CN106800397A - A kind of colored ecological permeable terrace and preparation method thereof - Google Patents
A kind of colored ecological permeable terrace and preparation method thereof Download PDFInfo
- Publication number
- CN106800397A CN106800397A CN201611241043.4A CN201611241043A CN106800397A CN 106800397 A CN106800397 A CN 106800397A CN 201611241043 A CN201611241043 A CN 201611241043A CN 106800397 A CN106800397 A CN 106800397A
- Authority
- CN
- China
- Prior art keywords
- colored
- ecological permeable
- cementing agent
- haydite
- permeable terrace
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of colored ecological permeable terrace and preparation method thereof, the colored ecological permeable terrace includes the material of following weight portion：Crushed stone aggregate 30% 40%, brick grain 20% 30%, haydite 20% 30%, cementing agent 5% 10%, portland cement 10% 25%, inorganic pigment 3% 5%；Wherein, cementing agent is 5% 10% hardening agents by weight portion, 10% 15% flowables, 5% 10% stabilizers, 60% 80% fibers constitute；The colored ecological permeable terrace has the advantages that intensity is high, wearability is good, good water permeability.The preparation method is comprised the following steps that：A, stirring；B, use water-soaked roadbed；C, pave；D, rolling；E, light compacting of shaking；F, moisture-keeping maintaining, until pervious concrete layer is completely dried, colored ecological permeable terrace is prepared and completed；Designed by above-mentioned processing step, the preparation method can effectively prepare above-mentioned colored ecological permeable terrace.
Description
Technical field
The present invention relates to permeable terrace technical field, more particularly to a kind of colored ecological permeable terrace and preparation method thereof.
Background technology
Permeable terrace is increasingly subject to people's particularly industry as a kind of new environment-friendly type, ecotypic pavement material
Concern, the earth's surface of modern city is more to be covered by the building construction of armored concrete and fluid-tight road surface, with natural soil
Compare, common concrete road surface lacks breathing, absorbs heat and the ability of infiltration rainwater, brings a series of environment to ask therewith
Topic, and concrete is also therefore be considered as always the natural arch-criminal of destruction, but as long as enabling continuous gap to be formed, can just create
With the connecting points of natural environment.
Used as carrying capacity of environment reduction type concrete, permeable terrace is one for improving and recovering the earth environment for wrecking
Creative material is planted, human lives is got along amiably and peacefully with the Nature, sustainable development is gone down.
The content of the invention
It is an object of the invention to provide a kind of colored ecological permeable terrace, the colored ecological permeable terrace intensity is high, resistance to
The good, good water permeability of mill property.
Another object of the present invention is to provide a kind of preparation method of colored ecological permeable terrace, the preparation method can be effective
Ground prepares above-mentioned colored ecological permeable terrace.
To reach above-mentioned purpose, the present invention is achieved through the following technical solutions.
A kind of colored ecological permeable terrace, includes the material of following weight portion, specially：
Crushed stone aggregate 30%-40%
Brick grain 20%-30%
Haydite 20%-30%
Cementing agent 5%-10%
Portland cement 10%-25%
Inorganic pigment 3%-5%；
Wherein, cementing agent is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, hardening agent in cementing agent, flowable,
Stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：5%-10%、10%-15%、5%-10%、60%-80%；
The particle size values of crushed stone aggregate are 3mm-10mm, and the particle size values of brick grain are 5mm-15mm, and the particle size values of haydite are 10mm-
20mm。
Wherein, the material of following weight portion is included, specially：
Crushed stone aggregate 30%-35%
Brick grain 20%-25%
Haydite 20%-25%
Cementing agent 5%-10%
Portland cement 10%-20%
Inorganic pigment 3%-5%.
Wherein, the material of following weight portion is included, specially：
Crushed stone aggregate 30%
Brick grain 25%
Haydite 25%
Cementing agent 5%
Portland cement 10%
Inorganic pigment 5%.
Wherein, hardening agent, flowable, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by the cementing agent：10%、
10%、10%、70%。
A kind of preparation method of colored ecological permeable terrace, includes following processing step, specially：
A, crushed stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment are poured into forced mixer, and
Add running water toward forced mixer, start forced mixer and by forced mixer by crushed stone aggregate, brick,
Haydite, cementing agent, portland cement, inorganic pigment, originally water mixture stir；
B, use water-soaked roadbed；
C, the mixture laying that will be uniformly mixed via forced mixer form one in road bed with road bed
Pervious concrete layer；
D, by roller by the surface rolling of pervious concrete layer；
E, pervious concrete layer is carried out by plate vibrator gently shaking compacting；
F, moisture-keeping maintaining is carried out in time to pervious concrete layer surface, until pervious concrete layer is completely dried, it is colored it is ecological thoroughly
Water terrace is prepared and completed.
