CN106753050A - 水溶性环保喷胶 - Google Patents
水溶性环保喷胶 Download PDFInfo
- Publication number
- CN106753050A CN106753050A CN201710018105.3A CN201710018105A CN106753050A CN 106753050 A CN106753050 A CN 106753050A CN 201710018105 A CN201710018105 A CN 201710018105A CN 106753050 A CN106753050 A CN 106753050A
- Authority
- CN
- China
- Prior art keywords
- water
- glue spraying
- emulsion
- polyurethane
- protective glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水溶性环保喷胶,按照重量百分比的原料包括:聚氨酯系弹性体7~10%,水性氯丁胶乳18~23%,水性丙烯酸乳液15~20%,乙烯‑醋酸乙烯共聚物乳液12~15%,十二烷基苯磺酸钠1~4%,丁二烯苯乙烯溴化共聚物6~11%,水性乳化剂1~3%,改性松香乳液6~12%,聚氨酯缔合型增稠剂2~6%,PH调整剂1~2%,水性消泡剂0.1~0.7%,去离子水8~15%。无需加热活化,环保无毒,粘接力强,干燥速度快,胶膜韧性好,防冻,阻燃,安全性好。
Description
技术领域
本发明属于环保胶粘剂领域,具体涉及一种水溶性环保喷胶。
背景技术
喷胶是一种具有适合粘度,将两种不同的物质界面紧密连接起来,起到传递应用作用的胶粘剂,广泛用于家具,皮革和装饰行业。目前,市面上的喷胶主要以溶剂型喷胶(油性喷胶)为主。市场上销售的喷胶均含有三苯(苯、甲苯、二甲苯)类有毒或者高毒性溶剂,在产品使用过程中都会不同程度地造成工人中毒,而且严重污染环境,如甲苯和氯化溶剂,这些有机溶剂进入空气,严重影响了人们的生活环境,损害人们身体健康。另外,溶剂型喷胶也存在易燃易爆的问题,频频引发火灾。因此,世界各国竞相研究用水溶剂替代有机溶剂的环保型水性喷胶。在德国,美国和日本等发达国家,推出了水性聚氨酯喷胶和水性氯丁喷胶。其中,水性聚氨酯喷胶需要加热活化后才能使用,但是,喷胶行业一般都采取冷粘,因此,限制了水性聚氨酯喷胶的使用。
发明内容
本发明目的是提供一种水溶性环保喷胶,无需加热活化,环保无毒,粘接力强,干燥速度快,胶膜韧性好,防冻,阻燃,安全性好。
为了实现以上目的,本发明采用的技术方案为:一种水溶性环保喷胶,按照重量百分比的原料包括:聚氨酯系弹性体7~10%,水性氯丁胶乳18~23%,水性丙烯酸乳液15~20%,乙烯-醋酸乙烯共聚物乳液12~15%,十二烷基苯磺酸钠1~4%,丁二烯苯乙烯溴化共聚物6~11%,水性乳化剂1~3%,改性松香乳液6~12%,聚氨酯缔合型增稠剂2~6%,PH 调整剂1~2%,水性消泡剂0.1~0.7%,去离子水8~15%。
优选的,所述的水溶性环保喷胶,按照重量百分比的原料包括:聚氨酯系弹性体9%,水性氯丁胶乳20%,水性丙烯酸乳液18%,乙烯-醋酸乙烯共聚物乳液13%,十二烷基苯磺酸钠3%,丁二烯苯乙烯溴化共聚物9%,水性乳化剂2%,改性松香乳液9%,聚氨酯缔合型增稠剂5%,PH 调整剂1.5%,水性消泡剂0.5%,去离子水10%。
进一步的,所述的聚氨酯系弹性体为聚醚型聚氨酯系弹性体。
