CN106751163A - A kind of heat-resistant PVC composite foamed plate high of graphene oxide hydroxyapatite reinforcement and preparation method thereof - Google Patents
A kind of heat-resistant PVC composite foamed plate high of graphene oxide hydroxyapatite reinforcement and preparation method thereof Download PDFInfo
- Publication number
- CN106751163A CN106751163A CN201611108125.1A CN201611108125A CN106751163A CN 106751163 A CN106751163 A CN 106751163A CN 201611108125 A CN201611108125 A CN 201611108125A CN 106751163 A CN106751163 A CN 106751163A
- Authority
- CN
- China
- Prior art keywords
- graphene oxide
- heat
- hydroxyapatite
- preparation
- foamed plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Heat-resistant PVC composite foamed plate high the invention discloses a kind of graphene oxide hydroxyapatite reinforcement and preparation method thereof, the composite foamed plate is with PVC and NBR, liquid silastic is blended as foaming macromolecular base-material, this foaming system has toughness and plasticity higher, the composite modified filler of nanometer hydroxyapatite/graphene oxide of addition can effectively lift the heat resistance and mechanical property of foamed board, improve the intensity and mobility of melt, obtain more preferably foaming effect, in conjunction with other auxiliary materials, it is final to prepare with high heat-resisting, it is fire-retardant, environmental protection, there is prominent application prospect in multiple building materials fields.
Description
Technical field
The present invention relates to PVC foam plate technique field, more particularly to a kind of graphene oxide-hydroxyapatite reinforcement height
Heat-resistant PVC composite foamed plate and preparation method thereof.
Background technology
PVC foam plate has the characteristic such as waterproof, fire-retardant, acid and alkali-resistance, mothproof, light weight, insulation, sound insulation, damping, be timber,
The ideal substitute of aluminium, composite board, is widely used in car, railway carriage ceiling, casing sandwich layer, interior decoration and uses
Plate, skin plate, interior trim plate, office, house, public place building compartment, commercial decorative frame, used in dustless room
The aspects such as plate, ceiling board.
Although PVC foam plate has so is widely applied space, but its actual occupation rate of market is relatively low, especially exists
Fitment material for family aspect, main restraining factors are very different products, product at aspects such as intensity, rigidity, heat endurances not to the utmost
Such as people's will, there is potential safety hazard when using, in order to improve the combination property of PVC board, use macromolecular material and inorganic filler
Blending and modifying is most common method.《The research of flame retardant type NBR/PVC expanded materials》NBR and PVC is blended foaming by one text, is obtained
Obtained the more excellent product of mechanical property, but its poor heat resistance, fire retardant need to be added and reach flame retardant effect, but to material
Effect on Mechanical Properties it is larger, using being restricted.
The content of the invention
The object of the invention is exactly to make up the defect of prior art, there is provided a kind of graphene oxide-hydroxyapatite is mended
Strong heat-resistant PVC composite foamed plate high and preparation method thereof.
The present invention is achieved by the following technical solutions:
A kind of heat-resistant PVC composite foamed plate high of graphene oxide-hydroxyapatite reinforcement, the composite foamed plate is by following weight
The raw material of part is obtained:PVC 40-50, NBR 20-30, nanometer hydroxyapatite 8-10, liquid silastic 8-10, oxidic polyethylene
Wax 3-5, graphene oxide 1-2, white carbon 1-2, AC foaming agent 2-5, triethyl borate 1-2, light stabilizer 0.5-1, calcium zinc are steady
Determine agent 4-5, Vulcanization accelerator TMTD 0.4-0.5, stearic acid 0.5-1, vulcanizing agent PDM 1-1.5, epoxy aliphatic acid methyl ester 5-8, methyl
Zinc acrylate resin 2-4, sodium lignin sulfonate 0.1-0.2, deionized water 20-30.
A kind of preparation method bag of the heat-resistant PVC composite foamed plate high of described graphene oxide-hydroxyapatite reinforcement
Include following steps:
(1)First by sodium lignin sulfonate input deionized water, stirring is completely dissolved it, then puts into nano-hydroxy-apatite
Stone, graphene oxide, drying for standby after mixed grinding dispersion 20-30min;
(2)Banburying 20-30min in 160 DEG C of banburies is put into after being first well mixed NBR, liquid silastic, is then sequentially added
PVC, OPE, white carbon, epoxy aliphatic acid methyl ester, light stabilizer, calcium zinc stabilizer, zinc methacrylate and step
Suddenly(1)Resulting material, composite base-material is obtained after continuing banburying 30-50min, and it is standby that base-material naturally cools to room temperature;
(3)By step(2)The base-material of preparation is put into rubber mixing machine with other residual components, and 20-30min is kneaded under the conditions of 50 DEG C
Discharge after thin logical three times afterwards;
(4)By step(3)Resulting sheet in a mold, the hot-pressing and foaming 15-20min under the conditions of 170-175 DEG C, 12-16MPa,
Subsequent release cooling, obtains final product the composite foamed plate.
