CN106747847A - 一种提高碳酸氢铵稳定性的方法 - Google Patents
一种提高碳酸氢铵稳定性的方法 Download PDFInfo
- Publication number
- CN106747847A CN106747847A CN201710197649.0A CN201710197649A CN106747847A CN 106747847 A CN106747847 A CN 106747847A CN 201710197649 A CN201710197649 A CN 201710197649A CN 106747847 A CN106747847 A CN 106747847A
- Authority
- CN
- China
- Prior art keywords
- hydrogen carbonate
- ammonium hydrogen
- map
- semi
- activated carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种提高碳酸氢铵稳定性的方法,涉及农业肥料技术领域。该方法包括:将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉粉碎预处理后按照重量比为4‑8:5‑10:4‑12:2‑6:3‑6,将混合后的物料与碳酸氢铵按18‑42:58‑82进行混合得到混合物;再将该混合物进行挤压造粒,即可大大提高碳酸氢铵的稳定性。本发明以含有大量植物生长必需营养元素的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵为原料制备的颗粒状稳定性碳酸氢铵,工艺简单,无需复杂设备,产品有效成分多样,应用于农业生产,适用于各种土壤和作物,可有效降低农业种植成本,提高作物产量,改善农产品品质。
Description
技术领域
本发明涉及农业肥料领域,更具体的涉及一种提高碳酸氢铵稳定性的方法。
背景技术
由于碳酸氢铵晶粒比表面积较大,含游离水较高,一等品含水量3.5%以下,二等品含水量6.0%以下,且是一种对水敏感性的物质,化学性质很不稳定,若暴露于空气中,常温下即可分解,同时还极易吸湿,产生结块,用作农业肥料时,对运输、贮存极为不便,施用不当还会造成养分的大量流失和分解损失,造成氮素利用率降低和污染环境,肥效期短,浪费能源,农业投入成本高等。故此,为延长碳酸氢铵肥效、提高氮素利用率,最大限度地提高碳酸氢铵稳定性,是本发明的的最主要目的。
发明内容
本发明的目的正是针对上述现有技术的不足而提供一种提高碳酸氢铵稳定性的方法,它以含有大量植物生长必需营养元素的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵粉碎预处理后按照重量比进行混合并造粒得到的颗粒状混合物,可使碳酸氢铵的稳定性大大提高,且工艺简单,无需复杂设备,产品含有多种有效成分,用作农业肥料,可明显降低农业生产成本,提高土壤肥力,提高作物产量和农产品品质。
本发明的目的可通过下述技术措施来实现:
本发明的提高碳酸氢铵稳定性的方法包括以下步骤:
a、将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵分别进行粉碎预处理;
b、将粉碎预处理后的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉按质量比为4-8:5-10:4-12:2-6:3-6的比例搅拌混合后,再将混合后的物料与碳酸氢铵按质量比为18-42: 58-82的比例混合;
c、将混合粉料置于造粒机中进行造粒,得到颗粒状混合物;
d、将颗粒状混合物进行粒度筛选;
e、将筛选出不同粒度的颗粒状混合物分别进行包装密封,即得高稳定性碳酸氢铵成品。
优选的,经粉碎预处理后,活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵的粒度均为80-110目。
优选的,筛选的颗粒状混合物的颗粒直径为2-6mm。
本发明的原理是:由于碳酸氢铵晶粒比表面积较大,含游离水较高,一等品含水量3.5%以下,二等品含水量6.0%以下,且是一种对水敏感性的物质,化学性质很不稳定,易产生结块、挥发和分解,若能有效降低其游离水含量,则其稳定性会大大提高。
本发明提高碳酸氢铵稳定性的方法原理,是最大限度地降低碳酸氢铵的游离水含量。所选择的材料包括活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉,上述材料可以通过下述3种途径有效降低碳酸氢铵中的游离水含量。
途径1:一水硫酸镁、半水石膏是结晶水不饱和的物质,一水硫酸镁可吸收碳酸氢铵中的游离水形成七水硫酸镁,半水石膏可吸收碳酸氢铵中的游离水形成二水石膏,有效降低了碳酸氢铵中的游离水含量;
途径2:活性炭是一种多孔性物质,碳酸氢铵中的游离水可以进入到活性炭的空隙中,并被有效吸持,降低了碳酸氢铵中的游离水含量;
途径3:煅烧白云石粉的主要成分是氧化镁,氧化镁和磷酸一铵可与碳酸氢铵中的游离水形成六水合磷酸镁铵,使碳酸氢铵中的游离水转化为结晶水,有效降低了碳酸氢铵中的游离水含量。
将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉通过预处理与碳酸氢铵按一定比例混合后,通过上述3种途径,可使碳酸氢铵游的离水含量大幅降低,形成了改性的碳酸氢铵,大大提高了其稳定性。
