CN106884263A - A kind of preparation method of woven fabric spun-laced cleaning cloth - Google Patents
A kind of preparation method of woven fabric spun-laced cleaning cloth Download PDFInfo
- Publication number
- CN106884263A CN106884263A CN201710046778.XA CN201710046778A CN106884263A CN 106884263 A CN106884263 A CN 106884263A CN 201710046778 A CN201710046778 A CN 201710046778A CN 106884263 A CN106884263 A CN 106884263A
- Authority
- CN
- China
- Prior art keywords
- spun
- woven fabric
- combing
- laced
- cleaning cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of preparation method of woven fabric spun-laced cleaning cloth, it is comprised the following steps:Tangerine valve type is divided into woven fabric shredding and is sufficiently mixed, respectively through first, second combing;Through the fibre web MD of first, second combing:CD is respectively 4 ~ 5:1 and 1 ~ 2.5:1;The fibre web of the first combing, entirely viscous spun laced fabric, the fibre web of the second combing are stacked successively from top to bottom, and the lower grammes per square metre ratio of upper, neutralization is 20:30:20 or 25:30:25;Through the fine current spray thorn in 5 roads, spun lacing suction is 85 ~ 115mbar, and the hydraulic pressure of the fine current spray thorn effect in first, second, third, fourth and fifth road is respectively 20 ~ 40bar, 190 ~ 210bar, 190 ~ 210bar, 50 ~ 70bar and 20 ~ 40bar;Clamping is advanced, and the mode that hot blast is penetrated during advance is dried;Batch, cut, packing processes, have the advantages that improve wiping effect.
Description
Technical field
It is more particularly to a kind of the present invention relates to the non-weaving cloth being entirely or primarily made up of chopped fiber or similar relatively chopped fiber
The preparation method of woven fabric spun-laced cleaning cloth.
Background technology
Spun-laced cleaning cloth is, by the fine water flow jet of high pressure to one or more layers fleece, fiber is mutually become entangled in one
Rise, so that fibre web is able to reinforce and possess certain strength, the fabric for obtaining as spun-laced cleaning cloth.Existing spun-laced cleaning cloth
Wiping effect is general, and the scope of application is small.
The content of the invention
It is an object of the invention to provide a kind of preparation method of woven fabric spun-laced cleaning cloth, wiping effect is which solved general
Problem, has the advantages that to improve wiping effect.
Above-mentioned technical purpose of the invention technical scheme is that:
A kind of preparation method of woven fabric spun-laced cleaning cloth, comprises the following steps:
(1)Pretreatment:Tangerine valve type is divided into woven fabric shredding and is sufficiently mixed, while being ready to fine with 1.5D × 40mm white viscose glues high
The entirely viscous spun laced fabric that dimension is made;
(2)Combing is processed:Pretreated tangerine valve type division woven fabric is taken, then respectively through the first combing and the second combing, point
Fibre web is not formed;Wherein, the MD of the fibre web for being obtained by the first combing:CD is 4 ~ 5:1, the fibre web obtained by the second combing
MD:CD is 1 ~ 2.5:1;
(3)Spun lacing treatment:Pretreated complete viscous spun laced fabric is overlayed the fibre web top of the second combing formation, by the first combing
The fibre web of formation overlays viscous spun laced fabric top entirely, overlaps it, and the grammes per square metre ratio of the upper, middle and lower is 20:30:20 or
25:30:25;Then the fine current spray thorn effect in 5 roads is passed it through, spun lacing fiber is punctured and is tangled, obtain hygrometric state spun-laced cleaning
Cloth;Wherein, spun lacing suction is 85 ~ 115mbar, and the hydraulic pressure of first fine current spray thorn effect is 20 ~ 40bar, second
The hydraulic pressure of road fine current spray thorn effect is 190 ~ 210bar, the hydraulic pressure of the fine current spray thorn effect in the 3rd road for 190 ~
210bar, the hydraulic pressure of the fine current spray thorn effect in the 4th road is 50 ~ 70bar, and the hydraulic pressure of the fine current spray thorn effect in the 5th road is
20~40bar;
(4)Dried process:Hygrometric state spun-laced cleaning cloth is taken, clamping is advanced, and the mode that hot blast is penetrated during advance is to spun-laced cleaning
Cloth is dried;
(5)Post processing:Dried spun-laced cleaning cloth is taken, batched, cut, packing processes.
