CN106867044A - High resiliency, wear-resistant, shock resistance conveyer belt and preparation method thereof - Google Patents
High resiliency, wear-resistant, shock resistance conveyer belt and preparation method thereof Download PDFInfo
- Publication number
- CN106867044A CN106867044A CN201710008523.4A CN201710008523A CN106867044A CN 106867044 A CN106867044 A CN 106867044A CN 201710008523 A CN201710008523 A CN 201710008523A CN 106867044 A CN106867044 A CN 106867044A
- Authority
- CN
- China
- Prior art keywords
- parts
- canvas
- wear
- rubber
- shock resistance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention proposes a kind of high resiliency, wear-resistant, shock resistance conveyer belt and preparation method thereof, including belt carcass and rubber cover, and belt carcass is that belt carcass is the one kind in NN canvas, EP canvas or NN/EP canvas, and rubber cover includes the component of following parts by weight:50~80 parts of natural rubber, 20~50 parts of synthetic rubber, 1.6~2.3 parts of sulphur, 4~6 parts of zinc oxide, 1.5~3 parts of stearic acid, 1.2~2.3 parts of accelerator, 50~70 parts of reinforcing agent, 0.3~2 part of antiwear additive, 10~18 parts of softening agent, 2~5 parts of age resistor.Conveyer belt proposed by the present invention has high resiliency, strong wear-resisting, resistance to shock resistance, resistance to ag(e)ing, under the block building stones working condition of conveying, have shock resistance, wear-resistant dual-use function concurrently, the impact of larger drop stone and unclassified stores can be resisted, itself wears away small, long service life, can meet the long-term use needs under the conditions of coarse block or granular material.
Description
Technical field
It is particularly a kind of defeated suitable for fields such as metallurgy, harbour, building materials and mines the present invention relates to conveyer belt technical field
Send the high resiliency of lump material, wear-resistant, shock resistance conveyer belt and preparation method thereof.
Background technology
Conveyer belt is the important component of ribbon conveyer, and its value accounts for the 40% of conveyer, is the master of conveyer
Want accessory, transported material have continuity and it is efficient the features such as.No matter indoor and field, long-distance and short distance, level and inclination,
Conveying, dispersion and the concentration of material are capable of achieving under various different working conditions.Compared with automobile, railway transportation, belt conveying
Mode shortens transportation range, reduces construction costs and cost of transportation.The framework material of current conveyer belt to nylon and gathers
Ester develops, and nylon and polyester backbone material have accounted for more than 80%, big, the resistance to flexion of synthetic fibers belt carcass strength, meet it is wet does not go mouldy, solve
Low, belt carcass is cross-section for duck framework material strength of having determined, glue and cloth and cloth and the quality problems of cloth delamination.But, prior art
In, the rubber cover poor flexibility of conveyor belt surface, not wear-resisting, service life are short.As the consumable accessory of ribbon conveyer, conveyer belt
These defects drastically influence the conveying effect and service life of ribbon conveyer.How the structure of existing conveyer belt is improved,
Improve the elasticity and wearability of its surface covering rubber, improve its service life, be current to economize on resources, reduce use cost
It is badly in need of the technical problem for solving.
The content of the invention
In order to solve the above technical problems, the present invention proposes a kind of high resiliency, wear-resistant, shock resistance conveyer belt and its preparation side
Method.
The technical proposal of the invention is realized in this way:
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, including belt carcass and rubber cover, belt carcass are NN canvas, EP canvas or NN/
EP canvas, rubber cover includes the component of following parts by weight:50~80 parts of natural rubber, 20~50 parts of synthetic rubber, sulphur 1.6
~2.3 parts, 4~6 parts of zinc oxide, 1.5~3 parts of stearic acid, 1.2~2.3 parts of accelerator, 50~70 parts of reinforcing agent, antiwear additive 0.3
~2 parts, 10~18 parts of softening agent, 2~5 parts of age resistor.
Preferably, rubber cover includes the component of following parts by weight:60 parts of natural rubber, 40 parts of synthetic rubber, sulphur 2.0
Part, 5 parts of zinc oxide, 3 parts of stearic acid, 1.2 parts of accelerator, 55 parts of reinforcing agent, 0.5 part of antiwear additive, 10 parts of softening agent, age resistor 4
Part.
It is further preferred that NN canvas, EP canvas or NN/EP canvas model 100~400, NN canvas, EP canvas or NN/
EP canvas plunger bond strength is 6.5~12N/mm.
