CN106833268A - A kind of aqueous sealing primer for fat content ground high and preparation method thereof - Google Patents
A kind of aqueous sealing primer for fat content ground high and preparation method thereof Download PDFInfo
- Publication number
- CN106833268A CN106833268A CN201710044384.0A CN201710044384A CN106833268A CN 106833268 A CN106833268 A CN 106833268A CN 201710044384 A CN201710044384 A CN 201710044384A CN 106833268 A CN106833268 A CN 106833268A
- Authority
- CN
- China
- Prior art keywords
- curing agent
- fat content
- cosolvent
- diluent
- ground high
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of aqueous sealing primer for fat content ground high, it is made up of mian paint, curing agent and diluent, the mian paint is made up of the component of following mass percent:Epoxy resin 40~55%, defoamer 0.2~0.5%, moistening flatting agent 0.3~0.5%, reactive diluent 8~12%, cosolvent 36~47%;The cosolvent is made up of following mass percent component:Propylene glycol monomethyl ether 35%, ethanol 60%, dry vegetable oil 5%;The curing agent is the mixture of modified polyamide and distearyl dimethylammonium hectorite.Seal coat of the invention solidifies in wet condition, form film relatively compact, there is good sealing effect and adhesive force to fat content ground high, grease oozes out in ground effectively being prevented, effectively solve existing water-borne wood coating and be also easy to produce poor adhesive force in application high content grease ground, film heaves the range of application for expanding water-borne wood coating down to disadvantages such as peelings.
Description
Technical field
The present invention relates to a kind of decorative paint, more particularly to a kind of aqueous sealing primer for fat content ground high and
Its preparation method.
Background technology
Water-borne wood coating has the advantages that health environment-friendly with water as solvent, is increasingly welcome by market.But water
Also there is limitation in property woodwork coating, whether one pack system or bi-component waterborne woodwork coating in terms of key technology, due to
Solid content is low, and containing hydrophilic radical, film compactness and water resistance are poor, is difficult in the presence of many solve particularly in work progress
Problem certainly.Different type is wooden and timber in vegetable fat species numerous and complicated, water-borne wood coating be sprayed on containing
On the timber of vegetable fat, particularly scabbed as cypress is this, rich grease-contained ground, sealing effect is not good, causes application more
Afterwards with the change of weather, especially temperature is raised, and the vegetable oil contained in timber is slowly infiltrated, and is readily migrate into film
In, cause the place's of scabbing film of high content grease to heave, the adverse consequences such as come off.This has a strong impact on painting effect, causes product
Do over again or scrap, production cost increases, these problems all constrain developing rapidly and occupation rate of market for water-borne wood coating
Expand.Therefore it is badly in need of preparing a kind of aqueous sealing primer with good oil sealing fat effect.
The content of the invention
It is an object of the invention to solve at least the above and/or defect, and provide at least will be described later excellent
Point.
A further object of the invention is directed to the deficiency that aqueous woodware paint is present in the prior art, there is provided one kind is used for
The aqueous wooden ware seal coat of fat content ground high, with excellent chemical-resistant and closure, can effectively prevent small
The materials such as molecule grease ooze out, and heaving occurs in film after solving grease substrate coating high, and adhesive force is bad, fall the disadvantages such as paint.
It is a still further object of the present invention to provide a kind of preparation side of the aqueous sealing primer for fat content ground high
Method, prepare function admirable can be by grease closing aqueous sealing primer in wood.
In order to realize object of the present invention and further advantage, there is provided a kind of for the aqueous of fat content ground high
Seal coat, is made up of mian paint, curing agent and diluent, it is characterised in that the weight ratio of mian paint, curing agent and diluent is 1:
0.25: 0.5~1;The mian paint is made up of the component of following mass percent:Epoxy resin 40~55%, defoamer 0.2~
0.5%th, moistening flatting agent 0.3~0.5%, reactive diluent 8~12%, cosolvent 36~47%;The epoxy resin is liquid
State epoxy resin, 213~233g/Eq of its epoxide equivalent, solids content is more than 99.4%;The reactive diluent is lived for hydrophily
Property diluent C12~C14 alkyl glycidyl ethers;The cosolvent is made up of following mass percent component:Propylene glycol monomethyl ether
35%th, ethanol 60%, dry vegetable oil 5%;The curing agent is modified polyamide and distearyl dimethylammonium hectorite with weight
Mixture of the amount than 3~5: 1.
