CN106835428A - A kind of double-layered structure's fabric for being exclusively used in fireman's fire extinguishing protective garment - Google Patents
A kind of double-layered structure's fabric for being exclusively used in fireman's fire extinguishing protective garment Download PDFInfo
- Publication number
- CN106835428A CN106835428A CN201710151711.2A CN201710151711A CN106835428A CN 106835428 A CN106835428 A CN 106835428A CN 201710151711 A CN201710151711 A CN 201710151711A CN 106835428 A CN106835428 A CN 106835428A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fiber
- fanglun
- double
- layered structure
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of double-layered structure's fabric for being exclusively used in fireman's fire extinguishing protective garment, including positive layer and backing layer, positive layer and backing layer include fabric A and fabric B, the reverse side of fabric A is fabric B, the reverse side of fabric B is fabric A, fabric A and fabric B are heat-resistance and flame-retardant fiber, and fabric A is different with the percent thermal shrinkage of fabric B.The present invention support double-layered structure's fabric by the yarn of different percent thermal shrinkages by weaving cotton cloth, when high temperature is run into, the big fibrage of dimensional stability to heating in house can shrink, cause the small fibrage of shrinkage factor raised, there are two layers of phenomenon that all can be raised so as to cause the fabric, certain space is produced, so as to play more preferable heat-insulated protection effect.
Description
Technical field
The present invention relates to a kind of double-layered structure's fabric, more particularly, to a kind of bilayer for being exclusively used in fireman's fire extinguishing protective garment
Tissue fabric.
Background technology
Fireman's fire extinguishing protective garment is that protection is fought in one of safe important equipment of fireman's life of fire-fighting First Line,
It is the necessary article of terrible disaster rescue site, while being also the protection-gear for protecting fire fighter's body to escape injury.Therefore, it must
Must have fire resistance, heat resistance and thermal insulation.The outer shell fabric of existing fireman's fire extinguishing protective garment, major part is all common
Monolayer organization, even with the double-layered structure after improvement, be also under heating status one side it is raised, its effect of heat insulation not ten
Divide notable, so as to mitigating, preferable effect can not be reached for the weight of fireman's fire extinguishing protective garment.It is therefore proposed that of the invention
It is very necessary.
The content of the invention
For the above-mentioned technical problem of prior art, fireman's fire extinguishing protection is exclusively used in it is an object of the invention to provide one kind
Double-layered structure's fabric of clothes, uses as the outer shell fabric of fireman's fire extinguishing protective garment, is knitted by the different yarn of percent thermal shrinkage
The double-layered structure's fabric made, the one side that percent thermal shrinkage is small during high temperature is raised, due to two kinds of different yarns of front and back,
The phenomenon of projection can be all produced per one side, bigger insulated space is produced than traditional raised fabric of only one side, so as to rise
To more preferable heat-insulated protection effect.
To reach above-mentioned purpose, the present invention is achieved by the following technical solutions:
A kind of double-layered structure's fabric for being exclusively used in fireman's fire extinguishing protective garment, including positive layer and backing layer, described positive layer
Reverse side with backing layer including fabric A and fabric B, the fabric A is that the reverse side of fabric B, the fabric B is fabric A, described
Fabric A and fabric B are heat-resistance and flame-retardant fiber, and fabric A is different with the percent thermal shrinkage of fabric B.
The pattern of the fabric A weavings is formed by some A warp thread and some A weft yarns, and the fabric B is knitted
The pattern made is formed by some B warp thread and some B weft yarns, and described pattern is square, circular or polygon.
Described fabric A and fabric B is yarn, silk or line.
The fabric A's and fabric B is organized as plain weave, twill or alternative construction.
The percent thermal shrinkage of the fabric A is less than fabric B.
Described fabric A is Fanglun l414 silvalin, and fabric B is aramid fiber 1313, Fanglun l414 fiber, aramid fiber 1313
The mixed yarn or aramid fiber 1313 and Fanglun l414 of the mixed yarn, Fanglun l414 fiber and conductive fiber of fiber and conductive fiber
The mixed yarn of fiber and conductive fiber.
When the mixed yarn that fabric B is aramid fiber 1313 and Fanglun l414 fiber and conductive fiber, based on number, by
93% aramid fiber 1313,5% Fanglun l414 fiber and 2% conductive fiber composition.
