CN106750857A - A kind of production technology of bubble film - Google Patents
A kind of production technology of bubble film Download PDFInfo
- Publication number
- CN106750857A CN106750857A CN201611085062.2A CN201611085062A CN106750857A CN 106750857 A CN106750857 A CN 106750857A CN 201611085062 A CN201611085062 A CN 201611085062A CN 106750857 A CN106750857 A CN 106750857A
- Authority
- CN
- China
- Prior art keywords
- parts
- agent
- raw material
- bubble film
- crosslinking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production technology of bubble film.Comprise the following steps, (1) refrigeration auxiliary agent the step of, refrigerating temperature range be 5 DEG C 25 DEG C;(2) the step of raw material mixes, raw material includes EVA resin, coupling agent, foaming agent, crosslinking agent, crosslinking coagent, antioxidant, UV absorbers and the light stabilizer that VA contents are 28 33%, 90 110 parts of EVA resin, 0.1 0.4 parts of coupling agent, 0.8 1.5 parts of foaming agent, 0.5 1.0 parts of crosslinking agent, 0.3 0.8 parts of crosslinking coagent, 0.1 0.3 parts of antioxidant, 0.1 0.3 parts of UV absorbers, 0.2 0.4 parts of light stabilizer are counted by weight;(3) the step of feeding intake, mixed raw material is put into the hopper of extruder, and dosing operation is carried out under air-proof condition, and time control is within 5min;(4) using casting film-forming Process Production bubble film the step of, this step temperature control is at 60 90 DEG C;(5) the step of finished product is refrigerated, the bubble film to obtaining carries out stored refrigerated, and refrigerated condition is 18 30 DEG C of constant refrigeration, and cold preservation time is less than 6 months.
Description
Technical field
The present invention relates to a kind of production technology of bubble film.
Background technology
In fields such as building decorations, doubling glass has obtained more and more widely should with its good characteristic such as attractive in appearance, firm
With doubling glass includes the glass film layers and the glass positioned at both sides positioned at center.Existing glass film is generally monochrome,
It is typically also that opaque monochrome is adjusted, it is necessary to when representing combination colour effect to produce the doubling glass for being formed, typically by multicolour
Doubling glass is applied in combination.However as the lifting and transformation of people's estheticism, the doubling glass of monotone can not expire
The aesthetic requirement of sufficient people, the technology that people are badly in need of to represent on a piece of doubling glass similar bubble effect occurs, existing
Have in technology and there is not yet above-mentioned production technology.
The content of the invention
The present invention provides a kind of production technology of bubble film to solve technical problem present in known technology, makes glue
Piece possesses bubble effect.
The present invention is adopted the technical scheme that to solve technical problem present in known technology:A kind of bubble film
Production technology is comprised the following steps, (1) refrigeration auxiliary agent the step of, auxiliary agent is helped including coupling agent, foaming agent, crosslinking agent and crosslinking
Agent, refrigerating temperature range is -5 DEG C -25 DEG C;(2) the step of raw material mixes, raw material is mixed in mixer, raw material bag
Include EVA resin, coupling agent, foaming agent, crosslinking agent, crosslinking coagent, antioxidant, UV absorbers that VA contents are 28-33%
And light stabilizer, 90-110 parts of EVA resin, coupling agent 0.1-0.4 parts, foaming agent 0.8-1.5 parts, crosslinking agent are counted by weight
0.5-1.0 parts, crosslinking coagent 0.3-0.8 parts, antioxidant 0.1-0.3 parts, UV absorbers 0.1-0.3 parts, light stabilizer
0.2-0.4 parts;(3) the step of feeding intake, mixed raw material is put into the hopper of extruder, and dosing operation is in air-proof condition
Under carry out, time control is within 5min;(4) using casting film-forming Process Production bubble film the step of, this step temperature control
System is at 60-90 DEG C;(5) the step of finished product is refrigerated, the bubble film to obtaining carry out it is stored refrigerated, refrigerated condition be 18-30 DEG C
Constant refrigeration, cold preservation time be less than 6 months.
Advantages and positive effects of the present invention are:The invention provides a kind of production technology of bubble film, by that will pass
The glass film production technology of system is combined with foam process, has obtained the film product with bubble effect, improves doubling
The alternative of glass production, whole production procedure is concise, easily operated.
Preferably:The step of raw material mixes in step (2) is carried out under air-proof condition, and incorporation time is 5-10min.
Preferably:The coupling agent is chosen for aminopropyl trimethoxysilane, aminopropyltriethoxy dimethoxysilane, ammonia third
Ethyl triethoxy silicane alkane, aminoethylaminopropyl trimethoxy silane, aminoethylaminopropyl triethoxysilane, aminoethylaminopropyl
Methyl dimethoxysilane, vinyltrimethoxy silane, VTES, methacryloxy trimethoxy
One or more in silane.
