CN106928519A - A kind of soft fishing bait of emulation - Google Patents
A kind of soft fishing bait of emulation Download PDFInfo
- Publication number
- CN106928519A CN106928519A CN201710165260.8A CN201710165260A CN106928519A CN 106928519 A CN106928519 A CN 106928519A CN 201710165260 A CN201710165260 A CN 201710165260A CN 106928519 A CN106928519 A CN 106928519A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- emulation
- bait
- fishing bait
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of soft fishing bait of emulation, is related to bait processing and fabricating technical field, it is characterised in that：It is made up of the material of following weight portion, 36 40 parts of junked tire, 58 parts of waste ceramic powder, 9 12 parts of Universal carbon black, 13 parts of stearic acid, 14 parts of zinc oxide, 25 parts of age resistor, 25 parts of PETO, 0.5 1.5 parts of 12 part, nanometer Tea Polyphenols of molybdenum trioxide.The inventive method is reasonable, easy to operate, work well.
Description
Technical field
The present invention relates to bait processing and fabricating technical field, and in particular to a kind of soft fishing bait of emulation.
Background technology
The food that bait, i.e. fish are eaten.It is the food for luring fish to rise to the bait when fishing, further says, is the energy in fishing
Enough play poly- fish effect or being capable of all materials that can be used for rising to the bait of attracting.Be also it is essential as thing.By luring
Fish principle point, bait can be divided into true bait and false bait.
So-called true bait, is the common name of the edible animal and plant bait of fish, is mainly lured by causing the appetite of fish
Fish.False bait is also referred to as simulation bait or plug, is the small of the similar small fish, shrimp and the insects that are made with plastics, metal or other materials
Device.When fishing, by the operation of fisher, it is allowed to be similar to natural being in water, lures that the fish of ferociousness rise to the bait into.
And the species of false bait is more and more in present fishery, due to now with river, Jiang Li, in the pool, in the sea, in small stream
Etc. various place fishing, water quality also can be each different, is so accomplished by carrying out bait different processing and treatment, but not
What is become is the bait corrosion-resistant, waterproof of needs, so its usage cycles ability president, life-span ability president, thus more conforms to disappear
The psychology that expense person uses.
The content of the invention
The technical problems to be solved by the invention be overcome existing technological deficiency provide a kind of method rationally, operation side
A kind of soft fishing bait of the emulation for just, working well.
The technical problems to be solved by the invention are realized using following technical scheme：
A kind of soft fishing bait of emulation, it is characterised in that：It is made up of the material of following weight portion,
Junked tire 36-40 parts, 5-8 parts of waste ceramic powder, Universal carbon black 9-12 parts, stearic acid 1-3 parts, zinc oxide 1-
4 parts, age resistor 2-5 parts, PETO 2-5 parts, molybdenum trioxide 1-2 parts, 0.5-1.5 parts of nanometer Tea Polyphenols；
Including following preparation process,
Junked tire is ground into graininess by I with by disintegrating apparatus, removes the other impurities in addition to rubber, is then led to again
Cross smelting furnace and be fused into rubber liquid；
II is put into 62-70 DEG C of bucket rubber liquid, is then sequentially placed into remaining material, and one is put at intervals of two minutes
Kind, stirred when being put into；
III continues to stir 15-20 minutes after material is all put into, and stands 5 minutes Temperature falls, is subsequently adding material total
The dilute hydrochloric acid solution of the 1/13 of weight, continues to stir 10-15 minutes；
Material after stirring is stood 16-20 hour by IV in the place of ventilation, is then placed in machine-shaping in mould.
Beneficial effects of the present invention are：I material cost is not high, and cost of manufacture is not also high；
II preparation method is simple, easy to operate；
III toughness of material is good, and waterproof, Corrosion Protection are good；
IV PETO has that greasy property, viscosity index (VI) be high, flame resistance is good, and biological degradation rate is up to more than 90%
With good surface filming；Molybdenum trioxide fusing point is high, water insoluble；Nanometer Tea Polyphenols heat resistance, acid resistance are very good.
Specific embodiment
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, enter below
One step illustrates the present invention.
Embodiment 1
A kind of soft fishing bait of emulation, it is characterised in that：It is made up of the material of following weight portion,
Junked tire 36-40 parts, 5-8 parts of waste ceramic powder, Universal carbon black 9-12 parts, stearic acid 1-3 parts, zinc oxide 1-
4 parts, age resistor 2-5 parts, PETO 2-5 parts, molybdenum trioxide 1-2 parts, 0.5-1.5 parts of nanometer Tea Polyphenols；
Including following preparation process,
Junked tire is ground into graininess by I with by disintegrating apparatus, removes the other impurities in addition to rubber, is then led to again
Cross smelting furnace and be fused into rubber liquid；
II is put into 62-70 DEG C of bucket rubber liquid, is then sequentially placed into remaining material, and one is put at intervals of two minutes
Kind, stirred when being put into；
III continues to stir 15-20 minutes after material is all put into, and stands 5 minutes Temperature falls, is subsequently adding material total
The dilute hydrochloric acid solution of the 1/13 of weight, continues to stir 10-15 minutes；
Material after stirring is stood 16-20 hour by IV in the place of ventilation, is then placed in machine-shaping in mould.