Preferably, the diluent is water, and water consumption is by weight, mian paint: curing agent: water=1: 0.25: 1.
Preferably, the mian paint is made up of the component of following mass percent:Epoxy resin 50~53%, defoamer
0.2~0.3%, moistening flatting agent 0.3~0.4%, reactive diluent 8~10%, cosolvent 36~42%;The epoxy resin
213~233g/Eq of epoxide equivalent, solids content be more than 99.4%;The cosolvent is made up of following mass percent component:
Propylene glycol monomethyl ether 35%, ethanol 60%, dry vegetable oil 5%;The curing agent is modified polyamide and distearyl dimethylammonium lithium
Montmorillonite compares 5: 1 mixture with weight.
Preferably, the amine value of the modified polyamide is 180~220mgKOH/g.
Preferably, the defoamer is that polyethers based polysiloxane and octanol compare 10 with weight:1 mixture.
Preferably, the moistening flatting agent is polyether-based dimethyl silicone polymer.
Preferably, the polyether-based dimethyl silicone polymer is carboxy-modified polyether-based dimethyl silicone polymer.
Preferably, the dry vegetable oil is tung oil or linseed oil.
A kind of preparation method of aqueous sealing primer for fat content ground high, comprises the following steps:
(1) mian paint is prepared
A. raw material is weighed by following mass percent:Epoxy resin 40~55%, defoamer 0.2~0.5%, wetting levelling
Agent 0.3~0.5%, reactive diluent 8~12%, cosolvent 36~47%;
B. by epoxy resin and, reactive diluent and part cosolvent add in reaction vessel, with 600~800rpm of rotating speed
Dispersed with stirring 8min, obtains mixed liquor A;
C. to defoamer and moistening flatting agent is added dropwise in mixed liquor A while stirring, rate of addition is 10mL/min, stirring speed
Degree 1000~1200rpm, after completion of dropping, stop stirring, then with supersonic oscillations disperse 10min, ultrasonic frequency be 50~
70MHz, obtains mixture B;
D. by remaining cosolvent addition mixture B, supersonic oscillations dispersion 5min is continued, ultrasonic frequency is
50MHz, obtains mian paint;
(2) curing agent is prepared
By the weight of modified polyamide and distearyl dimethylammonium hectorite weighed respectively than 3~5: 1 modified polyamide and
Distearyl dimethylammonium hectorite;Modified polyamide and distearyl dimethylammonium hectorite are ground respectively using micro mist grinder
Mixing and stirring after being nanoscale to fineness, obtains curing agent;
(3) by weight mian paint:Curing agent:Diluent=1: 0.25: 0.5~1 weighs mian paint, curing agent and diluent,
First by diluent addition mian paint, curing agent is added after stirring 10min, continue to stir 10min, obtained for fat content bottom high
The aqueous sealing primer of material;
In the above method, the cosolvent is made up of following mass percent component:Propylene glycol monomethyl ether 35%, ethanol
, first be dissolved in dry vegetable oil in ethanol by the 60%th, dry vegetable oil 5%, and propylene glycol monomethyl ether is added after being well mixed, and mixing is equal
It is even, obtain cosolvent.
