CN106811136A - A kind of glue of PU materials vamp and preparation method thereof and application method - Google Patents
A kind of glue of PU materials vamp and preparation method thereof and application method Download PDFInfo
- Publication number
- CN106811136A CN106811136A CN201510862793.2A CN201510862793A CN106811136A CN 106811136 A CN106811136 A CN 106811136A CN 201510862793 A CN201510862793 A CN 201510862793A CN 106811136 A CN106811136 A CN 106811136A
- Authority
- CN
- China
- Prior art keywords
- glue
- parts
- vamp
- materials
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of glue of PU materials vamp, by following mass parts into being grouped into:30-35 parts, curing agent 2-3 parts, acetate emulsion 1-2 parts, calcium carbonate superfine powder 1-2 parts, tackifying resin 2-3 parts, surface conditioning agent 1-2 parts of PU glue.The glue gluing of PU materials vamp of the invention is good, water-tolerant, it is ensured that vamp can be used normally in the environment of moist, many water, improve its service life.
Description
Technical field
The present invention relates to a kind of glue, more particularly to a kind of PU materials vamp glue and its
Preparation method and application method.
Background technology
The species of footwear is various, but the function of footwear is mainly used for wearing, to the mill of footwear in general
Damage or the extent of damage be typically all comparing high, thus to the quality requirement of footwear be typically also compared with
It is high, simultaneously because people often wear shoes carry out different environment or places, so to footwear
Quality requirement is higher, such as, rainy weather, being so accomplished by vamp has certain waterproof
Effect, prevents vamp from soaking, but now some be used for vamp glue can not meet market and
The need for client, the quality also certain defect of glue, it is difficult to the service life of the footwear of raising.
The content of the invention
The purpose of the present invention cannot meet market and visitor for the glue of vamp in the prior art
The need for family, therefore, providing a kind of glue of PU materials vamp, the glue gluing is good,
Water-tolerant, it is ensured that vamp can be used normally in the environment of moist, many water, be improve
Its service life.
To achieve the above object, the technical solution adopted by the present invention is:A kind of PU materials vamp
Glue, by following mass parts into being grouped into:30-35 parts of PU glue, curing agent 2-3 parts,
Acetate emulsion 1-2 parts, calcium carbonate superfine powder 1-2 parts, tackifying resin 2-3 parts, at surface
1-2 parts of agent of reason.
Further, a kind of system of the glue of PU materials vamp as claimed in claim 1
Preparation Method, its preparation process is:By PU glue and curing agent, acetate emulsion, thickening tree
Fat carries out mixing 2-3min by said ratio, and adds calcium carbonate superfine powder in mixing, most
Surface conditioning agent is being added to be stirred mixed processing afterwards.
Further, a kind of application method of the glue of PU materials vamp, is using glue
When carrying out viscose to vamp, brushing treatment first is carried out to vamp with inorganic agent, then applied
Glue treatment.
Beneficial effect:The glue gluing of PU materials vamp of the invention is good, water-tolerant,
Ensure that vamp can be used normally in the environment of moist, many water, improve it and use the longevity
Life.
Specific embodiment
Embodiment 1
A kind of glue of PU materials vamp, by following mass parts into being grouped into:PU glue 30
Part, 2 parts of curing agent, 1 part of acetate emulsion, 1 part of calcium carbonate superfine powder, tackifying resin 2
Part, 1 part of surface conditioning agent, the preparation process of glue is:By PU glue and curing agent, acetic acid
Vac emulsion, tackifying resin carry out mixing 2min by said ratio, and are added in mixing
Calcium carbonate superfine powder, is finally adding surface conditioning agent to be stirred mixed processing, the use of glue
Method is, when viscose is carried out to vamp using glue, vamp to be carried out at brushing with inorganic agent first
Reason, is then carrying out gluing treatment.
Embodiment 2
A kind of glue of PU materials vamp, by following mass parts into being grouped into:PU glue 32
Part, 2.5 parts of curing agent, 1.5 parts of acetate emulsion, 1.5 parts of calcium carbonate superfine powder, thickening
2.5 parts of resin, 1.5 parts of surface conditioning agent, the preparation process of glue is:By PU glue with it is solid
Agent, acetate emulsion, tackifying resin carry out mixing 2.5min by said ratio, and
Calcium carbonate superfine powder is added in mixing, is finally adding surface conditioning agent to be stirred at mixing
Reason, the application method of glue is when viscose is carried out to vamp using glue, first with inorganic agent pair
Vamp carries out brushing treatment, is then carrying out gluing treatment.
Embodiment 3
A kind of glue of PU materials vamp, by following mass parts into being grouped into:PU glue 35
Part, 3 parts of curing agent, 2 parts of acetate emulsion, 2 parts of calcium carbonate superfine powder, tackifying resin 3
Part, 2 parts of surface conditioning agent, the preparation process of glue is:By PU glue and curing agent, acetic acid
Vac emulsion, tackifying resin carry out mixing 3min by said ratio, and are added in mixing
Calcium carbonate superfine powder, is finally adding surface conditioning agent to be stirred mixed processing, the use of glue
Method is, when viscose is carried out to vamp using glue, vamp to be carried out at brushing with inorganic agent first
Reason, is then carrying out gluing treatment.
Embodiment described above is only that the preferred embodiment of the present invention is described, and
It is non-that the spirit and scope of the present invention are defined.The premise of design concept of the present invention is not being departed from
Under, all variations and modifications that this area ordinary person makes to technical scheme,
Protection scope of the present invention should be dropped into.
Claims (3)
1. a kind of glue of PU materials vamp, it is characterised in that by following mass parts composition
Composition:30-35 parts of PU glue, curing agent 2-3 parts, acetate emulsion 1-2 parts, it is ultra-fine
Calcium carbonate 1-2 parts, tackifying resin 2-3 parts, surface conditioning agent 1-2 parts.
2. a kind of preparation method of the glue of PU materials vamp as claimed in claim 1,
Characterized in that, its preparation process is:By PU glue and curing agent, acetate emulsion, increasing
Viscosity resin carries out mixing 2-3min by said ratio, and adds calcium carbonate superfine powder in mixing,
It is last to add surface conditioning agent to be stirred mixed processing.
3. a kind of application method of the glue of PU materials vamp as claimed in claim 1,
Characterized in that, when viscose is carried out to vamp using glue, first being carried out to vamp with inorganic agent
Brushing is processed, and is then carrying out gluing treatment.