CN106863532B - A kind of production method of wooden nicking disc - Google Patents
A kind of production method of wooden nicking disc Download PDFInfo
- Publication number
- CN106863532B CN106863532B CN201710078824.4A CN201710078824A CN106863532B CN 106863532 B CN106863532 B CN 106863532B CN 201710078824 A CN201710078824 A CN 201710078824A CN 106863532 B CN106863532 B CN 106863532B
- Authority
- CN
- China
- Prior art keywords
- production method
- nicking
- wooden
- plank
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to hammer-shears lithography fields, and in particular to a kind of production method of wooden nicking disc.A kind of production method of wooden nicking disc provided by the invention, the formula that soak including preparation is compounded with ammonium hydroxide, hydrogen peroxide and Boratex, it can obtain wood fibre softening effect under interaction, it is allowed to dissolve into wood-fibred using 60 75 DEG C of temperature hot iron wax stone after to be dried, wax stone can be dissolved well, wooden carbonization will not be caused to scorch disk body, moreover it is possible to increase the suppleness of the smoothness and disk body when feed.The present invention can improve the maintenanceability and service life of disk body to change patch made of same material and treatment process, while have simple production process, the cheap advantage of manufacturing cost, and performance is substantially better than a variety of handicraft backing plates common at present.
Description
Technical field
The invention belongs to hammer-shears lithography fields, more particularly, to a kind of production method of wooden nicking disc.
Background technology
Currently, being made using the manual part that icking tool scribe by hand and multi-purpose cutter carries out perhaps, it is required in handicraft pad
On plate complete such as paper-cut, carve characters, needle drawing, paper carve, figure for shadow-play, there are two types of common similar backing plates, and one is be with PVC or rubber
Raw material are made, and this backing plate is mostly piece bulk, and volume is relatively thin, and texture is too hard, and climate is affected, suitable for doing plane
Nicking and scribing use.But uncomfortable cooperation point of a knife is vertical, and the lifting sword for going deep into test cuts movement, moreover, when deeper with knife
It is easy to carve saturating backing plate, be repaired if there is defect is also inconvenient.Another kind is the cake wax and food tray of traditional paper-cut, is to use stone
Wax, plant ash or animal fat etc. are made, and this kind of backing plate quality soft can prick deeply partially is engraved, and unsuitable plane scribing cutting, right
In fine works, carving layer should not be too thick, otherwise will appear and smashes nest phenomenon.It is easy to be easy permeability during transporting knife, it can adhesion work
Product are polluted and are damaged.Currently, its can only single side use, there is also indentation overlapping, disk will appear uneven phenomenon,
Restore preferable use state process, it is more cumbersome.
Patent CN204432205U discloses a kind of three coordinate engraving machine of numerical control, including engraving platform, carves and is set on platform
There are two longitudinal slide rails and a zigzag tread patterns rack, be equipped with longitudinal beam between longitudinal slide rail, fixed on longitudinal beam there are one vertical
To motor, set on longitudinal motor main shaft there are one zigzag tread patterns gear, longitudinal beam is equipped with two horizontal slide rails and a transverse direction
Drive rack, horizontal slide rail are equipped with cross slide, fixed there are one cross motor on cross slide, on the main shaft of cross motor
If there are one laterally driven gear, three groups of vertical rails and three vertical driving cylinders are equipped on cross slide, every group vertical
Sliding rail is equipped with one piece of vertical slide plate, set successively in three pieces of fixed glides there are one longitudinal graver, a vertical graver and
One lateral graver.But do not disclose not only can be with the vertical plane cutting-up of cutting edge for the patent, but also deeper knife edge thorn can be made
It visits lifting sword to cut, the wooden two-sided interchangeable benefit nicking disc used of maintenance simplicity.
Invention content
The technical problem to be solved in the present invention is that the present invention provides a kind of production methods of wooden nicking disc, both
Can the vertical plane cutting-up of cutting edge, and the deeper knife edge can be made spy lifting sword to cut, and the wooden two-sided use of maintenance simplicity
It can change and mend nicking disc, good with knife sense, the flat very adhesion of disk carves part, can finely be engraved, and can locally change
The superiority of damage is studied for a second time courses one has flunked, longer service life can be provided.
