CN106927773A - Mining spraying wind leaking stoppage material and preparation facilities - Google Patents
Mining spraying wind leaking stoppage material and preparation facilities Download PDFInfo
- Publication number
- CN106927773A CN106927773A CN201710227402.9A CN201710227402A CN106927773A CN 106927773 A CN106927773 A CN 106927773A CN 201710227402 A CN201710227402 A CN 201710227402A CN 106927773 A CN106927773 A CN 106927773A
- Authority
- CN
- China
- Prior art keywords
- parts
- agitator
- leaking stoppage
- sodium sulfate
- wind leaking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to mining material, it is therefore an objective to provide a kind of mining spraying wind leaking stoppage material.Technical scheme is:The weight composition of material is 100 parts of water, 13~25 parts of flyash, 6~8 parts of gypsum, 20~26 parts of cement, 8~12 parts of white lime, 0.5~0.8 part of AEO, 0.4~0.8 part of HEMC, 1~2 part of lauryl sodium sulfate, 1~1.2 part of sodium sulfate of polyethenoxy ether of fatty alcohol, 1.8~2.5 parts of polyphosphoric acids, viscosity is 1.6~2 parts of the hydroxypropyl starch ether of 600~800mPas, 0.8~1.2 part of the redispersable latex powder of vinyl acetate ethylene copolymer type.Present invention process flow is simple, foams performance is excellent, is combined foaming agent reduces cost, and coefficient of foaming is high, high temperature resistant and heat-proof quality are good.Have in terms of colliery and coal-field fire ground crack closure and widely use value.
Description
Technical field
The present invention relates to a kind of mining spraying wind leaking stoppage material and preparation facilities.
Background technology
Spontaneous combustionof coal is one of Major Natural Disasters of China's coal-mine, causes great economic loss, seriously threatens coal
The safety of ore deposit personnel.Mine spontaneous combustionof coal leaks out what is caused mainly due to underground.Therefore, in order to efficiently prevent and treat mine coal certainly
Combustion, leaks out to underground and a little blocks, and reduces or prevent oxygen supply, prevents coal oxidation very crucial.In pit mining
The spontaneous combustion of coal occurs mainly in the presence of the goaf of passage of leaking out, open-off cut, stops adopting line, geological structural belt, tunnel caving place etc.
Place.Leaked out to effectively block underground coal mine, the country is frequently with grouting, gel, foamed resin, three-phase froth, expanding cement
Deng.But these methods all come with some shortcomings, thick loess grouting technology need to consume a large amount of soil, and the area of some scarce soil cannot use
And the easy seepage flow downwards of slurries, it is impossible to block crack;Ammonium salt gel discharges toxic and harmful, and colloid is easily cracked;Macromolecule
Gel high cost, wind leaking stoppage effect disappears after moisture evaporation;Three-phase froth does not have intensity, stabilization time only have 8~12 it is small
When, solidification is not implemented, once the effect that wind leaking stoppage is not had after bubble burst;Foamed resin high cost and to environment temperature requirement
Height, incendivity under hot conditions;Expanding cement sealing effectiveness is poor, it is impossible to block tiny crack.
Therefore in the prior art also without excellent performance, stable special wind leaking stoppage material.
The content of the invention
Technical problem solved by the invention is to provide based on a kind of inorganic raw material formula, easy to use, mechanical property
Can reliable mining spraying wind leaking stoppage material.
To reach above-mentioned purpose, the technical solution adopted by the present invention is:A kind of mining spraying wind leaking stoppage material, weight composition
It is 100 parts of water, 13~25 parts of flyash, 6~8 parts of gypsum, 20~26 parts of cement, 8~12 parts of white lime, aliphatic alcohol polyethenoxy
0.5~0.8 part of ether, 0.4~0.8 part of HEMC, 1~2 part of lauryl sodium sulfate, AEO
1~1.2 part of sodium sulphate, 1.8~2.5 parts of polyphosphoric acids, 1.6~2 parts of hydroxypropyl starch ether, the vinegar that viscosity is 600~800mPas
0.8~1.2 part of the redispersable latex powder of sour ethylene-vinyl copolymer type.