本发明的技术效果在于:按照上述材料配比得到的喷胶环保无毒、一粘即合、雾而不化,粘贴后的产品耐低温-20℃,耐高温90℃,耐火极限达到30min,安全性好。其中,聚氨酯系弹性体是由二苯甲烷二异氰酸酯(MDI)、甲苯二异氰酸酯(TDI)和大分子多元醇、扩链剂共同反应聚合而成的高分子材料,具备强度高、韧性好、耐磨、耐寒、耐油、耐水、耐老化、耐气候的特性,聚氨酯系弹性体中聚醚型聚氨酯系弹性体的抗水解性能强,保证胶水的质量;丁二烯苯乙烯溴化共聚物虽然含卤素,但是其属于环保的高分子聚合物阻燃剂,大分子不容易生物累积,对健康环保有利,在喷胶中应用,不会迁移析出,不会水解降解,耐老化耐水性能优异。
具体实施方式
下面将结合本发明实施例,对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例,都属于本发明保护的范围。
实施例1:一种水溶性环保喷胶,按照重量百分比的原料包括:聚氨酯系弹性体9%,水性氯丁胶乳20%,水性丙烯酸乳液18%,乙烯-醋酸乙烯共聚物乳液13%,十二烷基苯磺酸钠3%,丁二烯苯乙烯溴化共聚物9%,水性乳化剂2%,改性松香乳液9%,聚氨酯缔合型增稠剂5%,PH 调整剂1.5%,水性消泡剂0.5%,去离子水10%。
进一步的,所述的聚氨酯系弹性体为聚醚型聚氨酯系弹性体。
按照上述材料配比得到的喷胶环保无毒、一粘即合、雾而不化,粘贴后的产品耐低温-20℃,耐高温90℃,耐火极限为33min,安全性好。
实施例2:一种水溶性环保喷胶,按照重量百分比的原料包括:聚氨酯系弹性体8%,水性氯丁胶乳20%,水性丙烯酸乳液17%,乙烯-醋酸乙烯共聚物乳液13%,十二烷基苯磺酸钠3%,丁二烯苯乙烯溴化共聚物10%,水性乳化剂2%,改性松香乳液10%,聚氨酯缔合型增稠剂5%,PH 调整剂1.5%,水性消泡剂0.5%,去离子水10%。
进一步的,所述的聚氨酯系弹性体为聚醚型聚氨酯系弹性体。
按照上述材料配比得到的喷胶环保无毒、一粘即合、雾而不化,粘贴后的产品耐低温-20℃,耐高温90℃,耐火极限达到30min,安全性好。
实施例3:一种水溶性环保喷胶,按照重量百分比的原料包括:聚氨酯系弹性体10%,水性氯丁胶乳19%,水性丙烯酸乳液18%,乙烯-醋酸乙烯共聚物乳液13%,十二烷基苯磺酸钠3%,丁二烯苯乙烯溴化共聚物11%,水性乳化剂2%,改性松香乳液9%,聚氨酯缔合型增稠剂5%,PH 调整剂1.5%,水性消泡剂0.5%,去离子水8%。
进一步的,所述的聚氨酯系弹性体为聚醚型聚氨酯系弹性体。
按照上述材料配比得到的喷胶环保无毒、一粘即合、雾而不化,粘贴后的产品耐低温-20℃,耐高温90℃,耐火极限达到30min,安全性好。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。
Claims (3)
1.一种水溶性环保喷胶,其特征在于,按照重量百分比的原料包括:聚氨酯系弹性体7~10%,水性氯丁胶乳18~23%,水性丙烯酸乳液15~20%,乙烯-醋酸乙烯共聚物乳液12~15%,十二烷基苯磺酸钠1~4%,丁二烯苯乙烯溴化共聚物6~11%,水性乳化剂1~3%,改性松香乳液6~12%,聚氨酯缔合型增稠剂2~6%,PH 调整剂1~2%,水性消泡剂0.1~0.7%,去离子水8~15%。
2.根据权利要求1所述的水溶性环保喷胶,其特征在于,按照重量百分比的原料包括:聚氨酯系弹性体9%,水性氯丁胶乳20%,水性丙烯酸乳液18%,乙烯-醋酸乙烯共聚物乳液13%,十二烷基苯磺酸钠3%,丁二烯苯乙烯溴化共聚物9%,水性乳化剂2%,改性松香乳液9%,聚氨酯缔合型增稠剂5%,PH 调整剂1.5%,水性消泡剂0.5%,去离子水10%。
3.根据权利要求1或2所述的水溶性环保喷胶,其特征在于,所述的聚氨酯系弹性体为聚醚型聚氨酯系弹性体。