CN106863532A - A kind of preparation method of wooden nicking disc - Google Patents
A kind of preparation method of wooden nicking disc Download PDFInfo
- Publication number
- CN106863532A CN106863532A CN201710078824.4A CN201710078824A CN106863532A CN 106863532 A CN106863532 A CN 106863532A CN 201710078824 A CN201710078824 A CN 201710078824A CN 106863532 A CN106863532 A CN 106863532A
- Authority
- CN
- China
- Prior art keywords
- preparation
- nicking
- wooden
- plank
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to hammer-shears lithography field, and in particular to a kind of preparation method of wooden nicking disc.The preparation method of a kind of wooden nicking disc that the present invention is provided, including the formula that the soak for preparing is compounded with ammoniacal liquor, hydrogen peroxide and Boratex, it can obtain wood fibre softening effect under interaction, temperature hot iron wax stone using 60 75 DEG C after to be dried is allowed to dissolve into wood-fibred, wax stone can well be dissolved, do not result in wooden carbonization and scorch disk body, moreover it is possible to the suppleness of smoothness and disk body when increasing feed yet.The present invention is changed patch and can be improved the maintenanceability and service life of disk body with what same material and handling process were made, while having simple production process, advantage cheap for manufacturing cost, performance is substantially better than various handicraft backing plates common at present.
Description
Technical field
The invention belongs to hammer-shears lithography field, more particularly, to a kind of preparation method of wooden nicking disc.
Background technology
At present, the manual part for using icking tool scribe by hand and multi-purpose cutter is carried out perhaps makes, and is required in handicraft pad
Completed on plate such as paper-cut, carve characters, needle drawing, paper are carved, figure for shadow-play, common similar backing plate has two kinds, and one kind is to be with PVC or rubber
Raw material are made, and this backing plate is generally block piece, and volume is relatively thin, and the partially hard climate influence of quality is larger, suitably does plane
Nicking and scribing use.But uncomfortable cooperation point of a knife is vertical, and the lifting sword for going deep into test cuts motion, and, when deeper with knife
Backing plate is easily carved, if there is defect also inconvenience repairing.Another kind is the cake wax and food tray of traditional paper-cut, and it is to use stone
Wax, plant ash or animal fat etc. are made, and this kind of backing plate quality soft can bundle deeply partially is engraved, and unsuitable plane scribing cutting, right
In fine works, carving layer should not be too thick, otherwise occurs and smashes nest phenomenon.Easy permeability easy during knife is transported, can adhesion work
Product are polluted and damaged.At present, its can only one side use, there is also indentation overlap, card occur injustice phenomenon,
Recover preferable use state operation, it is more cumbersome.
Patent CN204432205U discloses a kind of coordinate engraving machine of numerical control three, including engraving platform, is set on engraving platform
There are two longitudinal slide rails and a zigzag tread patterns tooth bar, longitudinal beam is provided between longitudinal slide rail, one is fixed with longitudinal beam and is indulged
To motor, longitudinal motor main shaft is provided with a zigzag tread patterns gear, and longitudinal beam is provided with two horizontal slide rails and a transverse direction
Tooth bar is driven, horizontal slide rail is provided with cross slide, a cross motor is fixed with cross slide, on the main shaft of cross motor
A laterally driven gear is provided with, three groups of vertical rails and three vertical drive cylinders are equipped with cross slide, every group vertical
Slide rail is provided with one piece of vertical slide plate, be sequentially provided with three pieces of fixed glides a longitudinal graver, a vertical graver and
One horizontal graver.But the patent is not disclosed both can make deeper knife edge thorn with the vertical plane cutting-up of cutting edge again
Visit lifting sword to cut, the easy wooden two-sided interchangeable benefit nicking disc for using of maintenance.
The content of the invention
The technical problem to be solved in the present invention is, the invention provides a kind of preparation method of wooden nicking disc, both
Can the vertical plane cutting-up of cutting edge, the deeper knife edge can be made again spy lifting sword to cut, and easy wooden two-sided of maintenance using
Benefit nicking disc can be changed, it has knife sense good, the flat very adhesion of card carves part, can finely be engraved, and can locally change
The superiority of damage is studied for a second time courses one has flunked, longer service life can be provided.
