CN106926528A - Nanometer steel thermal insulation tile, its manufacturing line and its manufacture method - Google Patents
Nanometer steel thermal insulation tile, its manufacturing line and its manufacture method Download PDFInfo
- Publication number
- CN106926528A CN106926528A CN201710101810.XA CN201710101810A CN106926528A CN 106926528 A CN106926528 A CN 106926528A CN 201710101810 A CN201710101810 A CN 201710101810A CN 106926528 A CN106926528 A CN 106926528A
- Authority
- CN
- China
- Prior art keywords
- nanometer
- zinc
- steel
- nano
- glued membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention discloses a kind of nanometer steel thermal insulation tile, its manufacturing line and its manufacture method, the thermal insulation tile includes the nano-silicon glued membrane with the zinc-plated color steel of anti-rust action, transparent thermal resistance and sound insulation, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polymer compound film and based on sheet material galvanized aluminium board, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are fitted on galvanized aluminium board successively from inside to outside；Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate pad pasting production line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is polymer compound film.Shine upon down, the Nanometer gallium oxide film intercepts more than 90% ultraviolet and infrared ray, the nano-silicon glued membrane intercepts less than 10% after-heat and plays deadening.
Description
Technical field
The present invention relates to the technical field of building materials, more particularly to a kind of nanometer steel thermal insulation tile, its manufacturing line and its system
Make method.
Background technology
At present, galvanized iron micromicrowatt, sandwich color steel tile, plastic made tile, cement asbestos shingle product are used steel building watt material more
Come sun of realizing becalming, keep away, the purpose kept off the rain, however these products in process of production both not environmentally, highly energy-consuming, in practical function
Also it is barely satisfactory（Time one is grown, and 2-3 will leak because getting rusty, seep water）Effect of heat insulation is little.With the development in epoch, ring
The enhancing of consciousness is protected, people are to office, inhabitation, Leisure Environment comfort level requirement more and more higher, and the requirement to life security is more next
More pay attention to, the protective awareness to environment is strengthening, galvanized iron micromicrowatt, sandwich color steel tile with regard to current extensive utilization, plastic made tile, water
Mud asbestos shingle product has been increasingly difficult to meet the demand of present situation, therefore, invent a kind of new nanometer steel thermal insulation tile and carry out generation
There is the practical value and depth of energy-saving and emission-reduction for traditional galvanized iron micromicrowatt, sandwich color steel tile, plastic made tile, cement asbestos shingle product
Remote meaning.
The content of the invention
For weak point present in above-mentioned technology, the present invention provides a kind of can not only having keeped out wind and rain and keeps away sun but also can be every
Nanometer steel thermal insulation tile, its manufacturing line and its manufacture method that recuperation of heat is recycled.
A kind of in order to achieve the above object, nanometer steel thermal insulation tile of the invention, including the zinc-plated color steel with anti-rust action,
The nano-silicon glued membrane of transparent thermal resistance and sound insulation, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polymer compound film and
Based on sheet material galvanized aluminium board, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film
It is fitted on galvanized aluminium board successively from inside to outside；Shine upon down, the Nanometer gallium oxide film intercept more than 90% ultraviolet and
Infrared ray, the nano-silicon glued membrane intercepts less than 10% after-heat and plays deadening；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in the production of coiled steel plate pad pasting
Line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer multiple for macromolecule
Close film；Then after the temperature of heated oven being warmed into 200 DEG C -220 DEG C, above-mentioned four tunic is combined using up-down roller pressurization
It is pasted onto on galvanized aluminium board；The galvanized aluminium board that will be pasted again delivers into cooler, is rapidly cooled down sheet material using air-cooled, uses
Collecting machine is wound into coiled strip；Finally the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added, is suppressed
Tile shape.
Wherein, the dual coating of the nano-silicon glued membrane has UV glue, and on the UV glue outer surface on nano-silicon glued membrane two sides
It is pasted with one layer of PC film.
Wherein, the dual coating of the Nanometer gallium oxide film has UV glue, and in the UV glue outer surface on nano-silicon glued membrane two sides
On be pasted with one layer of PC film.
Wherein, the zinc-plated color steel is zinc-plated every square metre more than 70 grams of steel plate coiled material.
Wherein, the polymer compound film uses polyamide film coiled strip.
