CN106752014A - Stalk/weaving dead meal/plastic waste composite coining product and its manufacture method - Google Patents
Stalk/weaving dead meal/plastic waste composite coining product and its manufacture method Download PDFInfo
- Publication number
- CN106752014A CN106752014A CN201710022260.2A CN201710022260A CN106752014A CN 106752014 A CN106752014 A CN 106752014A CN 201710022260 A CN201710022260 A CN 201710022260A CN 106752014 A CN106752014 A CN 106752014A
- Authority
- CN
- China
- Prior art keywords
- plastic waste
- stalk
- dead meal
- weaving
- weaving dead
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of stalk/weaving dead meal/plastic waste composite coining product and its manufacture method, the composite coining product is fabricated by by stalk, weaving dead meal, plastic waste, isocyanate adhesive molding, and specific manufacture method is as follows：First, the form according to stalk is processed to stalk, obtains irregular crushed straw aggregate, dries to moisture content and is down to less than 15%；2nd, weaving dead meal is processed into irregular fragment, dries to moisture content and be down to less than 15%；3rd, plastic waste is processed into irregular fragment, dries to moisture content and be down to less than 15%；4th, enter glue mixer after mixing dried crushed straw aggregate, weaving dead meal and plastic waste in proportion, apply isocyanate adhesive, mat formation in a mold, send into hot press hot pressing compression molding.Raw materials for production of the present invention belong to twice laid, have greatly saved cost of goods manufactured, improve added value of product, while it also avoid the stacking and burning of discarded object, protect environment.
Description
Technical field
The present invention relates to a kind of composite coining product and its manufacture method.
Background technology
Stalk is the general name of ripe crops cauline leaf (fringe) part, belongs to string class.China as large agricultural country, often
Year can generate more than 700,000,000 tons of stalk.The utilization technology of current stalk mainly includes：Mechanized Straw also field, excessively abdomen also field, cultivation food
With bacterium, Biogas, as the raw material of industry, for modes such as biomass power generations.Stalk contains substantial amounts of cellulose, is alternative
The valuable renewable resource of timber.It is difficult gluing technique, adhesive price currently with the difficult point of stalk manufacture wood-based plate
Height, early investment is big etc..
Weaving dead meal is from the leftover bits of garment enterprise, and the species included in this kind of discarded object is more, such as acrylic fibers,
Terylene, linen-cotton etc., the mixture of often several fibers, ratio do not know, random composition.The recovery profit of current waste textile
With physiochemical mutagens, chemical recovery and energy regenerating can be divided into.Physiochemical mutagens refer to using mechanical means decomposition or crush textile, lead to
Classification, purification, drying, reprocessing treatment are crossed, the production of fabric is reused for；But classification is difficult, technical requirements are high, and pre-treatment should
It is many with equipment, high cost.Chemical recovery is to allow high molecular polymer depolymerization to decompose by chemical method to regroup, but technique is multiple
It is miscellaneous, and to add chemical solvent.Energy regenerating is, by burning generation heat, for thermal power generation, but environment to be produced dirty
Dye.
Plastic waste could be rotted for 500~1000 years, and landfill is easily polluted to soil and water quality, and burning can have been produced
Evil gas, pollutes to air.The purposes of current recycled plastic is used to produce regenerated plastics, but product quality is poor, property
It is unstable, easily become fragile, it is only used for the production of low grade products.
Above-mentioned three kinds of raw materials belong to mutually immiscible material in chemistry, and surface nature has obvious difference, therefore
There is larger difficulty in compound aspect, relevant report is had no at present.
The content of the invention
It is an object of the invention to provide a kind of stalk/weaving dead meal/plastic waste composite coining product and its manufacturer
Method, makes full use of weaving leftover bits, plastic waste that stalk and garment enterprise are produced as primary raw material, imposes isocyanates
Adhesive, forms the stalk with characteristic of environmental protection/weaving discarded object/plastic waste composite coining product, has both reduced to wood
Material demand, prevents pollution problem of these raw materials to environment again.
The purpose of the present invention is achieved through the following technical solutions：
A kind of stalk/weaving dead meal/plastic waste composite coining product, by stalk, weaving dead meal, plastic waste,
Isocyanate adhesive molding is fabricated by, wherein：The mass ratio of stalk, weaving dead meal and plastic waste is 20~90：10
~40：10~40, the applied amount of isocyanate adhesive for over dry material (stalk+weaving dead meal+plastic waste) quality 1~
6%.
A kind of manufacture method of above-mentioned wood particulate/weaving dead meal/plastic waste composite coining product, including following step
Suddenly：
First, the form according to stalk is processed to stalk, obtains irregular crushed straw aggregate, dries to moisture content drop
To less than 15%；
2nd, weaving dead meal is processed into irregular fragment, dries to moisture content and be down to less than 15%；
3rd, plastic waste is processed into irregular fragment, dries to moisture content and be down to less than 15%；
4th, enter glue mixer after mixing dried crushed straw aggregate, weaving dead meal and plastic waste in proportion, apply
Isocyanate adhesive, mats formation in a mold, sends into hot press hot pressing compression molding, controls hot pressing temperature for 160~200 DEG C,
Unit pressure is 4.0~7.0MPa, and the dwell time is 15~30 seconds/mm.