To solve the above problems, a kind of production method of wooden nicking disc provided by the invention, includes the following steps：
The trees felled in the recent period are first removed bark and obtain log by step 1), then by log be cut transversely into 10mm~
The plank of 20mm thickness, then it is 30%~40% that the plank uniform coding, which is placed on relative air humidity, temperature are 20-30 DEG C logical
In wind environment, the Free water in the lumen for scanning out plank is uniformly rushed with the compressed air of 200-230kPa, for reducing plank
Water content；
Step 2) prepares 30 parts~40 parts of the ammonium hydroxide of 28% concentration, the hydrogen peroxide 29 parts~30 of 35% concentration by weight
Part, 1 part~2 parts of Boratex, 35 parts~40 parts of pure water, after stirring evenly, the plank that will be obtained in step 1, soak at room temperature is extremely
It is pulled out after few 24 hours, carries out acetic acid or oxalic acid the preparation neutralizer with 1.2%~4.0%, soak at room temperature 10 hours after control water
After pull out, then the moisture swept in plank is uniformly rushed with the compressed air of 200-230kPa, after obtaining fiber softening and acid-base neutralization
Plank；
Step 3) is by the plank after the fiber softening obtained in step 2 and acid-base neutralization, to containing in timber drier
Water rate 8-15%；
For step 4) according to the requirement of processing specification, progress machine sanction, which pieces together, after step 3 is pre-designed the several of specification shape
What is blocky, then is tightened with hoop to prevent from cracking；
Step 5) is for there is the position of medulla, and with the drill bit more than plank medulla diameter, single hole, which bores, removes medulla position；
After step 6) is used with the timber gluing of diameter volume, the bore position in step 5 is carried out to change benefit；
Timber of the step 7) through being compressed in step 6, then be 60-75 with temperature after being polished smooth with sander surface
DEG C flatiron by paraffin：Beeswax presses 1~1.5:1~1.5 ratio, the wood fibre in the nicking disk wooden to this carry out hot iron and ooze
Thoroughly；
Step 8) carries out nature cool place to the wood fibre obtained after hot iron infiltration in step 7, and removes remaining wax, then carries out
Sanding and polishing completes the making of nicking disk disk body；
The plank for completing technique as above is cut into the fritter solid of same thickness plurality of specifications by step 9), is used for
Patch is changed, the disk body local damage for replacing repairing nicking disk；
When carrying out changing benefit operation in step 10) step 9, the patch that changes that need to will be slightly larger than damage part covers the part,
With thinner paintbrush contour line is drawn along the edge for changing patch；
Step 11) is reserved along the interior lines of contour line is slightly less than the distance for changing patch edge, with icking tool tip perpendicular to
Disk is made repeatedly test formula and is operated deeply, until carving disk body；
After step 12) takes out damage part, carving hole wall and changing patch side and apply glue, be allowed in the embedded hole that exerts a force with
Disk is equal to can be completed repairing continuation normal use.
Preferred technical solution, the production method include the drying steps of step 3), the plank phase of the drying steps
It is 35% to humidity, temperature is 20-30 DEG C, moisture content 12%.
Preferred technical solution, the production method, including the ammonia for being prepared as 28% concentration by weight in step 2)
30 parts of water, 29 parts of the hydrogen peroxide of 35% concentration, 1 part of Boratex, 40 parts of pure water, after stirring evenly, soak at room temperature is after 24 hours
It pulls out.
Preferred technical solution, the production method include being matched with 1.2% or 1.5% acetic acid or oxalic acid after carrying out control water
Neutralizer processed.
Preferred technical solution, the production method include step 7) with sander polish surface it is smooth after, hot iron infiltration
The temperature of the control of flatiron is 60 DEG C, 68 DEG C, 70 DEG C or 75 DEG C in step.
