CN106930547A - It is a kind of that infiltration renovation technique is blocked up to basement wall base plate based on XYPEX materials - Google Patents
It is a kind of that infiltration renovation technique is blocked up to basement wall base plate based on XYPEX materials Download PDFInfo
- Publication number
- CN106930547A CN106930547A CN201511007636.XA CN201511007636A CN106930547A CN 106930547 A CN106930547 A CN 106930547A CN 201511007636 A CN201511007636 A CN 201511007636A CN 106930547 A CN106930547 A CN 106930547A
- Authority
- CN
- China
- Prior art keywords
- xypex
- concentrating agents
- water
- mortar
- concrete
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The technique that infiltration is repaired is blocked up to basement wall base plate based on XYPEX materials the invention discloses a kind of, the present invention blocks up infiltration to basement wall base plate has good regulation effect, can realize the effect of not only reinforcement but also moisturizing；And can meet seam two-end structure generation relative settlement and longitudinal extension when sealing waterproof.
Description
Technical field
The invention belongs to building field, and in particular to a kind of the stifled infiltration of basement wall base plate is repaiied based on XYPEX materials
Return to work skill.
Background technology
Basement wall wall is brick structure, and the thorough brick wall body of lining is very loose, and percolating water is very serious, and repairing difficulty is suitable
It is difficult.Once failed using multiple materials such as slip casting, leak stopping spirits, failed.
The content of the invention
It is a kind of that infiltration renovation technique is blocked up to basement wall base plate based on XYPEX materials, in the technical process, match somebody with somebody
Close and use XYPEX materials；
The XYPEX materials be XYPEX " concentrating agents " mortar and, XYPEX " concentrating agents " half-dried dough,
One or more in XYPEX " admixture " mortars or XYPEX " sealing agent "；
Wherein, in XYPEX " concentrating agents " mortar, XYPEX " concentrating agents " powder is 5: 2~2.5 with the volume ratio of water；
In XYPEX " concentrating agents " half-dried dough, XYPEX " concentrating agents " powder is 6: 1 with the volume ratio of water；
In XYPEX " admixture " mortar, cement, the weight ratio of thick middle sand, water and XYPEX " admixture " are
1：2.5：0.4：0.03.
XYPEX " sealing agent " dough powder is 3.5: 1 with the volume ratio of water.
It is preferred that the use of XYPEX materials is comprised the following steps：
The first step:On brick face and institute it is seamed it is middle first apply brush one times XYPEX " concentrating agents " mortar bed；
Second step:Brush XYPEX " admixture " screed；
3rd step:Painting brushes one times XYPEX " concentrating agents " mortar bed；
4th step:Brush X XYPEX " admixture " screed；
5th step：Painting brushes one times XYPEX " concentrating agents " mortar bed；
6th step：Maintenance.
The XYPEX materials used in the present invention are XYPEX cement-base infiltration crystallization type materials.
XYPEX materials of the invention are purchased from city of Beijing honor waterproof material Co., Ltd or Sichuan generation Condar civil engineering skill
Art Co., Ltd.
The present invention not using only material hydrophilic it is nontoxic, it is tasteless, pollution-free, nonflammable, with waterproof, protect and change
The combination property of kind concrete.And it produces the complicated and confused shape for being insoluble in water to crystallize in the hole and capillary channel of concrete
Body.The packing of concrete can be improved, an entirety is turned into concrete, prevent any liquid from invading, prevent coagulation
Soil influences its quality because of severe environmental conditions.
By using material of the invention and technique, penetrant crystalline depth free from worldly cares can be obtained, the time is more long, and crystallization is oozed
It is thoroughly deeper.Japanese building association carries out overtesting, after test specimen is placed 12 months, measures its depth up to 300mm.
There is the ability of self-regeneration after the crack chance water of the 0.4~1mm occurred for concrete structure, if coagulation local products
Raw crack, running into water can be crystallized with secondary, three inferior multiple generations again, crack be blocked, with permanent waterproof action.