Using PVC and NBR, liquid silastic blending as foaming macromolecular base-material, this foaming system has more the present invention
Toughness and plasticity high, the composite modified filler of nanometer hydroxyapatite/graphene oxide of addition can effectively lift foamed board
Heat resistance and mechanical property, improve the intensity and mobility of melt, obtain more preferably foaming effect, it is auxiliary in conjunction with other
Material, finally prepares with heat-resisting, fire-retardant, environmental protection high, has prominent application prospect in multiple building materials fields.
Specific embodiment
A kind of heat-resistant PVC composite foamed plate high of graphene oxide hydroxyapatite reinforcement, the composite foamed plate is by following
The raw material of weight portion is obtained:PVC 40, NBR 20, nanometer hydroxyapatite 8, liquid silastic 8, OPE 3, oxidation
Graphene 1, white carbon 1, AC foaming agents 2, triethyl borate 1, light stabilizer 0.5, calcium zinc stabilizer 4, Vulcanization accelerator TMTD 0.4,
Stearic acid 0.5, vulcanizing agent PDM 1, epoxy aliphatic acid methyl ester 5, zinc methacrylate 2, sodium lignin sulfonate 0.1, deionized water
20。
The preparation method of the embodiment composite foamed plate is comprised the following steps:
(1)First by sodium lignin sulfonate input deionized water, stirring is completely dissolved it, then puts into nano-hydroxy-apatite
Stone, graphene oxide, drying for standby after mixed grinding dispersion 20min;
(2)Banburying 20min in 160 DEG C of banburies is put into after being first well mixed NBR, liquid silastic, is then sequentially added
PVC, OPE, white carbon, epoxy aliphatic acid methyl ester, light stabilizer, calcium zinc stabilizer, zinc methacrylate and step
Suddenly(1)Resulting material, composite base-material is obtained after continuing banburying 30min, and it is standby that base-material naturally cools to room temperature;
(3)By step(2)The base-material of preparation puts into rubber mixing machine with other residual components, after kneading 20min under the conditions of 50 DEG C
Discharged after thin logical three times;
(4)By step(3)In a mold, the hot-pressing and foaming 15min under the conditions of 170 DEG C, 12MPa, subsequent release is cold for resulting sheet
But, the composite foamed plate is obtained final product.
Obtained foamed board follows relevant criterion and carries out performance test, and the performance test results are:
Apparent density:0.424g/cm3;Tensile strength:43.5MPa;Elongation at break:208.6%;Tearing strength:3.76N/m;
Oxygen index (OI) >=30%;Heat resistance:5h is placed under the conditions of 80 DEG C unchanged.
Claims (2)
1. a kind of heat-resistant PVC composite foamed plate high of graphene oxide-hydroxyapatite reinforcement, it is characterised in that the compound hair
Bubble plate is obtained by the raw material of following weight portion:PVC 40-50, NBR 20-30, nanometer hydroxyapatite 8-10, liquid silastic
8-10, OPE 3-5, graphene oxide 1-2, white carbon 1-2, AC foaming agent 2-5, triethyl borate 1-2, light stabilization
Agent 0.5-1, calcium zinc stabilizer 4-5, Vulcanization accelerator TMTD 0.4-0.5, stearic acid 0.5-1, vulcanizing agent PDM 1-1.5, epoxidised fatty
Sour methyl esters 5-8, zinc methacrylate 2-4, sodium lignin sulfonate 0.1-0.2, deionized water 20-30.
2. the system of the heat-resistant PVC composite foamed plate high of a kind of graphene oxide-hydroxyapatite reinforcement as claimed in claim 1
Preparation Method, it is characterised in that described preparation method is comprised the following steps:
(1)First by sodium lignin sulfonate input deionized water, stirring is completely dissolved it, then puts into nano-hydroxy-apatite
Stone, graphene oxide, drying for standby after mixed grinding dispersion 20-30min;
(2)Banburying 20-30min in 160 DEG C of banburies is put into after being first well mixed NBR, liquid silastic, is then sequentially added
PVC, OPE, white carbon, epoxy aliphatic acid methyl ester, light stabilizer, calcium zinc stabilizer, zinc methacrylate and step
Suddenly(1)Resulting material, composite base-material is obtained after continuing banburying 30-50min, and it is standby that base-material naturally cools to room temperature;
(3)By step(2)The base-material of preparation is put into rubber mixing machine with other residual components, and 20-30min is kneaded under the conditions of 50 DEG C
Discharge after thin logical three times afterwards;
(4)By step(3)Resulting sheet in a mold, the hot-pressing and foaming 15-20min under the conditions of 170-175 DEG C, 12-16MPa,
Subsequent release cooling, obtains final product the composite foamed plate.