Wherein, colored ecological permeable terrace medium stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment
The weight portion of six kinds of materials is followed successively by：30%-40%、20%-30%、20%-30%、5%-10%、10%-25%、3%-5%.
Wherein, colored ecological permeable terrace medium stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment
The weight portion of six kinds of materials is followed successively by：30%-35%、20%-25%、20%-25%、5%-10%、10%-20%、3%-5%.
Wherein, colored ecological permeable terrace medium stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment
The weight portion of six kinds of materials is followed successively by：30%、25%、25%、5%、10%、5%.
Wherein, the cementing agent is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, strengthens in cementing agent
Agent, flowable, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：5%-10%、10%-15%、5%-10%、60%-80%.
Wherein, hardening agent, flowable, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by the cementing agent：10%、
10%、10%、70%。
Beneficial effects of the present invention are：A kind of colored ecological permeable terrace of the present invention, it includes following weight
The material of part：Crushed stone aggregate 30%-40%, brick grain 20%-30%, haydite 20%-30%, cementing agent 5%-10%, portland cement 10%-
25%th, inorganic pigment 3%-5%；Wherein, cementing agent is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, in cementing agent
Hardening agent, flowable, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：5%-10%、10%-15%、5%-10%、60%-
80%；The particle size values of crushed stone aggregate are 3mm-10mm.By above-mentioned material proportion, colored ecological permeable terrace of the invention has
Intensity is high, wearability is good, good water permeability advantage.
It is of the invention another to have the beneficial effect that：A kind of preparation method of colored ecological permeable terrace of the present invention, its
Following processing step is included, specially：A, crushed stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment are fallen
Enter into forced mixer, and toward running water is added in forced mixer, start forced mixer and by forced action type
Mixer by crushed stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment, originally water mixture stir；b、
Use water-soaked roadbed；C, the mixture laying that will be uniformly mixed via forced mixer in road bed, with roadbed
Surface forms a pervious concrete layer；D, by roller by the surface rolling of pervious concrete layer；E, by plate vibrator pair
Pervious concrete layer carries out compacting of gently shaking；F, moisture-keeping maintaining is carried out in time to pervious concrete layer surface, until pervious concrete
Layer is completely dried, and colored ecological permeable terrace is prepared and completed.Designed by above-mentioned processing step, the preparation method can be effectively
Prepare above-mentioned colored ecological permeable terrace.
Specific embodiment
With reference to specific embodiment, the present invention will be described.
A kind of embodiment one, colored ecological permeable terrace, includes the material of following weight portion, specially：
Crushed stone aggregate 30%
Brick grain 25%
Haydite 25%
Cementing agent 5%
Portland cement 10%
Inorganic pigment 5%.
Wherein, cementing agent is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, hardening agent, stream in cementing agent
Dynamic agent, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：10%、10%、10%、70%；
The particle size values of crushed stone aggregate are 3mm-10mm, and the particle size values of brick grain are 5mm-15mm, and the particle size values of haydite are 10mm-
20mm。
Need to be explained further, for the colored ecological permeable terrace of the present embodiment one, brick grain is by building waste
For fragment of brick is crushed, it is applied in colored ecological permeable terrace by by brick grain, the present embodiment one can be recycled effectively
Building waste, environment protecting is good.In addition, be applied to haydite in colored ecological permeable terrace by the present embodiment one, the inside of haydite
With cellular micropore, the haydite with micropore can further improve colored ecological permeable terrace water absorbing properties and thoroughly
Outlet capacity.So, by above-mentioned material proportion, the colored ecological permeable terrace of the present embodiment one has that intensity is high, wearability is good,
The advantage of good water permeability.
Wherein, the colored ecological permeable terrace of the present embodiment one can be prepared from using following preparation methods, specifically,
A kind of preparation method of colored ecological permeable terrace, it is characterised in that include following processing step, specially：
A, crushed stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment are poured into forced mixer, and
Add running water toward forced mixer, start forced mixer and by forced mixer by crushed stone aggregate, brick,
Haydite, cementing agent, portland cement, inorganic pigment, originally water mixture stir；
B, use water-soaked roadbed；
C, the mixture laying that will be uniformly mixed via forced mixer form one in road bed with road bed
Pervious concrete layer；
D, by roller by the surface rolling of pervious concrete layer；
E, pervious concrete layer is carried out by plate vibrator gently shaking compacting；
F, moisture-keeping maintaining is carried out in time to pervious concrete layer surface, until pervious concrete layer is completely dried, it is colored it is ecological thoroughly
Water terrace is prepared and completed.