Embodiment 2
A kind of soft fishing bait of emulation, it is characterised in that：It is made up of the material of following weight portion,
40 parts of junked tire, 7 parts of waste ceramic powder, 11 parts of Universal carbon black, 1 part of stearic acid, 2 parts of zinc oxide, age resistor 3
Part, 4 parts of PETO, 0.8 part of 1 part, nanometer Tea Polyphenols of molybdenum trioxide；
Including following preparation process,
Junked tire is ground into graininess by I with by disintegrating apparatus, removes the other impurities in addition to rubber, is then led to again
Cross smelting furnace and be fused into rubber liquid；
II is put into 63 DEG C of bucket rubber liquid, is then sequentially placed into remaining material, and one kind is put at intervals of two minutes,
Stirred when being put into；
III continues to stir 18 minutes after material is all put into, and stands 5 minutes Temperature falls, is subsequently adding material gross weight
1/13 dilute hydrochloric acid solution, continue stir 11 minutes；
Material after stirring is stood 18 hours by IV in the place of ventilation, is then placed in machine-shaping in mould.
Embodiment 3
A kind of soft fishing bait of emulation, it is characterised in that：It is made up of the material of following weight portion,
38 parts of junked tire, 6 parts of waste ceramic powder, 9 parts of Universal carbon black, 2 parts of stearic acid, 2 parts of zinc oxide, age resistor 4
Part, 3 parts of PETO, 0.1.1 parts of 1 part, nanometer Tea Polyphenols of molybdenum trioxide；
Including following preparation process,
Junked tire is ground into graininess by I with by disintegrating apparatus, removes the other impurities in addition to rubber, is then led to again
Cross smelting furnace and be fused into rubber liquid；
II is put into 62 DEG C of bucket rubber liquid, is then sequentially placed into remaining material, and one kind is put at intervals of two minutes,
Stirred when being put into；
III continues to stir 20 minutes after material is all put into, and stands 5 minutes Temperature falls, is subsequently adding material gross weight
1/13 dilute hydrochloric acid solution, continue stir 15 minutes；
Material after stirring is stood 17 hours by IV in the place of ventilation, is then placed in machine-shaping in mould.
Comparative example
A kind of soft fishing bait of emulation, it is characterised in that：It is made up of the material of following weight portion,
Junked tire 36-40 parts, 5-8 parts of waste ceramic powder, Universal carbon black 9-12 parts, stearic acid 1-3 parts, zinc oxide 1-
4 parts, age resistor 2-5 parts；
Including following preparation process,
Junked tire is ground into graininess by I with by disintegrating apparatus, removes the other impurities in addition to rubber, is then led to again
Cross smelting furnace and be fused into rubber liquid；
II is put into 62-70 DEG C of bucket rubber liquid, is then sequentially placed into remaining material, and one is put at intervals of two minutes
Kind, stirred when being put into；
III continues to stir 15-20 minutes after material is all put into, and stands 5 minutes Temperature falls, is subsequently adding material total
The dilute hydrochloric acid solution of the 1/13 of weight, continues to stir 10-15 minutes；
Material after stirring is stood 16-20 hour by IV in the place of ventilation, is then placed in machine-shaping in mould.
By the numerical value pair using the seed in embodiment of the present invention 2-3 later seed and comparative example when planting in the later stage
Than：
| Embodiment 2 | Embodiment 3 | Comparative example | |
| Water proofing property | It is excellent | It is excellent | It is good |
| Resistance to pressure | It is excellent | Excellent % | It is good |
| Anti-corrosive properties | It is excellent | It is excellent | It is good |
| Service life | 2-4 | 2-4 | 1 year -1 year half |
General principle of the invention and principal character and advantages of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not limited to the above embodiments, simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (2)
1. a kind of soft fishing bait of emulation, it is characterised in that：It is made up of the material of following weight portion,
Junked tire 36-40 parts, 5-8 parts of waste ceramic powder, Universal carbon black 9-12 parts, stearic acid 1-3 parts, zinc oxide 1-4 parts,
Age resistor 2-5 parts, PETO 2-5 parts, molybdenum trioxide 1-2 parts, 0.5-1.5 parts of nanometer Tea Polyphenols.
2. the soft fishing bait of a kind of emulation according to claim 1, it is characterised in that：Including following preparation process,
Junked tire is ground into graininess by I with by disintegrating apparatus, removes the other impurities in addition to rubber, then again by molten
Stove is fused into rubber liquid；
II is put into 62-70 DEG C of bucket rubber liquid, is then sequentially placed into remaining material, and one kind, side are put at intervals of two minutes
It is put into side stirring；
III continues to stir 15-20 minutes after material is all put into, and stands 5 minutes Temperature falls, is subsequently adding material gross weight
1/13 dilute hydrochloric acid solution, continue stir 10-15 minutes；
Material after stirring is stood 16-20 hour by IV in the place of ventilation, is then placed in machine-shaping in mould.