CN106800409A - A kind of preparation method of quantum potsherd - Google Patents
A kind of preparation method of quantum potsherd Download PDFInfo
- Publication number
- CN106800409A CN106800409A CN201710042200.7A CN201710042200A CN106800409A CN 106800409 A CN106800409 A CN 106800409A CN 201710042200 A CN201710042200 A CN 201710042200A CN 106800409 A CN106800409 A CN 106800409A
- Authority
- CN
- China
- Prior art keywords
- weight portions
- quantum
- potsherd
- preparation
- tourmaline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to new material technology field, and in particular to volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, monazite were crushed to 1500 mesh sieves by a kind of preparation method of quantum potsherd, S1. respectively;S2. volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, magnesium, monazite, magnesia are taken, is uniformly mixed, obtain compound;S3. compound is put into mould, the treatment of steam pressing mold is done at 1450 ~ 1550 DEG C, cooling shaping obtains quantum potsherd.Preparation method of the invention is simple, and quantum potsherd is obtained by steam pressing mold, classification cooling shaping, and preparation cost is low, efficiency and high yield rate, it is adaptable to industrializes, mass produce.
Description
Technical field
The present invention relates to new material technology field, and in particular to a kind of preparation method of quantum potsherd.
Background technology
Water is not only the primary condition of life presence, is also the basic structure sheet of life structure, the mankind with water resource is close can not
Point.With the progress and the development in city of human society, water is divided into drinking water and domestic water, but either drinking water is also
It is domestic water, while it is that the mankind service, is also polluted by the mankind all the time, and pollution level is on the rise,
The species of polluter increases increasingly, so that threatening the health and lives of the mankind.At present, it has been recognized that, drinking water
It is the mode of infection of harmful substance, in fact, the breathing of people and skin absorption are likely to make one to absorb these nuisances during shower
Matter, exactly domestic water is more through the various aspects of our daily lifes, for example, shower water, water for kitchen use, clothes
Water for cleaning, sanitary toilet water.Particularly shower water, due to hair and skin contact directly with human body, its purification is asked
Topic should cause the attention of people.
Tourmaline is a kind of mineral for uniquely carrying electric property on the earth in mineral, and main component has magnesium, aluminium, iron, boron
Deng more than the 10 kinds of trace elements favourable to human body.Tourmaline being capable of permanent generation micro-current, this electric current and human nerve
Electric current be similar to, can thus play and promote blood circulation, smoothly act on, in addition tourmaline can also anion releasing, this
A little anions can adjust human body ionic equilibrium, and body and mind loosens, activating cell, improve many effects such as self-healing rate, and can suppress
The oxidation of body and the effect for eliminating the unusual smell.Tourmaline can also anion releasing, these anions can adjust human body ionic equilibrium,
Body and mind loosens, activating cell, improves many effects such as self-healing rate, and can suppress the oxidation of body and effect for eliminating the unusual smell.Some
Research is also indicated that:Tourmaline once contact water, moment just can in water release current, this electric current is best suitable for human body
The weak current of 0.06mA, when water is contacted with above-mentioned weak current, hydrogen ion and hydroxyl ion in the hydrone of surrounding are just
Separate, the hydrogen ion for effectively dissociating in absorption water makes water in faintly acid, and oxygen in water is increased, closest
Human body cell water, it is highly beneficial to health.
And ceramic material absorption Nanometer Copper, zinc, silver alloy, because remaining during alloying metal cluster can effectively go to remove water
Chlorine, in the harmful substance such as soluble heavy metal ion and nitrate, fluoride, carbonate and sulfate, and controllable water
Bacterium and algae growth and breeding and prevent the accumulation of hard scale, while can remove the water delivery pipe corrosion being made by ferrous materials
When the ferrous iron oxide colloid that is formed, purified water so as to reach.
In recent years, in the market has occurred in that the technology and product of many purified waters, including chemicals treatment technology and product
Product, activated carbon class filtration, purification treatment technology and product, ion exchange resin treatment technology and product, medical stone class purified treatment
Technology and product etc..But facts have proved above-mentioned various technologies and product, such as chemicals treatment technology and product because of excitant or
Generation chemically reacts and is eliminated, and other several treatment technologies and product mostly single effect or imperfection, also do not possess or
Not exclusively possess anion releasing, sterilization, antibacterial, the effect of dechlorination.
The content of the invention
It is an object of the invention to overcome the deficiencies in the prior art, there is provided a kind of preparation method of quantum potsherd, prepare
Method is simple, and quantum potsherd is obtained by steam pressing mold, classification cooling shaping, and preparation cost is low, efficiency and high yield rate, fits
For industrializing, mass producing.
