CN1069111C - 钼精矿焙砂粉的成型方法 - Google Patents
钼精矿焙砂粉的成型方法 Download PDFInfo
- Publication number
- CN1069111C CN1069111C CN98112625A CN98112625A CN1069111C CN 1069111 C CN1069111 C CN 1069111C CN 98112625 A CN98112625 A CN 98112625A CN 98112625 A CN98112625 A CN 98112625A CN 1069111 C CN1069111 C CN 1069111C
- Authority
- CN
- China
- Prior art keywords
- concentrated molybdenum
- molybdenum ore
- roasted
- roasted concentrated
- agglomerate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
一种钼精矿焙砂粉的成型方法，属于金属氧化物粉的压团领域，解决了钼精矿焙砂粉的成型问题。该方法是在粒度为5毫米以下的钼精矿焙砂粉中配加少量粘结剂和一定量的水份，充分混合后在常温下压制成型。该方法工艺简单，成型过程易于控制，成型效果好，成型率高，所得三氧化钼团块强度指标好，以尺寸为30×31×20毫米的方枕形团块为例，团块的抗压强度在600N/块以上，落下强度在30次/米以上，符合炼钢炉料的要求，且生产成本低。
Description
本发明涉及一种金属氧化物粉的压团成型，特别涉及一种通过配加粘结剂将钼精矿焙砂粉压团成型的团矿方法。
硫化钼精矿经氧化焙烧后得到氧化钼产品，其主要成分是三氧化钼，多为疏松结块状或粉状。该产品用作合金钢添加剂时，需要加工成氧化钼团块才能入炉冶炼。曾有人用水、水玻璃和生石灰等作粘结剂进行氧化钼粉的辊压成型试验，皆因成型率低、团块强度不够而未能成功。
本发明的目的是提供一种主要以可溶性碱作粘结剂的钼精矿焙砂粉在常温下压制成型的方法。
本发明的技术方案是：在粒度为5毫米以下的钼精矿焙砂粉中配加少量粘结剂和一定量的水份，与焙砂粉充分混合，使焙砂粉充分润湿，然后在常温下压制成氧化钼团块。以100份钼精矿焙砂粉计，水7-9份；粘结剂中可溶性碱0.1-0.7份，有机粘结剂0-1份。
可溶性碱与钼精矿焙砂粉颗粒表面的三氧化钼发生反应生成具有一定粘性的表面产物，这一表面产物在团块干燥过程中又可以在相邻颗粒之间结晶，形成连接桥，从而使团块具有很好的固结强度。有机粘结剂的加入，一是对团块强度特别是湿团块强度进行补充，二是减轻压制成型时脱模的难度。为了既能使成型团块符合炼钢炉料的要求，又尽量减少杂质的带入，上述粘结剂的优选范围为：可溶性碱0.1-0.5份，有机粘结剂0-0.5份。可溶性碱以氢氧化钠为佳，有机粘结剂以淀粉为佳。
由于采用可溶性碱和有机粘结剂，使钼精矿焙砂粉在常温下压制成型，该方法工艺简单，成型过程易于控制，成型率高，所得三氧化钼团块强度指标好，以尺寸为30×31×20毫米的方枕形团块为例，团块的抗压强度在600N/块以上，落下强度在30次/米以上，完全符合炼钢炉料的要求；且生产成本低，生产一吨三氧化钼团块所用的粘结剂总成本在40元以下。
下面根据实施过程及实施例对本发明进一步描述。
实施时，将钼精矿焙砂粉与有机粘结剂充分混合，加稀释了的可溶性碱溶液充分润湿，然后将混合料在轮碾机中碾压5-10分钟，或不经碾压而直接将混合料静置5-10分钟，再将混合料在对辊成型机中辊压成型得湿团块；湿团块自然干燥，或在100℃-600℃的温度下进行干燥即得成品氧化钼团块。
实施例一：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份淀粉、0.33份氢氧化钠和8份水，混合料静置10分钟后于对辊成型机中辊压成型，所得尺寸为30×31×20毫米的方枕形湿团块自然干燥，其团块抗压强度为732N/块，落下强度为31.8次/米。
实施例二：
在100份粒度为70％小于1毫米、30％1-5毫米的钼精矿焙砂粉中配入0.5份淀粉、0.33份氢氧化钠和7份水，混合料静置5分钟后于对辊成型机中辊压成型，所得尺寸为30×31×20毫米的方枕形湿团块在120℃温度下干燥，其团块抗压强度为753N/块，落下强度为33.5次/米。
实施例三：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.1份氢氧化钠和8份水，混合料静置10分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为645N/块，落下强度为31.4次/米。
实施例四：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份氢氧化钠和8份水，混合料静置10分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为979N/块，落下强度为48.8次/米。
实施例五：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份氢氧化钠和8份水，混合料在轮碾机中碾压5分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为1682N/块，落下强度为46.5次/米。
实施例六：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份氢氧化钠和8份水，混合料在轮碾机中碾压10分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为1845N/块，落下强度为84.2次/米。
实施例七：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份氢氧化钠、0.5份淀粉和8份水，混合料静置5分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于400℃下干燥，其团块抗压强度为913N/块，落下强度为43.4次/米。
实施例八：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份氢氧化钠、0.5份淀粉和8份水，混合料静置5分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于600℃下干燥，其团块抗压强度为894N/块，落下强度为39.5次/米。
实施例九：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.7份氢氧化钠和8份水，混合料静置5分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为1651N/块，落下强度为110次/米。
实施例十：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.3份氢氧化钠、0.5份腐植酸钠和8份水，混合料静置5分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为853N/块，落下强度为38.4次/米。
实施例十一：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份氢氧化钾和8份水，混合料静置10分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为974N/块，落下强度为45.3次/米。
实施例十二：
在100份粒度为100％小于1毫米的钼精矿焙砂粉中配入0.5份碳酸钠和8份水，混合料静置10分钟后于对辊成型机中辊压成型，所得尺寸为Φ30×20毫米的扁球形湿团块于120℃下干燥，其团块抗压强度为733N/块，落下强度为32.1次/米。
Claims (7)
1.一种钼精矿焙砂粉的成型方法，其特征在于：在粒度为5毫米以下的钼精矿焙砂粉中配加少量粘结剂和一定量的水份，与焙砂粉充分混合，使焙砂粉充分润湿，然后在常温下压制成三氧化钼团块；以100份钼精矿焙砂粉计，水7-9份；粘结剂中可溶性碱0.1-0.7份，有机粘结剂0-1份。
2.根据权利要求1的钼精矿焙砂粉的成型方法，其特征在于：所得的三氧化钼团块在100℃-600℃的温度下进行干燥。
3.根据权利要求1的钼精矿焙砂粉的成型方法，其特征在于：所述的在常温下压制成三氧化钼团块，是将钼精矿焙砂粉与粘结剂的混合料在轮碾机中碾压5-10分钟后于对辊成型机中辊压成型。
4.根据权利要求1的钼精矿焙砂粉的成型方法，其特征在于：所述的在常温下压制成三氧化钼团块，是将钼精矿焙砂粉与粘结剂的混合料静置5-10分钟后于对辊成型机中辊压成型。
5.根据权利要求1的钼精矿焙砂粉的成型方法，其特征在于：所述的粘结剂中可溶性碱为0.1-0.5份，有机粘结剂为0-0.5份。
6.根据权利要求1或4的钼精矿焙砂粉的成型方法，其特征在于：所述的可溶性碱为氢氧化钠。
7.根据权利要求1或4的钼精矿焙砂粉的成型方法，其特征在于：所述的有机粘结剂为淀粉。