CN106835443A - A kind of manufacturing process of the damping temperature control wool worsted face fabric of active particle - Google Patents
A kind of manufacturing process of the damping temperature control wool worsted face fabric of active particle Download PDFInfo
- Publication number
- CN106835443A CN106835443A CN201710055289.0A CN201710055289A CN106835443A CN 106835443 A CN106835443 A CN 106835443A CN 201710055289 A CN201710055289 A CN 201710055289A CN 106835443 A CN106835443 A CN 106835443A
- Authority
- CN
- China
- Prior art keywords
- active particle
- fabric
- fiber
- temperature control
- wool
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production technology of the damping temperature control wool worsted face fabric of active particle, be added to the active particle that the wet steam and far infrared that are distributed to human body have strong absorption in fiber by being mainly characterized by of the technique, and this kind of fiber and wool are carried out into blending, a kind of functional fabric product for being obtained.When human body sensory heat, the product can quickly absorb the wet steam of human body, so as to reduce the DIE Temperature of human body, play a part of cooling, just discharge wet steam before sweat is formed, it is to avoid perspire, and improve comfortableness.When human body sensory is cold, the energy of far infrared in the product is absorbed and stored, heat can be provided, play thermal effect.And the function has permanently, repeatedly after washing, function is unaffected.
Description
Technical field
Patent of the present invention belongs to poly-talented textile field, the intelligent damping temperature control wool of more particularly to active particle
The preparation technology of worsted fabric.
Background technology
Demand to clothes temperature adjustment function is long-standing, and especially in gym suit field, the current demand has been extended to
Townwear and commercial field.Earliest temperature adjustment product, is its astronaut by U.S. NASA, is developed as suit product,
During phase-change material mainly has been added into viscose glue or acrylic fiber, phase-change material is becoming liquid, or liquid by solid
During becoming solid, a part of heat can be absorbed or discharged, be adjusted using this original body temperature to human body, but should
Material is because fiber content is limited in conventional garment, and reality is very weak to the regulating power of body temperature, and in regulation once
Afterwards, the ability without Secondary Control if phase-change material can not return to original state, so the use value in townwear
It is limited.And obtained by the way of Final finishing more than in the market others temperature adjustment product, there is many lacking from environmental protection and durability
Point.
Patent of the present invention can meet demand of the existing market to temperature adjustment function, and eliminate in the market product in work(
Deficiency in energy property.Patented technology of the present invention is applied to dress-goods throughout the year.The mode of the main regulation body temperature of human body
It is discharge wet steam, human body is all in constantly discharge wet steam within 24 hours one day.The environment of sweltering heat is in when human body or when wet steam discharge
When being obstructed, human body will perspire, and so as to cause body surface temperature to raise, and bring discomfort.Patent of the present invention is produced
Product, mainly for be exactly human body wet steam, it can quickly absorb human body discharge wet steam, and using the far infrared of human body as
Energy source, the wet steam that will be absorbed on particle is discharged into external environment again；When human body is in cold environment, human body discharge
Wet steam can reduce, the energy of the far infrared that active particle is absorbed need not completely for the wet steam that volatilizees, so unnecessary is remote
Infrared energy will store and warming effect is played in the space of active particle；The thermal effect of still further aspect, main body
Now in cold environments, if human body has certain amount of exercise, after especially perspiring, the warmth retention property of clothes will decline, from
And cause clammy, and patented product of the present invention can quickly absorb human body wet steam, and the moment keeps dry skin, so as to obtain warming
Function.
The content of the invention
Patent of the present invention is related to a kind of production technology of the damping temperature control wool worsted face fabric of active particle, the technique
Be mainly characterized by the active particle that the wet steam and far infrared that are distributed to human body have strong absorption is added to fiber
In, and this kind of fiber and wool are carried out into blending, a kind of functional fabric product for being obtained.