And it does not influence the breathing of concrete, the infiltration of water can be stopped, concrete is kept dry and comfortable, it is not moist.
Concrete strength up to 20~29% can be effectively improved.
After using technique of the invention, puncture is not afraid of after curing period of having constructed and is collided with.
And the erosion of various chemical substances can be resisted, antiacid alkali Long Term Contact pH is up to 3.0~11.0, Intermittent Contact
PH2.0~12.0.Also radioresistance, without any damage under 5.76 × 104 rad gamma rays.
Anti-carbonation, the harm of resisting chloride ion penetration, alkali-aggregate reaction (AAR) can be suppressed.
Under -32 DEG C~+130 DEG C of sustaining temperature, it is kept to act at -185 DEG C~+1530 DEG C intermittent temperature.It is wet
The size of degree size, ultraviolet power and oxidation is on it without influence.
Freeze thawing resistance circulation is up to 350 with last time.
Reinforcing bar and metal embedded part can be protected not to be corroded.
Nontoxic, tasteless, pollution-free category environmental protection.
Construction method simplicity, therefore saving of labor, material-saving, overall economic efficiency rationally, the ability of self-regeneration are sewed with due to counterincision,
The maintenance cost in later stage can be reduced.
Not only coagulation soil characteristics can be improved with waterproof, antiseepage, anti-corrosion, administer the disease problem of concrete, extension is mixed
The service life of Xtah Crude Clay structure durability and building.
The use that the present invention passes through XYPEX " Sai Baisi " material, adds its cooperation and effective combination of special process, obtains
The unforeseen good result of those skilled in the art was obtained, the problem of long-standing problem building field technical staff was solved.
The present inventor not only for how using the material to have carried out substantial amounts of technology exploration, to how to be used in combination the material
While material, suitable technique is obtained so as to farthest play the effect of the material and has been also carried out substantial amounts of technical research,
Workman and the substantial amounts of energy of research staff are consumed, while also obtain good effect.
Specific embodiment
(1) rely mainly on prevention, the comprehensive regulation.Design of the invention is foundation, and waterproof material is crucial, and constructing operation is
Ensure.
(2) self waterproofing for establishing reinforced concrete structure is this, to the weakness of concrete structure, construction joint, hole, honeybee
The weak links such as nest pitted skin, structural cracks, the mouth of pipe, pipeline carry out concrete structure reinforcement reparation.To ensure waterproof entirety
Property, sealing reinforcement is carried out to the structural weak position such as junction, well construction prevents these positions from seepage occur.
Brick wall wall construction method：
(1) percolating water position and situation are found out before administering, Reason Of Leakange is differentiated, resolution is specified according to onsite application requirement.
(2) search and cut off seepage water source, make to repair stifled work as far as possible is carried out under anhydrous conditions.
(3) when carrying out repairing stifled under seepage water state, it is necessary to reduce seepage water area as far as possible, leak is converged or several
Point is following, reduces the seepage pressure at other positions, it is ensured that repair that stifled everything goes well with your work carries out.To reduce seepage water area, first
Conscientiously to carry out drainage work.The principle of diversion is that big leakage is changed into small leakage, shallow leakage height leakage, the leakage of seepage variable orifice.Using
The method of intubation diversion pressure release, is that feedwater reserves road by the purpose that water is drawn, and to carry out constructing operation, is prevented because of hydraulic pressure
The material of senior general's construction is washed out.
Specifically, there is following examples：
XXX engineering colleges Wen Guan buildings basement wall wall is brick structure, and the thorough brick wall body of lining is very loose, and percolating water is very tight
Weight, repairing difficulty is extremely difficult.Once failed using multiple materials such as slip casting, leak stopping spirits, failed.
Repairing waterproofing of the invention：Diversion pressure release leak stopping sealing, secondly sets one XYPEX " concentrating agents " ash first
Slurry and XYPEX " admixture " waterproof mortar course reach permanent water-resistant layer.