Preferred technical solution, the production method include step 7) with sander polish surface it is smooth after, be with temperature
60-75 DEG C of flatiron is by paraffin：Beeswax presses 1:1 ratio, the wood fibre in the nicking disk wooden to this carry out hot iron infiltration.
Preferred technical solution, log described in step 1) are soft wealthy trees.
The present invention provides a kind of production method of wooden nicking disc, has following invention effect：
1) formula that chip impregnation liquid prepared by the present invention is compounded with ammonium hydroxide, hydrogen peroxide and Boratex, can be in phase
Under interaction, preferable wood fibre softening effect is obtained, while preferable bleaching and anti-corrosion effect can be obtained.
2) it is allowed to dissolve into wood-fibred using 60-75 DEG C of temperature hot iron wax stone, wax stone can be dissolved well, it will not
Wooden carbonization is caused to scorch disk body.
3) use for changing patch improves the maintenanceability and service life of disk body.
4) invention has knife sense good, and disk is flat very, and adhesion carves part, is suitable for and finely engraves, can locally change and study for a second time courses one has flunked damage
Superiority and longer service life.
5) present invention has simple production process simultaneously, and manufacturing cost is cheap, and performance is substantially better than common at present a variety of
The advantages of handicraft backing plate.
Description of the drawings
Fig. 1 is the structural schematic diagram of the middle log of the production method of wooden nicking disc of the present invention；
Fig. 2 is cross section and the geometry block structural diagram of the middle log of the production method of wooden nicking disc of the present invention；
Fig. 3 be wooden nicking disc of the present invention production method in dewaxing and hot iron step schematic diagram；
Fig. 4 be wooden nicking disc of the present invention production method in it is parallel fortune knife scribing schematic diagram；
Fig. 5 be wooden nicking disc of the present invention production method in push fortune knife cutting schematic diagram；
Fig. 6 is the scribing steps schematic diagram in the production method of wooden nicking disc of the present invention；
Fig. 7 be wooden nicking disc of the present invention production method in change the use state diagram of patch.
Specific implementation mode
Specific embodiments of the present invention are described in detail below with reference to attached drawing.
Embodiment 1
As shown in Fig. 1 to 7, a kind of production method of wooden nicking disc provided by the invention includes the following steps：
The fresh trees felled in the recent period are first removed bark and obtain log by step 1), are then cut transversely into log centainly
The plank of thickness, in the present embodiment, the log is soft wealthy trees, such as poplar or birch, moreover it is possible to be selected wooden compared with hard
Timber such as toothed oak wood or pine, the thickness of the plank is preferably 10mm~20mm, then that the plank uniform coding is placed on air is opposite
Humidity is 30%~40%, in the ventilated environment that temperature is 20-30 DEG C, is uniformly rushed with the compressed air of 200-230kPa and scans out wood
Free water in the lumen of plate, for reducing the water content of plank；
Step 2) prepares 30 parts~40 parts of the ammonium hydroxide of 28% concentration, the hydrogen peroxide 29 parts~30 of 35% concentration by weight
Part, 1 part~2 parts of Boratex, 35 parts~40 parts of pure water, after stirring evenly, the plank that will be obtained in step 1, soak at room temperature is extremely
It is pulled out after few 24 hours, carries out acetic acid or oxalic acid the preparation neutralizer with 1.2%~4.0%, soak at room temperature 10 hours after control water
After pull out, then the moisture swept in plank is uniformly rushed with the compressed air of 200-230kPa, obtain neutralizing it is dry after plank；
Step 3) dries the plank after the fiber softening obtained in step 2 and acid-base neutralization in timber drier
Or naturally dry, relative humidity 35%, temperature are in 20-30 DEG C of environment, until moisture content 8-15%；
For step 4) according to the requirement of processing specification, progress machine sanction, which pieces together, after step 3 is pre-designed the several of specification shape
