CN106926528B - Nanometer steel thermal insulation tile, its manufacturing line and its manufacture method - Google Patents
Nanometer steel thermal insulation tile, its manufacturing line and its manufacture method Download PDFInfo
- Publication number
- CN106926528B CN106926528B CN201710101810.XA CN201710101810A CN106926528B CN 106926528 B CN106926528 B CN 106926528B CN 201710101810 A CN201710101810 A CN 201710101810A CN 106926528 B CN106926528 B CN 106926528B
- Authority
- CN
- China
- Prior art keywords
- nanometer
- nano
- steel
- zinc
- glued membrane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of nanometer steel thermal insulation tile, its manufacturing line and its manufacture method, the thermal insulation tile include with the zinc-plated color steel of anti-rust action, transparent thermal resistance and the nano-silicon glued membrane of sound insulation, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polymer compound film and based on sheet material galvanized aluminium board, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are fitted on galvanized aluminium board successively from inside to outside；Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate pad pasting production line, bottom is zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is polymer compound film.Shine upon down, the Nanometer gallium oxide film obstructs more than 90% ultraviolet and infrared ray, and the nano-silicon glued membrane obstructs less than 10% after-heat and plays deadening.
Description
Technical field
The present invention relates to the technical field of building materials, more particularly to a kind of nanometer steel thermal insulation tile, its manufacturing line and its system
Make method.
Background technology
At present, steel building watt material is more using galvanized iron micromicrowatt, sandwich color steel tile, plastic made tile, cement asbestos shingle product
Becalm to realize, keep away sun, the purpose kept off the rain, however these products in process of production both not environmentally, highly energy-consuming, in practical function
Also it is barely satisfactory（Time one is grown, and 2-3 will leak because getting rusty, seep water）Effect of heat insulation is little.With the development in epoch, ring
The enhancing of consciousness is protected, for people to handling official business, living, Leisure Environment comfort level requirement more and more higher, the requirement to life security is more next
More pay attention to, the protective awareness of environment is being strengthened, with regard to the galvanized iron micromicrowatt of current extensive utilization, sandwich color steel tile, plastic made tile, water
Mud asbestos shingle product has been increasingly difficult to meet the needs of present situation, therefore, is invented a kind of new nanometer steel thermal insulation tile and is carried out generation
There is the practical value and depth of energy-saving and emission-reduction for traditional galvanized iron micromicrowatt, sandwich color steel tile, plastic made tile, cement asbestos shingle product
Remote meaning.
The content of the invention
For weak point present in above-mentioned technology, the present invention provides a kind of can not only keep out wind and rain and keeps away sun but also can be every
Nanometer steel thermal insulation tile, its manufacturing line and its manufacture method that recuperation of heat recycles.
In order to achieve the above object, a kind of nanometer steel thermal insulation tile of the present invention, including the zinc-plated color steel with anti-rust action,
The nano-silicon glued membrane of transparent thermal resistance and sound insulation, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polymer compound film and
Based on sheet material galvanized aluminium board, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film
It is fitted in successively on galvanized aluminium board from inside to outside；Shine upon down, the Nanometer gallium oxide film obstruct more than 90% ultraviolet and
Infrared ray, the nano-silicon glued membrane obstruct less than 10% after-heat and play deadening；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate pad pasting
Production line, bottom are zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is high score
Sub- composite membrane；Then after the temperature of heated oven being warmed into 200 DEG C -220 DEG C, pressurizeed using up-down roller by above-mentioned four tunic
It is compound to be pasted onto on galvanized aluminium board；The galvanized aluminium board pasted is delivered into cooler again, using air-cooled rapidly that sheet material is cold
But, it is wound into coiled strip with collecting machine；Finally the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added,
Suppress tile shape.
Wherein, the dual coating of the nano-silicon glued membrane has UV glue, and on the UV glue outer surface on nano-silicon glued membrane two sides
It is pasted with one layer of PC film.
Wherein, the dual coating of the Nanometer gallium oxide film has UV glue, and in the UV glue outer surface on nano-silicon glued membrane two sides
On be pasted with one layer of PC film.
Wherein, the zinc-plated color steel is zinc-plated every square metre more than 70 grams of steel plate coiled material.
Wherein, the polymer compound film uses polyamide film coiled strip.