改性的碳酸氢铵主要用于农业肥料,在选用的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉中,分别含有不等的碳、磷、氮、硫、钙、镁等植物营养元素,碳可提改善土壤肥力,磷、氮、硫、钙、镁可提高作物产量,改善农产品品质。
本发明以价廉且含有对土壤和作物营养或有益元素的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵为基本原料,通过混合并造粒,提供一种可明显改善碳酸氢铵物化性能,提高碳酸氢铵稳定性的方法,应用于农业生产,可提高养分利用率,增强土壤肥力,提高作物产量,改善农产品品质。本发明提供的提高碳酸氢铵稳定性的方法,加工过程简单、成本低,极易实施,符合我国农业生产发展的要求。
附图说明
图1是本发明提供的提高碳酸氢铵稳定性的方法流程图。
具体实施方式
实施例1
本实施例包括以下步骤:
a、将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵分别进行粉碎预处理;粉碎预处理的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵的粒度均为80目;
b、将粉碎预处理后的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉按质量比为4:5:4:2:3的比例搅拌混合后,再将混合后的物料与碳酸氢铵按质量比为18: 58的比例混合;
c、将混合粉料置于造粒机中进行造粒,得到颗粒状混合物;
d、将颗粒状混合物进行粒度筛选;筛选的颗粒状混合物的颗粒直径为2mm;
e、将筛选出的颗粒状混合物以25kg/袋包装密封即得稳定性碳酸氢铵成品。
实施例2
本实施例包括以下步骤:
a、将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵分别进行粉碎预处理;粉碎预处理的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵的粒度均为80目;
b、将粉碎预处理后的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉按质量比为6:8:8:4:4的比例搅拌混合后,再将混合后的物料与碳酸氢铵按质量比为30: 70的比例混合;
c、将混合粉料置于造粒机中进行造粒,得到颗粒状混合物;
d、将颗粒状混合物进行粒度筛选;筛选的颗粒状混合物的颗粒直径为4mm;
e、将筛选出的颗粒状混合物以40kg/袋包装密封即得稳定性碳酸氢铵成品。
实施例3
本实施例包括以下步骤:
a、将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵分别进行粉碎预处理;粉碎预处理的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵的粒度均为100目;
b、将粉碎预处理后的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉按质量比为7:8:10:5:5的比例搅拌混合后,再将混合后的物料与碳酸氢铵按质量比为25: 65的比例混合;
c、将混合粉料置于造粒机中进行造粒,得到颗粒状混合物;
d、将颗粒状混合物进行粒度筛选;筛选的颗粒状混合物的颗粒直径为5mm;
e、将筛选出的颗粒状混合物以45kg/袋包装密封即得稳定性碳酸氢铵成品。
实施例4
本实施例包括以下步骤:
a、将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵分别进行粉碎预处理;粉碎预处理的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵的粒度均为110目;
b、将粉碎预处理后的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉按质量比为8:10:12:6:6的比例搅拌混合后,再将混合后的物料与碳酸氢铵按质量比为18: 58的比例混合;
c、将混合粉料置于造粒机中进行造粒,得到颗粒状混合物;
d、将颗粒状混合物进行粒度筛选;筛选的颗粒状混合物的颗粒直径为6mm;
e、将筛选出的颗粒状混合物以50kg/袋包装密封即得稳定性碳酸氢铵成品。
本发明上述实施例所制备的稳定性碳酸氢铵中含有大量元素碳、氢、氧、氮、磷,中量元素钙、镁,硫,微量元素锰、铁、锌等植物营养元素,能够促进植物光合作用,调节植物生长,增强植物的抗病抗倒伏能力,改善作物产品品质,提高作物产量。
Claims (3)
1.一种提高碳酸氢铵稳定性的方法,其特征在于:所述方法包括以下步骤:
a、将活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵分别进行粉碎预处理;
b、将粉碎预处理后的活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉按质量比为4-8:5-10:4-12:2-6:3-6的比例搅拌混合后,再将混合后的物料与碳酸氢铵按质量比为18-42: 58-82的比例混合;
c、将混合粉料置于造粒机中进行造粒,得到颗粒状混合物;
d、将颗粒状混合物进行粒度筛选;
e、将筛选出不同粒度的颗粒状混合物分别进行包装密封,即得高稳定性碳酸氢铵成品。
2.根据权利要求1所述的提高碳酸氢铵稳定性的方法,其特征在于:经粉碎预处理后,活性炭、磷酸一铵、半水石膏、一水硫酸镁、煅烧白云石粉、碳酸氢铵的粒度均为80-110目。
3.根据权利要求1所述的提高碳酸氢铵稳定性的方法,其特征在于:筛选的颗粒状混合物的颗粒直径为2-6mm。