What is blocky, then is tightened with hoop to prevent from cracking；
Step 5) is for there is the position of medulla, and with the drill bit slightly larger than plank medulla diameter, single hole, which bores, removes medulla position；
After step 6) is used with the mating timber gluing of diameter volume, the bore position in step 5 carries out changing benefit；
Timber of the step 7) through being compressed in step 6, then be 60-75 with temperature after being polished smooth with sander surface
DEG C flatiron by paraffin：Beeswax presses 1~1.5:1~1.5 ratio, the wood fibre in the nicking disk wooden to this carry out hot iron and ooze
Thoroughly, it is preferred that paraffin：Beeswax presses 1:1 ratio；
Step 8) carries out nature cool place to the plank obtained after hot iron infiltration in step 7, and removes remaining wax, then polishes
The making of nicking disk disk body is completed in polishing；
The plank for completing technique as above is cut into the fritter solid of same thickness plurality of specifications by step 9), is used for
Patch is changed, the disk body local damage for replacing repairing nicking disk；
When carrying out changing benefit operation in step 10) step 9, the patch that changes that need to will be slightly larger than damage part covers the part,
With thinner paintbrush contour line is drawn along the edge for changing patch；
Step 11) is reserved along the interior lines of contour line is slightly less than the distance for changing patch edge, vertical with the tip of icking tool
In disk, make repeated multiple times test formula and operate deeply, until carving saturating disk body；
It after step 12) takes out damage part, applies glue carving hole wall and changing patch side, is allowed in the embedded hole that exerts a force
It is equal with the plane of disk, you can to complete repairing and continue normal use.
Embodiment 2
The present embodiment is further improved on the basis of embodiment 1, and difference lies in provided by the invention wooden to cut
The production method for carving disc, the production method include the naturally dry step of step 3), the naturally dry step it is opposite
Humidity is 35%, and temperature is 20-30 DEG C, moisture content 12%.Wherein preferred technical solution is the production method, packet
Include 30 parts of the ammonium hydroxide for being prepared as 28% concentration by weight in step 2), 29 parts of the hydrogen peroxide of 35% concentration, 1 part of Boratex,
40 parts of pure water, after stirring evenly, soak at room temperature is pulled out after 24 hours.Therein, the production method preferably includes to be controlled
After water neutralizer is prepared with 1.2% or 1.5% acetic acid or oxalic acid.In wherein the step of, the production method includes preferred
In step, preferred steps 7) using sander polishing surface it is smooth after, the temperature of the control of flatiron is 60 in hot iron impregnation step
DEG C, 68 DEG C, 70 DEG C or 75 DEG C, the production method include step 7) with sander polish surface it is smooth after, be 60-75 with temperature
DEG C flatiron by paraffin：Beeswax presses 1:1 ratio, the wood fibre of plank carries out hot iron infiltration in the nicking disk wooden to this.
Embodiment 3
Embodiment is further improved on the basis of embodiment 1 and embodiment 2, and difference lies in the present invention provides
Wooden nicking disc production method, also included step：It is empty with the compression of 200-230kPa after completing neutralizer and impregnating
After gas uniformly rushes the moisture swept in plank, it is put into progress heat in boiling pond and boils processing, initial processing temperature is 20-25 DEG C, heating
Speed is to slow down heating rate when 10-15 DEG C is warming up to 40 DEG C or more per hour.Processing time is to pull within 24 hours stacking cool place out
With the compressed air of 200-230kPa, uniformly punching sweeps the moisture in wood chip and then processing is dried again afterwards.
The preferred embodiments of the disclosure and embodiment are explained in detail above in conjunction with attached drawing, but it is of the invention
The above-described embodiment and examples are not limited to, within the knowledge of those skilled in the art, can also not taken off
It is made a variety of changes under the premise of from present inventive concept.