Raw material, match ratio, material quantity
(1) raw material
1. 525# Portland cements；
2. sand in thick：Particle diameter is 1~3mm, and clay content is less than 2%；
3. XYPEX " concentrating agents "；
4. XYPEX " admixture "；
5. XYPEX " sealing agent "；
(2) match ratio
1. XYPEX " admixture " mortar：Cement: sand in thick: water=0.03:1∶2.5∶0.4
2. the half-dried dough powder of XYPEX " concentrating agents ": water=6: 1 (volume ratio)
3. XYPEX " concentrating agents " ash starch: water=5: 2 (volume ratios)
4. XYPEX " sealing agent " dough powder: water=3.5: 1 (volume ratio)
Construction technology
(1) base treatment
1. the original mortar of brick wall and debris must be cut to clean out to by brickwork joint and picks into the deep right angle grooves of 1cm, directly
To hard brick face is exposed, then rinsed well with water.
2. brick wall body is watered and is sufficiently humidified so as to.
3. bottom board concrete face dabbing, clean to eliminating impurities such as the anti-alkali in concrete surface, dust, oil stains.Make concrete surface have it is clean,
Hard, moist thick pitted skin.
(2) brick wall construction technique
(3) brick wall construction main points：
When 1. constructing, it is applied to layering and alternately smears densification reality, pore by XYPEX admixtures there is unique crystallization to make
Dry powder adds mixing in mortar ingredient, is equipped with suitable construction technology, is allowed to penetrate into each fine hair of mortar
Kong Zhong, reaction is produced using cement mortar composition in itself inside cement mortar, and the crystalline solid filling for reacting generation is tiny
Seepage aquaporin, so as to play improve mortar strength and waterproof, the effect of antiseepage.
2. waterproof layer itself have to be the entirety continuously closed, and must not have any hollowing, scaling, crack etc. to cause
The defect of percolating water.Some detail structures of globality, such as built-in fitting, break-through waterproof are closed for waterproof layer may be destroyed
The weak parts such as the door and window in the pipeline and underground engineering of layer must all take effective reinforcement waterproof measure, improve its tight
Close property, to ensure continuous, the closed globality of waterproof layer.
The requirement of brick wall waterproof quality and examination
(1) match ratio of XYPEX " concentrating agents " mortar and XYPEX " admixture " mortar has to comply with design requirement.
(2) should carry out self-inspection after the completion of waterproof construction is per procedure mutually to examine, accept as unavoidable after meeting the requirements, then be checked by special messenger,
Lower road construction of waterproof layer can be carried out after qualified.
(3) XYPEX " admixture " cement mortar waterproof layer surface should be closely knit, smooth, must be firmly combined between each layer, nothing
The defects such as hollowing, crackle, dusting." u "-shaped groove should be dug at negative and positive angle, with XYPEX " concentrating agents " half-dried dough
Make reinforcement treatment.
(4) cement mortar construction of waterproof layer seam Liu Cha positions should be correct, and connecing raft should be operated by hierarchical sequence, overlaps layer by layer tight.
(5) average thickness of waterproof layer should meet design requirement, and minimum thickness cannot be less than the 85% of design load.
Concrete structure base plate scheme：
1st, basal plane is cleared up
Cleaning basic unit exotic, loose material, laitance heavy slurry, surface dust, anti-alkali, the greasy dirt on surface, basic unit's polishing are coarse, inquire for
To solid firm concrete, then sweep and clean up, make whole basal plane infiltration moist, but there should not be bright water,
To be dried if any bright water.
2nd, leak stopping
(1) after cleaning basal plane, in the case of having infiltration, first with XYPEX " concentrating agents " mortar (or dry powder) and XYPEX
" sealing agent " dough leak stopping is used cooperatively.
(2) crack more than 0.4mm and the repairing of concrete defect and alveolate texture in the case where there is streamflow regime：
(3) in the case of having current：
1. slot：Crackle or junction are hollowed out U-type groove (digging deep when there are current) wide in 25mm, 35-70mm deep,
" V " type groove is not allowed.