Using above-mentioned technical proposal, tangerine valve type division woven fabric is symmetricly set on the both sides of complete viscous spun laced fabric, symmetrical configuration
The situation of shrinkage is reduced, upper and lower two layers are tangerine valve type division woven fabric, and intermediate layer is pure viscose glue spun laced fabric, levels tangerine valve type point
Split woven fabric and form superfine Denier fibre after the mechanicals efforts fibrillation of spun-laced machine water needle head water jets under high pressure, and with the pure viscose glue in intermediate layer
Spun laced fabric replaces entangled, formation stereoscopic three-dimensional structure, even good without pile, flexibility less with good hygroscopicity, pile
The features such as, and have superpower adsorption capacity, greatly improve cleaning capacity.The fibrillation of the product superfine fibre is by water jets under high pressure
Mechanicals efforts fibrillation, it is to avoid the alkali decrement treatment technique of traditional superfine fibre, substantially reduce the Product processing cycle,
Energy-saving consumes, and reduces sewage discharge;By MD:CD different fibre webs are stacked, and intersect laying, reduce the possibility of deformation, and enhancing is vertical
To with transverse breakage ability.
More preferably:Step(4)In, during advance hot blast by way of tow sides are penetrated to spun lacing nonwoven
Cloth is dried;Wherein, dry temperature is 70 ~ 90 DEG C.
Using above-mentioned technical proposal, cloth is to be clamped in advance between lace curtaining, is pressed by hot blast during advance
Cloth is dried according to the mode that tow sides are penetrated, drying efficiency is higher, cloth fluffy degree is better, cloth is softer;Two-sided hot blast is worn
Drying thoroughly penetrates drying saving energy consumption 10 ~ 20% than conventional one side hot blast, and can reach same drying with relatively low drying temperature imitates
Really, reduce that temperature is too high to make fiber molecule in cloth rigidly become strong, fiber fire damage is smaller, and pliability is good, product feel more preferably,
Strength is also higher.
More preferably:Step(2)In, during the first combing, main cylinder speed is 700~800m/min, working roll speed
It is 20~40m/min to spend, and strips 120~180m/min of roller speed;During the second combing, main cylinder speed is 700~800m/min,
Work roller speed is 15~35m/min, strips 100~160m/min of roller speed.
Using above-mentioned technical proposal, the degree tightened of cloth and the speed of control spun lacing are controlled by controlling speed
Degree, improves the uniformity of product.
More preferably:Step(3)In, 5 roads are fine, and the effect of current spray thorn is using single empty water needle plate and pitch-row is equal
It is 0.5~0.6mm;First fine active aperture of current spray thorn is 0.15~0.17mm, second and three fine current in road
The active aperture of spray thorn be the fine active aperture of current spray thorn in the roads of 0.07~0.08mm, the 4th and five be 0.05~
0.06mm。
Using above-mentioned technical proposal, spun lacing bounce-back improves flatness, more soft.
More preferably:The tangerine valve type division woven fabric divides woven fabric or 2.5D × 51mm from the valves of 2D × 51mm 16
32 valves divide woven fabric, and wherein the valves of 2D × 51mm 16 division woven fabric splits into 0.13D after spun lacing treatment, and 2.5D × 51mm 32
0.08D is split into after valve division woven fabric spun lacing treatment.
Using above-mentioned technical proposal, by the mechanicals efforts fibrillation of water jets under high pressure into woven fabric, increase specific surface area, enhancing is wiped
Wipe effect.
More preferably:The specification of the complete viscous spun laced fabric is 30g/m2。
Woven fabric using above-mentioned technical proposal, and lower both sides disposed thereon coordinates, and strengthens spun laced fabric stereoscopic three-dimensional structure, twines
Knot is more preferable, reduces and shrinks different situations, makes it more smooth.
In sum, the woven fabric spun-laced cleaning cloth for being prepared through the preparation method of the application has the advantages that:
1st, strong adsorption capacity, greatly improves cleaning capacity;
2nd, good hygroscopicity;
3rd, pile is less even without pile, surfacing, and flexibility is good;
4th, wearability is good;
5th, energy-conservation, reduces energy consumption.
Specific embodiment
This specific embodiment is only explanation of the invention, and it is not limitation of the present invention, people in the art
Member can make the modification without creative contribution to the present embodiment as needed after this specification is read, but as long as at this
All protected by Patent Law in the protection domain of invention.