Compared with prior art, the invention has the advantages that:
One, the aqueous sealing primer for fat content ground high disclosed by the invention, curing agent in its raw material components
The mixture of the modified polyamide of selection and a small amount of distearyl dimethylammonium hectorite, modified polyamide curing agent is both crosslinking agent
It is again emulsifying agent, it mutually acts synergistically with inorganic polymer surfactant distearyl dimethylammonium hectorite, makes curing agent
There is good compatibility with epoxy resin, the coating system latex particle particle diameter of formation is small, narrow distribution range, good penetrability,
With preferable workability, can solidify in wet environment, and with crosslink density very high, form the relatively compact heavily fortified point of film
Gu, it is strong to base material adhesive force, oil substances in ground are thoroughly closed with the external world, make this kind of material and top layer film completely every
From, oil substances are prevented to exosmosis, eliminate film and the disadvantage such as heave, this is that existing aqueous sealing primer cannot be compared
, so as to solve water-borne wood coating in coating process due to timber material complexity and influence film performance performance and
The problem of the constructional difficulties for causing, has widened the range of application of aqueous woodware paint significantly, and conventional aqueous woodware paint is solved very well
The deficiency of presence;
Secondly, the seal coat emulsifying agent is not used in preparation process, thoroughly solve standard aqueous coating water sensitive
Sex chromosome mosaicism, it is ensured that its excellent properties, with excellent chemical-resistant and adhesive force, it exists with solvent based coating state,
The problem of freeze-thaw stability and the stable storing difference often having in the absence of general water paint, with excellent storage stability;
Thirdly, this experimental selection replace part hydrotropy using hydrophilic active diluent C12~C14 alkyl glycidyl ethers
Agent, reduces the VOC of system, and it plays dissolved dilution to epoxy resin, and co-emulsifier makes coating system more stable, improves
During seal coat is to the wetting of ground basal plane and penetrating into base material, while it carries epoxide group participates in cross-linking and curing reaction, enter
One step improves sealing effect and richness;Selection propylene glycol monomethyl ether, ethanol and a small amount of dry vegetable oil are used cooperatively as hydrotropy
Agent, propylene glycol monomethyl ether environmental pollution is small, safe, and ethanol belongs to reproducible innoxious solvent, and dry vegetable oil is also nontoxic
It is harmless, and in vegetable oil unrighted acid content it is many, many containing double key number in unrighted acid, activation capacity is strong, into
Film speed is fast, therefore the seal coat has preferable drying property, and the paint film after doing does not soften, and conjunctiva is tough and tensile, water-fast, elasticity
Good, not only toxicity is low for the cosolvent system, and pollution will not be produced to environment;
Four, fat content ground high of the present invention, can be pine, cypress, and especially scab more cypress,
It should be understood, however, that the aqueous sealing primer for fat content ground high of the present invention, it is also possible to for other
The ground of low grease content;
Furthermore, strictly control in the preparation method of the aqueous sealing primer for fat content ground high of the invention it is each anti-
The technological parameter in the stage of answering, and using supersonic oscillations dispersion, disperse Quick uniform, accelerate to react, save the time, it is adaptable to work
Industry metaplasia is produced.
Further advantage of the invention, target and feature embody part by following explanation, and part will also be by this
The research and practice of invention and be understood by the person skilled in the art.
Specific embodiment
With reference to specific embodiment, the present invention is elaborated.
Embodiment 1
The method for preparing the aqueous sealing primer for fat content ground high, comprises the following steps:
(1) mian paint is prepared
A. raw material is weighed by following mass percent:Epoxy resin 40%, defoamer 0.5%, moistening flatting agent 0.5%,
Reactive diluent 12%, cosolvent 47%;The epoxy resin be liquid-state epoxy resin, 213~233g/Eq of its epoxide equivalent,
Solids content is more than 99.4%, and the defoamer is that polyethers based polysiloxane and octanol compare 10 with weight:1 mixture, it is described
Moistening flatting agent is polyether-based dimethyl silicone polymer, and reactive diluent is that hydrophilic active diluent C12~C14 alkyl shrinks
Glycerin ether;
B. epoxy resin, reactive diluent and 1/2 cosolvent are added in reaction vessel, with rotating speed 600rpm stirrings point
8min is dissipated, mixed liquor A is obtained;
C. to defoamer and moistening flatting agent is added dropwise in mixed liquor A while stirring, rate of addition is 10mL/min, stirring speed
Degree 1000rpm, after completion of dropping, stops stirring, then disperses 10min with supersonic oscillations, and ultrasonic frequency is 50MHz, is obtained
Mixture B;
D. by remaining 1/2 cosolvent addition mixture B, supersonic oscillations dispersion 5min is continued, ultrasonic frequency is
50MHz, obtains mian paint;
(2) curing agent is prepared
Modified polyamide and two hard is weighed respectively than 3: 1 by the weight of modified polyamide and distearyl dimethylammonium hectorite
Fat dimethylammonium hectorite, the amine value of the modified polyamide is 180~220mgKOH/g, will be changed respectively using micro mist grinder
Property polyamide and distearyl dimethylammonium hectorite be ground to fineness for mixing and stirring after nanoscale, obtain curing agent;
(3) by weight mian paint:Curing agent:Diluent=1: weigh mian paint, curing agent and diluent at 0.25: 0.5, first will
Diluent is added in mian paint, and curing agent is added after stirring 10min, continues to stir 10min, is obtained for fat content ground high
Aqueous sealing primer;
In the above method, the cosolvent is made up of following mass percent component:Propylene glycol monomethyl ether 35%, ethanol
, first be dissolved in tung oil in ethanol by the 60%th, tung oil 5%, and propylene glycol monomethyl ether is added after being well mixed, and is well mixed, and obtains hydrotropy
Agent.