The invention also discloses a kind of nanometer of preparation method of steel thermal insulation tile, comprise the following steps that：
S1, zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate pad pasting life
Producing line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is macromolecule
Composite membrane；
S2, the temperature of heated oven is warmed to 200 DEG C -220 DEG C after, using up-down roller pressurization will above-mentioned four tunic be compound glues
It is attached on galvanized aluminium board；
S3, the galvanized aluminium board that will be pasted deliver into cooler, are rapidly cooled down sheet material using air-cooled, are then received with collecting machine
It is rolled into coiled strip；
S4, the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added, suppress tile shape.
Wherein, the thickness of the zinc-plated color steel for being used in S1 is 0.3-2.0mm, and the thickness of nano-silicon glued membrane is 0.2-
10mm, the thickness of Nanometer gallium oxide film is 0.05-0.2mm, and the thickness of polymer compound film is 30-200mm.
Wherein, the mode of heating is in S2：During traveling, added rapidly using high frequency mode in the way of transmitting
Heat.
The invention also discloses a kind of nanometer of making production line of steel thermal insulation tile, including feeding machine, charger, heating baking
Case, the first rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and collecting machine, the feeding machine, charging
Machine, heated oven, the first rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and collecting machine are from front to back
It is sequentially arranged connection；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and galvanized aluminium board are placed in feeding machine
On；Starting device, using charger by zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and plating
Four kinds of membrane material feeding heated ovens of zinc-aluminium plate；Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and macromolecule are combined
Film is warmed to 200 DEG C -220 DEG C；Material is corrected using the first rectification machine in traveling process, prevent deflection after wind it is uneven；Profit
Pressurizeed with the up-down roller of make-up machine and four kinds of membrane materials are fitted on galvanized aluminium board；The sheet material of assembly is placed in cooling conveying
Platform；Sheet material is placed in cooler area using air-cooled reduction waste heat by cooling transport platform；The second rectification machine is continuing with by material again
Correct；The nanometer steel board fitted completely is wound into coiled material；As requested using the tile press of various standards, sheet material is suppressed
Into variously-shaped nanometer steel thermal insulation tile.
The beneficial effects of the invention are as follows：
Compared with prior art, nanometer steel thermal insulation tile of the invention, by zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film
And polymer compound film is placed in coiled steel plate pad pasting production line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, the
Three layers is Nanometer gallium oxide film, and the 4th layer is polymer compound film；In the case where shining upon, Nanometer gallium oxide film is effectively intercepted and is up to
More than 90% ultraviolet and infrared ray, the excellent heat-proof quality of nano-silicon glued membrane effectively intercepts 10% sunlight irradiation delayed heat
Amount, the soft material of nano-silicon glued membrane can also play a part of sound insulation, so as to realize excellent heat-insulated, sound insulation, antirust, anti-
Leakage, corrosion-resistant effect, product structure are simple, and substantially, environmental protection and energy saving are cheap for manufacturing cost for heat-insulated, sound insulation, antirust, leak preventing effect,
Save resources.The preparation technology flow is simple, require that equipment is low and workable.
Brief description of the drawings
Fig. 1 is the flow chart of the preparation method of nanometer steel thermal insulation tile of the present invention；
Fig. 2 is the making production line schematic diagram of nanometer steel thermal insulation tile of the present invention.
Main element symbol description is as follows：
10th, feeding machine 11, charger
12nd, heated oven 13, the first rectification machine
14th, make-up machine 15, cooling transport platform
16th, cooler 17, the second rectification machine
18th, collecting machine.
Specific embodiment
In order to more clearly state the present invention, the present invention is further described below in conjunction with the accompanying drawings.
A kind of nanometer steel thermal insulation tile of the present invention, including the zinc-plated color steel with anti-rust action, transparent thermal resistance and sound insulation
Nano-silicon glued membrane, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polymer compound film and based on sheet material plating
Zinc-aluminium plate, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are fitted successively from inside to outside
On galvanized aluminium board；Shine upon down, the Nanometer gallium oxide film intercepts more than 90% ultraviolet and infrared ray, the nanometer
Pellosil intercepts less than 10% after-heat and plays deadening；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in the production of coiled steel plate pad pasting
Line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer multiple for macromolecule
Close film；Then after the temperature of heated oven 12 being warmed into 200 DEG C -220 DEG C, above-mentioned four tunic is answered using up-down roller pressurization
Conjunction is pasted onto on galvanized aluminium board；The galvanized aluminium board that will be pasted again delivers into cooler 16, using air-cooled rapid that sheet material is cold
But, it is wound into coiled strip with collecting machine 18；Finally the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added
On, suppress tile shape.
