CN106893627A - A kind of surface moisturizing lubricant for clay pad and preparation method thereof - Google Patents
A kind of surface moisturizing lubricant for clay pad and preparation method thereof Download PDFInfo
- Publication number
- CN106893627A CN106893627A CN201710066674.5A CN201710066674A CN106893627A CN 106893627 A CN106893627 A CN 106893627A CN 201710066674 A CN201710066674 A CN 201710066674A CN 106893627 A CN106893627 A CN 106893627A
- Authority
- CN
- China
- Prior art keywords
- parts
- ethylene glycol
- clay pad
- vegetable oil
- lubricant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of surface moisturizing lubricant for clay pad, including ethylene glycol and vegetable oil.The present invention has advantages below：, with ethylene glycol and vegetable oil as main component, composition is simple, and convenient for production, cost is relatively low, easy to use, is applicable not only to large-scale industrial production, is also applied for individual applications for surface moisturizing lubricant for clay pad disclosed by the invention；Can be mixed with arbitrary proportion with vegetable oil provided by the present invention for the ethylene glycol in the surface moisturizing lubricant of clay pad, sodium tripolyphosphate be added, not only with lubrication, additionally it is possible to play moisture-keeping function；Surface moisturizing lubricant provided by the present invention for clay pad is applied to the outer layer of clay pad; clay pad can not only be enable smoothly to be stripped down from packing film; and clay pad can be protected; clay pad is set to avoid contact with air and corrosion, oxidation by materials such as the hydrone in air, acidic materials etc., so as to extend the pot-life of clay pad.
Description
Technical field
The present invention relates to moisturizing field of lubricant, and in particular to a kind of surface moisturizing lubricant and its system for clay pad
Preparation Method.
Background technology
Lubricant is the frictional resistance for reducing friction pair, the lubricant medium for slowing down its abrasion.Lubricant is to friction pair
Cooling can also be played, clean and prevent pollution etc..In order to improve greasy property, can be added in some lubricants and suitably added
Plus agent.During from lubricant, motion conditions, material, surface roughness, working environment and the work bar of friction pair must be typically considered
Part, and lubricant many factors such as performance.In plant equipment, lubricant gives each need by lubricating system transmission ＆ distribution mostly
The position to be lubricated.
Lubricant is used to lubricate, cool down and sealing machine friction portion material.
Mineral lubricant (such as machinery oil), vegetable lubricant (such as castor oil) and animality lubricant are had according to source
(such as tallow).Additionally, also syntholube, such as silicone oil, fatty acid amide, oleic acid, polyester, synthetic ester, carboxylic acid.
The semisolid lubricating grease of the lubricating oil of oily liquids, grease-like and kollag are had according to proterties.
Industrial lubricants (including lubricating oil and lubricating grease), human body lubricants can be divided into according to purposes.
Why lubricant can play lubrication, because its addition, reduces the friction of plastic melt, this friction
Friction and the class of external friction two in being divided to again.Thus should mutually there are in-lubricant and external lubricant.
1st, the effect of external lubricant mainly improves the andfrictional conditions of the hot metal surface of polymer melt and equipment, makes modeling
The easy demoulding of part, it is poor with the compatibility of polymer, easily from melt toward external migration, in forming process can melt with
One layer of very thin barrier film is formed between mould, plastics is not stick to die surface.
2nd, in-lubricant and polymer have good compatibility, and it is interior that it plays reduction polymer molecule in polymeric inner
The effect of poly- power, so as to improve the interior frictional heat of plastic melt and the mobility of melt.In-lubricant and polymer long-chain point
Combination between son is not strong, and they are there may be the effect similar to rolling bearing, therefore its own can be in melt flows side
Arrangement upwards, so as to slide over each other so that internal friction reduction, here it is the mechanism of interior lubrication.
The species of lubricant is a lot, is widely used.Lubricant is also commonly used for improving mobility and the demoulding in the processing such as plastics
Property.But existing lubricant is undesirable on mobility and release property is improved, for example, in slide gate nozzle system regions, through conventional
Other plastic products such as polybag, plastic sheeting packaging clay pad or other protection materials, when deployed, often occur glue
Mud pad or protection materials are sticked on plastic products, it is difficult to strip down, so on the one hand cause waste, are on the other hand caused
Work trouble is, it is necessary to pass through other some instruments or treatment stripping so that in use, have a strong impact on service efficiency
And operating efficiency.
The content of the invention
Present invention defect of the prior art for more than provides a kind of surface moisturizing lubricant for clay pad, should
Not only there is lubrication for the surface moisturizing lubricant of clay pad, under clay pad can be made conveniently to be peeled off from plastic sheeting
Come, and with moisture-keeping function.
The purpose of the present invention is achieved through the following technical solutions：
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, including ethylene glycol and vegetable oil.