Embodiment 2
The method for preparing the aqueous sealing primer for fat content ground high, comprises the following steps:
(1) mian paint is prepared
A. raw material is weighed by following mass percent:Epoxy resin 50%, defoamer 0.2%, moistening flatting agent 0.3%,
Reactive diluent 8%, cosolvent 41.5%, epoxy resin is liquid-state epoxy resin, 213~233g/Eq of its epoxide equivalent, solid
Content is more than 99.4%, and defoamer is that polyethers based polysiloxane and octanol compare 10 with weight:1 mixture, moistening flatting agent is
It is carboxy-modified polyether-based dimethyl silicone polymer, reactive diluent is that hydrophilic active diluent C12~C14 alkyl shrink is sweet
Oily ether;
B. epoxy resin, reactive diluent and part cosolvent are added in reaction vessel, with rotating speed 700rpm stirrings point
8min is dissipated, mixed liquor A is obtained;
C. to defoamer and moistening flatting agent is added dropwise in mixed liquor A while stirring, rate of addition is 10mL/min, stirring speed
Degree 1100rpm, after completion of dropping, stops stirring, then disperses 10min with supersonic oscillations, and ultrasonic frequency is 60MHz, is obtained
Mixture B;
D. by remaining cosolvent addition mixture B, supersonic oscillations dispersion 5min is continued, ultrasonic frequency is
50MHz, obtains mian paint;
(2) curing agent is prepared
Modified polyamide and two hard is weighed respectively than 4: 1 by the weight of modified polyamide and distearyl dimethylammonium hectorite
Fat dimethylammonium hectorite;Modified polyamide and distearyl dimethylammonium hectorite will be ground to respectively using micro mist grinder
Fineness obtains curing agent less than mixing and stirring after 50nm;
(3) by weight mian paint:Curing agent:Water=1: weigh mian paint, curing agent and water at 0.25: 1, first adds water to mian paint
In, 10min is stirred, curing agent is added, 10min is stirred, obtain the aqueous sealing primer for fat content ground high;
In the above method, the cosolvent is made up of following mass percent component:Propylene glycol monomethyl ether 35%, ethanol
, first be dissolved in linseed oil in ethanol by the 60%th, linseed oil 5%, and propylene glycol monomethyl ether is added after being well mixed, and is well mixed, and is obtained
Cosolvent.
