CN106872676A - No. 903 standard oils of rubber oil-resistant detection of a kind of replacement IRM and preparation method thereof - Google Patents

No. 903 standard oils of rubber oil-resistant detection of a kind of replacement IRM and preparation method thereof Download PDF

Info

Publication number
CN106872676A
CN106872676A CN201710259959.0A CN201710259959A CN106872676A CN 106872676 A CN106872676 A CN 106872676A CN 201710259959 A CN201710259959 A CN 201710259959A CN 106872676 A CN106872676 A CN 106872676A
Authority
CN
China
Prior art keywords
oil
rubber
naphthenic
standard
oils
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201710259959.0A
Other languages
Chinese (zh)
Other versions
CN106872676B (en
Inventor
周应斌
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Super Chemical Technology Co Ltd
Original Assignee
Anhui Super Chemical Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Super Chemical Technology Co Ltd filed Critical Anhui Super Chemical Technology Co Ltd
Priority to CN201710259959.0A priority Critical patent/CN106872676B/en
Publication of CN106872676A publication Critical patent/CN106872676A/en
Application granted granted Critical
Publication of CN106872676B publication Critical patent/CN106872676B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of standard oil of replacement IRM903 rubber oil-resistant detections and preparation method thereof, the standard oil is made up of the component of following weight proportion:Diisoamyl naphthalene 13.5 14.5%, KN4010 naphthenic rubbers oil 25 45%, the KN4006 naphthenic rubbers oil 45 65%, rubber oils 5 10% of KG 12, the rubber oils 5 15% of KG 06, antioxidant T501 0.1 0.5%.Independent research formula of the present invention, can be used to substitute IRM No. 903 standard oils of imported from America, and the raw material for using can the country buy, it is to avoid import, effectively reduce cost.

