CN106832465A - A kind of high temperature resistant plastic cement - Google Patents
A kind of high temperature resistant plastic cement Download PDFInfo
- Publication number
- CN106832465A CN106832465A CN201710046758.2A CN201710046758A CN106832465A CN 106832465 A CN106832465 A CN 106832465A CN 201710046758 A CN201710046758 A CN 201710046758A CN 106832465 A CN106832465 A CN 106832465A
- Authority
- CN
- China
- Prior art keywords
- parts
- plastic cement
- high temperature
- temperature resistant
- resistant plastic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high temperature resistant plastic cement, it is made up of according to weight ratio following component：36 parts of 40 60 parts of acrylonitrile, 30 50 parts of butadiene, 10 15 parts of polyarylsulfone (PAS), 5 10 parts of aromatic polyamide, 15 20 parts of epoxy resin, 18 28 parts of polytetrafluoroethylene (PTFE), 25 parts of di-iron trioxide and zinc oxide.The present invention improves the security that plastic cement is used.
Description
Technical field
The present invention relates to a kind of high temperature resistant plastic cement, belong to plastic material field.
Background technology
Plasthetics can be applied at many aspects, such as motorcycle pedal, electronic product, runway.Work as in plastic cement application
In, people are increasingly paid close attention to the performance of plastic cement.But, most of plastics make it have easily due to itself adding plasticizer etc.
Combustion property, temperature is slightly higher to be melted, therefore greatly reduces the security that plastics are used.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of high temperature resistant plastic cement, improves plastics safety in utilization.
In order to solve the above technical problems, the technical solution adopted by the present invention is：A kind of high temperature resistant plastic cement, is pressed by following component
According to weight than constituting：Acrylonitrile 40-60 parts, butadiene 30-50 parts, polyarylsulfone (PAS) 10-15 parts, aromatic polyamide 5-10 parts, ring
15-20 parts, polytetrafluoroethylene (PTFE) 18-28 parts, di-iron trioxide 2-5 parts and zinc oxide 3-6 parts of oxygen tree fat.
Further, it is made up of according to weight ratio following component：Acrylonitrile 45-55 parts, butadiene 35-45 parts, polyarylsulfone (PAS)
11-13 parts, aromatic polyamide 6-8 parts, epoxy resin 16-18 parts, polytetrafluoroethylene (PTFE) 21-25 parts, di-iron trioxide 3-4 parts and
Zinc oxide 4-5 parts.
Further, it is made up of according to weight ratio following component：49 parts of acrylonitrile, 38 parts of butadiene, polyarylsulfone (PAS) 12.4
Part, 7.6 parts of aromatic polyamide, 16.8 parts of epoxy resin, 23 parts of polytetrafluoroethylene (PTFE), 3.2 parts of di-iron trioxide and zinc oxide 4.3
Part.
Beneficial effects of the present invention：The good flame retardation effect of high temperature resistant plastic cement of the invention, improves the security that plastic cement is used.
Specific embodiment
Embodiment 1
A kind of high temperature resistant plastic cement, is made up of following component according to weight ratio：40 parts of acrylonitrile, 30 parts of butadiene, polyarylsulfone (PAS) 10
Part, 5 parts of aromatic polyamide, 15 parts of epoxy resin, 18 parts of polytetrafluoroethylene (PTFE), 2 parts of di-iron trioxide and 3 parts of zinc oxide.
Embodiment 2
A kind of high temperature resistant plastic cement, is made up of following component according to weight ratio：60 parts of acrylonitrile, 50 parts of butadiene, polyarylsulfone (PAS) 15
Part, 10 parts of aromatic polyamide, 20 parts of epoxy resin, 28 parts of polytetrafluoroethylene (PTFE), 5 parts of di-iron trioxide and 6 parts of zinc oxide.
Embodiment 3
A kind of high temperature resistant plastic cement, is made up of following component according to weight ratio：45 parts of acrylonitrile, 35 parts of butadiene, polyarylsulfone (PAS) 11
Part, 6 parts of aromatic polyamide, 16 parts of epoxy resin, 21 parts of polytetrafluoroethylene (PTFE), 3 parts of di-iron trioxide and 4 parts of zinc oxide.
Embodiment 4
A kind of high temperature resistant plastic cement, is made up of following component according to weight ratio：55 parts of acrylonitrile, 45 parts of butadiene, polyarylsulfone (PAS) 13
Part, 8 parts of aromatic polyamide, 18 parts of epoxy resin, 25 parts of polytetrafluoroethylene (PTFE), 4 parts of di-iron trioxide and 5 parts of zinc oxide.
Embodiment 5
A kind of high temperature resistant plastic cement, is made up of following component according to weight ratio：49 parts of acrylonitrile, 38 parts of butadiene, polyarylsulfone (PAS) 12.4
Part, 7.6 parts of aromatic polyamide, 16.8 parts of epoxy resin, 23 parts of polytetrafluoroethylene (PTFE), 3.2 parts of di-iron trioxide and zinc oxide 4.3
Part.
Embodiment described above is only that the preferred embodiment of the present invention is described, not to design of the invention
It is defined with scope, on the premise of design concept of the present invention is not departed from, ordinary skill technical staff is to this hair in this area
The all variations and modifications that bright technical scheme is made all should fall into protection scope of the present invention, claimed skill of the invention
Art content, is all documented in technical requirements book.
Claims (3)
1. a kind of high temperature resistant plastic cement, it is characterised in that：It is made up of according to weight ratio following component：Acrylonitrile 40-60 parts, butadiene
30-50 parts, polyarylsulfone (PAS) 10-15 parts, aromatic polyamide 5-10 parts, epoxy resin 15-20 parts, polytetrafluoroethylene (PTFE) 18-28 parts, three
Aoxidize two iron 2-5 parts and zinc oxide 3-6 parts.
2. a kind of high temperature resistant plastic cement according to claim 1, it is characterised in that：It is made up of according to weight ratio following component：
Acrylonitrile 45-55 parts, butadiene 35-45 parts, polyarylsulfone (PAS) 11-13 parts, aromatic polyamide 6-8 parts, epoxy resin 16-18 parts,
Polytetrafluoroethylene (PTFE) 21-25 parts, di-iron trioxide 3-4 parts and zinc oxide 4-5 parts.
3. a kind of high temperature resistant plastic cement according to claim 1, it is characterised in that：It is made up of according to weight ratio following component：
49 parts of acrylonitrile, 38 parts of butadiene, 12.4 parts of polyarylsulfone (PAS), 7.6 parts of aromatic polyamide, 16.8 parts of epoxy resin, polytetrafluoroethyl-ne
4.3 parts of 23 parts of alkene, 3.2 parts of di-iron trioxide and zinc oxide.