Embodiment 3
The method for preparing the aqueous sealing primer for fat content ground high, comprises the following steps:
(1) mian paint is prepared
A. raw material is weighed by following mass percent:Epoxy resin 55%, defoamer 0.3%, moistening flatting agent 0.4%,
Reactive diluent 8%, cosolvent 36.3%, the epoxy resin be liquid-state epoxy resin, 213~233g/Eq of its epoxide equivalent,
Solids content is more than 99.4%, and the defoamer is that polyethers based polysiloxane and octanol compare 10 with weight:1 mixture, it is described
Moistening flatting agent is polyether-based dimethyl silicone polymer, and the reactive diluent is hydrophilic active diluent C12~C14 alkyl
Glycidol ether;
B. epoxy resin, reactive diluent and part cosolvent are added in reaction vessel, with rotating speed 800rpm stirrings point
8min is dissipated, mixed liquor A is obtained;
C. to defoamer and moistening flatting agent is added dropwise in mixed liquor A while stirring, rate of addition is 10mL/min, stirring speed
Degree 1200rpm, after completion of dropping, stops stirring, then disperses 10min with supersonic oscillations, and ultrasonic frequency is 70MHz, is obtained
Mixture B;
D. by remaining cosolvent addition mixture B, supersonic oscillations dispersion 5min is continued, ultrasonic frequency is
50MHz, obtains mian paint;
(2) curing agent is prepared
Modified polyamide and two hard is weighed respectively than 5: 1 by the weight of modified polyamide and distearyl dimethylammonium hectorite
Fat dimethylammonium hectorite;Modified polyamide and distearyl dimethylammonium hectorite will be ground to respectively using micro mist grinder
Fineness is mixing and stirring after nanoscale, obtains curing agent;
(3) by weight mian paint:Curing agent:Diluent=1: weigh mian paint, curing agent and diluent at 0.25: 0.8, first will
Diluent is added in mian paint, stirs 10min, adds curing agent, stirs 10min, obtains the water for fat content ground high
Property seal coat;
In the above method, the cosolvent is made up of following mass percent component:Propylene glycol monomethyl ether 35%, ethanol
, first be dissolved in dry vegetable oil in ethanol by the 60%th, dry vegetable oil 5%, and propylene glycol monomethyl ether is added after being well mixed, and mixing is equal
It is even, obtain cosolvent.
Performance test
Under normal temperature condition, the aqueous sealing primer for fat content ground high prepared by above-mentioned 3 embodiments is entered
Row spraying is brushed in woodenware surface, spontaneously dries or low-temperature bake is dried, and the construction term of validity is 4h.Construction technology:Take without
The cypress plate of polishing is crossed, by after carefully polishing, spraying different seal coats, is slightly polished after drying, spray aqueous wooden ware
Transparent priming two is throughout aqueous dull finishing coat one time, after drying 24h, room temperature, contrast test oil sealing fat effect.It is of the invention
Priming paint and the Performance comparision of the aqueous sealing primer sample bought back on the market, see the table below:
The sealing effect of different aqueous sealing primers
Model | Sealing effect |
Mono-component aqueous seal coat | The place of scabbing heaves within 10 days |
Bi-component waterborne seal coat | The place of scabbing heaves within 20 days |
Embodiment 1 | Film half a year is without exception |
Embodiment 2 | Film half a year is without exception |
Embodiment 3 | Film half a year is without exception |
Test result is visible, and the place's of scabbing film of standard aqueous seal coat is substantially heaved after 20 days, has illustrated grease
Toward exosmosis, cause film to heave, significantly impact painting effect.And spray the cypress of seal coat prepared by 3 embodiments
Plate, film coated surface is still smooth without exception after half a year, and the place of scabbing does not heave, and thus illustrates that seal coat of the invention has excellent
Different sealing process, can effectively prevent oozing out for the materials such as ground small molecule grease, be prevented effectively from film and heave, and come off
Disadvantage, adhesive force is good, solves the deficiency that existing water-borne wood coating is present.
It can be that professional and technical personnel in the field realize or use that above-mentioned implementation method is intended to illustrate the present invention, to above-mentioned
Implementation method is modified and will be apparent for those skilled in the art, therefore the present invention is included but is not limited to
Above-mentioned implementation method, it is any to meet the claims or specification description, meet with principles disclosed herein and novelty,
The method of inventive features, technique, product, each fall within protection scope of the present invention.
Claims (9)
1. a kind of aqueous sealing primer for fat content ground high, is made up of mian paint, curing agent and diluent, and its feature exists
In the weight ratio of mian paint, curing agent and diluent is 1: 0.25: 0.5~1;The mian paint by following mass percent component
Constitute:Epoxy resin 40~55%, defoamer 0.2~0.5%, moistening flatting agent 0.3~0.5%, reactive diluent 8~
12%, cosolvent 36~47%;The epoxy resin is liquid-state epoxy resin, and 213~233g/Eq of its epoxide equivalent, solid contains
Amount is more than 99.4%;The reactive diluent is hydrophilic active diluent C12~C14 alkyl glycidyl ethers;The hydrotropy
Agent is made up of following mass percent component:Propylene glycol monomethyl ether 35%, ethanol 60%, dry vegetable oil 5%;The curing agent is
The mixture of modified polyamide and distearyl dimethylammonium hectorite with weight than 3~5: 1.