To solve the above problems, the preparation method of a kind of wooden nicking disc that the present invention is provided is comprised the following steps：
Step 1) the recent trees felled first are removed into bark obtain log, log is then cut transversely into certain thickness
Plank, then the plank uniform coding is placed on relative air humidity for 30%~40%, temperature is 20-30 DEG C of ventilated environment
In, the Free water uniformly rushed in the lumen for scanning out plank with the compressed air of 200-230kPa, for reducing the aqueous of plank
Amount；
Step 2) 30 parts~40 parts of the ammoniacal liquor of 28% concentration, the hydrogen peroxide 29 parts~30 of 35% concentration are prepared by weight
Part, 1 part~2 parts of Boratex, 35 parts~40 parts of pure water, after stirring, the plank that will be obtained in step 1, soak at room temperature is extremely
Pulled out after few 24 hours, neutralizer, soak at room temperature 10 hours are prepared with 1.2%~4.0% acetic acid or oxalic acid after carrying out control water
After pull out, then the moisture swept in plank is uniformly rushed with the compressed air of 200-230kPa, after obtaining fiber softening and acid-base neutralization
Plank；
Step 3) plank after the fiber softening that will be obtained in step 2 and acid-base neutralization, to containing in timber drier
Water rate 8-15%；
Step 4) according to the requirement of processing specification, machine carried out after step 3 cut out to piece together and be pre-designed the several of specification shape
What is block, then is tightened with hoop and prevent cracking；
Step 5) for the position that has medulla, with the drill bit more than plank medulla diameter, single hole is bored and removes medulla position；
Step 6) using after with the timber gluing of diameter volume, the bore position in step 5 is carried out to change benefit；
Step 7) timber through being compressed in step 6, then be 60-75 with temperature after being polished smooth with sander surface
DEG C flatiron by paraffin：Beeswax presses 1~1.5:1~1.5 ratio, the wood fibre in the nicking disk wooden to this carries out hot iron and oozes
Thoroughly；
Step 8) wood fibre to being obtained after hot iron infiltration in step 7 carries out nature cool place, and remaining wax is removed, then carry out
Sanding and polishing, completes the making of nicking disk disk body.
Preferred technical scheme, the preparation method is further comprising the steps of：
Step 9) plank for completing as above technique is cut into the fritter solid of same thickness plurality of specifications, it is used for
Patch is changed, the disk body local damage for replacing repairing nicking disk；
Step 10) when carrying out changing benefit operation in step 9, need to will be slightly larger than and damage the local patch that changes and cover the part,
With thinner paintbrush, along the edge for changing patch, contour line is drawn；
Step 11) reserved along the interior lines of contour line and be slightly less than the distance for changing patch edge, with icking tool tip perpendicular to
Card, makees repeatedly test formula and operates deeply, to carving disk body；
Step 12) take out and damage part after, carving hole wall and change patch side and apply glue, be allowed in force embedded hole with
Repairing is completed by card is equal to continue normally to use.
Preferred technical scheme, the preparation method includes step 3) drying steps, the plank phase of the drying steps
It is 35% to humidity, temperature is 20-30 DEG C, and moisture content is 12%.
Preferred technical scheme, the preparation method, including step 2) in the ammonia for being prepared as 28% concentration by weight
30 parts of water, 29 parts of the hydrogen peroxide of 35% concentration, 1 part of Boratex, 40 parts of pure water, after stirring, soak at room temperature is after 24 hours
Pull out.
Preferred technical scheme, the preparation method includes being matched somebody with somebody with 1.2% or 1.5% acetic acid or oxalic acid after carrying out control water
Neutralizer processed.
Preferred technical scheme, the preparation method includes step 7) with sander polish surface it is smooth after, hot iron infiltration
The temperature for controlling of flatiron is 60 DEG C, 68 DEG C, 70 DEG C or 75 DEG C in step.