The purpose of the present invention is achieved through the following technical solutions:
A kind of preparation method of quantum potsherd, comprises the following steps:
S1. volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, monazite were crushed to 1500 mesh sieves respectively;
S2. volcanic rock, the tourmaline of 5-8 weight portions, the germanite of 6-10 weight portions, the 20-24 weight portions of 20-25 weight portions are taken
Rare earth, the medical stone of 3-6 weight portions, the aluminite of 2-5 weight portions, the magnesium of 4-6 weight portions, the monazite of 10-12 weight portions,
The magnesia of 15-20 weight portions, is uniformly mixed, and obtains compound;
S3. compound is put into mould, the treatment of steam pressing mold is done at 1450 ~ 1550 DEG C, cooling shaping obtains quantum ceramics
Piece.
Further, the magnesium is the particle of 5 ~ 10 μm of particle diameter.
Further, the magnesia is the particle of 1 ~ 20 μm of particle diameter.
Further, mixing is stirred in the step S2 is carried out in agitator.
Further, the agitator speed is 400 ~ 800rpm.
Further, the stirring incorporation time is 3 ~ 5h.
Further, the step S3 is concretely comprised the following steps:Compound is put into mould, in steam ambient, 1450 ~
Pressing mold is made at 1550 DEG C and processes 30 ~ 90min, then temperature is down to 1100 ~ 1150 DEG C, steady 30 ~ 45min of temperature, then it is cooled to 600 ~
700 DEG C, 20 ~ 30min of steady temperature, then natural cooling shaping, obtains quantum potsherd.
The beneficial effects of the invention are as follows:Preparation method of the invention is simple, is obtained by steam pressing mold, classification cooling shaping
Quantum potsherd, preparation cost is low, efficiency and high yield rate, it is adaptable to industrializes, mass produce, while obtained quantum is made pottery
The enough disinfectants that will be remained in water of ceramics and halogenated compound reduction conversion, adjust the acid-base balance of water, to reducing hypertension, height
Blood sugar has facilitation, realizes healthy water;The macroelement, micro- of release high nutritive value that simultaneously can also be continual and steady
There is secondary element and rare earth element, these elements thermogenetic effect, antibacterial dredging collateral, enhancing to absorb, improve metabolism, improve body
Immune function;Healthy water can be realized with human activin cell, enhancing blood circulation and adjustment microcirculation in human body simultaneously,
The purpose of health care.
Specific embodiment
Technical scheme is described in further detail with reference to specific embodiment, but protection scope of the present invention is not
It is confined to as described below.
Embodiment 1
A kind of preparation method of quantum potsherd:
S1. volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, monazite were crushed to 1500 mesh sieves respectively;
S2. volcanic rock, the tourmaline of 5 weight portions, the germanite of 6 weight portions, the rare earth of 24 weight portions, 3 weights of 20 weight portions are taken
The medical stone, the aluminite of 5 weight portions, the magnesium of 4 weight portions, the monazite of 10 weight portions, the magnesia of 15 weight portions of part are measured, is being stirred
Mix in device with 400 ~ 800rpm rotating speeds stirring mixing 4h, obtain compound;The magnesium is the particle of 5 ~ 10 μm of particle diameter, the oxidation
Magnesium is the particle of 1 ~ 20 μm of particle diameter;
S3. compound is put into mould, in steam ambient, pressing mold treatment 60min is at 1450 ~ 1550 DEG C, then temperature
1100 ~ 1150 DEG C are down to, steady temperature 40min, then it is cooled to 600 ~ 700 DEG C, steady temperature 30min, then natural cooling shaping, the amount of obtaining
Sub- potsherd.
Embodiment 2
A kind of preparation method of quantum potsherd:
S1. volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, monazite were crushed to 1500 mesh sieves respectively;
S2. volcanic rock, the tourmaline of 6 weight portions, the germanite of 8 weight portions, the rare earth of 20 weight portions, 4 weights of 25 weight portions are taken
The medical stone, the aluminite of 3 weight portions, the magnesium of 5 weight portions, the monazite of 12 weight portions, the magnesia of 17 weight portions of part are measured, is being stirred
Mix in device with 400 ~ 800rpm rotating speeds stirring mixing 5h, obtain compound;The magnesium is the particle of 5 ~ 10 μm of particle diameter, the oxidation
Magnesium is the particle of 1 ~ 20 μm of particle diameter;
S3. compound is put into mould, in steam ambient, pressing mold treatment 90min is at 1450 ~ 1550 DEG C, then temperature
1100 ~ 1150 DEG C are down to, steady temperature 45min, then it is cooled to 600 ~ 700 DEG C, steady temperature 30min, then natural cooling shaping, the amount of obtaining
Sub- potsherd.