It is further preferred that the physical property requirements of rubber cover are:Pull apart strength >=18Mpa, elongation at break >=
450%, wear loss≤90mm3, 56~65A of hardness(Shao Er).
It is further preferred that synthetic rubber is butadiene rubber or butadiene-styrene rubber.
It is more highly preferred to, reinforcing agent is the mixture of intermediate super abrasion furnace black N220 or intermediate super abrasion furnace black N220 and N330.
Highly preferred, softening agent is the mixture of coumarone indene resin and aromatic naphtha.
The invention allows for above-mentioned high resiliency, wear-resistant, shock resistance conveyer belt preparation method, prepared in advance during preparation
Rubber cover, the preparation method of rubber cover is as follows:
After natural rubber is through over-mastication, in banbury with synthetic rubber and refine, adding small powder, reinforcing agent, softening agent is carried out
One section of mixing, small powder includes zinc oxide, stearic acid, antiwear additive and age resistor, and one section of rotating speed of mixing is 40r/min, floating weight
Pressure 0.6Mpa, rubber 60s, small powder 20s, reinforcing agent 70s, softening agent 50s, 140 DEG C of dumping slices;Park more than 16 hours,
Two-stage mixing, two-stage mixing rotating speed 30r ∕ min, ram piston pressure are carried out to sulphur, accelerator is added in one section of elastomeric compound
0.6MPa, one section of elastomeric compound and sulphur promote 90s, rise the s of bolt 20,110 DEG C of dumping slices.
Compared with prior art, the present invention has the advantages that:
1st, conveyor belt surface is smooth, and defect is little, with impact-resistant high resiliency, good fatigue performance and super large
Strongly, rubber cover is difficult to collapse block, tear in sharp keen lump material transportation, is particularly well-suited to large-scale building stones, harbour
HI high impact, the use of drop conveyer high;
2nd, conveyer belt abrasiveness is extremely low, wear loss≤90mm3Even if, the long-term strong abrasive conditions in coarse block or shot-like particle
Under use, itself abrasion it is also little;
3rd, long service life, is at least 2-3 times of duck conveyor belt;1.2-1.3 times of low cost, only duck conveyor belt, pole
The earth improves cost performance;
4th, production process is green, pollution-free, meets the requirement of sustainable development.
The present invention solves the contradiction that high resiliency can not have concurrently with low abrasion in the prior art so that conveyer belt has simultaneously
Standby high resiliency and low abrasion, drastically increase the service life of conveyer belt, reduce the use cost of conveyer belt.
Brief description of the drawings
In order to illustrate more clearly about the embodiment of the present invention or technical scheme of the prior art, below will be to embodiment or existing
The accompanying drawing to be used needed for having technology description is briefly described, it should be apparent that, drawings in the following description are only this
Some embodiments of invention, for those of ordinary skill in the art, without having to pay creative labor, may be used also
Other accompanying drawings are obtained with according to these accompanying drawings.
Fig. 1 is cross-sectional structure schematic diagram of the invention;
Fig. 2 is production technological process of the invention.
In figure:1st, upper rubber cover;2nd, belt carcass;21st, sticking adhesive layer;3rd, lower rubber cover;4th, side glue.
Specific embodiment
Below in conjunction with the accompanying drawing in the embodiment of the present invention, the technical scheme in the embodiment of the present invention is carried out clear, complete
Site preparation is described, it is clear that described embodiment is only a part of embodiment of the invention, rather than whole embodiments.It is based on
Embodiment in the present invention, it is every other that those of ordinary skill in the art are obtained under the premise of creative work is not made
Embodiment, belongs to the scope of protection of the invention.
Embodiment 1
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, its cross-sectional structure are as shown in Figure 1:Including belt carcass 2, located at belt carcass 2
The upper rubber cover 1 of upper surface, the lower rubber cover 3 located at the lower surface of belt carcass 2 and the side glue 4 located at the two ends of belt carcass 2, belt carcass 2 are type
Numbers 100 NN canvas, is bonded between each layer NN canvas by sticking adhesive layer 21, and the plunger bond strength of each layer NN canvas is 6.5N/
mm。
Rubber cover includes the component of following parts by weight:50~80 parts of natural rubber, 20~50 parts of synthetic rubber, sulphur
1.6~2.3 parts, 4~6 parts of zinc oxide, 1.5~3 parts of stearic acid, 1.2~2.3 parts of accelerator, 50~70 parts of reinforcing agent, antiwear additive
0.3~2 part, 10~18 parts of softening agent, 2~5 parts of age resistor.
