CN106752127A - A kind of building coating with air purification function and its preparation method and application - Google Patents
A kind of building coating with air purification function and its preparation method and application Download PDFInfo
- Publication number
- CN106752127A CN106752127A CN201611035015.7A CN201611035015A CN106752127A CN 106752127 A CN106752127 A CN 106752127A CN 201611035015 A CN201611035015 A CN 201611035015A CN 106752127 A CN106752127 A CN 106752127A
- Authority
- CN
- China
- Prior art keywords
- parts
- mixture
- building coating
- illite
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of building coating with air purification function and its preparation method and application, the building coating is made up of the following raw material according to weight portion:41 49 parts of illite, 6 14 parts of methyl α-naphthyl acetate, 3 11 parts of activated carbon, 22 30 parts of 1,2 propane diols, 8 16 parts of only angle gold.Illite is crushed, the treatment of naphthalene acid solution heating stirring is added, mixture A is obtained;By activated carbon, 1,2 propane diols, the gold mixing heated sealed stirring of only angle are obtained mixture B;Mixture A and mixture B Hybrid Heatings are stirred, adds that deionized water is ultrasonically treated, be down to room temperature obtains final product.Obtained building coating of the invention, can not only remove formaldehyde and peculiar smell, improve air quality, but also the effect with anion releasing, purify air, it is reusable, to people's nonhazardous, non-corrosiveness, stable performance, preparation method is simple to operate, environment friendly and pollution-free, is easy to industrialized production.
Description
Technical field
The present invention relates to building material technical field, specifically a kind of building coating and its system with air purification function
Preparation Method and application.
Background technology
There is different degrees of VOC emission after existing interior decoration, the health of serious threat people.As society is sent out
Exhibition, economic progress, people more focus on the features such as health, comfortableness, the feature of environmental protection, the aesthetic property of house decorative material.
Illite is a kind of common clay mineral, and the mother's ﹑ potassium feldspar weathering of Chang Youbai clouds is formed, and is originated in argillaceous rocks,
Or formed by other mineral alterations.It is often the middle transition mineral to form other clay minerals.Illite is the one of China
Plant new mineral.Domestic initially to find Erie's stone ore in ferryboat head village of agger township, Antu, Jilin Province illite resource is enriched very much,
Resource reserve is verified more than 1.4 hundred million tons, prospective reserves surpasses 200,000,000 tons, belonged to single super-huge chiltern illite mineral deposit.
Illite has rich potassium, high alumina, low iron and superior chemistry, the physical property such as smooth, bright, fine and smooth, heat-resisting.She
Sharp stone can free anion releasing and far infrared.Many researchs have shown that there is pole by the illite processed in the world in recent years
Strong fungistatic effect, and can the various harmful heavy metals of absorption and pernicious gas.But illite is and it in the prior art
Its various raw material complex role with identical effect, single illite is adsorbed with toxic gas DeGrain, existing
Technology is to its complex disposal process, high cost, it is impossible to meet needs.
The content of the invention
It is an object of the invention to provide a kind of removing formaldehyde and peculiar smell, anion releasing, with air purification function
Building coating and its preparation method and application, to solve the problems, such as to be proposed in above-mentioned background technology.
To achieve the above object, the present invention provides following technical scheme:
A kind of building coating with air purification function, is made up of the following raw material according to weight portion:Illite 41-49
Part, methyl α-naphthyl acetate 6-14 parts, activated carbon 3-11 parts, 22-30 parts of 1,2- propane diols, 8-16 parts of only angle gold.
As further scheme of the invention:The building coating with air purification function, by following according to weight
The raw material composition of part:Illite 43-47 parts, methyl α-naphthyl acetate 8-12 parts, activated carbon 5-9 parts, 24-28 parts of 1,2- propane diols, only angle gold
10-14 parts.
As further scheme of the invention:The building coating with air purification function, by following according to weight
The raw material composition of part:45 parts of illite, 10 parts of methyl α-naphthyl acetate, 7 parts of activated carbon, 26 parts of 1,2- propane diols, 12 parts of only angle gold.
