CN106893483A - A kind of organosilicon concrete protection emulsion and preparation method thereof - Google Patents
A kind of organosilicon concrete protection emulsion and preparation method thereof Download PDFInfo
- Publication number
- CN106893483A CN106893483A CN201710133780.0A CN201710133780A CN106893483A CN 106893483 A CN106893483 A CN 106893483A CN 201710133780 A CN201710133780 A CN 201710133780A CN 106893483 A CN106893483 A CN 106893483A
- Authority
- CN
- China
- Prior art keywords
- span
- organosilicon
- emulsifying agent
- protection emulsion
- tween
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of building coating, and in particular to a kind of organosilicon concrete protection emulsion and preparation method thereof.Technical scheme is as follows:A kind of organosilicon concrete protection emulsion, including silicone oil, emulsifying agent and water, its quality proportioning is:10 12 parts of silicone oil, 78 parts of emulsifying agent, 82 83 parts of water;The emulsifying agent is two kinds of compositions of surfactant, and its formula is:Span 80+OP 10, Tween 60+Span 60 or Tween 60+Span 80.The organosilicon concrete protection emulsion that the present invention is provided, being painted on after concrete structure can improve the water proofing property of concrete, can especially lift road and bridge agent on crack resistance of concrete except freezing salt corrosion.
Description
Technical field
The present invention relates to one kind the present invention relates to a kind of building coating, and in particular to a kind of organosilicon concrete protection emulsion
And preparation method thereof.
Background technology
With the increasingly extension of concrete structure range of application, its endurance issues in the presence of a harsh environment also gradually causes
The attention of people.In China's cold district, winter sleety weather is more, in order to ensure the unimpeded of highway, often in bridge and tunnel
A large amount of deicer salts are put on road, makes this area's concrete structure be subject to salt corrosion, particularly chlorion a large amount of using deicer salts
Penetrate into so as to change cement concrete interior tissue and structure, the use of concrete has been had a strong impact under Frozen-thawed cycled effect
Performance and endurance quality, make concrete construction sealer peeling and peeling in large area, and internal reinforcing bar is exposed and accelerates
Corrosion.It is the effective means for preventing deicing salting liquid from permeating in concrete surface applying protective coating, frequently with ring in engineering
The materials such as oxygen tree fat, polyurethane resin, fluorocarbon resin are formed with certain thickness fine and close flexibility in concrete structural surface
Diaphragm, prevents the infiltration of harmful solution.Degree of drying requirement of the type coating to inside concrete before construction is very high, because
While preventing the aqueous solution from entering concrete, the moisture of inside concrete cannot also be excluded for it, coating is played drum, or even
The freezing up layer on surface is formed in parallel with concrete superficial, causes the breakage of concrete structure.
The emulsion particle diameter of organosilicon concrete protection emulsion is less than 0.15 μm, and outward appearance is translucent to transparent, between emulsion
A kind of state between solution, can make up the not enough defect of stability of organic silicone emulsion, with good storage stability and
Excellent permeability.Organosilicon material forms the permeable formation of certain depth by the pore of concrete surface, is mixed in permeable formation
The polycondensation of solidifying soil capillary hole surface organosilicon forms hydrophobic film, concrete surface is had the performance of permeable watertight, is mixed
The ideal material of solidifying soil surfacecti proteon.
The content of the invention
The present invention provides a kind of organosilicon concrete protection emulsion, and the anti-of concrete can be improved after being painted on concrete structure
It is aqueous, road and bridge agent on crack resistance of concrete can be especially improved except jelly salt corrosion.
Technical scheme is as follows:
A kind of organosilicon concrete protection emulsion, including silicone oil, emulsifying agent and water, its quality proportioning is:Silicone oil 10-12
Part, emulsifying agent 7-8 parts, water 82-83 parts;The emulsifying agent is two kinds of compositions of surfactant, and the surfactant is
Sorbitan monooleate (Span-80), sorbitan fatty ester (OP-10), sorbitan monostearate
(Span-60) or polyoxyethylene sorbitan monostearate (Tween-60), its formula is:Span-80+OP-10、
Tween-60+Span-60 or Tween-60+Span-80.
Described organosilicon concrete protection emulsion, its preferred scheme is that the silicone oil is dimethicone, its HLB value
It is 10.5, viscosity is 500cs.
Described organosilicon concrete protection emulsion, its preferred scheme is that the quality proportioning of the emulsifying agent is:Span-
80:OP-10=19:31, Tween-60:Span-60=43:57, Tween-60:Span-80=41:59.