After tested, the physical property of the rubber cover is:Pull apart strength 22Mpa, elongation at break 550%, wear loss
59mm3, hardness 60A(Shao Er), elasticity 44.
Embodiment 2
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, its cross-sectional structure are as shown in Figure 1:Including belt carcass 2, located at belt carcass 2
The upper rubber cover 1 of upper surface, the lower rubber cover 3 located at the lower surface of belt carcass 2 and the side glue 4 located at the two ends of belt carcass 2, belt carcass 2 are type
Number for 200 EP canvas, bonded by sticking adhesive layer 21 between each layer EP canvas, each layer EP canvas plunger bond strength be 12N/
mm。
Rubber cover includes the component of following parts by weight:50 parts of natural rubber, 50 parts of butadiene-styrene rubber, 1.6 parts of sulphur, oxidation
6 parts of zinc, 1.5 parts of stearic acid, 2.3 parts of accelerator, 50 parts of intermediate super abrasion furnace black N220,2 parts of antiwear additive, coumarone indene resin and virtue
15 parts of the mixture of hydrocarbon ils(Wherein, 10 parts of coumarone indene resin, 5 parts of aromatic naphtha), 2 parts of age resistor.
After tested, the physical property of the rubber cover is:Pull apart strength 28Mpa, elongation at break 750%, wear loss
60mm3, hardness 62A(Shao Er), elasticity 50.
Embodiment 3
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, its cross-sectional structure are as shown in Figure 1:Including belt carcass 2, located at belt carcass 2
The upper rubber cover 1 of upper surface, the lower rubber cover 3 located at the lower surface of belt carcass 2 and the side glue 4 located at the two ends of belt carcass 2, belt carcass 2 are type
Number for 400 NN/EP, bonded by sticking adhesive layer 21 between each layer NN/EP canvas, each layer NN/EP canvas plunger bond strengths are
8N/mm。
Rubber cover includes the component of following parts by weight:80 parts of natural rubber, 20 parts of butadiene rubber, 2.3 parts of sulphur, oxidation
4 parts of zinc, 3 parts of stearic acid, 1.2 parts of accelerator, 70 parts of the mixture of intermediate super abrasion furnace black N220 and N330(Wherein, middle super abrasive
40 parts of carbon black N220,30 parts of N330), 0.3 part of antiwear additive, 18 parts of the mixture of coumarone indene resin and aromatic naphtha(Wherein, ancient horse
8 parts of grand resin, 10 parts of aromatic naphtha), 5 parts of age resistor.
After tested, the physical property of the rubber cover is:Pull apart strength 23Mpa, elongation at break 750%, wear loss
50mm3, hardness 65A(Shao Er), elasticity 49.
Embodiment 4
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, its cross-sectional structure are as shown in Figure 1:Including belt carcass 2, located at belt carcass 2
The upper rubber cover 1 of upper surface, the lower rubber cover 3 located at the lower surface of belt carcass 2 and the side glue 4 located at the two ends of belt carcass 2, belt carcass 2 are type
Numbers 250 NN canvas, is bonded between each layer NN canvas by sticking adhesive layer 21, and each layer NN canvas plunger bond strength is 9N/mm.
Rubber cover includes the component of following parts by weight:60 parts of natural rubber, 40 parts of butadiene rubber, 2.0 parts of sulphur, oxidation
5 parts of zinc, 3 parts of stearic acid, 1.2 parts of accelerator, 55 parts of intermediate super abrasion furnace black N220,0.5 part of antiwear additive, coumarone indene resin and virtue
10 parts of the mixture of hydrocarbon ils(Wherein, 2 parts of coumarone indene resin, 8 parts of aromatic naphtha), 4 parts of age resistor.
After tested, the physical property of the rubber cover is:Pull apart strength 25Mpa, elongation at break 630%, wear loss
65mm3, hardness 59A(Shao Er), elasticity 48.
Embodiment 5
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, its cross-sectional structure are as shown in Figure 1:Including belt carcass 2, located at belt carcass 2
The upper rubber cover 1 of upper surface, the lower rubber cover 3 located at the lower surface of belt carcass 2 and the side glue 4 located at the two ends of belt carcass 2, belt carcass 2 are type
Numbers 350 NN/EP canvas, is bonded, each layer NN/EP canvas plunger bond strengths between each layer NN/EP canvas by sticking adhesive layer 21
It is 12N/mm.