Another object of the present invention is to provide a kind of preparation method of the building coating with air purification function, by following step
Rapid composition:
1) 30% ethanol of 11.5 times of methyl α-naphthyl acetate and its quality is mixed, naphthalene acid solution is obtained;By illite crushing, mistake
100 mesh sieves, add naphthalene acid solution, insert in reactor and the stir process 1.3h at a temperature of 92 DEG C, and mixture A is obtained;
2) by activated carbon, 1,2-PD, the gold mixing of only angle, stir process 40-45min is sealed at a temperature of 67 DEG C,
Mixture B is obtained;
3) mixture A is mixed with mixture B, then in 200 DEG C of stir process 1.5h, then adds illite quality
2.8 times of deionized water, is heated to 86 DEG C and at such a temperature ultrasonically treated 48min, and ultrasonic power is 900W, is being down to room temperature
Obtain final product building coating.
Another object of the present invention is to provide application of the building coating in air-treatment.
Compared with prior art, the beneficial effects of the invention are as follows:
The present invention illite is processed using methyl α-naphthyl acetate, then with activated carbon, 1,2-PD, only angle metallographic interaction
Obtained building coating, can not only remove formaldehyde and peculiar smell, improve air quality, but also empty with anion releasing, purification
The effect of gas.Coating of the invention is not lost, i.e. reusable after used coating is calcined again, does not result in and builds
Building refuse.The present invention is to people's nonhazardous, non-corrosiveness, stable performance, with high absorption adhesion, energy quick adsorption purification
Formaldehyde, gas with foreign flavor in air, though it is quick in the case where visible ray or light are very weak, efficiently, enduringly eliminate first
Aldehyde, gas with foreign flavor, purification efficiency are higher, and purifying formaldehyde efficiency reaches 87-96%, and toluene purification efficiency reaches 58-68%, purification
Effect persistence is higher, and purifying formaldehyde effect persistence reaches 82-92%, and toluene clean-up effect persistence reaches 46-56%.This
Invention green health is pollution-free, can discharge anion in air, and anion average increase is 80-108/cm3, pure and fresh sky
Gas.Preparation method of the present invention is simple to operate, environment friendly and pollution-free, is easy to industrialized production.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, a kind of building coating with air purification function, by the following raw material according to weight portion
Composition:41 parts of illite, 6 parts of methyl α-naphthyl acetate, 3 parts of activated carbon, 22 parts of 1,2- propane diols, 8 parts of only angle gold.
11.5 times of 30% ethanol of methyl α-naphthyl acetate and its quality is mixed, naphthalene acid solution is obtained;By illite crushing, mistake
100 mesh sieves, add naphthalene acid solution, insert in reactor and the stir process 1.3h at a temperature of 92 DEG C, and mixture A is obtained.
By activated carbon, 1,2-PD, the gold mixing of only angle, stir process 40min is sealed at a temperature of 67 DEG C, mixture B is obtained.Will
Mixture A mixes with mixture B, then in 200 DEG C of stir process 1.5h, then add 2.8 times of illite quality go from
Sub- water, is heated to 86 DEG C and at such a temperature ultrasonically treated 48min, and ultrasonic power is 900W, and building painting is obtained final product room temperature is down to
Material.
Embodiment 2
In the embodiment of the present invention, a kind of building coating with air purification function, by the following raw material according to weight portion
Composition:49 parts of illite, 14 parts of methyl α-naphthyl acetate, 11 parts of activated carbon, 30 parts of 1,2- propane diols, 16 parts of only angle gold.
11.5 times of 30% ethanol of methyl α-naphthyl acetate and its quality is mixed, naphthalene acid solution is obtained;By illite crushing, mistake
100 mesh sieves, add naphthalene acid solution, insert in reactor and the stir process 1.3h at a temperature of 92 DEG C, and mixture A is obtained.