In the present embodiment, the thickness of the nano-silicon glued membrane is 0.2-10mm, and its dual coating has UV glue, and is receiving
One layer of PC film is pasted with the UV glue outer surface on rice pellosil two sides.
In the present embodiment, the thickness of the Nanometer gallium oxide film is 0.05-0.2mm, and its dual coating has UV glue, and
One layer of PC film is pasted with the UV glue outer surface on nano-silicon glued membrane two sides.
In the present embodiment, the thickness of the zinc-plated color steel is 0.3-2.0mm, and zinc-plated color steel is zinc-plated every square metre
More than 70 grams of steel plate coiled material.
In the present embodiment, the thickness of the polymer compound film is 30-200mm, and it uses polyamide film coiled strip.
The standard that so materials are combined is based on Nanometer gallium oxide film and effectively intercepts up to more than 90% ultraviolet and infrared
Line, the excellent heat-proof quality of nano-silicon glued membrane effectively intercepts 10% sunlight irradiation after-heat, the soft material of nano-silicon glued membrane
Matter can also play a part of sound insulation, so as to realize excellent heat-insulated, sound insulation, antirust, leakproof, corrosion-resistant effect, product structure
Simply, substantially, environmental protection and energy saving are cheap for manufacturing cost, save resources for heat-insulated, sound insulation, antirust, leak preventing effect.
Summer tests：Compared with traditional galvanized iron micromicrowatt more than 26-45 DEG C of the top layer temperature difference, on year-on-year basis room temperature differ 10 DEG C with
On.This product has already been through " national building materials test center " detection, A grades of standard has been reached, with " National Fire building materials matter
Amount Supervision Test Center " detection, has reached A1 grades of examination criteria.
Fig. 1 is referred to, the invention also discloses a kind of nanometer of preparation method of steel thermal insulation tile, is comprised the following steps that：
S1, zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate pad pasting life
Producing line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is macromolecule
Composite membrane；
S2, during traveling, the temperature of heated oven 12 is warmed to 200 using high frequency mode is rapid in the way of transmitting
After DEG C -220 DEG C, it is pasted onto above-mentioned four tunic is compound on galvanized aluminium board using up-down roller pressurization；
S3, the galvanized aluminium board that will be pasted deliver into cooler 16, are rapidly cooled down sheet material using air-cooled, then use collecting machine
18 are wound into coiled strip；
S4, the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added, suppress tile shape.
In the present embodiment, the thickness of the zinc-plated color steel for being used in S1 is 0.3-2.0mm, the thickness of nano-silicon glued membrane
It is 0.2-10mm to spend, and the thickness of Nanometer gallium oxide film is 0.05-0.2mm, and the thickness of polymer compound film is 30-200mm.
Fig. 2 is further regarded to, the invention also discloses a kind of nanometer of making production line of steel thermal insulation tile, including feeding machine
10th, charger 11, heated oven 12, the first rectification machine 13, make-up machine 14, cooling transport platform 15, cooler 16, the second rectification machine
17 and collecting machine 18, feeding machine 10, charger 11, heated oven 12, the first rectification machine 13, make-up machine 14, cooling transport platform
15th, cooler 16, the second rectification machine 17 and collecting machine 18 are sequentially arranged connection from front to back；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and galvanized aluminium board are placed in feeding machine 10
On；Starting device, using charger 11 by zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and
Four kinds of membrane material feeding heated ovens 12 of galvanized aluminium board；By zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and macromolecule
Composite membrane is warmed to 200 DEG C -220 DEG C；Material is corrected using the first rectification machine 13 in traveling process, is wound not after preventing deflection
Together；Four kinds of membrane materials are fitted on galvanized aluminium board using the up-down roller pressurization of make-up machine 14；The sheet material of assembly is placed in
Cooling transport platform 15；Sheet material is placed in the area of cooler 16 using air-cooled reduction waste heat by cooling transport platform 15；Second is continuing with to entangle
Inclined machine 17 corrects material again；The nanometer steel board fitted completely is wound into coiled material；As requested using various standards
Tile press, variously-shaped nanometer steel thermal insulation tile is pressed into by sheet material.