The invention also discloses the preparation method of a kind of nanometer of steel thermal insulation tile, comprise the following steps that：
S1, zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate patch
Film production line, bottom are zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is height
Molecular compound film；
S2, after the temperature of heated oven is warmed into 200 DEG C -220 DEG C, is pressurizeed using up-down roller and answer above-mentioned four tunic
Conjunction is pasted onto on galvanized aluminium board；
S3, the galvanized aluminium board pasted delivered into cooler, sheet material is cooled down rapidly using air-cooled, then uses rewinding
Machine is wound into coiled strip；
S4, the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard added, suppress tile shape.
Wherein, the thickness of the zinc-plated color steel used in S1 is 0.3-2.0mm, and the thickness of nano-silicon glued membrane is 0.2-
10mm, the thickness of Nanometer gallium oxide film is 0.05-0.2mm, and the thickness of polymer compound film is 30-200mm.
Wherein, the mode heated in S2 is：During traveling, added rapidly using high frequency mode in a manner of transmission
Heat.
The invention also discloses the making production line of a kind of nanometer of steel thermal insulation tile, including feeding machine, charger, heating baking
Case, the first rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and collecting machine, the feeding machine, charging
Machine, heated oven, the first rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and collecting machine are from front to back
It is sequentially arranged connection；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and galvanized aluminium board are placed in blowing
On machine；Starting device, using charger by zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and
Four kinds of membrane materials of galvanized aluminium board are sent into heated oven；Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and macromolecule are answered
Close film and be warmed to 200 DEG C -220 DEG C；Material is corrected using the first rectification machine in traveling process, prevent deviation after wind it is uneven；
Pressurizeed using the up-down roller of make-up machine and four kinds of membrane materials are fitted on galvanized aluminium board；It is defeated that the sheet material of assembly is placed in cooling
Send platform；Sheet material is placed in cooler area and utilizes air-cooled reduction waste heat by cooling transport platform；The second rectification machine is continuing with by material again
Secondary correction；The nanometer steel board being bonded completely is wound into coiled material；The tile press of various standards is utilized as requested, by sheet material pressure
Variously-shaped nanometer steel thermal insulation tile is made.
The beneficial effects of the invention are as follows：
Compared with prior art, nanometer steel thermal insulation tile of the invention, by zinc-plated color steel, nano-silicon glued membrane, nano oxidized
Gallium film and polymer compound film are placed in coiled steel plate pad pasting production line, and bottom is zinc-plated color steel, and the second layer is nanometer silica gel
Film, third layer are Nanometer gallium oxide film, and the 4th layer is polymer compound film；In the case where shining upon, Nanometer gallium oxide film effectively hinders
Every up to more than 90% ultraviolet and infrared ray, the excellent heat-proof quality of nano-silicon glued membrane effectively obstructs 10% sunlight
After-heat, the soft material of nano-silicon glued membrane can also play a part of sound insulation, so as to realize excellent heat-insulated, sound insulation, anti-
Rust, leakproof, corrosion-resistant effect, product structure is simple, and heat-insulated, sound insulation, antirust, leak preventing effect are obvious, environmental protection and energy saving, manufacturing cost
It is cheap, save resource.The preparation technology flow is simple, requires that equipment is low and workable.
Brief description of the drawings
Fig. 1 is the flow chart of the preparation method of nanometer steel thermal insulation tile of the present invention；
Fig. 2 is the making production line schematic diagram of nanometer steel thermal insulation tile of the present invention.
Main element symbol description is as follows：
10th, feeding machine 11, charger
12nd, heated oven 13, the first rectification machine
14th, make-up machine 15, cooling transport platform
16th, cooler 17, the second rectification machine
18th, collecting machine.
Embodiment
In order to more clearly state the present invention, the present invention is further described below in conjunction with the accompanying drawings.
A kind of nanometer steel thermal insulation tile of the present invention, including the zinc-plated color steel with anti-rust action, transparent thermal resistance and sound insulation
Nano-silicon glued membrane, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polymer compound film and based on sheet material plating
Zinc-aluminium plate, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are bonded successively from inside to outside
On galvanized aluminium board；Shine upon down, the Nanometer gallium oxide film obstructs more than 90% ultraviolet and infrared ray, the nanometer
Pellosil obstructs less than 10% after-heat and plays deadening；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate pad pasting
Production line, bottom are zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is high score
Sub- composite membrane；Then after the temperature of heated oven 12 being warmed into 200 DEG C -220 DEG C, pressurizeed using up-down roller by above-mentioned four layers
Film is compound to be pasted onto on galvanized aluminium board；The galvanized aluminium board pasted is delivered into cooler 16 again, using air-cooled rapidly by plate
Material is cooled down, and coiled strip is wound into collecting machine 18；The ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is finally placed in the pressure of standard
Watt add, suppress tile shape.