Rubber cover includes the component of following parts by weight:60 parts of natural rubber, 40 parts of butadiene-styrene rubber, 2.0 parts of sulphur, oxidation
5 parts of zinc, 3 parts of stearic acid, 1.2 parts of accelerator, 55 parts of the mixture of intermediate super abrasion furnace black N220 and N330(Wherein, middle super abrasive
20 parts of carbon black N220,35 parts of N330), 0.5 part of antiwear additive, 10 parts of the mixture of coumarone indene resin and aromatic naphtha(Wherein, ancient horse
5 parts of grand resin, 5 parts of aromatic naphtha), 4 parts of age resistor.
After tested, the physical property of the rubber cover is:Pull apart strength 22Mpa, elongation at break 650%, wear loss
70mm3, hardness 59A(Shao Er), elasticity 44.
Embodiment 6
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, its cross-sectional structure are as shown in Figure 1:Including belt carcass 2, located at belt carcass 2
The upper rubber cover 1 of upper surface, the lower rubber cover 3 located at the lower surface of belt carcass 2 and the side glue 4 located at the two ends of belt carcass 2, belt carcass 2 are type
Numbers 200 NN canvas, is bonded between each layer NN canvas by sticking adhesive layer 21, and each layer NN canvas plunger bond strength is 11.5N/
mm。
Rubber cover includes the component of following parts by weight:60 parts of natural rubber, 40 parts of butadiene-styrene rubber, 1.8 parts of sulphur, oxidation
5 parts of zinc, 2 parts of stearic acid, 1.3 parts of accelerator, 60 parts of the mixture of intermediate super abrasion furnace black N220 and N330(Wherein, middle super abrasive
30 parts of carbon black N220,30 parts of N330), 0.5 part of antiwear additive, 17 parts of the mixture of coumarone indene resin and aromatic naphtha(Wherein, ancient horse
10 parts of grand resin, 7 parts of aromatic naphtha), 4 parts of age resistor.
After tested, the performance of the rubber cover is:Pull apart strength 20.5Mpa, elongation at break 580%, wear loss
81mm3, hardness 62A(Shao Er), elasticity 43.
Embodiment 7
A kind of high resiliency, wear-resistant, shock resistance conveyer belt, its cross-sectional structure are as shown in Figure 1:Including belt carcass 2, located at belt carcass 2
The upper rubber cover 1 of upper surface, the lower rubber cover 3 located at the lower surface of belt carcass 2 and the side glue 4 located at the two ends of belt carcass 2, belt carcass 2 are type
Numbers 200 EP canvas, is bonded between each layer EP canvas by sticking adhesive layer 21, and each layer EP canvas plunger bond strength is 10.5N/
mm。
Rubber cover includes the component of following parts by weight:50 parts of natural rubber, 50 parts of butadiene-styrene rubber, 2.0 parts of sulphur, oxidation
5 parts of zinc, 3 parts of stearic acid, 1.2 parts of accelerator, 55 parts of the mixture of intermediate super abrasion furnace black N220 and N330(Wherein, middle super abrasive
25 parts of carbon black N220,30 parts of N330), 0.5 part of antiwear additive, 10 parts of the mixture of coumarone indene resin and aromatic naphtha(Wherein, ancient horse
6 parts of grand resin, 4 parts of aromatic naphtha), 4 parts of age resistor.
After tested, the performance of the rubber cover is:Pull apart strength 22.6Mpa, elongation at break 521%, wear loss
62mm3, hardness 65A(Shao Er), elasticity 46.
The preparation technology of the rubber cover used by above-described embodiment 1-7 is as follows:
After natural rubber is through over-mastication, in banbury with synthetic rubber and refine, adding small powder, reinforcing agent, softening agent is carried out
One section of mixing, small powder includes zinc oxide, stearic acid, antiwear additive and age resistor, and one section of rotating speed of mixing is 40r/min, floating weight
Pressure 0.6Mpa, rubber 60s, small powder 20s, reinforcing agent 70s, softening agent 50s, 140 DEG C of dumping slices;
Park more than 16 hours, two-stage mixing, two-stage mixing rotating speed 30r ∕ are carried out to sulphur, accelerator is added in one section of elastomeric compound
Min, ram piston pressure 0.6MPa, one section of elastomeric compound and sulphur promote 90s, rise the s of bolt 20,110 DEG C of dumping slices.
