CN106758506B - A kind of freeze proof maceration extract of corrugated case waterproof and its preparation and application - Google Patents
A kind of freeze proof maceration extract of corrugated case waterproof and its preparation and application Download PDFInfo
- Publication number
- CN106758506B CN106758506B CN201611132263.3A CN201611132263A CN106758506B CN 106758506 B CN106758506 B CN 106758506B CN 201611132263 A CN201611132263 A CN 201611132263A CN 106758506 B CN106758506 B CN 106758506B
- Authority
- CN
- China
- Prior art keywords
- maceration extract
- corrugated case
- waterproof
- freeze proof
- ethylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of freeze proof maceration extract of corrugated case waterproof, its raw material composition and its weight part ratio include: dipping solution 50~70, ethylene-propylene diene copolymer EPDM 10~15, ethylene-vinyl acetate copolymer EVA 10~15, thermoplastic acrylic resin 3~5, coupling agent 0.5~0.8, nano grade titanium white powder 3~5, jute staple fiber 8~10, when preparation, each raw material is mixed at 100~110 DEG C, when use, first corrugated board is impregnated in the maceration extract, then successively carries out hot baking, cooling.The design not only improves the waterproof, cryogenic property and mechanical strength of corrugated case, and method is simple, economical.
Description
Technical field
The invention belongs to polymeric material fields, and in particular to a kind of freeze proof maceration extract of corrugated case waterproof and its preparation
And application method, suitable for improving the cryogenic property and mechanical strength of corrugated case.
Background technique
Currently, with the generally raising of living standards of the people, frozen food is generally seen under the advocating of nutrition new concept
Good, consumption figure is increasing, and freezing (hiding) food feature convenient, fast with its, hygienic becomes very popular in recent years
Commodity.Frozen food is easy to maintain simultaneously, easy storage, long fresh-keeping period, full of nutrition, delicious flavour various features are allowed to depth and are consumed
Person's likes.Make a general survey of entire frozen food market, dairy products, fruit juice, cold drink, meat consumption figure have and significantly promoted.Freezing
The main still corrugated case of the current packed and transported material of food, but in corrugated case packaging industry, there is water suction and softens, becomes in carton
Shape phenomenon, or after being subjected to fat migration, flat crushing strength, the side pressure strength of corrugated board reduce particularly evident, seriously affect packaging
Quality using effect, there are quality problems.In addition, carton is carrying out the storage of cold chain food low-temperature, refrigeration transportation, it is desirable that in tide
Still have in wet, low temperature circulation environment and continues high compressive strength requirement.In cold operation industry, especially quick-frozen food is relevant cold
With transportation art, frozen food storage temperature should be at -18 DEG C hereinafter, cold store temperature fluctuation is no more than ± 2 DEG C of limit values, fortune for hiding
Temperature fluctuation during defeated is no more than 3 DEG C of limit values, and product handling or disengaging freezer are rapid, tight during loading and unloading goods
Lattice control operating environment temperature and time, guarantee that food temperature is not higher than -12 DEG C, the freezing food in retail link refrigerated display case
Product temperature degree should be maintained at -15 DEG C hereinafter, short time temperature recovery should not be higher than -12 DEG C.Above-mentioned condition requires that packing case is necessary
With biggish compression strength and also want with higher moisture-proof and waterproof ability, if carton pull out water degree it is not high enough if,
Water can be seeped into body paper, thus be easy to the compressive resistance and stiffness of corrugated case to destroy, corrugated case will lose
His safeguard function causes protected food that rotten rot occurs.The corrugated case used on the market at present will appear mostly
Anti-freezing property and the bad problem of mechanical strength.
Summary of the invention
The purpose of the present invention is overcoming the problems, such as that anti-freezing property of the existing technology and intensity are bad, providing a kind of can have
Effect improves the freeze proof maceration extract of waterproof and its preparation and application of the cryogenic property and mechanical strength of corrugated case.
In order to achieve the above object, the present invention provides following technical schemes:
A kind of freeze proof maceration extract of corrugated case waterproof, raw material composition and its weight part ratio include: dipping solution 50~
70, ethylene-propylene diene copolymer EPDM 10~15, ethylene-vinyl acetate copolymer EVA 10~15, thermoplastic acrylic resin 3~
5, coupling agent 0.5~0.8, reinforcing agent 11~15.