By activated carbon, 1,2-PD, the gold mixing of only angle, stir process 45min is sealed at a temperature of 67 DEG C, mixture B is obtained.Will
Mixture A mixes with mixture B, then in 200 DEG C of stir process 1.5h, then add 2.8 times of illite quality go from
Sub- water, is heated to 86 DEG C and at such a temperature ultrasonically treated 48min, and ultrasonic power is 900W, and building painting is obtained final product room temperature is down to
Material.
Embodiment 3
In the embodiment of the present invention, a kind of building coating with air purification function, by the following raw material according to weight portion
Composition:43 parts of illite, 8 parts of methyl α-naphthyl acetate, 5 parts of activated carbon, 24 parts of 1,2- propane diols, 10 parts of only angle gold.
11.5 times of 30% ethanol of methyl α-naphthyl acetate and its quality is mixed, naphthalene acid solution is obtained;By illite crushing, mistake
100 mesh sieves, add naphthalene acid solution, insert in reactor and the stir process 1.3h at a temperature of 92 DEG C, and mixture A is obtained.
By activated carbon, 1,2-PD, the gold mixing of only angle, stir process 42min is sealed at a temperature of 67 DEG C, mixture B is obtained.Will
Mixture A mixes with mixture B, then in 200 DEG C of stir process 1.5h, then add 2.8 times of illite quality go from
Sub- water, is heated to 86 DEG C and at such a temperature ultrasonically treated 48min, and ultrasonic power is 900W, and building painting is obtained final product room temperature is down to
Material.
Embodiment 4
In the embodiment of the present invention, a kind of building coating with air purification function, by the following raw material according to weight portion
Composition:47 parts of illite, 12 parts of methyl α-naphthyl acetate, 9 parts of activated carbon, 28 parts of 1,2- propane diols, 14 parts of only angle gold.
11.5 times of 30% ethanol of methyl α-naphthyl acetate and its quality is mixed, naphthalene acid solution is obtained;By illite crushing, mistake
100 mesh sieves, add naphthalene acid solution, insert in reactor and the stir process 1.3h at a temperature of 92 DEG C, and mixture A is obtained.
By activated carbon, 1,2-PD, the gold mixing of only angle, stir process 42min is sealed at a temperature of 67 DEG C, mixture B is obtained.Will
Mixture A mixes with mixture B, then in 200 DEG C of stir process 1.5h, then add 2.8 times of illite quality go from
Sub- water, is heated to 86 DEG C and at such a temperature ultrasonically treated 48min, and ultrasonic power is 900W, and building painting is obtained final product room temperature is down to
Material.
Embodiment 5
In the embodiment of the present invention, a kind of building coating with air purification function, by the following raw material according to weight portion
Composition:45 parts of illite, 10 parts of methyl α-naphthyl acetate, 7 parts of activated carbon, 26 parts of 1,2- propane diols, 12 parts of only angle gold.
11.5 times of 30% ethanol of methyl α-naphthyl acetate and its quality is mixed, naphthalene acid solution is obtained;By illite crushing, mistake
100 mesh sieves, add naphthalene acid solution, insert in reactor and the stir process 1.3h at a temperature of 92 DEG C, and mixture A is obtained.
By activated carbon, 1,2-PD, the gold mixing of only angle, stir process 42min is sealed at a temperature of 67 DEG C, mixture B is obtained.Will
Mixture A mixes with mixture B, then in 200 DEG C of stir process 1.5h, then add 2.8 times of illite quality go from
Sub- water, is heated to 86 DEG C and at such a temperature ultrasonically treated 48min, and ultrasonic power is 900W, and building painting is obtained final product room temperature is down to
Material.
Comparative example 1
In addition to methyl α-naphthyl acetate is not contained, its material content and preparation process are consistent with embodiment 5.
Comparative example 2
In addition to only angle gold is not contained, its material content and preparation process are consistent with embodiment 5.
Comparative example 3
In addition to methyl α-naphthyl acetate and only angle gold is not contained, its material content and preparation process are consistent with embodiment 5.
