CN106833042B - Special coating for hot steel billet marking machine - Google Patents
Special coating for hot steel billet marking machine Download PDFInfo
- Publication number
- CN106833042B CN106833042B CN201710098992.XA CN201710098992A CN106833042B CN 106833042 B CN106833042 B CN 106833042B CN 201710098992 A CN201710098992 A CN 201710098992A CN 106833042 B CN106833042 B CN 106833042B
- Authority
- CN
- China
- Prior art keywords
- nano
- steel billet
- special coating
- steel
- hot steel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The special coating for hot steel billet number spraying machine comprises, by weight, 10-15% of nano titanium dioxide, 2-5% of nano zirconium oxide, 2-5% of sodium dihydrogen phosphate, 5-10% of nano barium sulfate, 5-15% of nano rare earth micro powder, 2-5% of dispersant, 2-5% of aluminum sulfate and the balance of water. The paint is used for spraying codes, marks and writing marks are clear, and the paint is wear-resistant, waterproof and not easy to fall off. No toxicity and pollution, and its temp. resistance is up to 2000 deg.C. The spray gun is suitable for high-temperature environments of steel plants, can be applied to imported and domestic various spray gun lengths, does not block the spray gun, is non-toxic, environment-friendly, pollution-free, flame-retardant and antioxidant. The steel mixing accident caused by unclear marks in the steel plant is completely avoided.
Description
Technical Field
The invention relates to a special coating for a hot steel billet marking machine, belonging to the technical field of metal material surface spraying.
Background
With the rapid development of the steel industry, metal castings are more and more widely applied under the condition of high-temperature working conditions. After the continuous casting and drawing billet comes out, the surface is required to be marked, and the steel mixing event of various materials caused by unclear marks is eliminated. The marking materials applied at present in China comprise paint, aluminum wires and copper wires. In practical application, the temperature of the coating can generally resist about 300 ℃, and the effect is not ideal when the temperature is higher than 300 ℃, because the components are generally phenolic aldehyde, modified epoxy coating and organosilicon coating, the temperature resistance is poor, and the coating is inflammable. And materials such as aluminum, copper and the like have high cost, a large amount of electric energy needs to be consumed to dissolve the materials into liquid to spray, the mechanical failure rate is high, and the actual production requirements cannot be met.
Disclosure of Invention
In order to solve the existing problems, the invention provides a special coating for a hot steel billet marking machine, which can resist high temperature up to 2000 ℃.
The purpose of the invention is realized by the following technical scheme: the special coating for the hot steel billet number spraying machine is characterized by comprising, by weight, 10-15% of nano titanium dioxide, 2-5% of nano zirconium oxide, 2-5% of sodium dihydrogen phosphate, 5-10% of nano barium sulfate, 5-15% of nano rare earth micro powder, 2-5% of a dispersing agent, 2-5% of aluminum sulfate and the balance of water.
The preferable mixture ratio is as follows: 15% of nano titanium dioxide, 5% of nano zirconium oxide, 3% of sodium dihydrogen phosphate, 10% of nano barium sulfate, 10% of nano rare earth micro powder, 2% of dispersing agent, 3% of aluminum sulfate and 52% of water.
The special coating for the hot steel billet marking machine comprises the following preparation methods: the preparation method comprises the steps of preparing the raw materials except water according to the ratio by metering, premixing the prepared raw materials for 3-5 minutes by using stirring equipment, adding water for stirring, stirring for 10-20 minutes to obtain a coating, and filling by using a filling machine.
The invention has the beneficial effects that: the invention adopts the scheme, is an innovation for the high-temperature coating, and the selected materials have heat resistance and non-combustibility. When the paint is used, the paint and the surface of steel react quickly to generate an inorganic polymer with a three-dimensional structure, the coating and the surface of steel are connected into a whole, and the paint is used for spraying codes, labels and handwriting marks clearly, is wear-resistant and waterproof and is not easy to fall off. No toxicity and pollution, and its temp. resistance is up to 2000 deg.C. The spray gun is suitable for high-temperature environments of steel plants, can be applied to imported and domestic various spray gun lengths, does not block the spray gun, is non-toxic, environment-friendly, pollution-free, flame-retardant and antioxidant. The steel mixing accident caused by unclear marks in the steel plant is completely avoided.
Detailed Description
The special coating for the hot steel billet spray marking machine comprises the following components in percentage by weight:
example 1 | Example 2 | Example 3 | |
Nano titanium dioxide | 15% | 10% | 12% |
Nano zirconium oxide | 5% | 2% | 5% |
Sodium dihydrogen phosphate | 3% | 3% | 5% |
Nano barium sulfate | 10% | 6% | 5% |
Nano rare earth micro powder | 10% | 8% | 15% |
Dispersing agent | 2% | 5% | 2% |
Aluminium sulphate | 3% | 5% | 2% |
Water (W) | 52% | 61% | 54% |
The preparation process comprises the following steps: the preparation method comprises the steps of preparing the raw materials except water according to the ratio by metering, premixing the prepared raw materials for 3-5 minutes by using stirring equipment, adding water for stirring, stirring for 10-20 minutes to obtain a coating, and filling by using a filling machine.
The performance indexes of the special coating for the hot steel billet spray marking machine prepared in the embodiment are shown in the following table:
serial number | Item | Technical index | Test method |
1 | Density g/cm3 | 1.17 | GB/T1724 |
2 | Solid content by volume | 63% | GB/T1725 |
3 | Appearance of coating film | Smooth, milky white and matt | GB/T1729 |
4 | Fineness of mum | ≤ 55 | GB/T1724 |
5 | Viscosity (25 ℃) scribble-4 viscometer | 25 | GB/T1723 |
6 | Drying time (25 +/-1 ℃) h | Surface dryness is less than or equal to 0.5; solid stem is less than or equal to 2 | GB/T1728 |
7 | Grade of adhesion | 1 | GB/T1720 |
8 | Hardness H of coating film | ≥ 8 | GB/T6739 |
9 | Heat resistance | (several hours at 2000 ℃) without falling off | GB/T1733 |
The special coating for the hot steel billet number spraying machine prepared by the method can be directly sprayed on hot steel billets, steel pieces, continuous casting slabs and hot rolling coils at the temperature of 200-2000 ℃, and the sprayed marks are not easy to fall off and are not discolored.
Claims (2)
1. The special coating for the hot steel billet number spraying machine is characterized by comprising the following components, by weight, 10% of nano titanium dioxide, 2% of nano zirconium oxide, 3% of sodium dihydrogen phosphate, 6% of nano barium sulfate, 8% of nano rare earth micro powder, 5% of a dispersing agent, 5% of aluminum sulfate and 61% of water.
2. The special coating for the hot steel billet spray marking machine according to claim 1, which is prepared by the following steps: the preparation method comprises the steps of preparing the raw materials except water according to the ratio by metering, premixing the prepared raw materials for 3-5 minutes by using stirring equipment, adding water for stirring, stirring for 10-20 minutes to obtain a coating, and filling by using a filling machine.