CN106746641A - A kind of formula of porcelain red crystal rod - Google Patents
A kind of formula of porcelain red crystal rod Download PDFInfo
- Publication number
- CN106746641A CN106746641A CN201710062414.0A CN201710062414A CN106746641A CN 106746641 A CN106746641 A CN 106746641A CN 201710062414 A CN201710062414 A CN 201710062414A CN 106746641 A CN106746641 A CN 106746641A
- Authority
- CN
- China
- Prior art keywords
- crystal rod
- formula
- porcelain
- red
- cadmium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of formula of porcelain red crystal rod, solves the problems, such as that existing crystal rod has that colour purity is inadequate, transparency has been short of and barred body formula cannot once develop the color in electric smelter.A kind of formula of porcelain red crystal rod, the formula of the porcelain red crystal rod includes that the mass percent of following component and each component is:Silica 51.03 53.86%, soda ash 21.19 21.63%, zinc oxide 6.69 6.82%, borax 3.75 3.88%, potassium carbonate 2.85 3.21%, calcium carbonate 1.86 2.11%, sodium chloride 0.54 0.90%, prodan 0.87 1.02%, feldspar 7.05 7.77%, selenium powder 0.33 0.36%, cadmium red 0.53 0.61%, cadmium yellow 0.48 0.66%.
Description
Technical field
The present invention relates to a kind of formula of porcelain red crystal rod.
Background technology
Crystal rod is used as ornament, it is adaptable to different living scenes.However, existing crystal rod has the following problems:
1st, colour purity is inadequate;2nd, transparency has been short of;3rd, the formula of crystal rod cannot once develop the color in electric smelter.
The content of the invention
Of the invention is the formula for overcoming the deficiencies in the prior art to provide a kind of red crystal rod of porcelain, to realize crystal rod
Formula once develops the color in electric smelter, and after the cooling period, formation color is gorgeous, barred body is penetrating for the melting crystal after being processed through electric smelter
Crystal rod.
In order to solve the above technical problems, the present invention is adopted the following technical scheme that:
A kind of formula of porcelain red crystal rod, the formula of the porcelain red crystal rod includes the matter of following component and each component
Measuring percentage is:Silica 51.03-53.86%, soda ash 21.19-21.63%, zinc oxide 6.69-6.82%, borax
3.75-3.88%, potassium carbonate 2.85-3.21%, calcium carbonate 1.86-2.11%, sodium chloride 0.54-0.90%, prodan
0.87-1.02%, feldspar 7.05-7.77%, selenium powder 0.33-0.36%, cadmium red 0.53-0.61%, cadmium yellow 0.48-0.66%.
Further, the mass percent of the formula each component of the porcelain red crystal rod is:Silica 52.75%,
Soda ash 21.58%, zinc oxide 6.71%, borax 3.84%, potassium carbonate 2.88%, calcium carbonate 1.92%, sodium chloride 0.72%, fluorine
Sodium metasilicate 0.96%, feldspar 7.19%, selenium powder 0.34%, cadmium red 0.58%, cadmium yellow 0.55%.
Further, the formula each group of the porcelain red crystal rod is divided into:Silica 220g, soda ash 90g, zinc oxide
28g, borax 16g, potassium carbonate 12g, calcium carbonate 8g, sodium chloride 3g, prodan 4g, feldspar 30g, selenium powder 1.4g, cadmium red 2.4g,
Cadmium yellow 2.3g.
Further, the mass percent of the formula each component of the porcelain red crystal rod is:Silica 53.86%,
Soda ash 21.19%, zinc oxide 6.69%, borax 3.75%, potassium carbonate 2.85%, calcium carbonate 1.86%, sodium chloride 0.54%, fluorine
Sodium metasilicate 0.87%, feldspar 7.05%, selenium powder 0.33%, cadmium red 0.53%, cadmium yellow 0.48%.
Further, the mass percent of the formula each component of the porcelain red crystal rod is:Silica 51.03%,
Soda ash 21.63%, zinc oxide 6.82%, borax 3.88%, potassium carbonate 3.21%, calcium carbonate 2.11%, sodium chloride 0.90%, fluorine
Sodium metasilicate 1.02%, feldspar 7.77%, selenium powder 0.36%, cadmium red 0.61%, cadmium yellow 0.66%.
Beneficial effects of the present invention:
1st, in the present invention, soda ash and prodan be used to accelerate porcelain red crystal rod formula in other components in electric smelter
Thawing speed;Borax and prodan are used to strengthen the ability of the resistance to deformation after porcelain red crystal rod cooling shaping, additionally,
Adding borax and prodan in porcelain red crystal rod can also improve the resistance to elevated temperatures of barred body;The oxygen of extra fine quality percentage
The cadmium yellow for changing zinc, the selenium powder of extra fine quality percentage, the cadmium red of extra fine quality percentage and extra fine quality percentage is mutually mixed
And make the crystal of melting that porcelain red is presented, to realize that crystal rod of the invention comes with traditional red crystal rod significant difference;
Sodium chloride is used to remove the impurity in porcelain red crystal rod, so that it is internal without obvious flaw color spot after porcelain red crystal rod cooling,
Crystal stick body i.e. of the invention is penetrating;Calcium carbonate is used to improve the speed that the crystal rod of molten condition is cooled down in a mold, with
Time needed for saving the production of porcelain red crystal rod.
2nd, in the present invention, by adjusting the mass percent of soda ash, cadmium red and cadmium yellow in porcelain red crystal rod, to realize
The formula of porcelain red crystal rod can once develop the color in electric smelter.Additionally, red in porcelain by adjusting soda ash, cadmium red and cadmium yellow
Mass percent in crystal rod, to realize reducing the quantity that soda ash is volatilized in the electric smelter course of work.
