CN106832735A - A kind of ABS modified plastics of anticorrosive anti-wear - Google Patents
A kind of ABS modified plastics of anticorrosive anti-wear Download PDFInfo
- Publication number
- CN106832735A CN106832735A CN201510893911.6A CN201510893911A CN106832735A CN 106832735 A CN106832735 A CN 106832735A CN 201510893911 A CN201510893911 A CN 201510893911A CN 106832735 A CN106832735 A CN 106832735A
- Authority
- CN
- China
- Prior art keywords
- temperature
- area
- parts
- wear
- modified plastics
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of ABS modified plastics of anticorrosive anti-wear, including following weight portion material：Acrylonitrile-butadiene-styrene terpolymer 60-70 parts, 0.1-1 parts of poly- 1,3- butylene adipates, ATBC 1-2 parts, dibutyl phthalate 0.5-1 parts, 0.1-2 parts of PE waxes, thiol methyl tin 1-5 parts, 1-5 parts of ACR processing aids, 2-3 parts of ACR impact modifiers, silicone plasties anti-wear agent 0.5-1.5, tetrafluoroethene Ultramicro-powder 0.5-1.5, toughener 0.5-1.5；The ABS modified plastics of anticorrosive anti-wear prepared by the present invention, anticorrosive anti-wear is good, with preferable pliability, extensibility；There is preferable compatibility and dispersiveness between low cost, no murder by poisoning, each component.
Description
Technical field
The present invention relates to a kind of modified plastics, the modified modelings of more particularly to a kind of ABS of anticorrosive anti-wear
Material.
Background technology
ABS plastic process is simple, low cost, performance are high, in industry, are agriculturally widely used；
Not modified ABS plastic, its corrosion-resistant, abrasion resistance properties are bad, have impact on ABS plastic
Market prospects；
Chinese CN201510449048.5 is patent specification discloses a kind of modified modelings of corrosion resistant ABS
Material, its characteristic is decay resistance, and with preferable pliability, but it does not possess abrasion resistance properties and makes
With being limited in scope.
The content of the invention
(1) technical problem to be solved
The technical problem to be solved in the present invention is to provide a kind of possesses anticorrosive anti-wear performance, cost
The low ABS without anticorrosive anti-wear with preferable compatibility and dispersiveness between each component that is poisoning
Modified plastics.
(2) technical scheme
In order to solve the above technical problems, the present invention provides a kind of modified modelings of ABS of anticorrosive anti-wear
Material, including：
Acrylonitrile-butadiene-styrene terpolymer 60-70 parts, poly- 1,3- butylene adipates 0.1-1
Part, ATBC 1-2 parts, dibutyl phthalate 0.5-1 parts, 0.1-2 parts of mercaptan of PE waxes
1-5 parts of methyl tin, 1-5 parts of ACR processing aids, 2-3 parts of ACR impact modifiers, tetrafluoroethene
Ultramicro-powder 0.5-1.5 parts, toughener 0.5-1.5 parts.
Further, anticorrosive anti-wear ABS modified plastics includes the material of following weight portion：Third
Alkene nitrile -60 parts of butadiene-styrene terpolymer, 0.5 part of poly- 1,3- butylene adipates, citric acid
1.5 parts of tributyl, 0.5 part of dibutyl phthalate, 0.1 part of PE waxes, 2 parts of thiol methyl tin,
1 part of ACR processing aids, 2 parts of ACR impact modifiers.
Further, anticorrosive anti-wear ABS modified plastics includes the material of following weight portion：Third
Alkene nitrile -70 parts of butadiene-styrene terpolymer, 1 part of poly- 1,3- butylene adipates, citric acid three
2 parts of butyl ester, 1 part of dibutyl phthalate, 2 parts of PE waxes, 5 parts of thiol methyl tin, ACR
5 parts of processing aid, 3 parts of ACR impact modifiers.
Further, the preparation method comprises the following steps：Material is weighed, is stirred, mixed
Compound；In feeding the mixture into double screw extruder, the processing temperature of double screw extruder：One area's temperature
160-170 DEG C of degree, two area's temperature are 180-185 DEG C, and three area's temperature are 195-215 DEG C, four area's temperature
It it is 250-255 DEG C, five area's temperature are 235-245 DEG C, six area's temperature are 215-220 DEG C, seven area's temperature
It it is 225-235 DEG C, eight area's temperature are 225-230 DEG C, and engine speed is 350-450rpm；It is cold after extrusion
But check rod, air-dried pelletizing, that is, prepare corrosion-resistant ABS modified plastics of the present invention.
Further, the processing temperature of double screw extruder：One 160 DEG C of area's temperature, two area's temperature
It it is 175 DEG C, three area's temperature are 200 DEG C, four area's temperature are 245 DEG C, five area's temperature are 235 DEG C, six
Area's temperature is 210 DEG C, and seven area's temperature are 225 DEG C, and eight area's temperature are 230 DEG C.
Further, the rotating speed of the main frame is 400rpm.