Description

A kind of standard oil of replacement IRM-903 rubber oil-resistant detections and preparation method thereof
Technical field
The invention belongs to rubber detection field, and in particular to a kind of standard working solution for rubber oil-resistant detection.
Background technology
Rubber oil-resistant performance is the important performance indexes of oil resistant rubber.Ke Biao inspection centers provide according to GB, HB, ISO, The standards such as ASTM, EN provide rubber oil-resistant test, and provide report.In existing detection, more using the ASTM standard pair in the U.S. Rubber carries out oil resistant test.
Because current U.S. ASTM new standards are adjusted to the quality of its oil product, and in new standard by former 1,2, 3rd, No. 5 experiment standard oils are upgraded to IRM 901, IRM902, IRM903, IRM905.They are mainly used in rubber seal product Oil resistant test, such as oil sealing(NBR nitrile rubber oil sealings, ACM acrylate oil sealings etc.), O-ring and sebific duct class product test. Different elastomeric materials, can be tested according to the different qualities of U.S.'s ASTM D471 standards and each money test oil.
But, it is necessary to use each money test standard oil IRM for arriving when being tested using U.S.'s ASTM D471 standards 901st, IRM902, IRM903, IRM905, the country are required to from imported from America without corresponding product and formula, expensive, are increased Cost is added.Therefore it is badly in need of a experiment standard oil for meeting U.S.'s ASTM D471 standards of research and development, instead of the standard of import Oil.
The content of the invention
The invention aims to solve defect present in prior art, there is provided one kind can effectively substitute IRM 903 rubber oil-resistant detection experiment oil.
In order to achieve the above object, the invention provides a kind of rubber oil-resistant detection standard oil, by following weight proportion Component composition:Diisoamyl naphthalene 13.5-14.5%, KN4010 naphthenic rubber oil 25-45%, KN4006 naphthenic rubber oil 45-65%, KG-12 rubber oil 5-10%, KG-06 rubber oil 5-15%, antioxidant T501 0.1-0.5%.
The preferred ingredient weight proportion of standard oil of the present invention is:Diisoamyl naphthalene 13.5-14.5%, KN4010 cycloalkyl rubber It is glue oil 25-40%, KN4006 naphthenic rubber oil 45-60%, KG-12 rubber oil 5-10%, KG-06 rubber oil 5-10%, anti- Oxygen agent T501 0.1-0.5%, polyisobutene 0-2%.Best composition weight proportion is:Diisoamyl naphthalene 13.8%, KN4010 rings Alkyl rubber oil 26.1%, KN4006 naphthenic rubbers oil 46%, KG-12 rubber oils 7%, KG-06 rubber oils 6.2%, antioxygen Agent T501 0.3%, polyisobutene 0.6%.
Wherein, KN4010 and KN4006 naphthenic rubbers oil is respectively selected from the production of Kelamayi lubricating oil plant of CNPC KN4010 and KN4006 high-quality naphthenic rubber oil;KG-12 and KG-06 rubber oils are respectively selected from the prosperous profit limited public affairs of petrochemical industry in Xiamen KG12 the and KG06 rubber oils of department;Antioxidant T501 is selected from the antioxidant T501 of Nanjing Datang chemical industry Co., Ltd.
Present invention also offers the preparation method of above-mentioned standard oil, step is as follows:By diisoamyl naphthalene, KN4010 cycloalkyl After rubber oil, KN4006 naphthenic rubbers oil, KG-12 rubber oils, KG-06 rubber oils, antioxidant T501 are mixed in proportion, Its viscosity is detected, polyisobutene is subsequently adding, viscosity of the standard oil at 38 DEG C is reached 32-34 mm2/s。
The present invention has advantages below compared to existing technology:
1st, the present invention by the diisoamyl naphthalene of specific proportioning, KN4010 naphthenic rubbers oil, KN4006 naphthenic rubbers it is oily, KG-12 rubber oils, KG-06 rubber oils adjust the aniline point of oil product of the present invention;While utilization KN4010 naphthenic rubbers oil, The naphthene content of KN4006 naphthenic rubbers oil regulation oil product;Pass through KG-12 rubber oils, the proportioning of KG-06 rubber oils respectively The content of regulation cycloalkane and alkane;Strengthen the antioxygenic property of oil product by antioxidant T501;Made by adding polyisobutene It is thickener, improves the viscosity of product.
2nd, by the research to formula composition and each group distribution ratio, the final product formula for determining can fully meet the present invention Requirement of U.S.'s ASTM D471 standards to experiment oil IRM903, it is adaptable to test rubber oil-resistant.
3rd, independent research formula of the present invention, can be used to substitute No. 903 standard oils of IRM of imported from America, and the raw material for using Can the country buy, it is to avoid import, effectively reduce cost.
Specific embodiment
With reference to specific embodiment, the present invention is described in detail.
Naphthenic rubber oil KN4010 and KN4006 is purchased from Kelamayi lubricating oil plant of CNPC;Rubber oil KG-12 and KG-06 is purchased from Xiamen Heng Run petrochemical industry Co., Ltd;Antioxidant T501 is purchased from Nanjing Datang chemical industry Co., Ltd.
Embodiment 1
The composition weight proportioning of rubber liquid influence experiment standard oil of the present invention is as follows:
Diisoamyl naphthalene 13.6kg, KN4010 naphthenic rubber oil 25.5kg, KN4006 naphthenic rubber oil 45.6kg, KG- 12 rubber oil 6kg, KG-06 rubber oil 9kg, antioxidant T501 0.3kg.
By above-mentioned diisoamyl naphthalene, KN4010 naphthenic rubbers oil, KN4006 naphthenic rubbers oil, KG-12 rubber oils, KG-06 rubber oils, antioxidant T501 are well mixed.
Embodiment 2
The composition weight proportioning of rubber liquid influence experiment standard oil of the present invention is as follows:
Diisoamyl naphthalene 13.8kg, KN4010 naphthenic rubber oil 26.1kg, KN4006 naphthenic rubber oil 46kg, KG-12 rubber Glue oil 7kg, KG-06 rubber oil 6.2kg, antioxidant T501 0.3kg, polyisobutene 0.6kg.
By above-mentioned diisoamyl naphthalene, KN4010 naphthenic rubbers oil, KN4006 naphthenic rubbers oil, KG-12 rubber oils, KG-06 rubber oils, antioxidant T501, polyisobutene are well mixed.
Embodiment 3
Rubber liquid influence experiment of the present invention is as follows with standard oil configuration process:
Take diisoamyl naphthalene 14kg, KN4010 naphthenic rubber oil 28kg, KN4006 naphthenic rubber oil 45.7kg, KG-12 Rubber oil 5.6kg, KG-06 rubber oil 5.8kg, antioxidant T501 0.3kg are well mixed, and its viscosity is 31 after testing, is added Polyisobutene 0.6kg, it is well mixed to obtain final product.
Embodiment 4
Rubber liquid influence experiment of the present invention is as follows with standard oil configuration process:
Take diisoamyl naphthalene 14.2kg, KN4010 naphthenic rubber oil 26kg, KN4006 naphthenic rubber oil 46.6kg, KG- 12 rubber oil 6.5kg, KG-06 rubber oil 5.4kg, antioxidant T501 0.3kg are well mixed, and its viscosity is 30.5 after testing, Polyisobutene 1kg is added, it is well mixed to obtain final product.
The particular product performance parameters that the present invention is prepared are as shown in table 1 below with the performance comparison of IRM903 standard oils:
The performance comparison of the standard oil of the present invention of table 1 and IRM903 standard oils
As can be seen from Table 1, the standard oil performance indications that the present invention is prepared reach requirement, are entirely capable of substituting IRM903 marks Quasi- oil carries out rubber oil-resistant test.
The standard oil prepared to various embodiments of the present invention carries out performance test, as a result as shown in table 2 below:
Standard oil performance comparison prepared by the various embodiments of the present invention of table 2
As can be seen from Table 2, the standard oil performance indications that the present invention is prepared reach requirement, are entirely capable of substituting IRM903 marks Quasi- oil carries out rubber oil-resistant test.And standard oil performance that embodiment 2 is prepared is optimal.