The high resiliency of above-described embodiment 1-7 propositions, wear-resistant, shock resistance conveyer belt the technological process of production are as shown in Figure 2:
Wherein, calendering technology:NN canvas or EP canvas or NN/EP canvas are once rolled into double spreading on four-roll calender
Canvas, canvas rubberizing will have certain thickness, and rubberizing is uniform, does not allow to show money or valuables one carries unintentionally;Glue is continuously supplied by extruder heat refining for glue
Or mill heat refining supplies glue, film can on calender slice, it is also possible to double finished product belt carcass is disposably combined in four-roller
Upper and lower overlap film;
Moulding process:By determining tension force or identical tension forming machine, calendering canvas is built up into belt carcass, its technique and duck conveyor belt into
Type technique is identical;
Sulfuration process:Vulcanization compression ratio 4~10%, other are identical with duck conveyor belt sulfuration process.
Claims (8)
1. a kind of high resiliency, wear-resistant, shock resistance conveyer belt, including belt carcass and rubber cover, it is characterised in that the belt carcass is NN
One kind in canvas, EP canvas or NN/EP canvas, the rubber cover includes the component of following parts by weight:Natural rubber 50~
80 parts, 20~50 parts of synthetic rubber, 1.6~2.3 parts of sulphur, 4~6 parts of zinc oxide, 1.5~3 parts of stearic acid, accelerator 1.2~
2.3 parts, 50~70 parts of reinforcing agent, 0.3~2 part of antiwear additive, 10~18 parts of softening agent, 2~5 parts of age resistor.
2. high resiliency according to claim 1, wear-resistant, shock resistance conveyer belt, it is characterised in that the rubber cover includes
The component of following parts by weight:60 parts of natural rubber, 40 parts of synthetic rubber, 2.0 parts of sulphur, 5 parts of zinc oxide, 3 parts of stearic acid promotees
Enter 1.2 parts of agent, 55 parts of reinforcing agent, 0.5 part of antiwear additive, 10 parts of softening agent, 4 parts of age resistor.
3. high resiliency according to claim 1, wear-resistant, shock resistance conveyer belt, it is characterised in that the NN canvas, institute
The model 100~400 of EP canvas or the NN/EP canvas is stated, the NN canvas, the EP canvas or the NN/EP canvas
Plunger bond strength is 6.5~12N/mm.
4. high resiliency according to claim 1 and 2, wear-resistant, shock resistance conveyer belt, it is characterised in that the rubber cover
Physical property requirements be:Pull apart strength >=18Mpa, elongation at break >=450%, wear loss≤90mm3, hardness 56~
65A(Shao Er).
5. high resiliency according to claim 1 and 2, wear-resistant, shock resistance conveyer belt, it is characterised in that the synthesis rubber
Glue is butadiene rubber or butadiene-styrene rubber.
6. high resiliency according to claim 1 and 2, wear-resistant, shock resistance conveyer belt, it is characterised in that the reinforcing agent
It is intermediate super abrasion furnace black N220 or the mixture of intermediate super abrasion furnace black N220 and N330.
7. high resiliency according to claim 1 and 2, wear-resistant, shock resistance conveyer belt, it is characterised in that the softening agent
It is coumarone indene resin and the mixture of aromatic naphtha.
8. a kind of high resiliency as claimed in claim 1, wear-resistant, shock resistance conveyer belt preparation method, it is characterised in that first
The rubber cover is prepared, the preparation method of the rubber cover is as follows:
After natural rubber is through over-mastication, in banbury with synthetic rubber and refine, adding small powder, reinforcing agent, softening agent is carried out
One section mixing, the small powder include zinc oxide, stearic acid, antiwear additive and age resistor, one section mixing rotating speed for 40r/min, on
Push up bolt pressure 0.6Mpa, rubber 60s, small powder 20s, reinforcing agent 70s, softening agent 50s, 140 DEG C of dumping slices;Park 16 hours with
On, carry out two-stage mixing, two-stage mixing rotating speed 30r ∕ min, ram piston pressure to sulphur, accelerator is added in one section of elastomeric compound
0.6MPa, one section of elastomeric compound and sulphur promote 90s, rise the s of bolt 20,110 DEG C of dumping slices.