Embodiment 1:A kind of preparation method of woven fabric spun-laced cleaning cloth, comprises the following steps:
(1)Pretreatment:The commercially available valves of 2D × 51mm 16 are divided into woven fabric(Bag more than 0.13D shreddings is split into after spun lacing treatment mixed
Close), get out specification for 30g/m2Entirely viscous spun laced fabric;
(2)Combing is processed:Pretreated tangerine valve type division woven fabric is taken, then respectively through the first combing and the second combing, point
Fibre web is not formed;
During the first combing, main cylinder speed is 700~800m/min, and work roller speed is 20~40m/min, strips roller speed
120~180m/min;The MD of the fibre web obtained by the first combing:CD is 4 ~ 5:1;
During the second combing, main cylinder speed is 700~800m/min, and work roller speed is 15~35m/min, strips roller speed
100~160m/min;The MD of the fibre web obtained by the second combing:CD is 1 ~ 2.5:1;
(3)Spun lacing treatment:Pretreated complete viscous spun laced fabric is overlayed the fibre web top of the second combing formation, by the first combing
The fibre web of formation overlays viscous spun laced fabric top entirely, overlaps it, and the grammes per square metre ratio of the upper, middle and lower is 20g/m2:30g/
m2:20g/m2;Then the fine current spray thorn effect in 5 roads is passed it through, spun lacing fiber is punctured and is tangled, obtain hygrometric state spun-laced cleaning
Cloth;Spun lacing suction is 85 ~ 115mbar;
The hydraulic pressure of first fine current spray thorn effect is 20 ~ 40bar, use single row of holes water needle plate and pitch-row for 0.5~
0.6mm, aperture is 0.15~0.17mm;
The hydraulic pressure of second fine current spray thorn effect is 190 ~ 210bar, use single row of holes water needle plate and pitch-row for 0.5~
0.6mm, aperture is 0.07~0.08mm;
The hydraulic pressure of the 3rd road fine current spray thorn effect is 190 ~ 210bar, use single row of holes water needle plate and pitch-row for 0.5~
0.6mm, aperture is 0.07~0.08mm;
The hydraulic pressure of the 4th road fine current spray thorn effect is 50 ~ 70bar, use single row of holes water needle plate and pitch-row for 0.5~
0.6mm, aperture is 0.05~0.06mm;
The hydraulic pressure of the 5th road fine current spray thorn effect is 20 ~ 40bar, use single row of holes water needle plate and pitch-row for 0.5~
0.6mm, aperture is 0.05~0.06mm;
(4)Dried process:Hygrometric state spun-laced cleaning cloth is taken, clamping is advanced, the side that hot blast is penetrated by tow sides during advance
Formula is dried to spunlace non-woven cloth;Dry temperature is 70 ~ 90 DEG C;
(5)Post processing:Dried spun-laced cleaning cloth is taken, batched, cut, packing processes.
Embodiment 2:A kind of preparation method of woven fabric spun-laced cleaning cloth, the difference with embodiment 1 is, by 2D ×
The valves of 51mm 16 divide the woven fabric valves of 2.5D × 51mm 32 and divide woven fabric(0.08D is split into after spun lacing treatment)Substitute.
Embodiment 3:A kind of preparation method of woven fabric spun-laced cleaning cloth, the difference with embodiment 1 is, upper strata, in
The grammes per square metre ratio of layer and lower floor is 25g/m:30g/m:25g/m.
Embodiment 4:A kind of preparation method of woven fabric spun-laced cleaning cloth, the difference with embodiment 1 is, step(4)
In, drying temperature is 110 DEG C;Compared to embodiment 4, the woven fabric spun-laced cleaning measuring fiber fire damage that embodiment 1 is prepared is small, soft
More preferably, strength is also higher for softness.
Embodiment 5:A kind of preparation method of woven fabric spun-laced cleaning cloth, the difference with embodiment 1 is, step(4)
In, hot blast is dried by the way of one side is penetrated to spunlace non-woven cloth during advance;Compared to embodiment 5, embodiment 1
The possibility of the more fluffy soft, shrinkage of preparation method power consumption woven fabric spun-laced cleaning cloth that is low and obtaining is low.
Embodiment 6:A kind of preparation method of woven fabric spun-laced cleaning cloth, the difference with embodiment 1 is, step(2)
In, during the first combing, main cylinder speed is 1000m/min, and work roller speed is 50m/min, strips roller speed 200m/min;The
During two combings, main cylinder speed is 1000m/min, and work roller speed is 50m/min, strips roller speed 200m/min;Compared to reality
The woven fabric spun-laced cleaning cloth that example 6 is prepared is applied, the woven fabric spun-laced cleaning cloth that embodiment 1 is prepared is evenly fine and smooth.
