CN106751276A - One kind inhales ripple bionic composite material and preparation method - Google Patents
One kind inhales ripple bionic composite material and preparation method Download PDFInfo
- Publication number
- CN106751276A CN106751276A CN201611212445.1A CN201611212445A CN106751276A CN 106751276 A CN106751276 A CN 106751276A CN 201611212445 A CN201611212445 A CN 201611212445A CN 106751276 A CN106751276 A CN 106751276A
- Authority
- CN
- China
- Prior art keywords
- parts
- composite material
- biomimetic
- ripple
- bionic composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Ripple bionic composite material and preparation method are inhaled the invention discloses one kind, ripple bionic composite material is inhaled to be made up of organic biomimetic material and absorbing material, organic biomimetic material is planted on absorbing material with careless pencil, and organic biomimetic material includes that the component of following weight portion is made:Polyvinyl alcohol water soluble polymer is 18 parts;17 parts of metal chloride;26 parts of coloring agent;Crosslinking agent is 29 parts;Catalyst is 56 parts.Suction ripple bionic composite material simulating plant outward appearance, spectral reflectance and absorbing radar wave characteristic have the purpose of infrared, light spectrum image-forming camouflage, forest land background visual camouflage and radar invisible concurrently so as to reach.
Description
Technical field
The invention belongs to technical field of polymer materials, and in particular to one kind inhales ripple bionic composite material and preparation method,
Inhale ripple bionic composite material simulating plant outward appearance, spectral reflectance and absorbing radar wave characteristic so as to reach have concurrently infrared, spectrum into
As the purpose of camouflage, forest land background visual camouflage and radar invisible.
Background technology
With the development of modern science and technology, influence of the electromagenetic wave radiation to environment increasingly increases.Airport, machine flight because
Electromagnetic Interference cannot take off and overdue;The normal work of various electronic instrument for diagnosing and curing diseases devices can be often disturbed in hospital, mobile phone.Cause
This, administers electromagnetic pollution, finds a kind of material that can be kept out and weaken electromagenetic wave radiation --- absorbing material, it has also become material supply section
The big problem learned.So-called absorbing material, refers to the class material that can absorb the electromagnetic wave energy for projecting its surface.Should in engineering
Use, in addition to requiring absorbing material and there is absorptivity high to electromagnetic wave in broad frequency band, also require that it has light weight, resistance to
The performance such as temperature, moisture-proof, anticorrosive.
Referring to Chinese publication CN102087081A(Publication date is on June 8th, 2011), specifically disclosing one kind has
The stealthy pedaline of wave energy, including careless silk, careless base fabric and gum layer are inhaled, the careless silk is fixed on the careless base fabric, described
Gum layer is coated on the back side of the careless base fabric, and absorbing material is present in the careless silk, careless base fabric or gum layer, can absorb
Electromagenetic wave radiation, can be used in military affairs or wartime anti-radar detection, play military airfield, military limp base, shell storing place,
The stealthy effect in land for military use on a large scale such as underground civil defense engineering.But, above-mentioned pedaline only has absorbing radar wave and reaches thunder
Up to the absorbing material of stealthy purpose, without the material and processing method that have radar, visible ray and infrared stealth performance concurrently, with very big
Limitation.
The content of the invention
For the limitation in existing field, the present invention devises a kind of radar, visible ray and infrared stealth performance of having concurrently
Inhale ripple bionic composite material and preparation method thereof.
To achieve the above object, the present invention uses following technical proposals:
One kind inhales ripple bionic composite material, it is characterised in that inhale ripple bionic composite material by organic biomimetic material and absorbing material
Composition, biomimetic material is planted on absorbing material with careless pencil, and machine biomimetic material is made up of the component of following weight portion:Polyethylene
Alcohol-soluble and water-soluble macromolecule is 1-8 parts;Metal chloride 1-7 parts;Coloring agent 2-6 parts;Crosslinking agent is 2-9 parts;Catalyst is 5-6
Part.
Further, the metal chloride refers to the stronger inorganic salts of hygroscopicity.
Further, the inorganic salts are lithium chloride or calcium chloride.
Further, the crosslinking agent is L MALIC ACID or edible apple vinegar.
Further, the catalyst is acetic acid.
Further, the coloring agent is that chrome oxide green or careless silk are yellow.