Claims (7)
1. a kind of production method of wooden nicking disc, which is characterized in that the production method includes the following steps：
The trees felled in the recent period are first removed bark and obtain log by step 1), and log is then cut transversely into 10mm~20mm thickness
The plank of degree, then it is 30%~40% that the plank uniform coding, which is placed on relative air humidity, the ventilated environment that temperature is 20-30 DEG C
In, the Free water in the lumen for scanning out plank is uniformly rushed with the compressed air of 200-230kPa, for reducing the aqueous of plank
Amount；
Step 2) prepares 30 parts~40 parts of the ammonium hydroxide of 28% concentration, 29 parts~30 parts of the hydrogen peroxide of 35% concentration, boron by weight
1 part~2 parts of sour sodium, 35 parts~40 parts of pure water after stirring evenly, will obtain crosscutting plank, soak at room temperature is at least in step 1
It is pulled out after 24 hours, carries out preparing neutralizer with 1.2%~4.0% acetic acid or oxalic acid after control water, soak at room temperature is after 10 hours
It pulls out, then the moisture swept in plank is uniformly rushed with the compressed air of 200-230kPa, after obtaining fiber softening and acid-base neutralization
Plank；
Step 3) is by the plank after the fiber softening obtained in step 2 and acid-base neutralization, to containing in timber drier drying
Water rate 8-15%；
Step 4) carries out machine and cuts out the geometry for piecing together the specification shape being pre-designed after step 3 according to the requirement of processing specification
Bulk, then tightened with hoop to prevent from cracking；
Step 5) is for there is the position of medulla, and with the drill bit more than plank medulla diameter, single hole, which bores, removes medulla position；
After step 6) is used with the mating timber gluing of diameter volume, the bore position in step 5 is carried out to change benefit；
Step 7) is 60-75 DEG C with temperature through carrying out treated timber in step 6, then after being polished smooth with sander surface
Flatiron paraffin and beeswax are pressed 1~1.5:1~1.5 ratio, the wood fibre in the nicking disk wooden to this carry out hot iron and ooze
Thoroughly；
Step 8) carries out nature cool place to the plank obtained after hot iron infiltration in step 7, and removes remaining wax, then carries out polishing throwing
Light completes the making of nicking disk disk body；
The plank for completing technique as above is cut into the fritter solid of same thickness plurality of specifications by step 9), for changing
Patch, the disk body local damage for replacing repairing nicking disk；
When carrying out changing benefit operation in step 10) step 9, the patch that changes that need to will be greater than damage part covers the part, and use is thinner
Paintbrush draw contour line along the edge for changing patch；
Step 11) is reserved along the interior lines of contour line less than the distance for changing patch edge, with the tip of icking tool perpendicular to disk,
Make repeated multiple times test formula to operate deeply, until carving saturating disk body；
It after step 12) takes out damage part, in delineation hole wall and changes patch side and applies glue, be allowed in the embedded hole that exerts a force and disk
Face is equal, you can completes repairing and continues normal use.
2. the production method of wooden nicking disc according to claim 1, which is characterized in that the production method includes step
3) relative humidity of drying steps, the drying steps is 35%, and temperature is 20-30 DEG C, moisture content 12%.
3. the production method of wooden nicking disc according to claim 1, which is characterized in that the production method, including step
It is rapid 2) in 30 parts of ammonium hydroxide for being prepared as 28% concentration by weight, 29 parts of the hydrogen peroxide of 35% concentration, 1 part of Boratex is pure
40 parts of water, after stirring evenly, soak at room temperature is pulled out after 24 hours.
4. the production method of wooden nicking disc according to claim 3, which is characterized in that the production method includes carrying out
After control water neutralizer step is prepared with 1.2% or 1.5% acetic acid or oxalic acid.
5. the production method of wooden nicking disc according to claim 1, which is characterized in that the production method includes step
7) in sander polishing surface it is smooth after, in hot iron impregnation step the temperature of the control of flatiron be 60 DEG C, 68 DEG C, 70 DEG C or 75
℃。
6. the production method of wooden nicking disc according to claim 1, which is characterized in that the production method includes step
7) with sander polishing surface it is smooth after, the flatiron for being 60-75 DEG C with temperature is by paraffin：Beeswax presses 1:1 ratio, it is wooden to this
Wood fibre in nicking disk carries out hot iron infiltration.
7. the production method of wooden nicking disc according to claim 1, which is characterized in that log described in step 1) is soft
Wealthy trees.