Embodiment 3
A kind of preparation method of quantum potsherd:
S1. volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, monazite were crushed to 1500 mesh sieves respectively;
S2. volcanic rock, the tourmaline of 6 weight portions, the germanite of 8 weight portions, the rare earth of 22 weight portions, 5 weights of 21 weight portions are taken
The medical stone, the aluminite of 3 weight portions, the magnesium of 6 weight portions, the monazite of 11 weight portions, the magnesia of 18 weight portions of part are measured, is being stirred
Mix in device with 400 ~ 800rpm rotating speeds stirring mixing 3h, obtain compound;The magnesium is the particle of 5 ~ 10 μm of particle diameter, the oxidation
Magnesium is the particle of 1 ~ 20 μm of particle diameter;
S3. compound is put into mould, in steam ambient, pressing mold treatment 30min is at 1450 ~ 1550 DEG C, then temperature
1100 ~ 1150 DEG C are down to, steady temperature 30min, then it is cooled to 600 ~ 700 DEG C, steady temperature 20min, then natural cooling shaping, the amount of obtaining
Sub- potsherd.
Embodiment 4
A kind of preparation method of quantum potsherd:
S1. volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, monazite were crushed to 1500 mesh sieves respectively;
S2. volcanic rock, the tourmaline of 8 weight portions, the germanite of 10 weight portions, the rare earth of 21 weight portions, 6 weights of 22 weight portions are taken
The medical stone, the aluminite of 2 weight portions, the magnesium of 4.5 weight portions, the monazite of 10 weight portions, the magnesia of 19 weight portions of part are measured,
With 400 ~ 800rpm rotating speeds stirring mixing 3h in agitator, compound is obtained;The magnesium is the particle of 5 ~ 10 μm of particle diameter, the oxygen
It is the particle of 1 ~ 20 μm of particle diameter to change magnesium;
S3. compound is put into mould, in steam ambient, pressing mold treatment 30min is at 1450 ~ 1550 DEG C, then temperature
1100 ~ 1150 DEG C are down to, steady temperature 30min, then it is cooled to 600 ~ 700 DEG C, steady temperature 20min, then natural cooling shaping, the amount of obtaining
Sub- potsherd.
The above is only the preferred embodiment of the present invention, it should be understood that the present invention is not limited to described herein
Form, is not to be taken as the exclusion to other embodiment, and can be used for various other combinations, modification and environment, and can be at this
In the text contemplated scope, it is modified by the technology or knowledge of above-mentioned teaching or association area.And those skilled in the art are entered
Capable change and change does not depart from the spirit and scope of the present invention, then all should be in the protection domain of appended claims of the present invention
It is interior.
Claims (7)
1. a kind of preparation method of quantum potsherd, it is characterised in that comprise the following steps:
S1. volcanic rock, tourmaline, germanite, rare earth, medical stone, aluminite, monazite were crushed to 1500 mesh sieves respectively;
S2. volcanic rock, the tourmaline of 5-8 weight portions, the germanite of 6-10 weight portions, the 20-24 weight portions of 20-25 weight portions are taken
Rare earth, the medical stone of 3-6 weight portions, the aluminite of 2-5 weight portions, the magnesium of 4-6 weight portions, the monazite of 10-12 weight portions,
The magnesia of 15-20 weight portions, is uniformly mixed, and obtains compound;
S3. compound is put into mould, the treatment of steam pressing mold is done at 1450 ~ 1550 DEG C, cooling shaping obtains quantum ceramics
Piece.
2. the preparation method of a kind of quantum potsherd according to claim 1, it is characterised in that the magnesium is particle diameter 5 ~ 10
μm particle.
3. the preparation method of a kind of quantum potsherd according to claim 1, it is characterised in that the magnesia is particle diameter
1 ~ 20 μm of particle.
4. the preparation method of a kind of quantum potsherd according to claim 1, it is characterised in that stirred in the step S2
Mixing is carried out in agitator.
5. the preparation method of a kind of quantum potsherd according to claim 4, it is characterised in that the agitator speed is
400~800rpm。
6. a kind of preparation method of quantum potsherd according to claim 4, it is characterised in that the stirring incorporation time
It is 3 ~ 5h.
7. the preparation method of a kind of quantum potsherd according to claim 1, it is characterised in that the step S3's is specific
Step is:Compound is put into mould, in steam ambient, pressing mold treatment 30 ~ 90min, Ran Houwen is at 1450 ~ 1550 DEG C
Degree is down to 1100 ~ 1150 DEG C, steady 30 ~ 45min of temperature, then is cooled to 600 ~ 700 DEG C, surely 20 ~ 30min of temperature, then natural cooling into
Type, obtains quantum potsherd.