A kind of processing method for inhaling ripple bionic composite material, comprises the following steps:
(1)Each component raw material is weighed by weight, by 1-8 parts of polyvinyl alcohol water soluble polymer addition 250mL deionized water
Dissolving, is made poly-vinyl alcohol solution;
(2)1-7 parts of metal chloride, 2-9 parts of crosslinking agent, 5-6 parts of catalyst, 2-6 parts of coloring agent are dissolved in above-mentioned polyvinyl alcohol
In solution, under conditions of being 60-90 DEG C in temperature, by cross-linking reaction 5-6 hours, casting solution is made;
(3)By step(2)In casting solution take out, be placed in baking oven be heated to 80-100 DEG C, 1-1.5h promote polyvinyl alcohol to hand over
Connection will be laid on customization plate after vacuumizing and defoaming again;
(4)Customization plate is placed in climatic chamber and is heated, 40 DEG C of temperature, humidity 45%, heat time 16h obtain sheet organic
Biomimetic material;
(5)By above-mentioned steps(4)The obtained organic biomimetic material of sheet is cut into thread organic biomimetic material using chopping equipment;
(6)Thread organic biomimetic material is bundled into careless beam with 5-10 roots;
(7)Absorbing material is fixed in automatically dropping glue equipment using frock, after careless beam is planted on absorbing material;
(8)Absorbing material and biomimetic material are combined using automatically dropping glue equipment, obtain inhaling ripple bionic composite material.
Further, the step(5)In thread organic biomimetic material width be 1mm.
Further, the step(3)In, casting solution vacuumizing and defoaming is specifically included:By casting solution be placed in bottle,suction or
After being vacuumized in vacuum drying oven, sealing and standing at room temperature is placed in, the time is 18-24h.
The present invention has the following advantages that compared with prior art:
The effect of the crosslinking agent and catalyst that are added in biomimetic material is that both promote polyvinyl alcohol to crosslink reaction jointly.Oxygen
It is bottle green pigment to change chrome green, it is ensured that organic biomimetic material has similar color and spectral reflection characteristic to plant leaf blade.
Metal chloride is that with hygroscopic, in organic biomimetic material adding metal chloride can ensure that composite can be inhaled
It is wet, can adapt to adverse circumstances.Casting solution is to prevent the water loss in casting solution by sealing and standing process.All materials
There is spectral reflectance performance after material fusion, infrared and neighbouring infrared spectrum can be reflected.
Suction ripple bionic composite material prepared by the present invention is carried out into chemical characterization, from Fig. 3-4 as can be seen that prepared by the present invention
Suction ripple bionic composite material compared with RAC16 type absorbing materials, absorbing radar wave characteristic is substantially suitable, illustrates the suction ripple material
After material is compound with biomimetic material, biomimetic material does not have influence substantially on the absorption Radar Objective Characteristics of absorbing material, so as to reach radar
Stealthy effect.Fig. 5-6 is the degree of closeness contrast of biomimetic material and plant, as can be seen from the figure biomimetic material of the invention
It is similar with common plant blade, can simulating plant outward appearance, meanwhile, the biomimetic material has spectral reflection characteristic, reach it is infrared,
Light spectrum image-forming camouflage, forest land background visual camouflage.
Organic biomimetic material in the present invention, can simultaneously realize that the transpiration and spectral reflectance of simulating plant are special
Property.Absorbing material has the characteristic for absorbing radar.Organic biomimetic material and absorbing material are combined into composite, so that this is compound
Material ensure that suction ripple bionic composite material simulating plant outward appearance, spectral reflectance and absorbing radar wave characteristic have concurrently so as to reach
The effect of infrared, light spectrum image-forming camouflage, forest land background visual camouflage and radar invisible.
Brief description of the drawings
Fig. 1 is the structural representation of absorbing material in the present invention.
Fig. 2 is to inhale ripple bionic composite material recombination process to be intended to.
Fig. 3 is to inhale ripple bionic composite material high frequency reflectance test curve.
Fig. 4 is to inhale ripple bionic composite material bass reflex rate test curve.
Fig. 5 is the infrared spectrum emissivity of biomimetic material and Folium Ginkgo.
Fig. 6 is the solar spectrum reflectivity of plant leaf blade and biomimetic material.
Specific embodiment
Following embodiments are further illustrating as the explaination to the technology of the present invention content for present invention, but
Substance of the invention is not limited in described in following embodiments, one of ordinary skill in the art can with and should know appoint
What simple change or replacement based on true spirit all should belong to protection domain of the presently claimed invention.
Dongxin Micro-Wave Absorbing Material Co., Ltd., Dalian, model are selected in the present invention:RAC16, specification:200*200*
The absorbing material of 17mm, its specific composition is rubber and powdered carbonyl iron, and the shape of absorbing material is as shown in Figure 1.
Absorbing material and biomimetic material recombination process are intended to as shown in Fig. 2 biomimetic material is planted in suction ripple material with careless pencil
On material.