2. clear and rich (cleaning and wetting)：Bulk materials are removed, water retting basal plane is used.Water saturates concrete is allowed then to remove
Bright water on surface.
3. plugging leaks (with XYPEX " concentrating agents " mortar and XYPEX " sealing agent " dough)：After removing bright water,
At the half of groove depth, 3.5 parts of material are taken by volume in pressure, the XYPEX that 1 part of water is mixed repairs the siccative of sealing agent half
Group, tamps in the region of fluting in good time, and extrusion time is directly proportional (usually 2-5 minutes) to water-carrying capacity.
4. swabbing：5 parts of material, 2 parts of water are reconciled into XYPEX " concentrating agents " mortar by volume, in groove and along notch
One layer of mortar is applied at the 150mm wide of two sides, gloves smearing can be worn with brush or with hand.
5. XYPEX " concentrating agents " half-dried dough is used again when " U " type groove is done in joint filling：When mortar coating is dried about ten minutes,
But still when having adherence, with the half-dried dough that XYPEX " concentrating agents " takes a water by volume, six parts of material mix
Fill up groove and fill and lead up tamping with surface.The surface of wet joint filling is being spilt with water, one XYPEX is then being applied again on the region repaired
" concentrating agents " mortar.
(4) in the case of non-water flow：
1. slot：Crackle or junction are hollowed out " U " type groove wide in 25mm, 35-70mm deep.It is XYPEX " dense
The treatment of contracting agent " " U " type groove reinforcement and repair.
2. basal plane cleaning and wetting：Bulk materials are removed, water retting basal plane is used.Water saturates concrete is allowed then to remove surface
On bright water.
3. XYPEX " concentrating agents " mortar presses volume and 5 parts of material, 2 parts of water is reconciled, in groove and along the two sides 150mm wide of notch
Place applies one layer of mortar, can wear gloves smearing with brush or with hand.
4. XYPEX " concentrating agents " half-dried dough is used during joint filling again：The treatment of " U " type groove, when mortar coating about ten minutes,
But still when having adherence, with the half-dried dough that XYPEX " concentrating agents " takes a water by volume, six parts of material mix
Fill up groove and flush (be tuned into half-dried agglomerate with trowel mix when mixing, wear gloves filling, then with pneumatic or
Hand tools, firmly tamps).The surface of wet joint filling is spilt with water, one XYPEX is then applied again on the region repaired
" concentrating agents " mortar.
3rd, construction of bottom plates way
XYPEX " concentrating agents " dry powder, consumption 0.8kg/ ㎡, crannied position XYPEX " concentrating agents " are spread on the surface of basic unit
Consumption increases consumption about 3~4.5kg/ linear meter(lin.m.)s along seam and neat seam both sides.XYPEX " concentrating agents " dry powder, 30 minutes are spread
Interior casting concrete bed course, concrete must vibration compacting.
(1) two-way concrete slabs of colligation ∮ 6,100 × 100mm of spacing, bottom protective layer thickness 15mm.
(2) the dry dustings of XYPEX " concentrating agents "；
(3) during pouring reinforcement concrete, every 20m or so sets a construction joint (position of seam is preferably disposed in the center of beam), there is rule
Rule control concrete shrinkage occurs at construction joint, to avoid the occurrence of irregular crack.Treat that concrete shrinkage is basicly stable
Processed again afterwards.
(4) C20 pea gravel concrete bed courses are poured, rub concora crush with the hands with wooden float is twisted into thick pitted skin in fact, after intensity reaches design 70%
Next procedure can be carried out.