The fabric A is the mixed yarn of Fanglun l414 fiber or Fanglun l414 fiber and aramid fiber 1313, the fabric
B is the mixed yarn of aramid fiber 1313, Fanglun l414 fiber, aramid fiber 1313 and conductive fiber, Fanglun l414 fiber and leads
The mixed yarn or aramid fiber 1313 and Fanglun l414 fiber of electric fiber and conductive fiber and/or the mixed yarn of PSA fiber.
When the mixed yarn that fabric A is Fanglun l414 fiber and aramid fiber 1313, by 50% Fanglun l414 fiber with
50% aramid fiber 1313 blending is formed.
When the mixed yarn that fabric B is aramid fiber 1313 and Fanglun l414 fiber and conductive fiber, by 80% aramid fiber
1313 fibers, 6% Fanglun l414 fiber, 2% conductive fiber and 12% PSA fiber blending are formed.
Beneficial effects of the present invention are as follows:
The present invention is exclusively used in double-layered structure's fabric of fireman's fire extinguishing protective garment, by weaving cotton cloth the yarn branch of different percent thermal shrinkages
Support double-layered structure fabric, when high temperature is run into, the big fibrage of dimensional stability to heating in house can shrink, and cause the small fibrage of shrinkage factor can be convex
Rise, there are two layers so as to cause the fabric(That is positive layer and backing layer)The raised phenomenon in capital, produces certain space, so as to rise
To more preferable heat-insulated protection effect.
Brief description of the drawings
Fig. 1 is the structural representation of positive layer of the present invention;
Fig. 2 is the structural representation of backing layer of the present invention;
Fig. 3 is cross-sectional structure schematic diagram of the present invention at 500 DEG C;
Wherein, 1 be fabric A, 2 be fabric B.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated, but protection scope of the present invention is not limited to
This.
Embodiment 1
As Figure 1-3, the present embodiment 1 is exclusively used in fireman and puts out a fire double-layered structure's fabric of protective garment, including positive layer and anti-
Surface layer, double-layered structure's fabric is formed by woven weaving, and the institutional framework of positive layer and backing layer can be with identical, it is also possible to no
Together, can be according to actual demand come unrestricted choice.Positive layer and backing layer include fabric A1 and fabric B2, and fabric A1's is anti-
Face is fabric B2, and the reverse side of fabric B2 is heat-resistance and flame-retardant fiber for fabric A1, fabric A1 and fabric B2, and fabric A1 with knit
The percent thermal shrinkage of thing B2 is different.In the present embodiment 1, the percent thermal shrinkage of fabric A1 is less than fabric B2.
Fabric A1 and fabric B2 in the present embodiment 1 are yarn, silk or line, and its fabric tissue is plain weave, twill or change group
Knit, the pattern of fabric A1 weavings is formed by some A warp thread and some A weft yarns, the figure of fabric B2 weavings
Case is formed by some B warp thread and some B weft yarns, and its pattern is square, circular or polygon, can be according to actual need
Select the shapes and sizes of pattern.
Fabric A1 in the present embodiment 1 is Fanglun l414 silvalin, and fabric B2 is aramid fiber 1313, Fanglun l414 fibre
Dimension, the mixed yarn of aramid fiber 1313 and conductive fiber, the mixed yarn of Fanglun l414 fiber and conductive fiber or aramid fiber 1313 fibre
The mixed yarn of peacekeeping Fanglun l414 fiber and conductive fiber.
When the mixed yarn that fabric B2 is aramid fiber 1313 and Fanglun l414 fiber and conductive fiber, based on number, by
93% aramid fiber 1313,5% Fanglun l414 fiber and 2% conductive fiber composition.
Embodiment 2
Fabric A1 in the present embodiment 2 is Fanglun l414 fiber or Fanglun l414 fiber and the mixed yarn of aramid fiber 1313, is knitted
Thing B2 is the mixed yarn of aramid fiber 1313, Fanglun l414 fiber, aramid fiber 1313 and conductive fiber, Fanglun l414 fiber with
The mixed yarn or aramid fiber 1313 and Fanglun l414 fiber of conductive fiber and conductive fiber and/or the mixed yarn of PSA fiber.
When the mixed yarn that fabric A1 is Fanglun l414 fiber and aramid fiber 1313, by 50% Fanglun l414 fiber with
50% aramid fiber 1313 blending is formed.
When the mixed yarn that fabric B2 is aramid fiber 1313 and Fanglun l414 fiber and conductive fiber, by 80% aramid fiber
1313 fibers, 6% Fanglun l414 fiber, 2% conductive fiber and 12% PSA fiber blending are formed.