By above-mentioned processing step, the preparation method can effectively prepare the colored ecological permeable ground of the present embodiment one
Level ground.
A kind of embodiment two, colored ecological permeable terrace, includes the material of following weight portion, specially：
Crushed stone aggregate 35%
Brick grain 20%
Haydite 20%
Cementing agent 10%
Portland cement 10%
Inorganic pigment 5%.
Wherein, cementing agent is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, hardening agent, stream in cementing agent
Dynamic agent, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：8%、12%、5%、75%；
The particle size values of crushed stone aggregate are 3mm-10mm, and the particle size values of brick grain are 5mm-15mm, and the particle size values of haydite are 10mm-
20mm。
Need to be explained further, for the colored ecological permeable terrace of the present embodiment two, brick grain is by building waste
For fragment of brick is crushed, it is applied in colored ecological permeable terrace by by brick grain, the present embodiment two can be recycled effectively
Building waste, environment protecting is good.In addition, be applied to haydite in colored ecological permeable terrace by the present embodiment two, the inside of haydite
With cellular micropore, the haydite with micropore can further improve colored ecological permeable terrace water absorbing properties and thoroughly
Outlet capacity.So, by above-mentioned material proportion, the colored ecological permeable terrace of the present embodiment two has that intensity is high, wearability is good,
The advantage of good water permeability.
Wherein, the colored ecological permeable terrace of the present embodiment two can be prepared from using following preparation methods, specifically,
A kind of preparation method of colored ecological permeable terrace, it is characterised in that include following processing step, specially：
A, crushed stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment are poured into forced mixer, and
Add running water toward forced mixer, start forced mixer and by forced mixer by crushed stone aggregate, brick,
Haydite, cementing agent, portland cement, inorganic pigment, originally water mixture stir；
B, use water-soaked roadbed；
C, the mixture laying that will be uniformly mixed via forced mixer form one in road bed with road bed
Pervious concrete layer；
D, by roller by the surface rolling of pervious concrete layer；
E, pervious concrete layer is carried out by plate vibrator gently shaking compacting；
F, moisture-keeping maintaining is carried out in time to pervious concrete layer surface, until pervious concrete layer is completely dried, it is colored it is ecological thoroughly
Water terrace is prepared and completed.
By above-mentioned processing step, the preparation method can effectively prepare the colored ecological permeable ground of the present embodiment two
Level ground.
A kind of embodiment three, colored ecological permeable terrace, includes the material of following weight portion, specially：
Crushed stone aggregate 40%
Brick grain 20%
Haydite 20%
Cementing agent 5%
Portland cement 10%
Inorganic pigment 5%.
Wherein, cementing agent is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, hardening agent, stream in cementing agent
Dynamic agent, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：5%、10%、5%、80%；
The particle size values of crushed stone aggregate are 3mm-10mm, and the particle size values of brick grain are 5mm-15mm, and the particle size values of haydite are 10mm-
20mm。
Need to be explained further, for the colored ecological permeable terrace of the present embodiment three, brick grain is by building waste
For fragment of brick is crushed, it is applied in colored ecological permeable terrace by by brick grain, the present embodiment three can be recycled effectively
Building waste, environment protecting is good.In addition, be applied to haydite in colored ecological permeable terrace by the present embodiment three, the inside of haydite
With cellular micropore, the haydite with micropore can further improve colored ecological permeable terrace water absorbing properties and thoroughly
Outlet capacity.So, by above-mentioned material proportion, the colored ecological permeable terrace of the present embodiment three has that intensity is high, wearability is good,
The advantage of good water permeability.
Wherein, the colored ecological permeable terrace of the present embodiment three can be prepared from using following preparation methods, specifically,
A kind of preparation method of colored ecological permeable terrace, it is characterised in that include following processing step, specially：
A, crushed stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment are poured into forced mixer, and
Add running water toward forced mixer, start forced mixer and by forced mixer by crushed stone aggregate, brick,
Haydite, cementing agent, portland cement, inorganic pigment, originally water mixture stir；
B, use water-soaked roadbed；
C, the mixture laying that will be uniformly mixed via forced mixer form one in road bed with road bed
Pervious concrete layer；
D, by roller by the surface rolling of pervious concrete layer；
E, pervious concrete layer is carried out by plate vibrator gently shaking compacting；
F, moisture-keeping maintaining is carried out in time to pervious concrete layer surface, until pervious concrete layer is completely dried, it is colored it is ecological thoroughly
Water terrace is prepared and completed.