When human body sensory heat, human body will perspire, and so as to cause body surface temperature to raise, and bring uncomfortable
Sense.This product can quickly absorb the wet steam of human body, so as to reduce the DIE Temperature of human body, play a part of cooling, formed
Just wet steam is discharged before sweat, it is to avoid perspire, improve comfortableness.When human body sensory is cold, absorb and store in the product is remote
Infrared energy, can provide heat, play thermal effect.The thermal effect of still further aspect, is mainly reflected in cold environment
Under, if human body has certain amount of exercise, after especially perspiring, the warmth retention property of clothes will decline, clammy so as to cause, and
Patented product of the present invention can quickly absorb human body wet steam, and the moment keeps dry skin, so as to obtain heat-preserving function.
The function of patent of the present invention has permanently, and repeatedly after washing, function is unaffected.When patent of the present invention is used to paste
During body clothes, Final finishing must be processed using moisture absorbing and sweat releasing；When patented product of the present invention is used as external-cover-type clothes, the fabric can
With using conventional Final finishing, or water repellent type postfinishing process.
The acquisition of the active particle that patent of the present invention is first related to, the active particle, refers to superhigh specific surface area
Carbon particle, can by the existing material of nature by carbonization or industrialized treatment after obtain, the active particle can
With but be not limited only to following composition：Volcanic ash, the coconut shell powder of carbonization, graphene nano particle and its mixture, the 1g mixing
The specific surface area ＞ 600m of thing2；1200 DEG C of carburizing temperature, time 30mins.
Secondly, patent of the present invention is that the active particle for obtaining is added during fibre spinning, and by spinning technique
Control so that active particle is dispersed in fiber surface；The fiber can with but be not only limited to following type of fibers：Wash
Synthetic fibre, viscose glue, acrylic fibers, polyamide fibre, PTT etc.；Active particle content in the fibre is 0.5-2%, and more than 80% is uniformly distributed in fiber
Surface；The need for actual product, fibre fineness can be 0.9D-3.0D, and fibre length can be 38mm-102mm.
3rd step, by the fiber containing active particle and wool or other conventional fibre blending.But active particle
Fiber content have to be larger than 25%, and wool content can be 30-65% as needed, other fibers can with but be not limited to terylene, brocade
Synthetic fibre, viscose glue, acrylic fibers, spandex etc., its ratio are 15-50%.
4th step, if patented product of the present invention is finally applied to clothes next to the skin, the fabric will during Final finishing
Processed using the softening agent of moisture absorbing and sweat releasing auxiliary agent or hydrophilic, auxiliary dosage 20-50/L will be helped by the way of padding
Agent is added on fabric, rolls rod pressure 1.0-3.0Bar, speed 10-30m/min, 100-170 DEG C of drying temperature, pick-up rate 60-
85%；If patented product of the present invention is finally applied to external-cover-type clothes, the Final finishing of fabric is carried out using three-prevention finishing auxiliary agent
Be added to auxiliary agent on fabric by the way of padding by treatment, auxiliary dosage 25-80/L, rolls rod pressure 1.0-3.0Bar, speed
10-30m/min, 130-190 DEG C of drying temperature, setting temperature：175-195 DEG C, pick-up rate 60-85%.
Specific embodiment
Embodiment 1
Fabric composition：Wool 50%, intelligent damping temperature control fiber（Terylene base）25%, PTT 25%；Yarn count：72S/2*72S/2；
Tissue：2/1 twill；Grammes per square metre 295g/m；Breadth 157cm；Color：Black.
Final finishing：Conventional Final finishing.
Purposes：Suiting.