The other structures of the present embodiment 2 are same as Example 1, do not repeat herein.
In embodiment 1 and embodiment 2, due to the difference of upper and lower layer fiber percent thermal shrinkage, the part of fabric A1 can be convex
Rise, that face of fabric B2 remains unchanged and keeps smooth, and due to the relation of upper and lower layer tissue, upper and lower layer has fabric A1 and fabric B2, from
And make the fabric A1 on upper strata can be downwardly convex, larger space can be produced, so as to play more preferable heat-insulated protection effect.
Institutional framework of the invention is double-layered structure, and fabric is divided into several small double-deckers again, different by two kinds
Yarn weaving is formed.Because two kinds of different yarn A are different with the percent thermal shrinkage of B, the percent thermal shrinkage of yarn A is smaller than yarn B.
In the state of high-temperature heating, a kind of small yarn of percent thermal shrinkage can be raised, produces air layer.Because being double-layered structure, often
In one layer tissue, the phenomenon of projection can be all produced, the raised property of one side, energy of the present invention are only produced compared to traditional double-layered structure
The effect that can produce two faces raised under heating status, the heat-insulated solid space inside fabric can be increased considerably, therefore very big
Improve to degree the effect of heat insulation of fabric.
Above-described embodiment is only used for illustrating inventive concept of the invention, rather than the restriction to rights protection of the present invention,
All changes for carrying out unsubstantiality to the present invention using this design, all should fall into protection scope of the present invention.
Claims (10)
1. it is a kind of be exclusively used in fireman put out a fire protective garment double-layered structure's fabric, it is characterised in that:Including positive layer and backing layer,
The reverse side of described positive layer and backing layer including fabric A and fabric B, the fabric A is fabric B, the reverse side of the fabric B
It is fabric A, the fabric A and fabric B is heat-resistance and flame-retardant fiber, and fabric A is different with the percent thermal shrinkage of fabric B.
2. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as claimed in claim 1, it is characterised in that:The fabric
A weaving pattern formed by some A warp thread and some A weft yarns, if the fabric B weaving pattern by
Dry root B warp thread and some B weft yarns are formed, and described pattern is square, circular or polygon.
3. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as claimed in claim 1, it is characterised in that:Described knits
Thing A and fabric B is yarn, silk or line.
4. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as claimed in claim 1, it is characterised in that:The fabric
A's and fabric B is organized as plain weave, twill or alternative construction.
5. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as claimed in claim 1, it is characterised in that:The fabric
The percent thermal shrinkage of A is less than fabric B.
6. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as described in claim 1-5 any claims, and it is special
Levy and be:Described fabric A is Fanglun l414 silvalin, and fabric B is aramid fiber 1313, Fanglun l414 fiber, aramid fiber 1313
The mixed yarn or aramid fiber 1313 and Fanglun l414 of the mixed yarn, Fanglun l414 fiber and conductive fiber of fiber and conductive fiber
The mixed yarn of fiber and conductive fiber.
7. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as claimed in claim 6, it is characterised in that:As fabric B
For aramid fiber 1313 and Fanglun l414 fiber and conductive fiber mixed yarn when, based on number, the aramid fiber 1313 by 93% is fine
Dimension, 5% Fanglun l414 fiber and 2% conductive fiber composition.
8. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as described in claim 1-5 any claims, and it is special
Levy and be:The fabric A is the mixed yarn of Fanglun l414 fiber or Fanglun l414 fiber and aramid fiber 1313, the fabric B
For the mixed yarn of aramid fiber 1313, Fanglun l414 fiber, aramid fiber 1313 and conductive fiber, Fanglun l414 fiber with it is conductive
The mixed yarn or aramid fiber 1313 and Fanglun l414 fiber of fiber and conductive fiber and/or the mixed yarn of PSA fiber.
9. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as claimed in claim 8, it is characterised in that:As fabric A
For Fanglun l414 fiber and aramid fiber 1313 mixed yarn when, by 50% Fanglun l414 fiber and 50% aramid fiber 1313
Blending is formed.
10. double-layered structure's fabric of fireman's fire extinguishing protective garment is exclusively used in as claimed in claim 8, it is characterised in that:As fabric B
For aramid fiber 1313 and Fanglun l414 fiber and conductive fiber mixed yarn when, by 80% aramid fiber 1313,6% aramid fiber
1414 fibers, 2% conductive fiber and 12% PSA fiber blending are formed.