Further, also including sodium tripolyphosphate, the weight of the sodium tripolyphosphate is that ethylene glycol is total with plant weight of oil
Less than the 5% of sum.
Further, in parts by weight, the ethylene glycol is 5-1250 parts, and the vegetable oil is 20-1300 parts.
Further, in parts by weight, the ethylene glycol is 255 parts, and the vegetable oil is 300 parts.
Further, in parts by weight, the ethylene glycol is 230 parts, and the vegetable oil is 50 parts.
Further, in parts by weight, the ethylene glycol is 5 parts, and the vegetable oil is 20 parts.
Further, in parts by weight, the ethylene glycol is 600 parts, and the vegetable oil is 1300 parts.
Further, in parts by weight, the ethylene glycol is 800 parts, and the vegetable oil is 100 parts.
The preparation method of the above-mentioned surface moisturizing lubricant for clay pad, ethylene glycol and plant are weighed according to weight portion
Oil, sodium tripolyphosphate is weighed according to part by weight, and by ethylene glycol, vegetable oil and sodium tripolyphosphate addition agitator, stirring is equal
It is even.
Compared with prior art, the present invention at least has advantages below：
1. the surface moisturizing lubricant for clay pad disclosed by the invention is with ethylene glycol and vegetable oil as main component, into
Divide simple, convenient for production, cost is relatively low, easy to use, is applicable not only to large-scale industrial production, be also applied for individual answering
With.
2. can be with any with vegetable oil provided by the present invention for the ethylene glycol in the surface moisturizing lubricant of clay pad
Ratio mixes.
3. provided by the present invention for adding sodium tripolyphosphate in the surface moisturizing lubricant of clay pad, not only with profit
Sliding effect, additionally it is possible to play moisture-keeping function.
4. the surface moisturizing lubricant provided by the present invention for clay pad is applied to the outer layer of clay pad, can not only make
Clay pad can be stripped down smoothly from packing film, and can protect clay pad, clay pad is avoided contact with air
And corrosion, oxidation by materials such as the hydrone in air, acidic materials etc., so as to extend the pot-life of clay pad.
Specific embodiment
To make the object, technical solutions and advantages of the present invention clearer, technical scheme is carried out with reference to embodiment
Clearly and completely describe, it is clear that described embodiment is a part of embodiment of the invention, rather than whole embodiments.Cause
This, the detailed description to embodiments of the invention is not intended to limit the scope of claimed invention below, but only
Represent selected embodiment of the invention.Based on the embodiment in the present invention, those of ordinary skill in the art are not making creation
Property work under the premise of the every other embodiment that is obtained, belong to the scope of protection of the invention.
Below by specific embodiment, the present invention is further illustrated.
A kind of surface moisturizing lubricant for clay pad, including ethylene glycol and vegetable oil, ethylene glycol and vegetable oil can be with
Mix according to arbitrary proportion, it is preferable that in parts by weight, ethylene glycol is 5-1250 parts, vegetable oil is 20-1300 parts.
Sodium tripolyphosphate, in parts by weight, its content can also be included in the implementation method that the present invention is provided
It is less than the 5% of ethylene glycol and plant weight of oil summation.
Sodium tripolyphosphate has alkalescent, and non-corrosiveness is a kind of mineral surfaces activating agent, has to lubrication oil ＆ fat
Strong emulsification.Adding it to can also be further in the surface moisturizing lubricant provided by the present invention for clay pad
Play moisture-keeping function.
For the preparation method of the surface moisturizing lubricant of clay pad, including ethylene glycol and plant are weighed according to weight portion
Oil, sodium tripolyphosphate is weighed according to part by weight, and by ethylene glycol, vegetable oil and sodium tripolyphosphate addition agitator, stirring is equal
It is even.
Ethylene glycol is insoluble with vegetable oil, general matching while using, or after preparing in advance, using preceding stirring.
Because diethanol is immiscible with vegetable oil, therefore, by provided by the present invention for the surface moisturizing lubricant of clay pad
Clay pad or the surface of other protection materials are applied to after stirring, or clay pad or other protection materials are directly immersed in
To in the surface moisturizing lubricant provided by the present invention for clay pad, then pull out, put it into sealing in packaging bag.