Technological process：Bar contaminates（3 kinds of fibers are dyeed respectively）--- silver mixing（By 3 kinds of fibers according to 50/25/25 ratio
Carry out blending）--- recombing（The impurity and chopped fiber in ribbon are removed, and fiber is made in order）--- rove（Lead
Stretch）--- spun yarn（Intelligent damping temperature control wool single thread is obtained, number of spindles 6000, the twist 750 twists with the fingers/m）--- doubling --- double twisting（Twist with the fingers
Spend 700 sth. made by twisting/m, speed 7500）--- yarn steaming（85 DEG C, 60min is vacuumized）--- --- weaving --- life is repaiied --- is flat for warping
Width braying（45 DEG C, 20m/min）--- it is double to boil（85 DEG C, 45mins）--- high speed braying（Shed open apart from 18cm, 200m/min,
45mins）--- dry（135 DEG C, 20m/min）--- thermal finalization（175 DEG C, 15m/min）--- middle inspection --- bristle --- is cut
Hair（6 knife cropping, 4 positive 2 is anti-）--- decatizing（0.8Bar, in-out-in：5-5-5）--- preshrunk（60% steam, 15m/min）.
Test result：The effect of intelligent damping temperature control fabric can be tested and table using AATCC200 and AATCC201
Levy, the fabric of generally routine Final finishing and water repellent type Final finishing is tested using AATCC201.This example fabric after tested, is done
Dry rate index is 1.6ml/h, and the fabric test result of same size is usually less than 1.2ml/h, damping capability improving 33%
Left and right.
Embodiment 2
Fabric composition：Wool 50%, intelligent damping temperature control fiber（Terylene base）30%, conventional polyester 20%；Yarn count：50S/1*
50S/1；Tissue：Plain weave；Grammes per square metre：200g/m；Breadth 154cm；Color：Lattice.
Final finishing：Hydrophilic is arranged.
Purposes：Shirt fabric.
Technological process：Bar contaminates（3 kinds of fibers are dyeed respectively）--- silver mixing（By 3 kinds of fibers according to 50/30/20 ratio
Carry out blending）--- recombing（The impurity and chopped fiber in ribbon are removed, and fiber is made in order）--- rove（Lead
Stretch）--- spun yarn（Intelligent damping temperature control wool single thread is obtained, number of spindles 6000, the twist 900 twists with the fingers/m）--- yarn steaming（85 DEG C,
60min, vacuumizes）--- warping --- weaving --- life is repaiied --- open width braying（45 DEG C, 20m/min）--- it is double to boil（85 DEG C,
45mins）--- high speed braying（Shed open is apart from 18cm, 200m/min, 45mins）--- dry（135 DEG C, 20m/min）——
Thermal finalization（Hydrophilic is arranged, auxiliary dosage 30g/l, pick-up rate 75%, 175 DEG C, 15m/min）--- middle inspection --- bristle ---
Cropping（6 knife cropping, 4 positive 2 is anti-）--- decatizing（0.8Bar, in-out-in：5-5-5）--- preshrunk（60% steam, 15m/
min）.
Test result：The effect of intelligent damping temperature control fabric can be tested and table using AATCC200 and AATCC201
Levy, the fabric of usual hydrophilic Final finishing is tested using AATCC200.After tested, rate of drying index is this example fabric
2.3ml/h, and the fabric test result of same size is usually less than 1.4ml/h, damping capability improving 64% or so.
Embodiment 3
Fabric composition：Non-shrinkable wool 60%, intelligent damping temperature control fiber（Terylene base） 40%；Yarn count：48S/1*48S/1；Tissue：
Knitting plain stitch grammes per square metre：180g/m2；Breadth 150cm；Color：Grey.
Final finishing：Hydrophilic is arranged.
Purposes：Underwear fabric.
Technological process：Bar contaminates（2 kinds of fibers are dyeed respectively）--- silver mixing（2 kinds of fibers are carried out according to 60/40 ratio
Blending）--- recombing（The impurity and chopped fiber in ribbon are removed, and fiber is made in order）--- rove（Drawing-off）--- it is thin
Yarn（Intelligent damping temperature control wool single thread is obtained, number of spindles 7000, the twist 600 twists with the fingers/m）--- yarn steaming（85 DEG C, 60min takes out true
It is empty）--- --- --- --- open-width --- sizing is repaiied in life to warping for weaving（160 DEG C, 15m/min）--- braying（80m/min,
45mins）--- dry（135 DEG C, 20m/min）--- thermal finalization（Hydrophilic is arranged, auxiliary dosage 40g/l, pick-up rate 75%,
175 DEG C, 15m/min）--- middle inspection --- bristle --- cropping（6 knife cropping, 4 positive 2 is anti-）--- decatizing（0.8Bar, in-out-
in：5-5-5）--- preshrunk（80% steam, 15m/min）.