Claims (5)

1. a kind of standard oil of replacement IRM903 rubber oil-resistant detections, it is characterised in that the standard oil includes following heavy Measure the component of proportioning:Diisoamyl naphthalene 13.5-14.5%, KN4010 naphthenic rubber oil 25-45%, KN4006 naphthenic rubber Oily 45-65%, KG-12 rubber oil 5-10%, KG-06 rubber oil 5-15%, antioxidant T501 0.1-0.5%.
2. the standard oil according to claim 1, it is characterised in that the standard oil by following weight proportion component Composition:Diisoamyl naphthalene 13.5-14.5%, KN4010 naphthenic rubber oil 25-40%, KN4006 naphthenic rubber oil 45- 60%th, KG-12 rubber oils 5-10%, KG-06 rubber oils 5-10%, antioxidant T501 0.1-0.5%, polyisobutene 0-2%.
3. standard oil according to claim 1 and 2, it is characterised in that KN4010 the and KN4006 naphthenic rubbers oil It is respectively selected from KN4010 the and KN4006 high-quality naphthenic rubber oil of Kelamayi lubricating oil plant of CNPC production;Described KG-12 and KG-06 rubber oils are respectively selected from KG12 the and KG06 rubber oils of Xiamen Heng Run petrochemical industry Co., Ltd;Described antioxidant T501 is selected from the antioxidant T501 of Nanjing Datang chemical industry Co., Ltd.
4. standard oil according to claim 3, it is characterised in that the standard oil by following weight proportion component group Into:Diisoamyl naphthalene 13.8%, KN4010 naphthenic rubbers oil 26.1%, KN4006 naphthenic rubbers oil 46%, KG-12 rubber Oil 7%, KG-06 rubber oils 6.2%, antioxidant T501 0.3%, polyisobutene 0.6%.
5. the preparation method of standard oil described in Claims 2 or 3, it is characterised in that the standard oil is prepared by the following method: By diisoamyl naphthalene, KN4010 naphthenic rubbers oil, KN4006 naphthenic rubbers oil, KG-12 rubber oils, KG-06 rubber oils, anti- After oxygen agent T501 is mixed in proportion, its viscosity is detected, be subsequently adding polyisobutene, make the standard oil viscous at 38 DEG C Degree reaches 32-34mm2/s。
CN201710259959.0A 2017-04-20 2017-04-20 A kind of standard oil of replacement IRM903 rubber oil-resistant detections and preparation method thereof Active CN106872676B (en)