(3) beneficial effect
Anticorrosive anti-wear ABS modified plastics of the present invention, with preferable pliability, extensibility；Into
There is preferable compatibility and dispersiveness between this low, no murder by poisoning, each component.
Specific embodiment
Case study on implementation 1：The present invention provides a kind of ABS modified plastics of anticorrosive anti-wear, including：
Acrylonitrile-butadiene-styrene terpolymer 60-70 parts, 0.1-1 parts of poly- 1,3- butylene adipates,
ATBC 1-2 parts, dibutyl phthalate 0.5-1 parts, 0.1-2 parts of thiol methyl of PE waxes
Tin 1-5 parts, 1-5 parts of ACR processing aids, 2-3 parts of ACR impact modifiers, tetrafluoroethene ultra micro
Powder 0.5-1.5 parts, toughener 0.5-1.5 parts.
Case study on implementation 2：Anticorrosive anti-wear ABS modified plastics includes the material of following weight portion：
60 parts of acrylonitrile-butadiene-styrene terpolymer, 0.5 part of poly- 1,3- butylene adipates, lemon
1.5 parts of sour tributyl, 0.5 part of dibutyl phthalate, 0.1 part of PE waxes, thiol methyl tin 2
Part, 1 part of ACR processing aids, 2 parts of ACR impact modifiers.
Case study on implementation 3：Anticorrosive anti-wear ABS modified plastics includes the material of following weight portion：
70 parts of acrylonitrile-butadiene-styrene terpolymer, 1 part of poly- 1,3- butylene adipates, citric acid
2 parts of tributyl, 1 part of dibutyl phthalate, 2 parts of PE waxes, 5 parts of thiol methyl tin, ACR
5 parts of processing aid, 3 parts of ACR impact modifiers.
The preparation method comprises the following steps：Material is weighed, is stirred, obtain mixture；Will be mixed
Compound is added in double screw extruder, the processing temperature of double screw extruder：One 160-170 DEG C of area's temperature,
Two area's temperature are 180-185 DEG C, and three area's temperature are 195-215 DEG C, and four area's temperature are 250-255 DEG C,
Five area's temperature are 235-245 DEG C, and six area's temperature are 215-220 DEG C, and seven area's temperature are 225-235 DEG C,
Eight area's temperature are 225-230 DEG C, and engine speed is 350-450rpm；Check rod is cooled down after extrusion, is air-dried
Pelletizing, that is, prepare corrosion-resistant ABS modified plastics of the present invention.
The processing temperature of double screw extruder：One 165 DEG C of area's temperature, two area's temperature are 180 DEG C, 3rd area
Temperature is 205 DEG C, and four area's temperature are 250 DEG C, and five area's temperature are 240 DEG C, and six area's temperature are 215 DEG C,
Seven area's temperature are 230 DEG C, and eight area's temperature are 235 DEG C.
The rotating speed of the main frame is 400rpm.
Anticorrosive anti-wear ABS modified plastics as obtained by above case study on implementation, with preferably soft
Toughness, extensibility；There is preferable compatibility and dispersiveness between low cost, no murder by poisoning, each component.
The above is only the preferred embodiment of the present invention, it is noted that for the art
For those of ordinary skill, on the premise of the technology of the present invention principle is not departed from, can also make some
Improvements and modifications, these improvements and modifications also should be regarded as protection scope of the present invention.
Claims (6)
1. the ABS modified plastics of anticorrosive anti-wear is torn open in a kind of, it is characterised in that including：
2. anticorrosive anti-wear ABS modified plastics according to claim 1, its feature
Be, including following weight portion material：
3. anticorrosive anti-wear ABS modified plastics according to claim 1, its feature exists
In, including following weight portion material：
4. the preparation method of the ABS modified plastics of anticorrosive anti-wear described in claim 1, its
It is characterised by, comprises the following steps：
Material is weighed, is stirred, obtain mixture；Feed the mixture into double screw extruder
In, the processing temperature of double screw extruder：One 150-160 DEG C of area's temperature, two area's temperature are
175-180 DEG C, three area's temperature are 190-210 DEG C, and four area's temperature are 245-250 DEG C, 5th area
Temperature is 230-240 DEG C, and six area's temperature are 210-215 DEG C, and seven area's temperature are 220-225
DEG C, eight area's temperature are 225-230 DEG C, and engine speed is 350-450rpm；Cooling is led after extrusion
Bar, air-dried pelletizing, that is, prepare anticorrosive anti-wear ABS modified plastics of the present invention.
5. the preparation side of the ABS modified plastics of anticorrosive anti-wear according to claim 4
Method, it is characterised in that the processing temperature of double screw extruder：One 160 DEG C of area's temperature, 2nd area
Temperature is 175 DEG C, and three area's temperature are 200 DEG C, and four area's temperature are 245 DEG C, and five area's temperature are
235 DEG C, six area's temperature are 210 DEG C, and seven area's temperature are 225 DEG C, and eight area's temperature are 230
℃。
6. the preparation side of the ABS modified plastics of anticorrosive anti-wear according to claim 4
Method, it is characterised in that：The rotating speed of the main frame is 400rpm.