CN106745695A - A kind of tower biological filter builds and uses paper honeycomb filtrate - Google Patents
A kind of tower biological filter builds and uses paper honeycomb filtrate Download PDFInfo
- Publication number
- CN106745695A CN106745695A CN201710058494.2A CN201710058494A CN106745695A CN 106745695 A CN106745695 A CN 106745695A CN 201710058494 A CN201710058494 A CN 201710058494A CN 106745695 A CN106745695 A CN 106745695A
- Authority
- CN
- China
- Prior art keywords
- parts
- biological filter
- powder
- paper honeycomb
- filtrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of tower biological filter structure paper honeycomb filtrate, it is related to tower biological filter packing technique field, is made up of the raw material of following parts by weight:20 25 parts of pulp powder, 5 10 parts of atlapulgite, 5 10 parts of PLA, 36 parts of modified waste tire rubber powder, 36 parts of polyvinyl alcohol resin, 36 parts of polyethylene glycol oxide, 24 parts of aromatic modified terpene resin, 24 parts of diphenyl methane dimaleimide, 24 parts of nanometer sepiolite composite powder, 12 parts of microwax, 12 parts of HPO, 0.5 1 parts of Firebrake ZB, 0.5 1 parts of N NMAs, 0.3 0.5 parts of diallyl dimethyl ammoniumchloride, maleic anhydride is grafted 0.05 0.1 parts of compatilizer.The made paper honeycomb filtrate of the present invention is applied to structure tower biological filter, and the filtrate light weight is unlikely to increase tower body burden, with larger specific surface area, is conducive to the distribution of air;And its rough surface, biomembrane easily adheres to, the quick biomembrane for being formed is conducive to shortening the sewage disposal time and improves treatment effect.
Description
Technical field:
The present invention relates to tower biological filter packing technique field, and in particular to a kind of tower biological filter builds and uses paper wasp
Nest filtrate.
Background technology:
Tower biological filter is on the basis of biofilter, with reference to the packed tower mode in chemical industry, to have built straight
Footpath is with height than being 1:6-1:8, up to 8-24 meters of filter tank.Tower biological filter is also with aerobic microbiological treatment sewage
A kind of structures, are a kind of basic skills of biomembrance process treatment sanitary sewage and organic industry sewage, at present in oil
The sewage disposal aspect of the industries such as work, coking, chemical fibre, papermaking, metallurgy is applied.By in recent years practice have shown that, tower
Formula filter tank is preferable containing poison sewage effects such as cyanogen, phenol, nitrile, aldehyde to treatment, processes out water energy and meets the requirements.Because it is with one
Row advantage, so obtained comparing be widely applied.
Filtrate is the important composition part of tower biological filter, and because tower body is high, if filtrate is very heavy, tower body must increase
Load-carrying members are reinforced, cost is not only increased, and construction and installation are more complicated.For this problem, lightweight has been used at present
Filtrate substitutes traditional coke, slag, ceramic grain filter.
Paper honeycomb filtrate is one of light filter material conventional at present, and with larger surface area, even structure is conducive to sky
The distribution of gas, and proportion is lighter, unlikely increase tower body burden.Vertical honeycomb is conducive to the excretion of the biomembrane for peeling off,
And because honeycomb surface is rougher, biomembrane easily adheres to, and biomembrane can be quickly formed in cultivation stage.But sewage from upper and
During lower flowing, easily trigger gross distortion under souring, cause internal voids to block, so as to influence sewage treating efficiency.
The content of the invention:
The technical problems to be solved by the invention are to provide a kind of strong scour resistance, high treating effect and long service life
Tower biological filter build use paper honeycomb filtrate.