2. the aqueous sealing primer of fat content ground high is used for as claimed in claim 1, it is characterised in that the diluent
It is water, water consumption is by weight, mian paint: curing agent: water=1: 0.25: 1.
3. as claimed in claim 2 be used for fat content ground high aqueous sealing primer, it is characterised in that the mian paint by
The component of following mass percent is constituted:Epoxy resin 50~53%, defoamer 0.2~0.3%, moistening flatting agent 0.3~
0.4%th, reactive diluent 8~10%, cosolvent 36~42%;213~the 233g/Eq of epoxide equivalent of the epoxy resin, Gu
Body content is more than 99.4%;The cosolvent is made up of following mass percent component:Propylene glycol monomethyl ether 35%, ethanol 60%,
Dry vegetable oil 5%;The curing agent is the mixing that modified polyamide and distearyl dimethylammonium hectorite compare 5: 1 with weight
Thing.
4. the aqueous sealing primer of fat content ground high is used for as claimed in claim 3, it is characterised in that described modified poly-
The amine value of acid amides is 180~220mgKOH/g.
5. the aqueous sealing primer of fat content ground high is used for as claimed in claim 1, it is characterised in that the defoamer
It is that polyethers based polysiloxane and octanol compare 10 with weight:1 mixture.
6. the aqueous sealing primer of fat content ground high is used for as claimed in claim 1, it is characterised in that the wetting stream
Flat agent is polyether-based dimethyl silicone polymer.
7. the aqueous sealing primer of fat content ground high is used for as claimed in claim 6, it is characterised in that the polyether-based
Dimethyl silicone polymer is carboxy-modified polyether-based dimethyl silicone polymer.
8. the aqueous sealing primer of fat content ground high is used for as claimed in claim 1, it is characterised in that the dryness is planted
Thing oil is tung oil or linseed oil.
9. the preparation method of a kind of aqueous sealing primer for fat content ground high, it is characterised in that comprise the following steps:
(1) mian paint is prepared
A. raw material is weighed by following mass percent:Epoxy resin 40~55%, defoamer 0.2~0.5%, moistening flatting agent
0.3~0.5%, reactive diluent 8~12%, cosolvent 36~47%;
B. epoxy resin, reactive diluent and part cosolvent are added in reaction vessel, with 600~800rpm of rotating speed stirrings point
8min is dissipated, mixed liquor A is obtained;
C. to defoamer and moistening flatting agent is added dropwise in mixed liquor A while stirring, rate of addition is 10mL/min, mixing speed
1000~1200rpm, after completion of dropping, stop stirring, then with supersonic oscillations disperse 10min, ultrasonic frequency be 50~
70MHz, obtains mixture B;
D. by remaining cosolvent addition mixture B, supersonic oscillations dispersion 5min is continued, ultrasonic frequency is 50MHz, is obtained
To mian paint;
(2) curing agent is prepared
Modified polyamide and two hard is weighed respectively than 3~5: 1 by the weight of modified polyamide and distearyl dimethylammonium hectorite
Fat dimethylammonium hectorite;Modified polyamide and distearyl dimethylammonium hectorite are ground to carefully respectively using micro mist grinder
It is mixing and stirring after nanoscale to spend, and obtains curing agent;
(3) by weight mian paint:Curing agent:Diluent=1: 0.25: 0.5~1 weighs mian paint, curing agent and diluent, first will
Diluent is added in mian paint, and curing agent is added after stirring 10min, continues to stir 10min, is obtained for fat content ground high
Aqueous sealing primer;
In the above method, the cosolvent is made up of following mass percent component:It is propylene glycol monomethyl ether 35%, ethanol 60%, dry
Property vegetable oil 5%, first dry vegetable oil is dissolved in ethanol, it is well mixed after add propylene glycol monomethyl ether, be well mixed, obtain
Cosolvent.