Preparation process is:
1):In main agitator tank add water, flyash, AEO, HEMC, gypsum, cement,
White lime, agitator is formed uniformly pulverized fuel ash slurry;
2):A small amount of water and polyphosphoric acids, hydroxypropyl starch ether, redispersable latex powder is added to stir to form mixed in agitator
Rubber alloy mucus;
3):Stirring and dissolving during lauryl sodium sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol are dissolved in into suitable quantity of water in pill tank
Form solution;
4):Above-mentioned solution and epoxy glue mucus are mixed into the pulverized fuel ash slurry of main agitator tank, agitator is with 100 ± 20 revs/min
Rotational speed, mixing time is 3~6min, is then encapsulated into spray tank, is prepared into mining spraying wind leaking stoppage material.
Accordingly, the preparation facilities of the stifled wind material of the present invention, including main agitator tank, sets agitator in main agitator tank, main
Agitator tank top sets closed gallery ports and mounting bracket, and mounting bracket is used to install the motor of agitator;Described device bag
Agitator and pill tank are included, the agitator and pill tank are located at main agitator tank top and pass through pipeline and valve and main agitator tank
Connection;Agitating paddle is set in the agitator, and agitating paddle is driven by motor.
Preferably, the main agitator tank connects vavuum pump by pipeline.
Beneficial effects of the present invention:The present invention is using AEO, HEMC as surface
Activating agent enables to pulverized fuel ash slurry solid phase particles dispersed, contributes to stable system, and contribute to aerated fluid thin
Seepage flow in rimala.Based on lauryl sodium sulfate and sodium sulfate of polyethenoxy ether of fatty alcohol, AEO, hydroxyl second
The organised surfactant systems of ylmethyl cellulose synergy can provide superior foams performance, when system material passes through
Abundance is produced by when clashing into the of short duration process for contacting with air contact during shower nozzle sprays and with mine palisades
Bubble.And will not increase bubble because dissolving in batches and stirring at low speed mixing in process.Polyphosphoric acids, hydroxypropyl form sediment
The organic gluing system that powder ether, redispersable latex powder are constituted can be provided stablizes quick glueability, can realize seepage flow
The quick leak stopping barrier for forming stabilization in 20min at ambient temperature after dispersion.The composite solid that cement, gypsum, white lime are constituted
Phase system promotes the hydration reaction of flyash so that solid matter rapid curing, foam compressive property is excellent.
In the prior art because foaming effect is poor after gypsum, cement, the increase of white lime consumption or is difficult to bubble,
Flyash large usage quantity;But flyash consumption directly results in the resistance to compression of material, the adhesive property reduction present invention by being combined bubble
With the foundation of organic system, this problem in the prior art is successfully solved.
Technological process on the whole of the invention is simple, foams performance is excellent, foaming agent reduces cost is combined, in spraying process
Enough bubbles are produced with air contact, coefficient of foaming is high, compression strength is big, high temperature resistant and heat-proof quality are good.And aerated fluid oozes
Permeability can be good, and solidification is quick, the time can suitably be adjusted by three kinds of gluing material amounts.Use rear wind leaking stoppage effect is significant, resistance
Combustion, it is antistatic.Whole cheap, low cost;Can also be right by strengthening stirring acquisition foam in the case where that cannot spray
Crack or hole leak stopping are coated afterwards, are had in terms of colliery and coal-field fire ground crack closure and are widely used value.
Brief description of the drawings
Fig. 1 is the structural representation of preparation facilities of the invention.