Embodiment 1
(1)Each component raw material is weighed by weight, will be molten in 1 part of polyvinyl alcohol water soluble polymer addition 250mL deionized water
Solution, is made poly-vinyl alcohol solution;
(2)1 part of lithium chloride, 2 parts of L MALIC ACIDs, 5 parts of acetic acid, 2 parts of chrome oxide greens are dissolved in above-mentioned poly-vinyl alcohol solution,
Temperature is under conditions of 60 DEG C, by cross-linking reaction 5 hours, to be made casting solution;
(3)By step(2)In casting solution take out, be placed in baking oven and be heated to 80 DEG C, 1h promotes polyvinyl alcohol crosslinked to take out again
It is laid in after vacuum defoamation on customization plate, vacuumizing and defoaming is specifically included:Taken out during casting solution is placed in into bottle,suction or vacuum drying oven
After vacuum, sealing and standing at room temperature is placed in, the time is 18h;
(4)Customization plate is placed in climatic chamber and is heated, 40 DEG C of temperature, humidity 45%, heat time 16h obtain sheet organic
Biomimetic material;
(5)By above-mentioned steps(4)The obtained organic biomimetic material of sheet is cut into thread organic biomimetic material, silk using chopping equipment
The width of the organic biomimetic material of shape is 1mm;
(6)Thread organic biomimetic material is bundled into careless beam with 5;
(7)Absorbing material is fixed in automatically dropping glue equipment using frock, after careless beam is planted on absorbing material;
(8)Absorbing material and biomimetic material are combined using automatically dropping glue equipment, obtain inhaling ripple bionic composite material.
Embodiment 2
(1)Each component raw material is weighed by weight, will be molten in 4 parts of polyvinyl alcohol water soluble polymers addition 250mL deionized waters
Solution, is made poly-vinyl alcohol solution;
(2)3 parts of lithium chlorides, 6 parts of L MALIC ACIDs, 5.5 parts of acetic acid, 4 parts of chrome oxide greens are dissolved in above-mentioned poly-vinyl alcohol solution,
Under conditions of being 75 DEG C in temperature, by cross-linking reaction 5.5 hours, casting solution is made;
(3)By step(2)In casting solution take out, be placed in baking oven be heated to 90 DEG C, 1.2h promote it is polyvinyl alcohol crosslinked again will
It is laid in after vacuumizing and defoaming on customization plate, vacuumizing and defoaming is specifically included:During casting solution is placed in into bottle,suction or vacuum drying oven
After vacuumizing, sealing and standing at room temperature is placed in, the time is 21h;
(4)Customization plate is placed in climatic chamber and is heated, 40 DEG C of temperature, humidity 45%, heat time 16h obtain sheet organic
Biomimetic material;
(5)By above-mentioned steps(4)The obtained organic biomimetic material of sheet is cut into thread organic biomimetic material, silk using chopping equipment
The width of the organic biomimetic material of shape is 1mm;
(6)Thread organic biomimetic material is bundled into careless beam with 7;
(7)Absorbing material is fixed in automatically dropping glue equipment using frock, after careless beam is planted on absorbing material;
(8)Absorbing material and biomimetic material are combined using automatically dropping glue equipment, obtain inhaling ripple bionic composite material.
Embodiment 3
(1)Each component raw material is weighed by weight, will be molten in 8 parts of polyvinyl alcohol water soluble polymers addition 250mL deionized waters
Solution, is made poly-vinyl alcohol solution;
(2)7 parts of lithium chlorides, 9 parts of L MALIC ACIDs, 6 parts of acetic acid, 6 parts of chrome oxide greens are dissolved in above-mentioned poly-vinyl alcohol solution,
Temperature is under conditions of 90 DEG C, by cross-linking reaction 6 hours, to be made casting solution;
(3)By step(2)In casting solution take out, be placed in baking oven be heated to 100 DEG C, 1.5h promote it is polyvinyl alcohol crosslinked again will
It is laid in after vacuumizing and defoaming on customization plate, vacuumizing and defoaming is specifically included:During casting solution is placed in into bottle,suction or vacuum drying oven
After vacuumizing, sealing and standing at room temperature is placed in, the time is 24h;
(4)Customization plate is placed in climatic chamber and is heated, 40 DEG C of temperature, humidity 45%, heat time 16h obtain sheet organic
Biomimetic material;
(5)By above-mentioned steps(4)The obtained organic biomimetic material of sheet is cut into thread organic biomimetic material, silk using chopping equipment
The width of the organic biomimetic material of shape is 1mm;
(6)Thread organic biomimetic material is bundled into careless beam with 10;
(7)Absorbing material is fixed in automatically dropping glue equipment using frock, after careless beam is planted on absorbing material;
(8)Absorbing material and biomimetic material are combined using automatically dropping glue equipment, obtain inhaling ripple bionic composite material.