(5) bottom slab concreting C30 pea gravel concretes
It is required that vibration compacting, (flatness should meet design requirement) is flattened with wooden float, compacting is twisted into and reaches engineering using will
The thick pitted skin asked, after after concrete final set, brushes two road XYPEX " concentrating agents " mortar beds, and consumption 1.2kg/ ㎡ are (no
Including the consumption containing repairing), then soak maintenance 120 hours with spray water.Base plate and side wall junction, up return
300mm -500mm, by XYPEX technological requirements to basal plane cleaning, plucking, brushing consumption and maintenance are ibid.
4th, new pouring does large-area concrete brushing XYPEX " concentrating agents " mortar construction requirement
Concrete surface debris must be removed totally, make concrete surface that there is the pitted skin of solid, cleaning and complete wetting,
Reflected with the active chemistry inner layer in sharp XYPEX and extended, it is ensured that crystal structure penetrates into concrete capillary system.
(1) construction equipment：XYPEX specific brush, size metal bucket, electric mixer, sprayer etc..
(2) technological process：Solid thick pitted skin → brushing two road XYPEX " concentrating agents " mortar bed → final set is completed pouring
Water purification is conserved three days afterwards.
(3) proportioning of XYPEX " concentrating agents " compound
1. the modulation of XYPEX " concentrating agents " mortar：XYPEX " concentrating agents " powder: water=5: 2 (volume ratios)
Powder and water by measuring are poured into blender, are bored (250r/min) drive blade with a low speed or are used other forms
Blender stirring, to ensure to be well mixed, if without mixing plant, it is also possible to stir by hand, but must mix it is uniform.
2. XYPEX " concentrating agents " modulates one-shot forming in strict accordance with ratio, first pours into water in proportion in bucket, then by than
Example charging stirring, never allows the another charging that adds water in modulated process, can otherwise influence the effect of XYPEX.XYPEX mixes
The quantity of material should be risen in 20min with spice and is finished, and should constantly be stirred during use.
3. construction of waterproof layer XYPEX specific brush is exerted oneself to come and go and rubs brush, and rubbing brush should be uniform, and materials are controlled in 1.2kg/ ㎡
±0.1kg/㎡。
4. maintenance processes are extremely important, and when XYPEX curing of coatings is motionless to use hand rubbing, maintenance can just start, must
Must conserve meticulously 120 hours, daily spray form water at least three times will avoid being washed away with water.To be remained during maintenance
The state of basal plane moistening.If (basement is moist big, needs aeration-drying, and ground floor XYPEX " concentrating agents " must solidify
Brush again afterwards second time)
Quality examination is checked and accepted
(1) should provide the XYPEX material technology performances of site operation examining report or other may certify that quality of materials
File.
(2) mix should meet regulation requirement with when coating constructing operation.
(3) to apply thickness uniform for XYPEX, is not allow for holiday and show-through, all undesirable to redress.
(4) XYPEX coatings consumption should meet regulation requirement, and coating should ensure that 1.2kg/ ㎡ ± 0.1kg/ ㎡.
(5) XYPEX coatings such as must not smash, collide with the phenomenon during construction and maintenance, if any need to be repaired.
Claims (8)
1. a kind of that infiltration renovation technique is blocked up to basement wall base plate based on XYPEX materials, its feature exists
In in the technical process, with the use of XYPEX materials；
The XYPEX materials be XYPEX " concentrating agents " mortar and, XYPEX " concentrating agents " it is half-dried
One or more in dough, XYPEX " admixture " mortars or XYPEX " sealing agent "；
Wherein, in XYPEX " concentrating agents " mortar, XYPEX " concentrating agents " powder is 5 with the volume ratio of water:
2~2.5；
In XYPEX " concentrating agents " half-dried dough, XYPEX " concentrating agents " powder is 6: 1 with the volume ratio of water；
In XYPEX " admixture " mortar, cement, the weight of thick middle sand, water and XYPEX " admixture "
Amount is than being 1：2.5：0.4：0.03.
XYPEX " sealing agent " dough powder is 3.5: 1 with the volume ratio of water.