Preferred technical scheme, the preparation method includes step 7) with sander polish surface it is smooth after, be with temperature
60-75 DEG C of flatiron is by paraffin：Beeswax presses 1:1 ratio, the wood fibre in the nicking disk wooden to this carries out hot iron infiltration.
Preferred technical scheme, step 1) described in log be soft wealthy trees.
The present invention provides a kind of preparation method of wooden nicking disc, with following invention effect：
1) formula that chip impregnation liquid prepared by the present invention is compounded with ammoniacal liquor, hydrogen peroxide and Boratex, can be in phase
Under interaction, preferable wood fibre softening effect is obtained, while preferably bleaching and antiseptic effect can be obtained.
2) it is allowed to dissolve into wood-fibred using 60-75 DEG C of temperature hot iron wax stone, can well dissolves wax stone, also will not
Wooden carbonization is caused to scorch disk body.
3) use for changing patch improves the maintenanceability of disk body, and service life.
4) invention has knife sense good, and card is flat very, and adhesion carves part, is suitable for and finely engraves, and can locally change and study for a second time courses one has flunked damage
Superiority and longer service life.
5) present invention has simple production process simultaneously, cheap for manufacturing cost, and performance is substantially better than common at present various
The advantage of handicraft backing plate.
Brief description of the drawings
Fig. 1 is the structural representation of the middle log of the preparation method of wooden nicking disc of the present invention；
Fig. 2 is cross section and the geometry block structural diagram of the middle log of the preparation method of wooden nicking disc of the present invention；
Fig. 3 be wooden nicking disc of the present invention preparation method in dewaxing and hot iron step schematic diagram；
Fig. 4 be wooden nicking disc of the present invention preparation method in it is parallel fortune knife scribing schematic diagram；
Fig. 5 be wooden nicking disc of the present invention preparation method in push fortune knife cutting schematic diagram；
Fig. 6 is the scribing steps schematic diagram in the preparation method of wooden nicking disc of the present invention；
Fig. 7 be wooden nicking disc of the present invention preparation method in change the use state schematic diagram of patch.
Specific embodiment
Specific embodiment of the invention is described in detail below with reference to accompanying drawing.
Embodiment 1
As shown in Fig. 1 to 7, the preparation method of a kind of wooden nicking disc that the present invention is provided is comprised the following steps：
Step 1) the recent fresh trees felled first are removed into bark obtain log, then log is cut transversely into necessarily
The plank of thickness, in the present embodiment, the log is soft wealthy trees, such as poplar or birch, moreover it is possible to from wooden compared with hard
Timber such as toothed oak wood or pine, the thickness of the plank is preferably 10mm~20mm, then that the plank uniform coding is placed on into air is relative
Humidity is 30%~40%, during temperature is for 20-30 DEG C of ventilated environment, is uniformly rushed with the compressed air of 200-230kPa and scans out wood
Free water in the lumen of plate, for reducing the water content of plank；
Step 2) 30 parts~40 parts of the ammoniacal liquor of 28% concentration, the hydrogen peroxide 29 parts~30 of 35% concentration are prepared by weight
Part, 1 part~2 parts of Boratex, 35 parts~40 parts of pure water, after stirring, the plank that will be obtained in step 1, soak at room temperature is extremely
Pulled out after few 24 hours, neutralizer, soak at room temperature 10 hours are prepared with 1.2%~4.0% acetic acid or oxalic acid after carrying out control water
After pull out, then the moisture swept in plank is uniformly rushed with the compressed air of 200-230kPa, obtain neutralizing dried plank；
Step 3) plank after the fiber softening that will be obtained in step 2 and acid-base neutralization, dried in timber drier
Or dry naturally, relative humidity is 35%, during temperature is for 20-30 DEG C of environment, to moisture content 8-15%；
Step 4) according to the requirement of processing specification, machine carried out after step 3 cut out to piece together and be pre-designed the several of specification shape