Embodiment 4
(1)Each component raw material is weighed by weight, will be molten in 5 parts of polyvinyl alcohol water soluble polymers addition 250mL deionized waters
Solution, is made poly-vinyl alcohol solution;
(2)5 parts of calcium chloride, 7 parts of edible apple vinegars, 5 parts of acetic acid, 5 parts of careless silk Huangs are dissolved in above-mentioned poly-vinyl alcohol solution,
Temperature is under conditions of 80 DEG C, by cross-linking reaction 6 hours, to be made casting solution;
(3)By step(2)In casting solution take out, be placed in baking oven be heated to 100 DEG C, 1.5h promote it is polyvinyl alcohol crosslinked again will
It is laid in after vacuumizing and defoaming on customization plate, vacuumizing and defoaming is specifically included:During casting solution is placed in into bottle,suction or vacuum drying oven
After vacuumizing, sealing and standing at room temperature is placed in, the time is 23h;
(4)Customization plate is placed in climatic chamber and is heated, 40 DEG C of temperature, humidity 45%, heat time 16h obtain sheet organic
Biomimetic material;
(5)By above-mentioned steps(4)The obtained organic biomimetic material of sheet is cut into thread organic biomimetic material, silk using chopping equipment
The width of the organic biomimetic material of shape is 1mm;
(6)Thread organic biomimetic material is bundled into careless beam with 8;
(7)Absorbing material is fixed in automatically dropping glue equipment using frock, after careless beam is planted on absorbing material;
(8)Absorbing material and biomimetic material are combined using automatically dropping glue equipment, obtain inhaling ripple bionic composite material.
The present invention inhales ripple bionic composite material and ensure that suction ripple bionic composite material has simulating plant outward appearance;Spectrum is anti-
Penetrate and have infrared, light spectrum image-forming camouflage, forest land background visual camouflage and radar invisible concurrently so as to reach with absorbing radar wave characteristic
Effect.
Claims (9)
1. it is a kind of to inhale ripple bionic composite material, it is characterised in that to inhale ripple bionic composite material by organic biomimetic material and inhale ripple material
Material composition, biomimetic material is planted on absorbing material with careless pencil, and organic biomimetic material is made up of the component of following weight portion:It is poly-
Vinyl alcohol water soluble polymer is 1-8 parts;Metal chloride 1-7 parts;Coloring agent 2-6 parts;Crosslinking agent is 2-9 parts;Catalyst is
5-6 parts.
2. one kind according to claim 1 inhales ripple bionic composite material, it is characterised in that the metal chloride refers to moisture absorption
The stronger inorganic salts of property.
3. it is according to claim 2 a kind of to inhale ripple bionic composite material, it is characterised in that the inorganic salts be lithium chloride or
Calcium chloride.
4. one kind according to claim 1 inhales ripple bionic composite material, it is characterised in that the crosslinking agent is L MALIC ACID
Or edible apple vinegar.
5. one kind according to claim 1 inhales ripple bionic composite material, it is characterised in that the catalyst is acetic acid.
6. one kind according to claim 1 inhales ripple bionic composite material, it is characterised in that the coloring agent is chrome oxide green
Or careless silk Huang.
7. it is a kind of inhale ripple bionic composite material processing method, it is characterised in that comprise the following steps:
(1)Each component raw material is weighed by weight, by 1-8 parts of polyvinyl alcohol water soluble polymer addition 250mL deionized water
Dissolving, is made poly-vinyl alcohol solution;
(2)1-7 parts of metal chloride, 2-9 parts of crosslinking agent, 5-6 parts of catalyst, 2-6 parts of coloring agent are dissolved in above-mentioned polyvinyl alcohol
In solution, under conditions of being 60-90 DEG C in temperature, by cross-linking reaction 5-6 hours, casting solution is made;
(3)By step(2)In casting solution take out, be placed in baking oven be heated to 80-100 DEG C, 1-1.5h promote polyvinyl alcohol to hand over
Connection will be laid on customization plate after vacuumizing and defoaming again;
(4)Customization plate is placed in climatic chamber and is heated, 40 DEG C of temperature, humidity 45%, heat time 16h obtain sheet organic
Biomimetic material;
(5)By above-mentioned steps(4)The obtained organic biomimetic material of sheet is cut into thread organic biomimetic material using chopping equipment;
(6)Thread organic biomimetic material is bundled into careless beam with 5-10 roots;
(7)Absorbing material is fixed in automatically dropping glue equipment using frock, after careless beam is planted on absorbing material;
(8)Absorbing material and biomimetic material are combined using automatically dropping glue equipment, obtain inhaling ripple bionic composite material.
8. it is according to claim 7 it is a kind of inhale ripple bionic composite material processing method, it is characterised in that the step
(5)In thread organic biomimetic material width be 1mm.
9. it is according to claim 7 it is a kind of inhale ripple bionic composite material processing method, it is characterised in that the step
(3)In, casting solution vacuumizing and defoaming is specifically included:After being vacuumized during casting solution is placed in into bottle,suction or vacuum drying oven, room is placed in
The lower sealing and standing of temperature, the time is 18-24h.