In the present invention, the weaving dead meal can be discarded weaving face fabric cotton, fiber crops, polyamide fibre, acrylic fibers, spandex, terylene, glutinous
The mixture of one or more compositions in glue fiber, acetate fiber, but it is not limited to these compositions.
In the present invention, the plastic waste is the mixture of one or more compositions in PE, PP, PET.
In the present invention, the adhesive be isocyanate adhesive or Urea-formaldehyde resin adhesive, wherein：Isocyanates is gluing
The applied amount of agent is the 1~6% of over dry material (wood particulate+weaving dead meal+plastic waste) quality, Urea-formaldehyde resin adhesive
Applied amount is the 8~15% of over dry material (wood particulate+weaving dead meal+plastic waste) quality.
In the present invention, the size of the composite coining product is：Length × width x thickness=(500~2440) mm × (500~
1220) mm × (8~180) mm.
In the present invention, the length of the irregular crushed straw aggregate is 1~20mm, width be 0.5~7mm, thickness be 0.2~
2mm。
In the present invention, the area of the weaving irregular fragment of dead meal is 100~400mm2。
In the present invention, the area of the irregular fragment of plastic waste is 100~400mm2。
The invention has the advantages that：
(1) raw materials for production belong to twice laid, and the purchase cost of stalk, weaving discarded object and plastic waste is extremely low, not even
Purchase cost is needed, cost of goods manufactured has greatly been saved, added value of product is improved, while it also avoid the stacking of discarded object
And burning, protect environment.
(2) stalk fibre is instead of to a certain extent using textile fabric, save the raw material output-input ratio of stalk, and
Increased the toughness of composite coining product.
(3) addition of plastic waste can a certain degree of consumption for reducing adhesive.
(4) the characteristics of composite coining product produced by the present invention has light weight, intensity high, low cost, without formaldehyde, ring
Protect and have concurrently certain water resistance and anti-flammability.
(5) the composite coining product properties is excellent, and without formaldehyde, MOR and elastic modelling quantity can meet use requirement,
Water resistance is good, dimensionally stable, and production cost is relatively low, widely used.Different according to material rate, finished product can be widely used for building
Build, interior decoration, the field such as transport.
Brief description of the drawings
Fig. 1 is the manufacturing process flow diagram of wood particulate/weaving dead meal/plastic waste composite coining product.
Specific embodiment
Technical scheme is further described with reference to embodiment, but is not limited thereto, it is every right
Technical solution of the present invention is modified or equivalent, without deviating from the spirit and scope of technical solution of the present invention, all should be contained
Cover in protection scope of the present invention.
Embodiment 1：
In the present embodiment, stalk/weaving dead meal/plastic waste composite coining product is by stalk, weaving dead meal, plastics
Waste material, isocyanate adhesive molding are fabricated by, wherein：The mass ratio of stalk, weaving dead meal and plastic waste is 80：
10：10, the applied amount of isocyanate adhesive is the 1~6% of over dry material (stalk+weaving dead meal+plastic waste) quality.Such as
Shown in Fig. 1, specific manufacture method is as follows：
First, the form according to stalk is processed to raw material, forms length for 2~5mm, width are that 1~3mm, thickness are
The irregular particle of 0.5~1mm；Into wet feed feed bin, treatment is dried, dries to moisture content and be down to less than 15%；
2nd, weaving dead meal is carried out into machinery to smash, is processed into area for 100~200mm2Irregular fragment；Into
Wet feed feed bin, is dried treatment, dries to moisture content and is down to less than 15%；
3rd, it is 100~200mm the method that plastic waste uses chopping or smashes to be processed into area2Irregular fragment；
Into wet feed feed bin, treatment is dried, dries to moisture content and be down to less than 15%；
4th, siccative feed bin is entered after mixing dried crushed straw aggregate, weaving dead meal and plastic waste in proportion；
5th, according to product needed, discharging in proportion enters glue mixer, applies adhesive, mats formation in a mold, sends into hot pressing
Machine hot pressing compression molding, it is 180 DEG C to control hot pressing temperature, and unit pressure is 5.5MPa, and the dwell time is 18 seconds/mm, forms tool
There is the composite coining product of certain geometrical shape.
In the present embodiment, composite coining product properties is excellent, and MOR 25MPa, elastic modelling quantity is 4500MPa, interior knot
It is that 4.5%, 24h thickness swelling rates are 14.5% to close intensity 0.84MPa, 2h thickness swelling rate.
In the present embodiment, the size of the composite coining product is：Length × width x thickness=1200mm × 1000mm × 15mm.
In the present embodiment, the weaving dead meal is discarded weaving face fabric cotton, fiber crops, polyamide fibre, acrylic fibers, spandex, terylene, viscose
The mixture of one or more compositions in fiber, acetate fiber, accounting 10%, you can obtain good toughening effect.