Embodiment 1
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and content such as table 1 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 1 of table 1
| Composition | Content |
| Ethylene glycol | 255 parts |
| Vegetable oil | 300 parts |
| Sodium tripolyphosphate | 11 |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 2
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 2 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 2 of table 2
| Composition | Content |
| Ethylene glycol | 230 parts |
| Vegetable oil | 50 parts |
| Sodium tripolyphosphate | 9 parts |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 3
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 3 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 3 of table 3
| Composition | Content |
| Ethylene glycol | 5 parts |
| Vegetable oil | 20 parts |
| Sodium tripolyphosphate | 1 part |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 4
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 4 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 4 of table 4
| Composition | Content |
| Ethylene glycol | 600 parts |
| Vegetable oil | 1300 parts |
| Sodium tripolyphosphate | 19 parts |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 5
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 5 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 5 of table 5
| Composition | Content |
| Ethylene glycol | 800 parts |
| Vegetable oil | 100 parts |
| Sodium tripolyphosphate | 9 parts |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 6
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 6 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 6 of table 6
| Composition | Content |
| Ethylene glycol | 1250 parts |
| Vegetable oil | 175 parts |
| Sodium tripolyphosphate | 57 parts |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 7
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 7 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 7 of table 7
| Composition | Content |
| Ethylene glycol | 30 parts |
| Vegetable oil | 470 parts |
| Sodium tripolyphosphate | 13 parts |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 8
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 8 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 8 of table 8
| Composition | Content |
| Ethylene glycol | 670 parts |
| Vegetable oil | 30 parts |
| Sodium tripolyphosphate | 11 parts |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Embodiment 9
A kind of surface moisturizing lubricant for clay pad, according to weight ratio, each composition and ratio such as table 9 below.
It is used for each composition of surface moisturizing lubricant and content of clay pad in the embodiment 9 of table 9
| Composition | Content |
| Ethylene glycol | 70 parts |
| Vegetable oil | 32 parts |
| Sodium tripolyphosphate | 5 parts |
Ethylene glycol and vegetable oil are weighed according to weight portion, sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, plant
Oil and sodium tripolyphosphate are added in agitator, are stirred.
Surface moisturizing lubricant provided by the present invention for clay pad is applied to the outer layer of clay pad, can make clay pad
Smoothly stripped down from packing film, the clay pad without any residual on packing film, both save stripping clay pad institute
Operating time, operating efficiency is improve, also improve the utilization rate of clay pad, it is to avoid because sticking on packing film and nothing
Method uses the waste for causing.
In addition, clay pad can be protected using the surface moisturizing lubricant provided by the present invention for clay pad, make clay
Pad avoids contact with air and corrosion, oxidation by materials such as the hydrone in air, acidic materials etc., so as to extend clay pad
Pot-life.The surface moisturizing lubricant for clay pad that embodiment of the present invention 1-9 is provided can make the storage life of clay pad
Limit at least can extend 30-45 days.
Surface moisturizing lubricant provided by the present invention for clay pad is not only applicable to slide gate nozzle, can also be applied to it
He requires field higher to intensity, sealing, corrosion resistance etc..
More than, the only present invention preferably specific embodiment, but the protection domain of invention is not limited thereto, any ripe
Know those skilled in the art the invention discloses technical scope in, the change or replacement that can be readily occurred in should all be contained
Cover within protection scope of the present invention.Therefore, protection scope of the present invention should be defined by the protection domain of claims.
Claims (9)
1. a kind of surface moisturizing lubricant for clay pad, it is characterised in that including ethylene glycol and vegetable oil.
2. the surface moisturizing lubricant for clay pad according to claim 1, it is characterised in that also including tripolyphosphate
Sodium, the weight of the sodium tripolyphosphate is ethylene glycol and less than the 5% of plant weight of oil summation.
3. the surface moisturizing lubricant for clay pad according to claim 1 and 2, it is characterised in that according to weight portion
Meter, the ethylene glycol is 5-1250 parts, and the vegetable oil is 20-1300 parts.
4. the surface moisturizing lubricant for clay pad according to claim 3, it is characterised in that in parts by weight,
The ethylene glycol is 255 parts, and the vegetable oil is 300 parts.
5. the surface moisturizing lubricant for clay pad according to claim 3, it is characterised in that in parts by weight,
The ethylene glycol is 230 parts, and the vegetable oil is 50 parts.
6. the surface moisturizing lubricant for clay pad according to claim 3, it is characterised in that in parts by weight,
The ethylene glycol is 5 parts, and the vegetable oil is 20 parts.
7. the surface moisturizing lubricant for clay pad according to claim 3, it is characterised in that in parts by weight,
The ethylene glycol is 600 parts, and the vegetable oil is 1300 parts.
8. the surface moisturizing lubricant for clay pad according to claim 3, it is characterised in that in parts by weight,
The ethylene glycol is 800 parts, and the vegetable oil is 100 parts.
9. the preparation method of the surface moisturizing lubricant for clay pad described in claim 1~8, it is characterised in that according to
Weight portion weighs ethylene glycol and vegetable oil, and sodium tripolyphosphate is weighed according to part by weight, by ethylene glycol, vegetable oil and tripolyphosphate
Sodium is added in agitator, is stirred.