CN106757470A - Polypropylene filament yarn based on composite antibacterial master batch - Google Patents
Polypropylene filament yarn based on composite antibacterial master batch Download PDFInfo
- Publication number
- CN106757470A CN106757470A CN201611122968.7A CN201611122968A CN106757470A CN 106757470 A CN106757470 A CN 106757470A CN 201611122968 A CN201611122968 A CN 201611122968A CN 106757470 A CN106757470 A CN 106757470A
- Authority
- CN
- China
- Prior art keywords
- nano
- filament yarn
- polypropylene
- polypropylene filament
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of polypropylene filament yarn based on composite antibacterial master batch, it is equipped by the following raw material by its mass percent：Polypropylene 85 is to 91wt%, Nano Silver 3 to 6wt%, nano cuprous oxide 3 to 6wt%, nano zine oxide 1 to 5wt%, zinc stearate 1 to 3wt%；Using the polypropylene filament yarn based on composite antibacterial master batch of above-mentioned technical proposal; it can using cooperatively by Nano Silver, nano cuprous oxide, nano zine oxide and zinc stearate; so that polypropylene filament yarn can realize good antibacterial characteristics in actual use, and then so that the medical instruments or clothes clothing that are prepared using the polypropylene filament yarn in the application can be improved for the protecting effect of user in actual use.
Description
Technical field
The present invention relates to textile processing field, especially a kind of polypropylene filament yarn based on composite antibacterial master batch.
Background technology
Polypropylene filament yarn is one of common textile material of field of textiles.It is easy that existing polypropylene filament yarn can apply to bacterium often
Under the environment of aggregation, in above-mentioned environment, conventional polypropylene filament yarn product easily attaches bacterium, and then causes polypropylene filament yarn
It is difficult to be played a good protection for user in actual use.
The content of the invention
The technical problem to be solved in the present invention is to provide a kind of polypropylene filament yarn, its spinning that may be such that polypropylene filament yarn and shaping
Fabric has good anti-microbial property, is played a good protection with for user.
In order to solve the above technical problems, the present invention relates to a kind of polypropylene filament yarn based on composite antibacterial master batch, it is by as follows
Raw material is equipped by its mass percent：Polypropylene 85 to 91wt%, Nano Silver 3 to 6wt%, nano cuprous oxide 3 to
6wt%, nano zine oxide 1 to 5wt%, zinc stearate 1 to 3wt%.
Used as a modification of the present invention, the polypropylene filament yarn based on composite antibacterial master batch is using the preparation of following technique
Into：
1) polypropylene, Nano Silver, nano cuprous oxide, nano zine oxide, zinc stearate are mixed by its mass percent
Close, drying and processing is carried out after it is well mixed；
2) by step 1）Middle mixed material carries out extrusion process by screw extruder, and expressing technique temperature is 190 to 220 DEG C,
And the material after extrusion is passed through in spinneret is extruded to form silk stream；
3) for step 2）In obtain a stream carry out receive silk treatment to form polypropylene filament yarn.
As a modification of the present invention, the step 1）In, Nano Silver, nano cuprous oxide, nano zine oxide press it
After mass percent is mixed, Nano Silver, nano cuprous oxide, nano zine oxide are entered under 50 to 80 DEG C of temperature environment
Row milled processed, and the mixture after grinding is mixed with polypropylene and zinc stearate by its mass percent.
Using the polypropylene filament yarn based on composite antibacterial master batch of above-mentioned technical proposal, it can be by Nano Silver, nano oxidized
Cuprous, nano zine oxide and zinc stearate are used cooperatively so that polypropylene filament yarn can be realized well in actual use
Antibacterial characteristics, and then cause that the medical instruments that are prepared using the polypropylene filament yarn in the application or clothes clothing are actually made
Can be improved for the protecting effect of user during.
Specific embodiment
With reference to specific embodiment, the present invention is furture elucidated, it should be understood that following specific embodiments are only used for
The bright present invention rather than limitation the scope of the present invention.
Embodiment 1
A kind of polypropylene filament yarn based on composite antibacterial master batch, it is equipped by the following raw material by its mass percent：Polypropylene
90wt%, Nano Silver 3wt%, nano cuprous oxide 3wt%, nano zine oxide 2wt%, zinc stearate 2wt%.
Used as a modification of the present invention, the polypropylene filament yarn based on composite antibacterial master batch is using the preparation of following technique
Into：
1) polypropylene, Nano Silver, nano cuprous oxide, nano zine oxide, zinc stearate are mixed by its mass percent
Close, drying and processing is carried out after it is well mixed；
2) by step 1）Middle mixed material carries out extrusion process by screw extruder, and expressing technique temperature is 190 DEG C, and will
Material after extrusion is passed through in spinneret and is extruded to form silk stream；
3) for step 2）In obtain a stream carry out receive silk treatment to form polypropylene filament yarn.