Specific embodiment
Mining spraying wind leaking stoppage material as shown in Figure 1 prepares special purpose device, including main agitator tank 10, in main agitator tank 10
Agitator 11 is set, and the bottom of main agitator tank 10 sets discharging opening 14 and valve, and the top of main agitator tank 10 sets closed charging
Door 13 and mounting bracket, mounting bracket are used to install the motor 12 of agitator 11;Described device includes agitator 20 and pill tank 30,
The agitator 20 and pill tank 30 are located at the top of main agitator tank 10 and are connected with main agitator tank 10 by pipeline and valve;It is described
Agitating paddle 21 is set in agitator 20, and agitating paddle 21 is driven by motor 22.The main agitator tank 10 connects vavuum pump by pipeline
40.Vacuumizing can keep vacuum state, reduce the amount for producing bubble with air contact after foaming agent is added.
Specific preparation process is illustrated with reference to above-mentioned special purpose device, so that those skilled in the art are more
Clear implementation of the invention and effect.
Embodiment one
Got the raw materials ready by following weight composition:100 parts of water, 25 parts of flyash, the gypsum 6 that the particle size range of particle is 0.5~300 μm
Part, 20 parts of 42.5R cement, 12 parts of white lime, 0.5 part of AEO, 0.8 part of HEMC, 12
2 parts of sodium alkyl sulfate, 1 part of sodium sulfate of polyethenoxy ether of fatty alcohol, 2.5 parts of polyphosphoric acids, the hydroxyl that viscosity is 600~800mPas
1.2 parts of the redispersable latex powder of 1.8 parts of propyl group starch ether, vinyl acetate-ethylene copolymer type.
Preparation process is:
1):80 parts of water and whole flyash, AEO, hydroxyethyl methyl fiber are added in main agitator tank
Element, gypsum, cement, white lime, agitator are formed uniformly pulverized fuel ash slurry, 1000 turns/min of speed of agitator;
2):Add water 15 parts in agitator and whole polyphosphoric acids, hydroxypropyl starch ether, redispersable latex powder stir shape
Into epoxy glue mucus, 200 turns/min of speed of agitator;
3):Hand operated mixing is molten during lauryl sodium sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol to be dissolved in 5 parts of water in pill tank
Solution forms solution;
4):Above-mentioned solution and epoxy glue mucus are mixed into the pulverized fuel ash slurry of main agitator tank, agitator is with 100 ± 20 revs/min
Rotational speed, mixing time is 6min, is then encapsulated into spray tank, is prepared into mining spraying wind leaking stoppage material.
Embodiment two
Got the raw materials ready by following weight composition:100 parts of water, 15 parts of flyash, the gypsum 6 that the particle size range of particle is 0.5~300 μm
Part, 25 parts of 42.5R cement, 10 parts of white lime, 0.8 part of AEO, 0.5 part of HEMC, 12
1.2 parts of sodium alkyl sulfate, 1 part of sodium sulfate of polyethenoxy ether of fatty alcohol, 2.5 parts of polyphosphoric acids, viscosity are 600~800mPas's
1 part of the redispersable latex powder of 1.6 parts of hydroxypropyl starch ether, vinyl acetate-ethylene copolymer type.
Preparation process is:
1):80 parts of water and whole flyash, AEO, hydroxyethyl methyl fiber are added in main agitator tank
Element, gypsum, cement, white lime, agitator are formed uniformly pulverized fuel ash slurry, 1000 turns/min of speed of agitator;
2):Add water 15 parts in agitator and whole polyphosphoric acids, hydroxypropyl starch ether, redispersable latex powder stir shape
Into epoxy glue mucus, 300 turns/min of speed of agitator;
3):Stirring and dissolving shape during lauryl sodium sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol to be dissolved in 5 parts of water in pill tank
Into solution;
4):Above-mentioned solution and epoxy glue mucus are mixed into the pulverized fuel ash slurry of main agitator tank, agitator is with 100 ± 20 revs/min
Rotational speed, mixing time is 5min, is then encapsulated into spray tank, is prepared into mining spraying wind leaking stoppage material.