Disclosed above is only several specific embodiments of the invention, but the present invention is not limited to this, any ability
What the technical staff in domain can think change should all fall into protection scope of the present invention.
Claims (9)
1. a kind of nanometer steel thermal insulation tile, it is characterised in that including the zinc-plated color steel with anti-rust action, transparent thermal resistance and sound insulation
Nano-silicon glued membrane, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polymer compound film and based on sheet material
Galvanized aluminium board, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are pasted successively from inside to outside
Close on galvanized aluminium board；Shine upon down, the Nanometer gallium oxide film intercepts more than 90% ultraviolet and infrared ray, described to receive
Rice pellosil intercepts less than 10% after-heat and plays deadening；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in the production of coiled steel plate pad pasting
Line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer multiple for macromolecule
Close film；Then after the temperature of heated oven being warmed into 200 DEG C -220 DEG C, above-mentioned four tunic is combined using up-down roller pressurization
It is pasted onto on galvanized aluminium board；The galvanized aluminium board that will be pasted again delivers into cooler, is rapidly cooled down sheet material using air-cooled, uses
Collecting machine is wound into coiled strip；Finally the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added, is suppressed
Tile shape.
2. according to claim 1 nanometer of steel thermal insulation tile, it is characterised in that the dual coating of the nano-silicon glued membrane has UV
Glue, and it is pasted with one layer of PC film on the UV glue outer surface on nano-silicon glued membrane two sides.
3. according to claim 1 nanometer of steel thermal insulation tile, it is characterised in that the dual coating of the Nanometer gallium oxide film has
UV glue, and it is pasted with one layer of PC film on the UV glue outer surface on nano-silicon glued membrane two sides.
4. according to claim 1 nanometer of steel thermal insulation tile, it is characterised in that the zinc-plated color steel is zinc-plated every square metre
More than 70 grams of steel plate coiled material.
5. according to claim 1 nanometer of steel thermal insulation tile, it is characterised in that the polymer compound film is thin using polyamide
Film roll material.
6. a kind of nanometer of preparation method of steel thermal insulation tile, it is characterised in that comprise the following steps that：
S1, zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate pad pasting life
Producing line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is macromolecule
Composite membrane；
S2, the temperature of heated oven is warmed to 200 DEG C -220 DEG C after, using up-down roller pressurization will above-mentioned four tunic be compound glues
It is attached on galvanized aluminium board；
S3, the galvanized aluminium board that will be pasted deliver into cooler, are rapidly cooled down sheet material using air-cooled, are then received with collecting machine
It is rolled into coiled strip；
S4, the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added, suppress tile shape.
7. the according to claim 6 nanometer of preparation method of steel thermal insulation tile, it is characterised in that what is used in S1 is zinc-plated
The thickness of color steel is 0.3-2.0mm, and the thickness of nano-silicon glued membrane is 0.2-10mm, and the thickness of Nanometer gallium oxide film is 0.05-
0.2mm, the thickness of polymer compound film is 30-200mm.
8. the according to claim 6 nanometer of preparation method of steel thermal insulation tile, it is characterised in that the mode heated in S2
For：During traveling, heated rapidly using high frequency mode in the way of transmitting.
9. a kind of nanometer of making production line of steel thermal insulation tile, it is characterised in that including feeding machine, charger, heated oven, first
Rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and collecting machine, the feeding machine, charger, heating are dried
Case, the first rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and the collecting machine company of being sequentially arranged from front to back
Connect；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and galvanized aluminium board are placed in feeding machine
On；Starting device, using charger by zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and plating
Four kinds of membrane material feeding heated ovens of zinc-aluminium plate；Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and macromolecule are combined
Film is warmed to 200 DEG C -220 DEG C；Material is corrected using the first rectification machine in traveling process, prevent deflection after wind it is uneven；Profit
Pressurizeed with the up-down roller of make-up machine and four kinds of membrane materials are fitted on galvanized aluminium board；The sheet material of assembly is placed in cooling conveying
Platform；Sheet material is placed in cooler area using air-cooled reduction waste heat by cooling transport platform；The second rectification machine is continuing with by material again
Correct；The nanometer steel board fitted completely is wound into coiled material；As requested using the tile press of various standards, sheet material is suppressed
Into variously-shaped nanometer steel thermal insulation tile.