is in 2um.The butt seam of the handling whole process use vacuum magnetic disc suspending of stainless steel billet, stainless steel billet and female base is 12
Silk.After stainless steel billet is docked with two composite surfaces of female base, spot welding, assembly are carried out using artificial.During spot welding, four edge point welderings of blank material
Length is 200mm solder joints, to realize fixation.Using 2 weldings, first time weld heat input 110KJ/cm during welding3, welding
Speed is 250mm/s;Second of weld heat input 140KJ/cm3, speed of welding is 150mm/s;Solder joint depth 50mm layer by layer.It is multiple
1220 DEG C of base maximum heating temperature is closed, 6 hours are incubated, is rolled using big pressure, you can obtain described stainless steel clad plate.
Result of implementation:Forging is closed in the shear strength 390Mpa of stainless steel clad plate, composite bed Percentage bound 100%, composite bed flaw detection
I grades of part.
Embodiment 5:The Rolling compund method of this stainless steel clad plate uses following concrete technologies.
Female base is DH36, and stainless steel billet is 310, and it is thick that specification is 35+3mm;After surface treated, female base composite surface it is thick
Rugosity is in 2um.The butt seam of the handling whole process use vacuum magnetic disc suspending of stainless steel billet, stainless steel billet and female base is at 12.No
After rust steel billet is docked with two composite surfaces of female base, spot welding, assembly are carried out using artificial.During spot welding, four edge point weldering length of blank material
For 200mm solder joints, to realize fixation.Using 2 weldings, first time weld heat input 100KJ/cm during welding3, speed of welding
For 280mm/s;Second of weld heat input 150KJ/cm3, speed of welding is 150mm/s;Solder joint depth 50mm layer by layer.Composite billet
1220 DEG C of maximum heating temperature, is incubated 3 hours, is rolled using big pressure, you can obtain described stainless steel clad plate.
Result of implementation:I is closed in the shear strength 365Mpa of stainless steel clad plate, composite bed Percentage bound 100%, composite bed flaw detection
Level.Mother metal performance meets standard requirement.
Embodiment 6:The Rolling compund method of this stainless steel clad plate uses following concrete technologies.
Female base is S355G10+N, and stainless steel billet is 316L, and it is thick that specification is 35+3mm;After surface treated, female base is combined
The roughness in face is in 3um.The butt seam of the handling whole process use vacuum magnetic disc suspending of stainless steel billet, stainless steel billet and female base is 10
Silk.After stainless steel billet is docked with two composite surfaces of female base, spot welding, assembly are carried out using artificial.During spot welding, four edge point welderings of blank material
Length is 200mm solder joints, to realize fixation.Using 2 weldings, first time weld heat input 110KJ/cm during welding3, welding
Speed is 250mm/s;Second of weld heat input 160KJ/cm3, speed of welding is 150mm/s;Solder joint depth 40mm layer by layer.It is multiple
1200 DEG C of base maximum heating temperature is closed, 4.5 hours are incubated, is rolled using big pressure, you can obtain described stainless steel clad plate.
Result of implementation:I is closed in the shear strength 455Mpa of stainless steel clad plate, composite bed Percentage bound 100%, composite bed flaw detection
Level.Mother metal performance meets standard requirement.
Claims (6)
1. a kind of Rolling compund method of stainless steel clad plate, it is characterised in that:The composite surface of female base is surface-treated, so
Docking relative with the composite surface of stainless steel billet, then two blank materials are welded as a whole afterwards, constitutes composite billet, finally by composite plate blanks heat
Roll into described composite plate.
2. a kind of Rolling compund method of stainless steel clad plate according to claim 1, it is characterised in that:Female base
Composite surface surface treated is to roughness in 2~5um.
3. a kind of Rolling compund method of stainless steel clad plate according to claim 1, it is characterised in that:Described two are combined
The butt seam in face is at 20 and following.
4. a kind of Rolling compund method of stainless steel clad plate according to claim 1, it is characterised in that:Two blank material
Four edge points weldering length be 200mm solder joint, solder joint layer depth is not less than 35mm.
5. a kind of Rolling compund method of stainless steel clad plate according to claim 4, it is characterised in that:During the welding
Using 2 weldings;First time, weld heat input was in 86~110KJ/cm3, speed of welding is 250~300mm/s;Second of weldering
Energy is connect in 135~160KJ/cm3, speed of welding is 150~200mm/s.
6. a kind of Rolling compund method of stainless steel clad plate according to claim 1-5 any one, its feature exists
In the hot rolling is:Composite plate blanks are heated to 1200~1240 DEG C, are incubated 3~6 hours, then roll.