The reinforcing agent includes nano grade titanium white powder, jute staple fiber, the weight of the meter level titanium dioxide and jute staple fiber
Amount part is compared for 3~5:8~10.
The dipping solution be paraffin oil, the thermoplastic acrylic resin by n-BMA monomer polymerization and
At the coupling agent is vinyl front three oxosilane.
A kind of preparation method of the freeze proof maceration extract of corrugated case waterproof, should the preparation method comprises the following steps: by each raw material in 100~
3~5min is mixed in required ratio at 110 DEG C.
A kind of application method of the freeze proof maceration extract of corrugated case waterproof, the application method are as follows: prior at 100~110 DEG C
Corrugated board is placed in the maceration extract 5~10s of dipping, then will complete the corrugated board after dipping at 110~130 DEG C into
Row heat is dried, and finally cools down 20min or more at room temperature.
Compared with prior art, the invention has the benefit that
1, a kind of raw material composition of freeze proof maceration extract of corrugated case waterproof of the present invention and its weight part ratio include: that dipping is molten
Body 50~70, ethylene-propylene diene copolymer EPDM 10~15, ethylene-vinyl acetate copolymer EVA 10~15, thermoplastic acrylic tree
Rouge 3~5, coupling agent 0.5~0.8, reinforcing agent 11~16, the silylation in the maceration extract is acrylic resin modified and active group
It can be cured and react with the isocyanate groups of carton surface, solidify maceration extract rapidly, form firm enhancing waterproof membrane,
The ethylene-propylene diene copolymer and ethylene-vinyl acetate copolymer that the design uses low temperature flexibility good simultaneously are as modifying agent, not only
The waterproof performance of carton is enhanced, and ensure that carton is also able to maintain the complete of waterproof membrane under subzero 18 DEG C or lower temperature
Whole performance.Therefore, the present invention has good waterproof and cryogenic property.
2, reinforcing agent uses nano grade titanium white powder and jute in a kind of freeze proof maceration extract of corrugated case waterproof of the present invention
Staple fiber, the addition of nano grade titanium white powder can not only increase waterproof film strength, anti-aging property and finish, and can protect
The uniformity of dipping process is demonstrate,proved, on the one hand jute staple fiber has good waterproof and dampproof performance, another party at low ambient temperatures
Face is remarkably improved the pop strength and bearing strength of corrugated case.Therefore, the present invention is being obviously improved corrugated case machinery by force
Waterproof and dampproof performance is further improved while spending.
3, a kind of application method of the freeze proof maceration extract of corrugated case waterproof of the present invention need to only be produced in original corrugated case
The dipping and heat for increasing corrugated board on the basis of line dry technique, simple, convenient, economical and practical.Therefore, the present invention makes
It is simple, economical with method.
Specific embodiment
The invention will be further described With reference to embodiment.
A kind of freeze proof maceration extract of corrugated case waterproof, raw material composition and its weight part ratio include: dipping solution 50~
70, ethylene-propylene diene copolymer EPDM 10~15, ethylene-vinyl acetate copolymer EVA 10~15, thermoplastic acrylic resin 3~
5, coupling agent 0.5~0.8, reinforcing agent 11~15.
The reinforcing agent includes nano grade titanium white powder, jute staple fiber, the weight of the meter level titanium dioxide and jute staple fiber
Amount part is compared for 3~5:8~10.
The dipping solution be paraffin oil, the thermoplastic acrylic resin by n-BMA monomer polymerization and
At the coupling agent is vinyl front three oxosilane.
A kind of preparation method of the freeze proof maceration extract of corrugated case waterproof, should the preparation method comprises the following steps: by each raw material in 100~
3~5min is mixed in required ratio at 110 DEG C.
A kind of application method of the freeze proof maceration extract of corrugated case waterproof, the application method are as follows: prior at 100~110 DEG C
Corrugated board is placed in the maceration extract 5~10s of dipping, then will complete the corrugated board after dipping at 110~130 DEG C into
Row heat is dried, and finally cools down 20min or more at room temperature.