Test result：The effect of intelligent damping temperature control fabric can be tested and table using AATCC200 and AATCC201
Levy, the fabric of usual hydrophilic Final finishing is tested using AATCC200.After tested, rate of drying index is this example fabric
2.4ml/h, and the fabric test result of same size is usually less than 1.5ml/h, damping capability improving 60% or so.
Claims (6)
1. the production technology of the damping temperature control wool worsted face fabric of a kind of active particle, the specific features of the technique are：Will
The active particle that the wet steam and far infrared distributed to human body have strong absorption is added in the spinning solution of fiber, obtains function
Property fiber, and by the fiber and wool or wool and the together blending of other fibers, so as to obtain with damping temperature controlling function
Wool worsted face fabric；When the intelligent damping temperature control fabric is used for clothes next to the skin, it is necessary to use hydrophilic finish；When the intelligence
When damping temperature control fabric is as external-cover-type clothes, the fabric can be using conventional Final finishing, or water repellency postfinishing process.
2. the production technology of the damping temperature control wool worsted face fabric of a kind of active particle according to claim 1, its
It is characterised by：Described active particle, refers to the carbon particle with superhigh specific surface area, can be by the existing material of nature
Matter by being obtained after carbonization or industrialized treatment, the active particle can with but be not limited only to following composition：Volcanic ash, carbonization
Coconut shell powder, graphene nano particle and its mixture, the specific surface area ＞ 600m of the 1g mixtures2；1200 DEG C of carburizing temperature,
Time 30mins.
3. the production technology of the damping temperature control wool worsted face fabric of a kind of active particle according to claim 1, its
It is characterised by：Described damping temperature control fiber, refers to that the fiber that active particle is obtained is added during fibre spinning；Should
Fiber can with but be not only limited to following type of fibers：Terylene, viscose glue, acrylic fibers, polyamide fibre, PTT etc.；The active particle is in the fibre
Content be 0.5-2%, more than 80% will be in fiber surface；Fibre fineness：0.9D-3.0D, fibre length 38mm-102mm.
4. the production technology of the damping temperature control wool worsted face fabric of a kind of active particle according to claim 1, its
It is characterised by：When fiber containing active particle is with wool or other fiber blends, the fiber content of active particle is necessary
More than 25%, wool content is 30-65% as needed, other fibers can with but be not limited to terylene, polyamide fibre, viscose glue, acrylic fibers,
Spandex etc., its ratio is 15-50%.
5. the production technology of the damping temperature control wool worsted face fabric of a kind of active particle according to claim 1, its
It is characterised by：Described hydrophilic finish, refers to fabric and moisture absorbing and sweat releasing auxiliary agent or hydrophilic is employed during Final finishing
The softening agent of type is processed, auxiliary dosage 20-50/L, and auxiliary agent is added on fabric by the way of padding, and rolls rod pressure
1.0-3.0Bar, speed 10-30m/min, 100-170 DEG C of drying temperature, pick-up rate 60-85%.
6. the production technology of the damping temperature control wool worsted face fabric of a kind of active particle according to claim 1, its
It is characterised by：Described water repellency is arranged, and refers to fabric and employ three-prevention finishing auxiliary agent during Final finishing being processed,
, be added to auxiliary agent on fabric by the way of padding by auxiliary dosage 25-80/L, rolls rod pressure 1.0-3.0Bar, speed 10-30m/
Min, 130-190 DEG C of drying temperature, setting temperature：175-195 DEG C, pick-up rate 60-85%.