What is block, then is tightened with hoop and prevent cracking；
Step 5) for the position that has medulla, with the drill bit slightly larger than plank medulla diameter, single hole is bored and removes medulla position；
Step 6) using after with the supporting timber gluing of diameter volume, the bore position in step 5 carries out changing benefit；
Step 7) timber through being compressed in step 6, then be 60-75 with temperature after being polished smooth with sander surface
DEG C flatiron by paraffin：Beeswax presses 1~1.5:1~1.5 ratio, the wood fibre in the nicking disk wooden to this carries out hot iron and oozes
Thoroughly, it is preferred that paraffin：Beeswax presses 1:1 ratio；
Step 8) plank to being obtained after hot iron infiltration in step 7 carries out nature cool place, and remaining wax is removed, then polished
Polishing, completes the making of nicking disk disk body；
Step 9) plank for completing as above technique is cut into the fritter solid of same thickness plurality of specifications, it is used for
Patch is changed, the disk body local damage for replacing repairing nicking disk；
Step 10) when carrying out changing benefit operation in step 9, need to will be slightly larger than and damage the local patch that changes and cover the part,
With thinner paintbrush, along the edge for changing patch, contour line is drawn；
Step 11) distance that patch edge is changed described in being slightly less than is reserved along the interior lines of contour line, the tip with icking tool is vertical
In card, make repeated multiple times test formula and operate deeply, until carving disk body；
Step 12) take out and damage part after, carving hole wall and changing patch side and apply glue, force is allowed in the embedded hole
Plane with card is equal, you can completes repairing and continues normally to use.
Embodiment 2
The present embodiment is further improved on the basis of embodiment 1, and difference is that the wooden of offer of the invention being cut
The preparation method for carving disc, the preparation method includes step 3) dry step naturally, it is described to dry the relative of step naturally
Humidity is 35%, and temperature is 20-30 DEG C, and moisture content is 12%.Wherein preferred technical scheme is that the preparation method is wrapped
Include step 2) in 30 parts of ammoniacal liquor for being prepared as 28% concentration by weight, 29 parts of the hydrogen peroxide of 35% concentration, 1 part of Boratex,
40 parts of pure water, after stirring, soak at room temperature is pulled out after 24 hours.Therein, the preparation method preferably includes to be controlled
After water neutralizer is prepared with 1.2% or 1.5% acetic acid or oxalic acid.In wherein the step of, the preparation method includes preferred
In step, preferred steps 7) using sander polish surface it is smooth after, the temperature for controlling of flatiron is 60 in hot iron impregnation step
DEG C, 68 DEG C, 70 DEG C or 75 DEG C, the preparation method include step 7) with sander polish surface it is smooth after, be 60-75 with temperature
DEG C flatiron by paraffin：Beeswax presses 1:1 ratio, wood fibre of plank carries out hot iron infiltration in the nicking disk wooden to this.
Embodiment 3
Embodiment is further improved on the basis of embodiment 1 and embodiment 2, and difference is that the present invention is provided
Wooden nicking disc preparation method, also included step：Compression with 200-230kPa after neutralizer immersion is completed is empty
After the gas moisture that uniformly punching is swept in plank, being put into boiling pond carries out heat and boils treatment, and initial processing temperature is 20-25 DEG C, intensification
Speed is to slow down programming rate when 10-15 DEG C is warming up to more than 40 DEG C per hour.Process time piles up cool place to pull out within 24 hours
Uniformly rush the moisture swept in wood chip with the compressed air of 200-230kPa again afterwards and be then dried treatment.
The preferred embodiments of the disclosure and embodiment are explained in detail above in conjunction with accompanying drawing, but it is of the invention
The above-described embodiment and examples are not limited to, in the ken that those skilled in the art possess, can also not taken off
Make a variety of changes on the premise of the present inventive concept.