The principle of the present invention is described as follows:
The invention proposes a kind of maceration extract for corrugated case, the maceration extract and corrugated case can directly be formed compared with
Strong chemical bond forms firm enhancing protective layer in corrugated case surface cure rapidly, even if so that corruggted wrapping case is long
Phase is in cryogenic freezing environment, its intensity will not be substantially reduced in soaking conditions in water, and non-volatile object pollutes, and can be used for cold
Freeze the packing and storing of product under transport product packaging, low temperature and moisture environment, it is also possible to ship live fish, marine product and water content pole
High class I goods.In addition, the maceration extract is clear, colorless thick liquid, it is impregnated in the color of back cardboard on corrugated board not
It can change, therefore not influence the overall appearances such as the pattern of body paper case, decorative pattern.
Impregnate solution: paraffin oil can reduce the viscosity of solution, enable jute staple fiber more as dipping solution after heating
It is uniform impregnated, meanwhile, paraffin also has waterproof, moisture-proof role, asepsis environment-protecting.
Thermoplastic acrylic resin: being polymerized by monomer methacrylic acid N-butyl, is had good elastic and higher
Gluing.
Modifying agent: ethylene-propylene diene copolymer, ethylene-vinyl acetate copolymer are the good modified material of low temperature flexibility, the two
The flexibility of waterproof membrane can be enhanced, increase waterproof film strength, be destroyed cardboard waterproof membrane in folding process not, increase simultaneously
The waterproof performance of strong waterproof membrane.In addition, also having using ethylene-vinyl acetate copolymer as waterproof membrane made from modifying agent molten
The advantages that melt-viscosity is low, cohesive force is high, cold resistance is high, but its softening point, hardness and strength are relatively low, and therefore, the present invention will
Ethylene-vinyl acetate copolymer is shared with ethylene-propylene diene copolymer, to make up above-mentioned deficiency.
Nanometer titanium dioxide: being a kind of non-toxic and tasteless free of contamination inorganic matter for unformed white powder.Its surface molecular shape
Three-dimensional netted structure is presented in state, can form network structure when waterproof membrane is dry after addition, dramatically increase waterproof film strength;
The ultraviolet radiation absorption effect for increasing cardboard, to improve the weatherability of cardboard, scratch resistant;Significantly improve the ageing resistance of waterproof membrane
Energy, finish;Guarantee fiber impregnation more evenly.In addition, it also has sterilization, the mould proof of corrugated case can be met
Performance requirement.
Jute staple fiber: the present invention uses very environmentally friendly jute staple fiber, and not only intensity is high, and length generally exists
400~900 μm, which is more suitable for impregnating.
Heat is dried: the solidification that can accelerate maceration extract using heat baking in application method of the present invention is qualitative, makes the smooth circle of paperboard surface
Whole, dipping is uniform.
Each raw material of the present invention are described as follows:
Paraffin oil: No. 10 paraffin oils, it is commercially available.
Ethylene-propylene diene copolymer: modified grain, Dow production, model 4725P are commercially available.
Ethylene-vinyl acetate copolymer: modified grain, model 2806, VA%=28, melt index 6g/10min.
Thermoplastic acrylic resin: modified resin, bead polymer.
Vinyl front three oxosilane: colourless transparent liquid, model A171 are commercially available.
Jute staple fiber: length 1mm, 20~30 μm of diameter.
Nano grade titanium white powder: white powder, rutile-type, average grain diameter≤100nm are commercially available.
Embodiment 1:
A kind of freeze proof maceration extract of corrugated case waterproof, raw material composition and its weight part ratio include: paraffin oil 50, ternary
The third glue of second EPDM 10, ethylene-vinyl acetate copolymer EVA 10, thermoplastic acrylic resin 3, vinyl front three oxosilane
0.5, nano grade titanium white powder 3, jute staple fiber 8, wherein the thermoplastic acrylic resin is by n-BMA monomer
It is polymerized.
The above-mentioned freeze proof maceration extract of corrugated case waterproof impregnates the preparation method comprises the following steps: above-mentioned raw materials are added in required ratio
In in slot, and 5min is mixed at 100 DEG C.