Embodiment three
Got the raw materials ready by following weight composition:100 parts of water, 20 parts of flyash, the gypsum 8 that the particle size range of particle is 0.5~300 μm
Part, 25 parts of 42.5R cement, 10 parts of white lime, 0.8 part of AEO, 0.7 part of HEMC, 12
1.5 parts of sodium alkyl sulfate, 1 part of sodium sulfate of polyethenoxy ether of fatty alcohol, 2 parts of polyphosphoric acids, the hydroxyl that viscosity is 600~800mPas
1.2 parts of the redispersable latex powder of 1.6 parts of propyl group starch ether, vinyl acetate-ethylene copolymer type.
Preparation process is:
1):82 parts of water and whole flyash, AEO, hydroxyethyl methyl fiber are added in main agitator tank
Element, gypsum, cement, white lime, agitator are formed uniformly pulverized fuel ash slurry, 1000 turns/min of speed of agitator;
2):Add water 12 parts in agitator and whole polyphosphoric acids, hydroxypropyl starch ether, redispersable latex powder stir shape
Into epoxy glue mucus, 400 turns/min of speed of agitator;
3):Stirring and dissolving shape during lauryl sodium sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol to be dissolved in 6 parts of water in pill tank
Into solution;
4):Above-mentioned solution and epoxy glue mucus are mixed into the pulverized fuel ash slurry of main agitator tank, agitator is with 100 ± 20 revs/min
Rotational speed, mixing time is 5min, is then encapsulated into spray tank, is prepared into mining spraying wind leaking stoppage material.
Example IV
Got the raw materials ready by following weight composition:100 parts of water, 25 parts of flyash, the gypsum 8 that the particle size range of particle is 0.5~300 μm
Part, 20 parts of 42.5R cement, 8 parts of white lime, 0.8 part of AEO, 0.6 part of HEMC, dodecane
1.5 parts of base sodium sulphate, 1 part of sodium sulfate of polyethenoxy ether of fatty alcohol, 2.0 parts of polyphosphoric acids, the hydroxyl that viscosity is 600~800mPas
1 part of the redispersable latex powder of 1.8 parts of propyl group starch ether, vinyl acetate-ethylene copolymer type.
Preparation process is:
1):82 parts of water and whole flyash, AEO, hydroxyethyl methyl fiber are added in main agitator tank
Element, gypsum, cement, white lime, agitator are formed uniformly pulverized fuel ash slurry, 1000 turns/min of speed of agitator;
2):Add water 12 parts in agitator and whole polyphosphoric acids, hydroxypropyl starch ether, redispersable latex powder stir shape
Into epoxy glue mucus, 200 turns/min of speed of agitator;
3):Stirring and dissolving shape during lauryl sodium sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol to be dissolved in 6 parts of water in pill tank
Into solution;
4):Above-mentioned solution and epoxy glue mucus are mixed into the pulverized fuel ash slurry of main agitator tank, agitator is with 100 ± 20 revs/min
Rotational speed, mixing time is 3min, is then encapsulated into spray tank, is prepared into mining spraying wind leaking stoppage material.
The material use high-pressure pump and shower nozzle of aforementioned four embodiment are ejected into the box-shaped mould of 300*300*300mm respectively
It is interior, flat surface is scraped after spray is full, it is achieved in that identical volume and height.Then firm time is observed and records, and it is small in hardening 2
When after take apart mould then conserve 5 days, each full of bubble foam-like wind leaking stoppage material top surface place identical weight, inspection
Survey bearing capacity.It was observed that being recorded most when square wind leaking stoppage material naked eyes visible damage or high deformation occurs more than 5mm
Big bearing capacity.The testing result of four embodiments is as shown in the table:
From said structure, stifled wind material bearing capacity of the invention, it is also possible to which it is that compression strength reaches to be approximately considered, while
The tensile bond strength of four embodiments reaches the national building material industry C1 grades of standard of 0.5MP, superior performance.Material dry weight without
Machine component reaches more than 90%, non-ignitable not decompose, and meets fire resistance rating A grades of standard, and need not add fire retardant.
