CN106832502A - A kind of high-temperature resistance plastice product - Google Patents
A kind of high-temperature resistance plastice product Download PDFInfo
- Publication number
- CN106832502A CN106832502A CN201510878480.6A CN201510878480A CN106832502A CN 106832502 A CN106832502 A CN 106832502A CN 201510878480 A CN201510878480 A CN 201510878480A CN 106832502 A CN106832502 A CN 106832502A
- Authority
- CN
- China
- Prior art keywords
- parts
- temperature resistance
- resistance plastice
- antioxidant
- carbon black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of high-temperature resistance plastice product, it is made up of following ratio of weight and number：Polyolefin 80-120 parts, pearl filler 5-10 parts, tourmaline particle 25-35 parts, ethylene-propylene diene copolymer 6-8 parts, carbon black 8-12 parts, antioxidant 6-10 parts, heat stabilizer 5-8 parts, stabilizer 2-3 parts and auxiliary agent 1-4 parts；The high-temperature resistance plastice product can solve the problem that current plastic products resistance to elevated temperatures is poor, the problem being limited using scope.
Description
Technical field
The present invention relates to a kind of high-temperature resistance plastice product.
Background technology
Plastic cement is that a class has plastic synthesis macromolecular material.It forms the big synthetic material of current daily life indispensable three with synthetic rubber, synthetic fibers.Specifically, plastics are, with natural or synthetic resin as main component, to add various additives, can be moulded under the conditions of uniform temperature and pressure etc. and be made definite shape, and the material of shape invariance is kept at normal temperatures.
Used as widely used packaging material, it has good moisture barrier property to polyolefin, but its gas barrier properties is poor.The defect poor to make up general polyolefine material gas barrier property, the method mainly taken has MULTILAYER COMPOSITE and blending and modifying.
Polyolefin plastic products in the market easily deform at high temperature, and so as to lose original shape, the use scope that result in plastic products is limited.
The content of the invention
It is poor to solve current plastic products resistance to elevated temperatures that the technical problems to be solved by the invention are to provide a kind of high-temperature resistance plastice product, the problem being limited using scope.
The purpose of the present invention is achieved by following technical proposals：
A kind of high-temperature resistance plastice product, is made up of following ratio of weight and number：Polyolefin 80-120 parts, pearl filler 5-10 parts, tourmaline particle 25-35 parts, ethylene-propylene diene copolymer 6-8 parts, carbon black 8-12 parts, antioxidant 6-10 parts, heat stabilizer 5-8 parts, stabilizer 2-3 parts and auxiliary agent 1-4 parts,
Further, it is made up of following ratio of weight and number：1 part of 80 parts of polyolefin, 5 parts of pearl filler, 25 parts of tourmaline particle, 6 parts of ethylene-propylene diene copolymer, 8 parts of carbon black, 6 parts of antioxidant, 5 parts of heat stabilizer, 2 parts of stabilizer and auxiliary agent.
Further, it is made up of following ratio of weight and number：4 parts of 120 parts of polyolefin, 10 parts of pearl filler, 35 parts of tourmaline particle, 8 parts of ethylene-propylene diene copolymer, 12 parts of carbon black, 10 parts of antioxidant, 8 parts of heat stabilizer, 3 parts of stabilizer and auxiliary agent.
Further, it is made up of following ratio of weight and number：3 parts of 100 parts of polyolefin, 7 parts of pearl filler, 30 parts of tourmaline particle, 7 parts of ethylene-propylene diene copolymer, 10 parts of carbon black, 8 parts of antioxidant, 7 parts of heat stabilizer, 2 parts of stabilizer and auxiliary agent.
Further, the polyolefin is polyethylene and/or polypropylene.
Further, the pearl filler is with lime stone as raw material, mixes and pass through plasticizing for 120-150 DEG C of high-speed mixer through excess temperature, granulates and form.
Further, the tourmaline particle by irony tourmaline with magnesia tourmaline according to 4:1 weight composition.