The application method of the above-mentioned freeze proof maceration extract of corrugated case waterproof are as follows: first with automatic paper feeding trigger by corrugated board
It is sent into the dipping tank equipped with 100 DEG C of maceration extracts and impregnates 10s, then the corrugated board after the dipping taken out out of dipping tank, and remove
More maceration extracts are removed, hot air chamber is then sent to, it is mobile with the speed of 10m/min at 110 DEG C, further permeate maceration extract
To inside cardboard, and extra maceration extract is made to flow away, finally cools down the corrugated board removed from hot air chamber at room temperature
20min.
Embodiment 2:
Step with embodiment 1, the difference is that:
The raw material of the freeze proof maceration extract of corrugated case waterproof forms and its weight part ratio are as follows: paraffin oil 70, ternary second
Third glue EPDM 15, ethylene-vinyl acetate copolymer EVA 15, thermoplastic acrylic resin 5, vinyl front three oxosilane
0.8, nano grade titanium white powder 5, jute staple fiber 10.
In the preparation method of the freeze proof maceration extract of corrugated case waterproof, mixing temperature is 110 DEG C, and incorporation time is
3min。
In the application method of the freeze proof maceration extract of corrugated case waterproof, the temperature of maceration extract is 110 DEG C, dip time
For 5s, the indoor temperature of hot wind is 130 DEG C, and the movement speed of corrugated board is 15m/min, cooling time 30min.
Embodiment 3:
Step with embodiment 1, the difference is that:
The raw material of the freeze proof maceration extract of corrugated case waterproof forms and its weight part ratio are as follows: paraffin oil 60, ternary second
Third glue EPDM 12.5, ethylene-vinyl acetate copolymer EVA 12.5, thermoplastic acrylic resin 4, vinyl trimethoxy silicon
Alkane 0.75, nano grade titanium white powder 4, jute staple fiber 9.
Now performance indicator detection will be carried out using corrugated case made from above-described embodiment application method, detection data is such as
Under:
1, cryogenic property detects
Test condition: corrugated case is placed in -18 ± 2 DEG C of freezer 7 days, is placed at room temperature after taking-up 1 hour.
Test result: pop strength: 1530Kpa, Punctured Strength: 36J, side pressure strength: 8300N/m, fantasy bearing strength:
5603N。
2, water-resistant capacity detects
Test condition: corrugated case is impregnated into 1 hour (corrugated case present position in the tap water for submerge 20 ± 2 DEG C
From the water surface at least 30mm).
Pop strength: >=1150Kpa
Punctured Strength: >=22.5J
Side pressure strength: >=5650N/m
Fantasy bearing strength: >=3750N.
Claims (4)
1. a kind of freeze proof maceration extract of corrugated case waterproof, it is characterised in that:
The raw material of the maceration extract form and its weight part ratio include: dipping solution 50~70, ethylene-propylene diene copolymer EPDM 10~
15, ethylene-vinyl acetate copolymer EVA 10~15, thermoplastic acrylic resin 3~5, coupling agent 0.5~0.8, enhancing
Agent 11~15, wherein the dipping solution is paraffin oil, and the thermoplastic acrylic resin is by n-BMA monomer
It is polymerized, the coupling agent is vinyl front three oxosilane.
2. a kind of freeze proof maceration extract of corrugated case waterproof according to claim 1, it is characterised in that: the reinforcing agent packet
Include nano grade titanium white powder, jute staple fiber, the weight part ratio of the nano grade titanium white powder and jute staple fiber be 3~5:8~
10。
3. a kind of preparation method of the freeze proof maceration extract of corrugated case waterproof described in claim 1, it is characterised in that:
The preparation method is that: 3~5min is mixed in required ratio at 100~110 DEG C in each raw material.
4. a kind of application method of the freeze proof maceration extract of corrugated case waterproof as claimed in claim 3, it is characterised in that:
The application method are as follows: corrugated board is placed in 5~10s of dipping in the maceration extract at prior to 100~110 DEG C, then will
Corrugated board after completing dipping carries out hot baking at 110~130 DEG C, finally cools down 20min or more at room temperature.