Described organosilicon concrete protection emulsion, its preferred scheme is that the HLB value of Span-80 is 4.1, OP-10's
HLB value is the HLB value of 14.5, Span-60 for the HLB value of 4.7, Tween-60 is 14.9.
A kind of preparation method of above-mentioned organosilicon concrete protection emulsion, comprises the following steps:First in normal temperature state
Under, silicone oil is weighed successively by quality proportioning and emulsifying agent is added in conical flask, it is slowly stirred, mix emulsifying agent and silicone oil
Uniformly, stirring electromechanical source is started, the water that will be measured under stirring is slowly added into conical flask, the initial stage forms W/O breasts
Liquid, continues the stirring that adds water, and to the O/W emulsions for forming bit bluish gloss, is made organosilicon concrete protection emulsion.
Beneficial effects of the present invention are:Organosilicon concrete protection emulsion of the invention have good standing stability and
Dewatering ability, its durability can be effectively improved after being painted on concrete structure.
Specific embodiment
The present invention is expanded on further with reference to embodiment;It should be understood that these embodiments are merely to illustrate the present invention, rather than
Limitation the scope of the present invention.
Embodiment 1
Raw material are as follows:
The organosilicon concrete protection emulsion stands still stablize without oil slick after 24h at room temperature, be put in centrifuge with
The centrifugation of 2500r/min after 20 minutes emulsion it is not stratified.After being painted on C50 concrete test blocks, freeze by one side salt and test
After measure, relative dynamic elastic modulus loss late be 4.3%, mass loss rate is 1.02%;By measuring its suction after waterproof test
Water rate is 0.57%;After chloride-penetration resistance experiment, its electric flux value is measured for 675.68 coulombs.
Embodiment 2
Raw material are as follows:
The organosilicon concrete protection emulsion stands still stablize without oil slick after 24h at room temperature, be put in centrifuge with
The centrifugation of 2500r/min after 20 minutes emulsion it is not stratified.After being painted on C50 concrete test blocks, freeze by one side salt and test
After measure, relative dynamic elastic modulus loss late be 5.9%, mass loss rate is 0.97%;By measuring its suction after waterproof test
Water rate is 0.79%;After chloride-penetration resistance experiment, its electric flux value is measured for 747.28 coulombs.
Embodiment 3
Raw material are as follows:
The organosilicon concrete protection emulsion stands still stablize without oil slick after 24h at room temperature, be put in centrifuge with
The centrifugation of 2500r/min after 20 minutes emulsion it is not stratified.After being painted on C50 concrete test blocks, freeze by one side salt and test
After measure, relative dynamic elastic modulus loss late be 7.44%, mass loss rate is 1.08%;By measuring its suction after waterproof test
Water rate is 0.72%;After chloride-penetration resistance experiment, its electric flux value is measured for 708.20 coulombs.
Claims (5)
1. a kind of organosilicon concrete protection emulsion, it is characterised in that including silicone oil, emulsifying agent and water, its quality proportioning is:Silicon
It is oily 10-12 parts, emulsifying agent 7-8 parts, water 82-83 parts;The emulsifying agent is two kinds of compositions of surfactant, and its formula is:
Span-80/OP-10, Tween-60/Span-60 or Tween-60/Span-80.
2. organosilicon concrete protection emulsion according to claim 1, it is characterised in that the silicone oil is dimethyl-silicon
Oil, its HLB value is 10.5, and viscosity is 500cs.
3. organosilicon concrete protection emulsion according to claim 1, it is characterised in that the quality proportioning of the emulsifying agent
For:Span-80:OP-10=19:31, Tween-60:Span-60=43:57, Tween-60:Span-80=41:59.
4. organosilicon concrete protection emulsion according to claim 1, it is characterised in that the HLB value of Span-80 is 4.1,
The HLB value of OP-10 is 14.9 for the HLB value that the HLB value of 14.5, Span-60 is 4.7, Tween-60.
5. a kind of preparation method of organosilicon concrete protection emulsion as described in one of Claims 1 to 4, including following step
Suddenly:First under normal temperature state, silicone oil is weighed successively by quality proportioning and emulsifying agent is added in conical flask, be slowly stirred,
Make emulsifying agent and silicone oil well mixed, start stirring electromechanical source, the water that will be measured under stirring is slowly added into taper
In bottle, the initial stage forms W/O emulsions, continues the stirring that adds water, and to the O/W emulsions for forming bit bluish gloss, is made organosilicon coagulation
Native protection emulsion.