The technical problems to be solved by the invention are realized using following technical scheme:
A kind of tower biological filter builds and uses paper honeycomb filtrate, is made up of the raw material of following parts by weight:
Pulp powder 20-25 parts, atlapulgite 5-10 parts, PLA 5-10 parts, it is 3-6 parts of modified waste tire rubber powder, poly-
Vinyl alcohol resin 3-6 parts, polyethylene glycol oxide 3-6 parts, aromatic modified terpene resin 2-4 parts, diphenyl methane dimaleimide 2-4
Part, 2-4 parts of nanometer sepiolite composite powder, microwax 1-2 parts, HPO 1-2 parts, Firebrake ZB 0.5-1 parts, N- methylols third
Acrylamide 0.5-1 parts, diallyl dimethyl ammoniumchloride 0.3-0.5 parts, maleic anhydride 0.05-0.1 parts of compatilizer of grafting.
Its preparation method comprises the following steps:
(1) to polyethylene glycol oxide and aromatic modified terpene resin is added in PLA, heated up with the programming rate of 5 DEG C/min
To 130-135 DEG C of insulation mixing 25min, the grafting of a nanometer sepiolite composite powder, HPO and maleic anhydride is added compatible
Agent, is continuously maintained at 130-135 DEG C of insulation mixing 15min, then naturally cools to room temperature, obtains final product material I;
(2) to polyvinyl alcohol resin and diphenyl methane dimaleimide is added in modified waste tire rubber powder, with 5
DEG C/programming rate of min is warming up to 125-130 DEG C of insulation mixing 20min, adds microwax and N hydroxymethyl acrylamide,
125-130 DEG C of insulation mixing 15min is continuously maintained at, room temperature is then cooled to the cooling rate of 10 DEG C/min, obtain final product material
II;
(3) to addition material II, pulp powder, atlapulgite, Firebrake ZB and diallyl dimethyl chlorination in material I
Ammonium, sends into extruder after being sufficiently mixed, and sets 125-130 DEG C of cross-head temperature, one section 90-95 DEG C of barrel zone temperature, two
105-110 DEG C, three sections 125-130 DEG C of section, extruded, cooling and shaping obtains the Ultrathin substrate of thickness 2-3mm, last drawn method
Alveolate texture is made, paper honeycomb filtrate is obtained final product.
The modified waste tire rubber powder is formed by the modified treatment of rubber powder of waste tire, and specific preparation method is:
To in rubber powder of waste tire add turpentine oil and hydrogenated rosin pentaerythritol ester, be sufficiently mixed after microwave frequency 2450MHz,
Microwave treatment 10min under power output 700W, and be transferred in 0-5 DEG C of environment and stand 30min, add allyl glycidol
Ether, HPMA and sulfurized lard, microwave treatment 10min is continued after being well mixed, then with the cooling speed of 5 DEG C/min
Degree is cooled to 50-55 DEG C of sealing thermal insulation and stands 30min, and in gained mixture feeding ball mill, the ground fineness that is made is less than 20 μ
The micro mist of m.
The rubber powder of waste tire, turpentine oil, hydrogenated rosin pentaerythritol ester, allyl glycidyl ether, hydrolysis are poly-
The amount ratio of maleic anhydride and sulfurized lard is 45-50:1-2:0.5-1:0.5-1:0.3-0.5:0.1-0.2.
Rubber powder of waste tire is by after above-mentioned modification, not only improving it with high molecular polymerization in filtrate preparing raw material
The comixing compatibility of thing, it is to avoid agglomeration occur, with the filling capacity for making full use of its excellent;Its bullet can also be significantly increased
Property, to assign made filtrate appropriate elastic deformability.
The nanometer sepiolite composite powder is made up of the raw material of following parts by weight:Sepiolite fibre 5-10 parts, flake asbestos
2-3 parts, ceramic 2-3 parts, 1-2 parts of poly alpha methylstyrene resin, chliorinated polyvinyl chloride 0.5-1 parts, hexamethylol trimerization
0.5-1 parts of cyanamide pregnancy ether, portland cement 0.3-0.5 parts, nano zine oxide 0.1-0.3 parts, its preparation method is:To Hai Pao
Ceramic, poly alpha methylstyrene resin and chliorinated polyvinyl chloride are added in mineral wool, is sufficiently mixed after microwave frequency
Microwave treatment 10min under 2450MHz, power output 700W, adds hexamethylolmelamine pregnancy ether and nano zine oxide,
Continue microwave treatment 5min after well mixed, flake asbestos and portland cement, gained mixture feeding nanometer are then added while hot
In grinder, ground prepared nanometer sepiolite composite powder.