Claims (8)
1. a kind of preparation method of wooden nicking disc, it is characterised in that the preparation method is comprised the following steps：
Step 1) the recent trees felled first are removed into bark obtain log, log is then cut transversely into certain thickness wood
Plate, then it is 30%~40% that the plank uniform coding is placed on into relative air humidity, during temperature is for 20-30 DEG C of ventilated environment, is used
The Free water that the compressed air of 200-230kPa is uniformly rushed in the lumen for scanning out plank, for reducing the water content of plank；
Step 2) prepare 30 parts~40 parts of the ammoniacal liquor of 28% concentration by weight, 29 parts of the hydrogen peroxide of 35% concentration~30 parts, boron
1 part~2 parts of sour sodium, 35 parts~40 parts of pure water after stirring, will obtain crosscutting plank in step 1, soak at room temperature is at least
Pulled out after 24 hours, neutralizer is prepared with 1.2%~4.0% acetic acid or oxalic acid after carrying out control water, soak at room temperature is after 10 hours
Pull out, then the moisture swept in plank is uniformly rushed with the compressed air of 200-230kPa, after obtaining fiber softening and acid-base neutralization
Plank；
Step 3) plank after the fiber softening that will be obtained in step 2 and acid-base neutralization, to containing in timber drier drying
Water rate 8-15%；
Step 4) according to the requirement of processing specification, machine is carried out after step 3 and cuts out the geometry for piecing together the specification shape being pre-designed
Bulk, then tightened with hoop prevent cracking；
Step 5) for the position that has medulla, with the drill bit more than plank medulla diameter, single hole is bored and removes medulla position；
Step 6) using after with the supporting timber gluing of diameter volume, the bore position in step 5 is carried out to change benefit；
Step 7) timber after being processed in step 6, then be 60-75 DEG C with temperature after being polished smooth with sander surface
Flatiron paraffin and beeswax are pressed 1~1.5:1~1.5 ratio, the wood fibre in the nicking disk wooden to this carries out hot iron and oozes
Thoroughly；
Step 8) plank to being obtained after hot iron infiltration in step 7 carries out nature cool place, and remaining wax is removed, then carry out polishing throwing
Light, completes the making of nicking disk disk body.
2. the preparation method of wooden nicking disc according to claim 1, it is characterised in that the preparation method also include with
Lower step：
Step 9) plank for completing as above technique is cut into the fritter solid of same thickness plurality of specifications, for changing
Patch, the disk body local damage for replacing repairing nicking disk；
Step 10) when carrying out changing benefit operation in step 9, need to will be greater than damaging the local patch that changes and cover the part, with thinner
Paintbrush, along the edge for changing patch, draw contour line；
Step 11) reserved less than the distance for changing patch edge along the interior lines of contour line, with the tip of icking tool perpendicular to card,
Make repeated multiple times test formula to operate deeply, until carving disk body；
Step 12) take out and damage part after, in delineation hole wall and change patch side and apply glue, be allowed to and disk in force embedded hole
Face is equal, you can completes repairing and continues normally to use.
3. the preparation method of wooden nicking disc according to claim 1, it is characterised in that the preparation method includes step
3) drying steps, the relative humidity of the drying steps is 35%, and temperature is 20-30 DEG C, and moisture content is 12%.
4. the preparation method of wooden nicking disc according to claim 1, it is characterised in that the preparation method, including step
It is rapid 2) in 30 parts of ammoniacal liquor for being prepared as 28% concentration by weight, 29 parts of the hydrogen peroxide of 35% concentration, 1 part of Boratex is pure
40 parts of water, after stirring, soak at room temperature is pulled out after 24 hours.
5. the preparation method of wooden nicking disc according to claim 4, it is characterised in that the preparation method includes carrying out
After control water neutralizer step is prepared with 1.2% or 1.5% acetic acid or oxalic acid.
6. the preparation method of wooden nicking disc according to claim 1, it is characterised in that the preparation method includes step
7) in sander polish surface it is smooth after, in hot iron impregnation step the temperature for controlling of flatiron be 60 DEG C, 68 DEG C, 70 DEG C or 75
℃。
7. the preparation method of wooden nicking disc according to claim 1, it is characterised in that the preparation method includes step
7) with sander polish surface it is smooth after, with the flatiron that temperature is 60-75 DEG C by paraffin：Beeswax presses 1:1 ratio, it is wooden to this
Wood fibre in nicking disk carries out hot iron infiltration.
8. the preparation method of wooden nicking disc according to claim 1, it is characterised in that step 1) described in log be soft
Wealthy trees.