Embodiment 6
The coating of embodiment 1-5 and comparative example 1-3 is respectively used on certain new indoor wall built up, interior is then carried out
Formaldehyde in air, peculiar smell material carry out formaldehyde, the detection of toluene purification efficiency and formaldehyde, the detection of toluene clean-up effect persistence
(commission national building materials industrial technology supervision research center), detection establishing criteria JC/T 1074-2008《Indoor air cleaning
Change function coating material purifying property》.
Experimental condition:Sample size 200g, temperature (20 ± 2) DEG C, relative humidity (50 ± 10) %, lighting time:48h.Inspection
Survey result as shown in table 1.
Table 1
From data in table 1, building coating of the invention is under the interaction of each raw material to formaldehyde in air, peculiar smell
Material purifying formaldehyde efficiency, purifying formaldehyde effect persistence, toluene purification efficiency, the testing result of toluene clean-up effect persistence
Meet standard JC/T 1074-2008《Function of purifying indoor air coating material purifying property》In " I classes material " technical indicator
It is required that.
Coating to embodiment 1-5 and comparative example 1-3 carries out anion-generating capacity detection (commission Building wood to room air
Material industrial environment inspection center), detection establishing criteria JC/T 1016-2006《The method of testing of material anion-generating capacity》.Survey
Method for testing is that 100g samples are positioned over into 0.25m3Closed bin in, closed 24h produces negative aeroion tester (Air with the U.S.
Ion Counter).Testing result is as shown in table 2.Testing conditions:T=25 DEG C of temperature, relative humidity RH=60%;Detection time
Number:16 times.
Table 2
From data in table 2, building coating of the invention averagely increases under the interaction of each raw material to anion
Dosage is >=80/cm3。
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be in other specific forms realized.Therefore, no matter
From the point of view of which point, embodiment all should be regarded as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires to be limited rather than described above, it is intended that all in the implication and scope of the equivalency of claim by falling
Change is included in the present invention.
Moreover, it will be appreciated that although the present specification is described in terms of embodiments, not each implementation method is only wrapped
Containing an independent technical scheme, this narrating mode of specification is only that for clarity, those skilled in the art should
Specification an as entirety, the technical scheme in each embodiment can also be formed into those skilled in the art through appropriately combined
May be appreciated other embodiment.
Claims (5)
1. a kind of building coating with air purification function, it is characterised in that be made up of the following raw material according to weight portion:She
Sharp stone 41-49 parts, methyl α-naphthyl acetate 6-14 parts, activated carbon 3-11 parts, 22-30 parts of 1,2- propane diols, 8-16 parts of only angle gold.
2. the building coating with air purification function according to claim 1, it is characterised in that by following according to weight
The raw material composition of part:Illite 43-47 parts, methyl α-naphthyl acetate 8-12 parts, activated carbon 5-9 parts, 24-28 parts of 1,2- propane diols, only angle gold
10-14 parts.
3. the building coating with air purification function according to claim 1, it is characterised in that by following according to weight
The raw material composition of part:45 parts of illite, 10 parts of methyl α-naphthyl acetate, 7 parts of activated carbon, 26 parts of 1,2- propane diols, 12 parts of only angle gold.
4. a kind of preparation method of building coating with air purification function as described in claim 1-3 is any, its feature
It is to comprise the steps of:
1) 30% ethanol of 11.5 times of methyl α-naphthyl acetate and its quality is mixed, naphthalene acid solution is obtained;Illite is crushed, 100 are crossed
Mesh sieve, adds naphthalene acid solution, inserts in reactor and the stir process 1.3h at a temperature of 92 DEG C, and mixture A is obtained;
2) by activated carbon, 1,2-PD, the gold mixing of only angle, stir process 40-45min is sealed at a temperature of 67 DEG C, is obtained
Mixture B;
3) mixture A is mixed with mixture B, then in 200 DEG C of stir process 1.5h, then adds illite quality 2.8
Deionized water again, is heated to 86 DEG C and at such a temperature ultrasonically treated 48min, and ultrasonic power is 900W, is being down to room temperature i.e.
Obtain building coating.
5. application of the building coating as described in claim 1-3 is any in air-treatment.