By above-mentioned processing step, the preparation method can effectively prepare the colored ecological permeable ground of the present embodiment three
Level ground.
Above content is only presently preferred embodiments of the present invention, for one of ordinary skill in the art, according to of the invention
Thought, will change in specific embodiments and applications, and this specification content should not be construed as to the present invention
Limitation.
Claims (10)
1. a kind of colored ecological permeable terrace, it is characterised in that include the material of following weight portion, specially：
Crushed stone aggregate 30%-40%
Brick grain 20%-30%
Haydite 20%-30%
Cementing agent 5%-10%
Portland cement 10%-25%
Inorganic pigment 3%-5%；
Wherein, cementing agent is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, hardening agent in cementing agent, flowable,
Stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：5%-10%、10%-15%、5%-10%、60%-80%；
The particle size values of crushed stone aggregate are 3mm-10mm, and the particle size values of brick grain are 5mm-15mm, and the particle size values of haydite are 10mm-
20mm。
2. a kind of colored ecological permeable terrace according to claim 1, it is characterised in that include the thing of following weight portion
Material, specially：
Crushed stone aggregate 30%-35%
Brick grain 20%-25%
Haydite 20%-25%
Cementing agent 5%-10%
Portland cement 10%-20%
Inorganic pigment 3%-5%.
3. a kind of colored ecological permeable terrace according to claim 2, it is characterised in that include the thing of following weight portion
Material, specially：
Crushed stone aggregate 30%
Brick grain 25%
Haydite 25%
Cementing agent 5%
Portland cement 10%
Inorganic pigment 5%.
4. a kind of colored ecological permeable terrace according to claim 3, it is characterised in that：Hardening agent in the cementing agent,
Flowable, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by：10%、10%、10%、70%.
5. a kind of preparation method of colored ecological permeable terrace, it is characterised in that include following processing step, specially：
A, crushed stone aggregate, brick grain, haydite, cementing agent, portland cement, inorganic pigment are poured into forced mixer, and
Add running water toward forced mixer, start forced mixer and by forced mixer by crushed stone aggregate, brick,
Haydite, cementing agent, portland cement, inorganic pigment, originally water mixture stir；
B, use water-soaked roadbed；
C, the mixture laying that will be uniformly mixed via forced mixer form one in road bed with road bed
Pervious concrete layer；
D, by roller by the surface rolling of pervious concrete layer；
E, pervious concrete layer is carried out by plate vibrator gently shaking compacting；
F, moisture-keeping maintaining is carried out in time to pervious concrete layer surface, until pervious concrete layer is completely dried, it is colored it is ecological thoroughly
Water terrace is prepared and completed.
6. the preparation method of a kind of colored ecological permeable terrace according to claim 4, it is characterised in that：It is colored ecological saturating
Water terrace medium stone aggregate, brick grain, haydite, cementing agent, portland cement, the weight portion of six kinds of materials of inorganic pigment are followed successively by：
30%-40%、20%-30%、20%-30%、5%-10%、10%-25%、3%-5%。
7. the preparation method of a kind of colored ecological permeable terrace according to claim 5, it is characterised in that：It is colored ecological saturating
Water terrace medium stone aggregate, brick grain, haydite, cementing agent, portland cement, the weight portion of six kinds of materials of inorganic pigment are followed successively by：
30%-35%、20%-25%、20%-25%、5%-10%、10%-20%、3%-5%。
8. the preparation method of a kind of colored ecological permeable terrace according to claim 6, it is characterised in that：It is colored ecological saturating
Water terrace medium stone aggregate, brick grain, haydite, cementing agent, portland cement, the weight portion of six kinds of materials of inorganic pigment are followed successively by：
30%、25%、25%、5%、10%、5%。
9. the preparation method of a kind of colored ecological permeable terrace according to claim 7, it is characterised in that：The cementing agent
It is made up of hardening agent, flowable, stabilizer, four kinds of materials of fiber, hardening agent, flowable, stabilizer, four kinds of fiber in cementing agent
The weight portion of material is followed successively by：5%-10%、10%-15%、5%-10%、60%-80%.
10. the preparation method of a kind of colored ecological permeable terrace according to claim 8, it is characterised in that：It is described cementing
Hardening agent, flowable, stabilizer, the weight portion of four kinds of materials of fiber are followed successively by agent：10%、10%、10%、70%.