Specific embodiment
For the content of the invention of the invention, feature and effect can be further appreciated that, following examples detailed description is hereby lifted as follows:
Embodiment 1
(1) auxiliary agent is refrigerated, auxiliary agent includes coupling agent, foaming agent, crosslinking agent and crosslinking coagent, and refrigerating temperature range is -3
℃;
(2) raw material is mixed in mixer, raw material includes EVA resin, coupling agent, the foaming that VA contents are 30%
Agent, crosslinking agent, crosslinking coagent, antioxidant, UV absorbers and light stabilizer;
95 parts of EVA resin, 0.15 part of coupling agent, 0.9 part of foaming agent, 0.6 part of crosslinking agent, crosslinking coagent are counted by weight
0.4 part, 0.1 part of antioxidant, 0.1 part of UV absorbers, 0.2 part of light stabilizer;
(3) mixed raw material is put into the hopper of extruder, dosing operation is carried out under air-proof condition, when feeding intake
Between be 2min;
(4) using casting film-forming Process Production bubble film the step of, this step temperature control is at 65 DEG C;
(5) the bubble film for obtaining is carried out stored refrigerated, refrigerated condition is 18 DEG C of constant refrigeration, and cold preservation time is 2
Individual month.
Wherein, the step of raw material mixes in step (2) is carried out under air-proof condition, and incorporation time is 5min;Coupling agent is selected
It is taken as aminopropyl trimethoxysilane.
Embodiment 2
(1) auxiliary agent is refrigerated, auxiliary agent includes coupling agent, foaming agent, crosslinking agent and crosslinking coagent, and refrigerating temperature range is 5 DEG C;
(2) raw material is mixed in mixer, raw material includes EVA resin, coupling agent, the foaming that VA contents are 30%
Agent, crosslinking agent, crosslinking coagent, antioxidant, UV absorbers and light stabilizer;
100 parts of EVA resin, 0.2 part of coupling agent, 1.2 parts of foaming agent, 0.7 part of crosslinking agent, crosslinking coagent are counted by weight
0.5 part, 0.2 part of antioxidant, 0.2 part of UV absorbers, 0.3 part of light stabilizer;
(4) mixed raw material is put into the hopper of extruder, dosing operation is carried out under air-proof condition, when feeding intake
Between be 3min;
(4) using casting film-forming Process Production bubble film the step of, this step temperature control is at 75 DEG C;
(5) the bubble film for obtaining is carried out stored refrigerated, refrigerated condition is 18 DEG C of constant refrigeration, and cold preservation time is 3
Individual month.
Wherein, the step of raw material mixes in step (2) is carried out under air-proof condition, and incorporation time is 7min;Coupling agent is selected
It is taken as aminoethylaminopropyl triethoxysilane.
Embodiment 3
(1) auxiliary agent is refrigerated, auxiliary agent includes coupling agent, foaming agent, crosslinking agent and crosslinking coagent, and refrigerating temperature range is 15
℃;
(2) raw material is mixed in mixer, raw material includes EVA resin, coupling agent, the foaming that VA contents are 32%
Agent, crosslinking agent, crosslinking coagent, antioxidant, UV absorbers and light stabilizer;
108 parts of EVA resin is counted by weight, and 0.35 part of coupling agent, 1.4 parts of foaming agent, 0.9 part of crosslinking agent, crosslinking are helped
0.8 part of agent, 0.3 part of antioxidant, 0.3 part of UV absorbers, 0.4 part of light stabilizer;
(5) mixed raw material is put into the hopper of extruder, dosing operation is carried out under air-proof condition, when feeding intake
Between be 4min;
(4) using casting film-forming Process Production bubble film the step of, this step temperature control is at 85 DEG C;
(5) the bubble film for obtaining is carried out stored refrigerated, refrigerated condition is 18 DEG C of constant refrigeration, and cold preservation time is 4
Individual month.
Wherein, the step of raw material mixes in step (2) is carried out under air-proof condition, and incorporation time is 8min;Coupling agent is selected
It is taken as VTES.
Claims (3)
1. a kind of production technology of bubble film, it is characterized in that:Comprise the following steps,
(1) the step of refrigerating auxiliary agent, auxiliary agent includes coupling agent, foaming agent, crosslinking agent and crosslinking coagent, and refrigerating temperature range is -5
℃-25℃;
(2) the step of raw material mixes, raw material is mixed in mixer, raw material includes that VA contents are the EVA trees of 28-33%
Fat, coupling agent, foaming agent, crosslinking agent, crosslinking coagent, antioxidant, UV absorbers and light stabilizer, count by weight
EVA resin 90-110 parts, coupling agent 0.1-0.4 parts, foaming agent 0.8-1.5 parts, crosslinking agent 0.5-1.0 parts, crosslinking coagent 0.3-
0.8 part, antioxidant 0.1-0.3 parts, UV absorbers 0.1-0.3 parts, light stabilizer 0.2-0.4 parts;
(3) the step of feeding intake, mixed raw material is put into the hopper of extruder, and dosing operation enters under air-proof condition
OK, time control is within 5min;
(4) using casting film-forming Process Production bubble film the step of, this step temperature control is at 60-90 DEG C;
(5) the step of finished product is refrigerated, the bubble film to obtaining carries out stored refrigerated, and refrigerated condition is cold for 18-30 DEG C of constant temperature
Hide, cold preservation time is less than 6 months.
2. the production technology of bubble film as claimed in claim 1, it is characterised in that:The step of raw material mixes in step (2)
Carried out under air-proof condition, incorporation time is 5-10min.
3. the production technology of bubble film as claimed in claim 1, it is characterised in that:The coupling agent is chosen for aminopropyl three
Methoxy silane, aminopropyltriethoxy dimethoxysilane, aminopropyl triethoxysilane, aminoethylaminopropyl trimethoxy silicon
Alkane, aminoethylaminopropyl triethoxysilane, aminoethylaminopropyl methyl dimethoxysilane, vinyltrimethoxy silane,
One or more in VTES, methacryloxy trimethoxy silane.