CN106876025A - 一种耐高温漆包线 - Google Patents

一种耐高温漆包线 Download PDF

Info

Publication number
CN106876025A
CN106876025A CN201710098627.9A CN201710098627A CN106876025A CN 106876025 A CN106876025 A CN 106876025A CN 201710098627 A CN201710098627 A CN 201710098627A CN 106876025 A CN106876025 A CN 106876025A
Authority
CN
China
Prior art keywords
wire
temperature
temperature resistant
enamelled wire
resistant
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201710098627.9A
Other languages
English (en)
Inventor
董桂香
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HAIAN COUNTY TIANXING ELECTRICAL MATERIALS Co Ltd
Original Assignee
HAIAN COUNTY TIANXING ELECTRICAL MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HAIAN COUNTY TIANXING ELECTRICAL MATERIALS Co Ltd filed Critical HAIAN COUNTY TIANXING ELECTRICAL MATERIALS Co Ltd
Priority to CN201710098627.9A priority Critical patent/CN106876025A/zh
Publication of CN106876025A publication Critical patent/CN106876025A/zh
Pending legal-status Critical Current

Abstract

本发明提供了一种耐高温漆包线，通过如下步骤制备而成：1）采用漆包线机放线，裸铜线退火，退火温度为640‑650度；2）涂漆：将耐高温漆包线漆用模具涂覆到裸铜线上；3）烘培，烘培温度为200‑300度；4）冷却润滑；5）收线后，得到耐高温漆包线。本发明制备出的漆包线，具有很好的耐热性能，适用于高、低压、中、大容量的电机电器产品绕组线。

Description

一种耐高温漆包线
技术领域
本发明涉及一种耐高温漆包线，属于电工材料技术领域。
背景技术
漆包线是绕组线的一个主要品种，由导体和绝缘层两部组成，裸线经退火软化后，再经过多次涂漆，烘焙而成。但要生产出既符合标准要求，又满足客户要求的产品并不容易，它受原材料质量，工艺参数，生产设备，环境等因素影响，因此，各种漆包线的质量特性各不相同，但都具备机械性能，化学性能，电性能，热性能四大性能。
目前,我国漆包线的生产厂家已超千家,年生产能力已超万吨。但总的来说我国漆包线的状况是低水平的重复,概括来说是“产量高、品位低、设备落后”。
电磁线必须满足多种使用和制造工艺上的要求。前者包括其形状、规格、能短时和长期在高温下工作，以及承受某些场合中的强烈振动和高速下的离心力，高电压下的耐受电晕和击穿，特殊气氛下的耐化学腐蚀等；后者包括绕制和嵌线时经受拉伸、弯曲和磨损的要求，以及浸渍和烘干过程中的溶胀、侵蚀作用等。现有的产品无法满足这一点要求。
发明内容
本发明的目的是克服现有技术的不足之处，提供一种耐高温漆包线。
本发明的耐高温漆包线，通过如下步骤制备而成：
1）采用漆包线机放线，裸铜线退火，退火温度为640-650度；
2）涂漆：将耐高温漆包线漆用模具涂覆到裸铜线上；
3）烘培，烘培温度为200-300度；
4）冷却润滑；
5）收线后，得到耐高温漆包线。
优选地，
所述的步骤2）中，所述的耐高温漆包线漆为聚乙烯醇缩醛漆。
本发明制备出的漆包线，具有很好的耐热性能，适用于高、低压、中、大容量的电机电器产品绕组线。
具体实施方式
实施例1
本发明的耐高温漆包线，通过如下步骤制备而成：
1）采用漆包线机放线，裸铜线退火，退火温度为640度；
2）涂漆：将耐高温漆包线漆用模具涂覆到裸铜线上；
3）烘培，烘培温度为200度；
4）冷却润滑；
5）收线后，得到耐高温漆包线。
所述的步骤2）中，所述的耐高温漆包线漆为聚乙烯醇缩醛漆。
实施例2
本发明的耐高温漆包线，通过如下步骤制备而成：
1）采用漆包线机放线，裸铜线退火，退火温度为650度；
2）涂漆：将耐高温漆包线漆用模具涂覆到裸铜线上；
3）烘培，烘培温度为300度；
4）冷却润滑；
5）收线后，得到耐高温漆包线。
所述的步骤2）中，所述的耐高温漆包线漆为聚乙烯醇缩醛漆。
实施例3
本发明的耐高温漆包线，通过如下步骤制备而成：
1）采用漆包线机放线，裸铜线退火，退火温度为645度；
2）涂漆：将耐高温漆包线漆用模具涂覆到裸铜线上；
3）烘培，烘培温度为250度；
4）冷却润滑；
5）收线后，得到耐高温漆包线。
所述的步骤2）中，所述的耐高温漆包线漆为聚乙烯醇缩醛漆。

Claims (2)

1.一种耐高温漆包线，其特征在于，通过如下步骤制备而成：
1）采用漆包线机放线，裸铜线退火，退火温度为640-650度；
2）涂漆：将耐高温漆包线漆用模具涂覆到裸铜线上；
3）烘培，烘培温度为200-300度；
4）冷却润滑；
5）收线后，得到耐高温漆包线。
2.根据权利要求1所述的耐高温漆包线，其特征在于，所述的步骤2）中，所述的耐高温漆包线漆为聚乙烯醇缩醛漆。
CN201710098627.9A 2017-02-23 2017-02-23 一种耐高温漆包线 Pending CN106876025A (zh)