In the present embodiment, the thickness of the nano-silicon glued membrane is 0.2-10mm, and its dual coating has UV glue, and is receiving
One layer of PC film is pasted with the UV glue outer surface on rice pellosil two sides.
In the present embodiment, the thickness of the Nanometer gallium oxide film is 0.05-0.2mm, and its dual coating has UV glue, and
One layer of PC film is pasted with the UV glue outer surface on nano-silicon glued membrane two sides.
In the present embodiment, the thickness of the zinc-plated color steel is 0.3-2.0mm, and zinc-plated color steel is zinc-plated every square metre
More than 70 grams of steel plate coiled material.
In the present embodiment, the thickness of the polymer compound film is 30-200mm, and it uses polyamide film coiled strip.
The standard that so materials combine is based on Nanometer gallium oxide film effectively barrier up to more than 90% ultraviolet and infrared
Line, the excellent heat-proof quality of nano-silicon glued membrane effectively obstruct 10% sunlight after-heat, the soft material of nano-silicon glued membrane
Matter can also play a part of sound insulation, so as to realize excellent heat-insulated, sound insulation, antirust, leakproof, corrosion-resistant effect, product structure
Simply, heat-insulated, sound insulation, antirust, leak preventing effect are obvious, and environmental protection and energy saving, manufacturing cost is cheap, save resource.
Summer tests：Compared with traditional galvanized iron micromicrowatt more than 26-45 DEG C of the top layer temperature difference, year-on-year room temperature differ 10 DEG C with
On.This product has already been through " national building materials test center " detection, has reached A level standards, with " National Fire building materials matter
Measure Supervision Test Center " detection, reach A1 level examination criterias.
Referring to Fig. 1, the invention also discloses the preparation method of a kind of nanometer of steel thermal insulation tile, comprise the following steps that：
S1, zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polymer compound film are placed in coiled steel plate patch
Film production line, bottom are zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is height
Molecular compound film；
S2, during traveling, the temperature of heated oven 12 is heated rapidly using high frequency mode in a manner of transmission
To after 200 DEG C -220 DEG C, it is pasted onto above-mentioned four tunic is compound using up-down roller pressurization on galvanized aluminium board；
S3, the galvanized aluminium board pasted delivered into cooler 16, rapidly cooled down sheet material using air-cooled, then with receiving
Material machine 18 is wound into coiled strip；
S4, the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard added, suppress tile shape.
In the present embodiment, the thickness of the zinc-plated color steel used in S1 is 0.3-2.0mm, the thickness of nano-silicon glued membrane
Spend for 0.2-10mm, the thickness of Nanometer gallium oxide film is 0.05-0.2mm, and the thickness of polymer compound film is 30-200mm.
Fig. 2 is further regarded to, the invention also discloses the making production line of a kind of nanometer of steel thermal insulation tile, including feeding machine
10th, charger 11, heated oven 12, the first rectification machine 13, make-up machine 14, cooling transport platform 15, cooler 16, the second rectification machine
17 and collecting machine 18, feeding machine 10, charger 11, heated oven 12, the first rectification machine 13, make-up machine 14, cooling transport platform
15th, cooler 16, the second rectification machine 17 and collecting machine 18 are sequentially arranged connection from front to back；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film and galvanized aluminium board are placed in blowing
On machine 10；Starting device, using charger 11 by zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polymer compound film
And four kinds of membrane materials of galvanized aluminium board are sent into heated oven 12；By zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and height
Molecular compound film is warmed to 200 DEG C -220 DEG C；Material is corrected using the first rectification machine 13 in traveling process, received after preventing deviation
Roll up uneven；Pressurizeed using the up-down roller of make-up machine 14 and four kinds of membrane materials are fitted on galvanized aluminium board；By the sheet material of assembly
It is placed in cooling transport platform 15；Sheet material is placed in the area of cooler 16 and utilizes air-cooled reduction waste heat by cooling transport platform 15；It is continuing with
Two rectification machines 17 correct material again；The nanometer steel board being bonded completely is wound into coiled material；Various marks are utilized as requested
Accurate tile press, sheet material is pressed into variously-shaped nanometer steel thermal insulation tile.
Disclosed above is only several specific embodiments of the present invention, but the present invention is not limited to this, any ability
What the technical staff in domain can think change should all fall into protection scope of the present invention.