Claims (9)
1. a kind of mining spraying wind leaking stoppage material, it is characterised in that:Mining spraying wind leaking stoppage material weight composition is water 100
Part, 13~25 parts of flyash, 6~8 parts of gypsum, 20~26 parts of cement, 8~12 parts of white lime, AEO 0.5~
0.8 part, 0.4~0.8 part of HEMC, 1~2 part of lauryl sodium sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol 1
~1.2 parts, 1.8~2.5 parts of polyphosphoric acids, 1.6~2 parts of the hydroxypropyl starch ether that viscosity is 600~800mPas, vinyl acetate-
0.8~1.2 part of the redispersable latex powder of ethylene copolymer species.
2. mining spraying wind leaking stoppage material according to claim 1, it is characterised in that:Preparation process is:
1):In main agitator tank add water, flyash, AEO, HEMC, gypsum, cement,
White lime, agitator is formed uniformly pulverized fuel ash slurry;
2):A small amount of water and polyphosphoric acids, hydroxypropyl starch ether, redispersable latex powder is added to stir to form mixed in agitator
Rubber alloy mucus;
3):Stirring and dissolving during lauryl sodium sulfate, sodium sulfate of polyethenoxy ether of fatty alcohol are dissolved in into suitable quantity of water in pill tank
Form solution;
4):Above-mentioned solution and epoxy glue mucus are mixed into the pulverized fuel ash slurry of main agitator tank, agitator is with 100 ± 20 revs/min
Rotational speed, mixing time is 3~6min, is then encapsulated into spray tank, is prepared into mining spraying wind leaking stoppage material.
3. mining spraying wind leaking stoppage material according to claim 2, it is characterised in that:Described step 4)In vacuum condition
Under carry out.
4. mining spraying wind leaking stoppage material according to claim 1, it is characterised in that:The weight is constituted:Water 100
Part, 15 parts of flyash, 6 parts of gypsum, 25 parts of 42.5R cement, 10 parts of white lime, 0.8 part of AEO, ethoxy first
It is 0.5 part of base cellulose, 1.2 parts of lauryl sodium sulfate, 1 part of sodium sulfate of polyethenoxy ether of fatty alcohol, 2.5 parts of polyphosphoric acids, viscous
Spend 1.6 parts of hydroxypropyl starch ether, the redispersable latex powder 1 of vinyl acetate-ethylene copolymer type for 600~800mPas
Part.
5. mining spraying wind leaking stoppage material according to claim 1, it is characterised in that:The weight is constituted:Water 100
Part, 25 parts of flyash, 8 parts of gypsum, 20 parts of 42.5R cement, 8 parts of white lime, 0.8 part of AEO, ethoxy first
It is 0.6 part of base cellulose, 1.5 parts of lauryl sodium sulfate, 1 part of sodium sulfate of polyethenoxy ether of fatty alcohol, 2.0 parts of polyphosphoric acids, viscous
Spend 1.8 parts of hydroxypropyl starch ether, the redispersable latex powder 1 of vinyl acetate-ethylene copolymer type for 600~800mPas
Part.
6. mining spraying wind leaking stoppage material according to claim 1, it is characterised in that:Described step 1)Water consumption is 80
Part, step 2)Water consumption is 12~15 parts.
7. step 3)Water consumption is 5~6 parts.
8. mining spraying wind leaking stoppage material according to claim 2, it is characterised in that:The preparation process utilizes special dress
Putting is carried out, and special purpose device includes setting agitator in main agitator tank, main agitator tank, and main agitator tank top sets closed charging
Door and mounting bracket, mounting bracket are used to install the motor of agitator;Described device includes agitator and pill tank, the agitator
Main agitator tank top is located at pill tank and be connected with main agitator tank by pipeline and valve;Stirring is set in the agitator
Oar, agitating paddle is driven by motor.
9. mining spraying wind leaking stoppage material according to claim 7, it is characterised in that:The main agitator tank is connected by pipeline
Connect vavuum pump.