In the present embodiment, the plastic waste is the mixture of one or more compositions in PE, PP, PET, and accounting does not surpass
Cross 10%, you can in the consumption of reduction adhesive to a certain degree, and increase the intensity of pressing.
In the present embodiment, the isocyanate adhesive is purchased from Wanhua Chemical Group Co., Ltd..Add in applying glue
Enter a certain amount of solvent (not higher than 10%), on the one hand reduce the cost of adhesive, on the other hand improve dividing for isocyanates
Property is dissipated, is more uniformly distributed glue spraying, improve product quality.
Embodiment 2：
The present embodiment is with the difference of embodiment 1 yes：The mass ratio of stalk, weaving dead meal and plastic waste is 50：20：
30, the applied amount of isocyanate adhesive is the 4% of over dry material (stalk+weaving dead meal+plastic waste) quality.Properties of product
It is as follows：MOR is 17MPa, and elastic modelling quantity is 3200MPa, and internal bond strength is 0.58MPa, and 2h thickness swelling rates are
4.0%, 24h thickness swelling rate are 9.8%.
Embodiment 3：
The present embodiment is with the difference of embodiment 1 yes：The mass ratio of stalk, weaving dead meal and plastic waste is 50：30：
20, the applied amount of isocyanate adhesive is the 4% of over dry material (stalk+weaving dead meal+plastic waste) quality.MOR
18MPa, elastic modelling quantity is 2200MPa, and internal bond strength 0.58MPa, 2h thickness swelling rate are 1.9%, 24h water sucting thickness
Expansion rate is 6.2%.
Embodiment 4：
The present embodiment is with the difference of embodiment 1 yes：The mass ratio of stalk, weaving dead meal and plastic waste is 20：40：
40, the applied amount of isocyanate adhesive is the 3% of over dry material (stalk+weaving dead meal+plastic waste) quality.Properties of product
It is as follows：MOR is 15MPa, and elastic modelling quantity is 1800MPa, and internal bond strength is 0.54MPa, and 2h thickness swelling rates are
3.6%, 24h thickness swelling rate are 8.3%.
Embodiment 5：
The present embodiment is with the difference of embodiment 1~4 yes：The adhesive is Urea-formaldehyde resin adhesive, and its applied amount is exhausted
The 10% of siccative quality.
Claims (8)
1. a kind of stalk/weaving dead meal/plastic waste composite coining product, it is characterised in that the composite coining product is by straw
Stalk, weaving dead meal, plastic waste, isocyanate adhesive molding are fabricated by, wherein：Stalk, weaving dead meal and plastics
The mass ratio of waste material is 20~90：10~40：10~:40, the applied amount of isocyanate adhesive is stalk, weaving dead meal and
The 1~6% of plastic waste absolute dry mass.
2. stalk according to claim 1/weaving dead meal/plastic waste composite coining product, it is characterised in that described
The size of composite coining product is：Length × width x thickness=(500~2440) mm × (500~1220) mm × (8~180) mm.
3. stalk according to claim 1/weaving dead meal/plastic waste composite coining product, it is characterised in that described
Weaving dead meal be one kind in discarded weaving face fabric cotton, fiber crops, polyamide fibre, acrylic fibers, spandex, terylene, viscose fiber, acetate fiber or
The mixture of several compositions.
4. stalk according to claim 1/weaving dead meal/plastic waste composite coining product, it is characterised in that described
Plastic waste is the mixture of one or more compositions in PE, PP, PET.
5. the wood particulate described in a kind of claim 1-4 any claims/weaving dead meal/plastic waste compound die compacting
The manufacture method of product, it is characterised in that methods described step is as follows：
First, the form according to stalk is processed to stalk, obtains irregular crushed straw aggregate, dries to moisture content and is down to
Less than 15%；
2nd, weaving dead meal is processed into irregular fragment, dries to moisture content and be down to less than 15%；
3rd, plastic waste is processed into irregular fragment, dries to moisture content and be down to less than 15%；
4th, enter glue mixer after mixing dried crushed straw aggregate, weaving dead meal and plastic waste in proportion, apply isocyanide
Acid esters adhesive, mats formation in a mold, sends into hot press hot pressing compression molding, and it is 160~200 DEG C, unit to control hot pressing temperature
Pressure is 4.0~7.0MPa, and the dwell time is 15~30 seconds/mm.
6. the manufacture method of stalk according to claim 5/weaving dead meal/plastic waste composite coining product, it is special
Levy in being the step one, the length of irregular crushed straw aggregate is 1~20mm, width be 0.5~7mm, thickness be 0.2~
2mm。
7. the manufacture method of stalk according to claim 5/weaving dead meal/plastic waste composite coining product, it is special
Levy in being the step 2, the area of irregular fragment is 100~400mm2。
8. the manufacture method of stalk according to claim 5/weaving dead meal/plastic waste composite coining product, it is special
Levy in being the step 3, the area of irregular fragment is 100~400mm2。