Claims (8)
1. a kind of nanometer steel thermal insulation tile, it is characterised in that including the zinc-plated color steel with anti-rust action, transparent thermal resistance and sound insulation
Nano-silicon glued membrane, can reflect sunlight and heat-insulated Nanometer gallium oxide film, polyamide film coiled strip and based on sheet material
Galvanized aluminium board, the zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polyamide film coiled strip from inside to outside according to
It is secondary to be fitted on galvanized aluminium board；Shine upon down, the Nanometer gallium oxide film obstructs more than 90% ultraviolet and infrared ray, institute
State the after-heat of nano-silicon glued membrane barrier less than 10% and play deadening；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polyamide film coiled strip are placed in the life of coiled steel plate pad pasting
Producing line, bottom are zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is polyamide
Film coiled strip；Then after the temperature of heated oven being warmed into 200 DEG C -220 DEG C, pressurizeed using up-down roller by above-mentioned four tunic
It is compound to be pasted onto on galvanized aluminium board；The galvanized aluminium board pasted is delivered into cooler again, using air-cooled rapidly that sheet material is cold
But, it is wound into coiled strip with collecting machine；Finally the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard is added,
Suppress tile shape.
2. according to claim 1 nanometer of steel thermal insulation tile, it is characterised in that the dual coating of the nano-silicon glued membrane has UV
Glue, and it is pasted with one layer of PC film on the UV glue outer surface on nano-silicon glued membrane two sides.
3. according to claim 1 nanometer of steel thermal insulation tile, it is characterised in that the dual coating of the Nanometer gallium oxide film has
UV glue, and it is pasted with one layer of PC film on the UV glue outer surface on nano-silicon glued membrane two sides.
4. according to claim 1 nanometer of steel thermal insulation tile, it is characterised in that the zinc-plated color steel is zinc-plated every square metre
More than 70 grams of steel plate coiled material.
5. the preparation method of a kind of nanometer of steel thermal insulation tile, it is characterised in that comprise the following steps that：
S1, zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polyamide film coiled strip be placed in coiled steel plate pad pasting
Production line, bottom are zinc-plated color steel, and the second layer is nano-silicon glued membrane, and third layer is Nanometer gallium oxide film, and the 4th layer is polyamides
Amine film coiled strip；
S2, after the temperature of heated oven is warmed into 200 DEG C -220 DEG C, pressurizeed using up-down roller above-mentioned four tunic is compound viscous
It is attached on galvanized aluminium board；
S3, the galvanized aluminium board pasted delivered into cooler, sheet material is cooled down rapidly using air-cooled, then received with collecting machine
It is rolled into coiled strip；
S4, the pressure watt that the ultra-thin zinc-plated color steel of the nanometer steel of composite film-stuck is placed in standard added, suppress tile shape.
6. the preparation method of according to claim 5 nanometer of steel thermal insulation tile, it is characterised in that what is used in S1 is zinc-plated
The thickness of color steel is 0.3-2.0mm, and the thickness of nano-silicon glued membrane is 0.2-10mm, and the thickness of Nanometer gallium oxide film is 0.05-
0.2mm, the thickness of polyamide film coiled strip is 30-200mm.
7. the preparation method of according to claim 5 nanometer of steel thermal insulation tile, it is characterised in that the mode heated in S2
For：During traveling, heated rapidly using high frequency mode in a manner of transmission.
8. the making production line of a kind of nanometer of steel thermal insulation tile, it is characterised in that including feeding machine, charger, heated oven, first
Rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and collecting machine, the feeding machine, charger, heating are dried
Case, the first rectification machine, make-up machine, cooling transport platform, cooler, the second rectification machine and the collecting machine company of being sequentially arranged from front to back
Connect；
Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polyamide film coiled strip and galvanized aluminium board are placed in feeding machine
On；Starting device, using charger by zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film, polyamide film coiled strip and
Four kinds of membrane materials of galvanized aluminium board are sent into heated oven；Zinc-plated color steel, nano-silicon glued membrane, Nanometer gallium oxide film and polyamide is thin
Film roll material is warmed to 200 DEG C -220 DEG C；Material is corrected using the first rectification machine in traveling process, wound not after preventing deviation
Together；Pressurizeed using the up-down roller of make-up machine and four kinds of membrane materials are fitted on galvanized aluminium board；The sheet material of assembly is placed in cold
But transport platform；Sheet material is placed in cooler area and utilizes air-cooled reduction waste heat by cooling transport platform；The second rectification machine is continuing with by material
Material is corrected again；The nanometer steel board being bonded completely is wound into coiled material；The tile press of various standards is utilized as requested, by plate
Material is pressed into variously-shaped nanometer steel thermal insulation tile.