Specific embodiment
Technical scheme is clearly and completely described below by embodiments of the invention, it is clear that retouched
The embodiment stated is a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, this area
The every other embodiment that those of ordinary skill is obtained under the premise of creative work is not made, belongs to protection of the present invention
Scope.
A kind of formula of porcelain red crystal rod, the formula of the porcelain red crystal rod includes the matter of following component and each component
Measuring percentage is:Silica 51.03-53.86%, soda ash 21.19-21.63%, zinc oxide 6.69-6.82%, borax
3.75-3.88%, potassium carbonate 2.85-3.21%, calcium carbonate 1.86-2.11%, sodium chloride 0.54-0.90%, prodan
0.87-1.02%, feldspar 7.05-7.77%, selenium powder 0.33-0.36%, cadmium red 0.53-0.61%, cadmium yellow 0.48-0.66%.
In the porcelain red crystal rod formula, the specific content of each component refers to specific examples below.
Embodiment 1
A kind of formula of porcelain red crystal rod, the formula of the porcelain red crystal rod includes the matter of following component and each component
Measuring percentage is:Silica 52.75%, soda ash 21.58%, zinc oxide 6.71%, borax 3.84%, potassium carbonate 2.88%,
Calcium carbonate 1.92%, sodium chloride 0.72%, prodan 0.96%, feldspar 7.19%, selenium powder 0.34%, cadmium red 0.58%, cadmium
Yellow 0.55%.
The mass percent of each component in porcelain red crystal rod formula is converted into specific mass figures, i.e. each component
Quality is:Silica 220g, soda ash 90g, zinc oxide 28g, borax 16g, potassium carbonate 12g, calcium carbonate 8g, sodium chloride 3g, fluorine
Sodium metasilicate 4g, feldspar 30g, selenium powder 1.4g, cadmium red 2.4g, cadmium yellow 2.3g.
The feldspar is compound particles, and the compound particles are calcics, the aluminum silicate material received with potassium, particle
Radial dimension is 100-200 mesh.
Embodiment 2
A kind of formula of porcelain red crystal rod, the formula of the porcelain red crystal rod includes the matter of following component and each component
Measuring percentage is:Silica 53.86%, soda ash 21.19%, zinc oxide 6.69%, borax 3.75%, potassium carbonate 2.85%,
Calcium carbonate 1.86%, sodium chloride 0.54%, prodan 0.87%, feldspar 7.05%, selenium powder 0.33%, cadmium red 0.53%, cadmium
Yellow 0.48%.
Embodiment 3
A kind of formula of porcelain red crystal rod, the formula of the porcelain red crystal rod includes the matter of following component and each component
Measuring percentage is:Silica 51.03%, soda ash 21.63%, zinc oxide 6.82%, borax 3.88%, potassium carbonate 3.21%,
Calcium carbonate 2.11%, sodium chloride 0.90%, prodan 1.02%, feldspar 7.77%, selenium powder 0.36%, cadmium red 0.61%, cadmium
Yellow 0.66%.
It should be appreciated that exemplary embodiment as herein described is illustrative and be not restrictive.Ordinary skill
Personnel should be appreciated that in the case of the spirit and scope of the present invention limited without departing from appended claims, can be with
Make the change of various forms and details.
Claims (5)
1. the formula of a kind of porcelain red crystal rod, it is characterised in that the formula of the porcelain red crystal rod include following component and
The mass percent of each component is:Silica 51.03-53.86%, soda ash 21.19-21.63%, zinc oxide 6.69-
6.82%th, borax 3.75-3.88%, potassium carbonate 2.85-3.21%, calcium carbonate 1.86-2.11%, sodium chloride 0.54-0.90%,
Prodan 0.87-1.02%, feldspar 7.05-7.77%, selenium powder 0.33-0.36%, cadmium red 0.53-0.61%, cadmium yellow 0.48-
0.66%.
2. the formula of porcelain red crystal rod according to claim 1, it is characterised in that:The formula of the porcelain red crystal rod is each
The mass percent of component is:Silica 52.75%, soda ash 21.58%, zinc oxide 6.71%, borax 3.84%, potassium carbonate
2.88%th, calcium carbonate 1.92%, sodium chloride 0.72%, prodan 0.96%, feldspar 7.19%, selenium powder 0.34%, cadmium red
0.58%th, cadmium yellow 0.55%.
3. the formula of porcelain red crystal rod according to claim 2, it is characterised in that:Silica 220g, soda ash 90g, oxygen
Change zinc 28g, borax 16g, potassium carbonate 12g, calcium carbonate 8g, sodium chloride 3g, prodan 4g, feldspar 30g, selenium powder 1.4g, cadmium red
2.4g, cadmium yellow 2.3g.
4. the formula of porcelain red crystal rod according to claim 1, it is characterised in that:The formula of the porcelain red crystal rod is each
The mass percent of component is:Silica 53.86%, soda ash 21.19%, zinc oxide 6.69%, borax 3.75%, potassium carbonate
2.85%th, calcium carbonate 1.86%, sodium chloride 0.54%, prodan 0.87%, feldspar 7.05%, selenium powder 0.33%, cadmium red
0.53%th, cadmium yellow 0.48%.
5. the formula of porcelain red crystal rod according to claim 1, it is characterised in that:The formula of the porcelain red crystal rod is each
The mass percent of component is:Silica 51.03%, soda ash 21.63%, zinc oxide 6.82%, borax 3.88%, potassium carbonate
3.21%th, calcium carbonate 2.11%, sodium chloride 0.90%, prodan 1.02%, feldspar 7.77%, selenium powder 0.36%, cadmium red
0.61%th, cadmium yellow 0.66%.