As a modification of the present invention, the step 1）In, Nano Silver, nano cuprous oxide, nano zine oxide press it
After mass percent is mixed, Nano Silver, nano cuprous oxide, nano zine oxide are ground under 55 DEG C of temperature environment
Mill treatment, and the mixture after grinding is mixed with polypropylene and zinc stearate by its mass percent.
Using the polypropylene filament yarn based on composite antibacterial master batch of above-mentioned technical proposal, it can be by Nano Silver, nano oxidized
Cuprous, nano zine oxide and zinc stearate are used cooperatively so that polypropylene filament yarn can be realized well in actual use
Antibacterial characteristics, and then cause that the medical instruments that are prepared using the polypropylene filament yarn in the application or clothes clothing are actually made
Can be improved for the protecting effect of user during.
Embodiment 2
A kind of polypropylene filament yarn based on composite antibacterial master batch, it is equipped by the following raw material by its mass percent：Polypropylene
85wt%, Nano Silver 5wt%, nano cuprous oxide 6wt%, nano zine oxide 1wt%, zinc stearate 3wt%.
Used as a modification of the present invention, the polypropylene filament yarn based on composite antibacterial master batch is using the preparation of following technique
Into：
1) polypropylene, Nano Silver, nano cuprous oxide, nano zine oxide, zinc stearate are mixed by its mass percent
Close, drying and processing is carried out after it is well mixed；
2) by step 1）Middle mixed material carries out extrusion process by screw extruder, and expressing technique temperature is 212 DEG C, and will
Material after extrusion is passed through in spinneret and is extruded to form silk stream；
3) for step 2）In obtain a stream carry out receive silk treatment to form polypropylene filament yarn.
As a modification of the present invention, the step 1）In, Nano Silver, nano cuprous oxide, nano zine oxide press it
After mass percent is mixed, Nano Silver, nano cuprous oxide, nano zine oxide are ground under 76 DEG C of temperature environment
Mill treatment, and the mixture after grinding is mixed with polypropylene and zinc stearate by its mass percent.
Remaining feature of the present embodiment is same as Example 1 with advantage.
Embodiment 3
A kind of polypropylene filament yarn based on composite antibacterial master batch, it is equipped by the following raw material by its mass percent：Polypropylene
87wt%, Nano Silver 4wt%, nano cuprous oxide 4wt%, nano zine oxide 3wt%, zinc stearate 2wt%.
Used as a modification of the present invention, the polypropylene filament yarn based on composite antibacterial master batch is using the preparation of following technique
Into：
1) polypropylene, Nano Silver, nano cuprous oxide, nano zine oxide, zinc stearate are mixed by its mass percent
Close, drying and processing is carried out after it is well mixed；
2) by step 1）Middle mixed material carries out extrusion process by screw extruder, and expressing technique temperature is 205 DEG C, and will
Material after extrusion is passed through in spinneret and is extruded to form silk stream；
3) for step 2）In obtain a stream carry out receive silk treatment to form polypropylene filament yarn.
As a modification of the present invention, the step 1）In, Nano Silver, nano cuprous oxide, nano zine oxide press it
After mass percent is mixed, Nano Silver, nano cuprous oxide, nano zine oxide are ground under 65 DEG C of temperature environment
Mill treatment, and the mixture after grinding is mixed with polypropylene and zinc stearate by its mass percent.
Remaining feature of the present embodiment is same as Example 1 with advantage.
Claims (3)
1. a kind of polypropylene filament yarn based on composite antibacterial master batch, it is characterised in that the polypropylene fibre based on composite antibacterial master batch is long
Silk is equipped by the following raw material by its mass percent：Polypropylene 85 is to 91wt%, Nano Silver 3 to 6wt%, nano oxidized Asia
Copper 3 is to 6wt%, nano zine oxide 1 to 5wt%, zinc stearate 1 to 3wt%.
2. according to the polypropylene filament yarn based on composite antibacterial master batch described in claim 2, it is characterised in that described based on compound anti-
The polypropylene filament yarn of starter grain is prepared from using following technique：
Polypropylene, Nano Silver, nano cuprous oxide, nano zine oxide, zinc stearate are mixed by its mass percent, is treated
Drying and processing is carried out after it is well mixed；
By step 1）Middle mixed material carries out extrusion process by screw extruder, and expressing technique temperature is 190 to 220 DEG C, and
Material after extrusion is passed through in spinneret and is extruded to form silk stream；
For step 2）In obtain a stream carry out receive silk treatment to form polypropylene filament yarn.
3. according to the polypropylene filament yarn based on composite antibacterial master batch described in claim 2, it is characterised in that the step 1）In,
After Nano Silver, nano cuprous oxide, nano zine oxide are mixed by its mass percent, under 50 to 80 DEG C of temperature environment
It is ground treatment to Nano Silver, nano cuprous oxide, nano zine oxide, and by the mixture after grinding and polypropylene and hard
Resin acid zinc is mixed by its mass percent.