Further, described carbon black is conductive carbon black.
Further, the antioxidant is sub- acid phosphide kind antioxidant and phenolic antioxidant according to 2:1 weight composition, the auxiliary agent is Tissuemat E.
The beneficial effects of the invention are as follows：Have the advantages that high mechanical strength, corrosion-resistant, antistatic, fire-retardant, processing cost are low, production efficiency is high, long service life.
Specific embodiment
In order to make the purpose , technical scheme and advantage of the present invention be clearer, below in conjunction with specific embodiment, the present invention will be described in further detail.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not intended to limit the present invention.
Embodiment
A kind of high-temperature resistance plastice product, is made up of following ratio of weight and number：1 part of 80 parts of polyolefin, 5 parts of pearl filler, 25 parts of tourmaline particle, 6 parts of ethylene-propylene diene copolymer, 8 parts of carbon black, 6 parts of antioxidant, 5 parts of heat stabilizer, 2 parts of stabilizer and auxiliary agent.
The polyolefin is polyethylene and/or polypropylene.
The pearl filler mixes and pass through plasticizing for 120-150 DEG C of high-speed mixer, granulates and form with lime stone as raw material through excess temperature.
The tourmaline particle is by irony tourmaline with magnesia tourmaline according to 4:1 weight composition.
Described carbon black is conductive carbon black.
The antioxidant is sub- acid phosphide kind antioxidant and phenolic antioxidant according to 2:1 weight composition, the auxiliary agent is Tissuemat E.
The beneficial effects of the invention are as follows：Have the advantages that high mechanical strength, corrosion-resistant, antistatic, fire-retardant, processing cost are low, production efficiency is high, long service life.
The above, specific embodiment only of the invention, but protection scope of the present invention is not limited thereto, any change or replacement expected without creative work, should all cover within the scope of the present invention.
Claims (9)
1. a kind of high-temperature resistance plastice product, it is characterised in that：It is made up of following ratio of weight and number：Polyolefin 80-120 parts, pearl filler 5-10 parts, tourmaline particle 25-35 parts, ethylene-propylene diene copolymer 6-8 parts, carbon black 8-12 parts, antioxidant 6-10 parts, heat stabilizer 5-8 parts, stabilizer 2-3 parts and auxiliary agent 1-4 parts.
2. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:It is made up of following ratio of weight and number：1 part of 80 parts of polyolefin, 5 parts of pearl filler, 25 parts of tourmaline particle, 6 parts of ethylene-propylene diene copolymer, 8 parts of carbon black, 6 parts of antioxidant, 5 parts of heat stabilizer, 2 parts of stabilizer and auxiliary agent.
3. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:It is made up of following ratio of weight and number：4 parts of 120 parts of polyolefin, 10 parts of pearl filler, 35 parts of tourmaline particle, 8 parts of ethylene-propylene diene copolymer, 12 parts of carbon black, 10 parts of antioxidant, 8 parts of heat stabilizer, 3 parts of stabilizer and auxiliary agent.
4. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:It is made up of following ratio of weight and number：3 parts of 100 parts of polyolefin, 7 parts of pearl filler, 30 parts of tourmaline particle, 7 parts of ethylene-propylene diene copolymer, 10 parts of carbon black, 8 parts of antioxidant, 7 parts of heat stabilizer, 2 parts of stabilizer and auxiliary agent.
5. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:The polyolefin is polyethylene and/or polypropylene.
6. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:The pearl filler mixes and pass through plasticizing for 120-150 DEG C of high-speed mixer, granulates and form with lime stone as raw material through excess temperature.
7. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:The tourmaline particle is by irony tourmaline with magnesia tourmaline according to 4:1 weight composition.
8. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:Described carbon black is conductive carbon black.
9. high-temperature resistance plastice product as claimed in claim 1, it is characterised in that:The antioxidant is sub- acid phosphide kind antioxidant and phenolic antioxidant according to 2:1 weight composition, the auxiliary agent is Tissuemat E.