2. technique according to claim 1, it is characterised in that the use of XYPEX materials include with
Lower step：
The first step:On brick face and institute it is seamed it is middle first apply brush one times XYPEX " concentrating agents " mortar bed；
Second step:Brush XYPEX " admixture " screed；
3rd step:Painting brushes one times XYPEX " concentrating agents " mortar bed；
4th step:Brush X XYPEX " admixture " screed；
5th step：Painting brushes one times XYPEX " concentrating agents " mortar bed；
6th step：Maintenance.
3. technique according to claim 2, it is characterised in that XYPEX is brushed in second step and " is blended
The thickness of agent " screed is 10mm~15mm.
4. technique according to claim 2, it is characterised in that XYPEX is brushed in the 4th step and " is blended
The thickness of agent " screed is 10mm.
5. technique according to claim 2, it is characterised in that the first step, the 3rd step and the 5th step
In, the consumption of XYPEX " concentrating agents " mortar bed is 0.5~0.6kg/ ㎡.
6. technique according to claim 1, it is characterised in that the technique is comprised the following steps：
1) slot：Crackle or junction are hollowed out " U " type groove wide in 25mm, 35-70mm deep；
2) it is clear and rich：Bulk materials are removed, water retting basal plane is used, allows water saturates concrete then to remove on surface
Bright water；
3) plugging leaks：Remove after bright water, XYPEX " sealing agent " is taken at the half of groove depth, in pressure
Half-dried dough, tamps in the region of fluting in good time, and extrusion time is directly proportional to water-carrying capacity；
4) swabbing：In groove and along one layer of XYPEX " concentrating agents " mortar of painting at the two sides 150mm wide of notch；
5) XYPEX " concentrating agents " half-dried dough is used again when " U " type groove is done in joint filling：When mortar coating is dried about
Ten minutes, but still when having adherence, fill up groove with XYPEX " concentrating agents " half-dried dough and filled out with surface
Flat tamping；The surface of wet joint filling is being spilt with water, one XYPEX " concentration is then being applied again on the region repaired
Agent " mortar.
7. technique according to claim 1, it is characterised in that the technique is comprised the following steps：
1) slot：Crackle or junction are hollowed out " U " type groove wide in 25mm, 35-70mm deep；Carry out
The treatment of XYPEX " concentrating agents " " U " type groove reinforcement and repair.
2) basal plane cleaning and wetting：Bulk materials are removed, water retting basal plane is used, water saturates concrete is allowed then
Remove the bright water on surface；
3) in groove and along one layer of XYPEX " concentrating agents " mortar of painting at the two sides 150mm wide of notch；
4) XYPEX " concentrating agents " mortar half-dried dough is used during joint filling again：" U " type groove treatment, when mortar is applied
Layer about ten minutes, but still when having adherence, groove and table are filled up with XYPEX " concentrating agents " half-dried dough
Face is concordant；The surface of wet joint filling is spilt with water, one XYPEX " concentrating agents " is then applied again on the region repaired
Mortar.
8. technique according to claim 1, it is characterised in that the technique is comprised the following steps：
XYPEX " concentrating agents " dry powder, consumption 0.8kg/ ㎡, crannied position XYPEX are spread on the surface of basic unit
" concentrating agents " consumption increases consumption about 3~4.5kg/ linear meter(lin.m.)s along seam and neat seam both sides；
XYPEX " concentrating agents " dry powder is spread, casting concrete bed course in 30 minutes, concrete must vibration compacting；
1) two-way concrete slabs of colligation ∮ 6,100 × 100mm of spacing, bottom protective layer thickness 15mm.
2) it is dry to spread XYPEX " concentrating agents " powder；
3) during pouring reinforcement concrete, every 20m or so sets a construction joint, and regular control concrete shrinkage occurs to exist
At construction joint, to avoid the occurrence of irregular crack；Processed again after concrete shrinkage is basicly stable；
4) C20 pea gravel concrete bed courses are poured, rub concora crush with the hands with wooden float is twisted into thick pitted skin in fact, and intensity reaches design 70%
Next procedure can be carried out afterwards.