Embodiment 7:A kind of preparation method of woven fabric spun-laced cleaning cloth, the difference with embodiment 1 is, step(3)
In, the fine current spray thorn effect in 5 roads is 0.5~0.6mm, aperture and is 0.2mm using single row of holes water needle plate, pitch-row;Phase
Than the woven fabric spun-laced cleaning cloth that embodiment 7 is prepared, the woven fabric spun-laced cleaning cloth surface that embodiment 1 is prepared is more smooth
Densification, fluffy degree is better and is difficult fluffing.
Claims (6)
1. a kind of preparation method of woven fabric spun-laced cleaning cloth, it is characterised in that comprise the following steps:
(1)Pretreatment:Tangerine valve type is divided into woven fabric shredding and is sufficiently mixed, while being ready to fine with 1.5D × 40mm white viscose glues high
The entirely viscous spun laced fabric that dimension is made;
(2)Combing is processed:Pretreated tangerine valve type division woven fabric is taken, then respectively through the first combing and the second combing, point
Fibre web is not formed;Wherein, the MD of the fibre web for being obtained by the first combing:CD is 4 ~ 5:1, the fibre web obtained by the second combing
MD:CD is 1 ~ 2.5:1;
(3)Spun lacing treatment:Pretreated complete viscous spun laced fabric is overlayed the fibre web top of the second combing formation, by the first combing
The fibre web of formation overlays viscous spun laced fabric top entirely, overlaps it, and the grammes per square metre ratio of the upper, middle and lower is 20:30:20 or
25:30:25;Then the fine current spray thorn effect in 5 roads is passed it through, spun lacing fiber is punctured and is tangled, obtain hygrometric state spun-laced cleaning
Cloth;Wherein, spun lacing suction is 85 ~ 115mbar, and the hydraulic pressure of first fine current spray thorn effect is 20 ~ 40bar, second
The hydraulic pressure of road fine current spray thorn effect is 190 ~ 210bar, the hydraulic pressure of the fine current spray thorn effect in the 3rd road for 190 ~
210bar, the hydraulic pressure of the fine current spray thorn effect in the 4th road is 50 ~ 70bar, and the hydraulic pressure of the fine current spray thorn effect in the 5th road is
20~40bar;
(4)Dried process:Hygrometric state spun-laced cleaning cloth is taken, clamping is advanced, and the mode that hot blast is penetrated during advance is to spun-laced cleaning
Cloth is dried;
(5)Post processing:Dried spun-laced cleaning cloth is taken, batched, cut, packing processes.
2. a kind of preparation method of woven fabric spun-laced cleaning cloth according to claim 1, it is characterised in that step(4)In, it is preceding
Hot blast is dried by way of tow sides are penetrated to spunlace non-woven cloth during entering;Wherein, dry temperature is 70 ~ 90
℃。
3. a kind of preparation method of woven fabric spun-laced cleaning cloth according to claim 1, it is characterised in that step(2)In, the
During one combing, main cylinder speed be 700~800m/min, work roller speed be 20~40m/min, strip roller speed 120~
180m/min;During the second combing, main cylinder speed is 700~800m/min, and work roller speed is 15~35m/min, angle stripper
100~160m/min of speed.
4. a kind of preparation method of woven fabric spun-laced cleaning cloth according to claim 1, it is characterised in that step(3)In, 5
Road is fine, and the effect of current spray thorn is using single empty water needle plate and pitch-row is 0.5~0.6mm;First fine current spray thorn is made
Aperture in is 0.15~0.17mm, second and three the fine active aperture of current spray thorn in road be 0.07~0.08mm, the
The fine active aperture of current spray thorn in four and five roads is 0.05~0.06mm.
5. a kind of preparation method of woven fabric spun-laced cleaning cloth according to claim 1, it is characterised in that the tangerine valve type point
Split woven fabric and divide woven fabric or the valves of 2.5D × 51mm 32 division woven fabric, the wherein valves of 2D × 51mm 16 point from the valves of 2D × 51mm 16
Split woven fabric and 0.13D is split into after spun lacing treatment, and 0.08D is split into after the division woven fabric spun lacing treatment of the valves of 2.5D × 51mm 32.
6. a kind of preparation method of woven fabric spun-laced cleaning cloth according to claim 1, it is characterised in that the entirely viscous spun lacing
The specification of cloth is 30g/m2。