The addition of above-mentioned nanometer sepiolite composite powder, can effectively strengthen the scour resistance through made filtrate, prevent it because forever
Deform long and reduce the treatment effect to sewage.
The beneficial effects of the invention are as follows:The made paper honeycomb filtrate of the present invention is applied to structure tower biological filter, the filtrate
Light weight is unlikely to increase tower body burden, with larger specific surface area, is conducive to the distribution of air;Its vertical stratification is conducive to peeling off
The excretion of the biomembrane for getting off, and its rough surface, biomembrane easily adhere to, and the quick biomembrane for being formed is conducive to shortening dirty
Treatment time of water;And the filtrate scour resistance is strong, can resist the impulsive force produced when sewage flows from top to bottom, makes in extension
Ensure the treatment effect to sewage while with the life-span.
Specific embodiment:
In order that technological means, creation characteristic, reached purpose and effect that the present invention is realized are easy to understand, tie below
Specific embodiment is closed, the present invention is expanded on further.
Embodiment 1
(1) to 3 parts of polyethylene glycol oxides and 3 parts of aromatic modified terpene resins are added in 5 parts of PLAs, with the liter of 5 DEG C/min
Warm speed be warming up to 130-135 DEG C insulation mixing 25min, add 2 parts of nanometer sepiolite composite powders, 1 part of HPO and
0.1 part of maleic anhydride is grafted compatilizer, is continuously maintained at 130-135 DEG C of insulation mixing 15min, then naturally cools to room temperature,
Obtain final product material I;
(2) acyl is carried out to 3 parts of polyvinyl alcohol resins of addition and 2 parts of diphenyl-methane spans in 4 parts of modified waste tire rubber powders
Imines, 125-130 DEG C of insulation mixing 20min is warming up to the programming rate of 5 DEG C/min, adds 1 part of microwax and 0.5 part of N-
NMA, is continuously maintained at 125-130 DEG C of insulation mixing 15min, is then lowered the temperature with the cooling rate of 10 DEG C/min
To room temperature, material II is obtained final product;
(3) to addition material II, 25 parts of pulp powders, 5 parts of atlapulgites, 0.5 part of Firebrake ZB and 0.5 part poly- two in material I
Allyl dimethyl ammonium chloride, sends into extruder after being sufficiently mixed, and sets 125-130 DEG C of cross-head temperature, machine barrel temperature
One section 90-95 DEG C, two sections 105-110 DEG C, three sections 125-130 DEG C of degree, extruded, cooling and shaping obtains the ultra-thin of thickness 2-3mm
Base material, last drawn method is made alveolate texture, obtains final product paper honeycomb filtrate.
The preparation of modified waste tire rubber powder:To addition 1 part of turpentine oil and 0.5 part of hydrogen in 45 parts of rubber powder of waste tire
Change pentalyn, be sufficiently mixed after microwave treatment 10min under microwave frequency 2450MHz, power output 700W, and turn
Enter and stand 30min in 0-5 DEG C of environment, add 0.5 part of allyl glycidyl ether, 0.3 part of HPMA and 0.2 part
Sulfurized lard, microwave treatment 10min is continued after being well mixed, and is then cooled to 50-55 DEG C of sealing with the cooling rate of 5 DEG C/min
Insulation stands 30min, ground to be made micro mist of the fineness less than 20 μm in gained mixture feeding ball mill.
The preparation of nanometer sepiolite composite powder:To 2 parts of ceramics, 1 part of poly- Alpha-Methyl of addition in 10 parts of sepiolite fibres
Styrene resin and 0.5 part of chliorinated polyvinyl chloride, are sufficiently mixed after microwave under microwave frequency 2450MHz, power output 700W
Treatment 10min, adds 0.5 part of hexamethylolmelamine pregnancy ether and 0.2 part of nano zine oxide, continues micro- after being well mixed
Ripple processes 5min, and 2 parts of flake asbestos and 0.5 part of portland cement are then added while hot, in gained mixture feeding nano-level grinder,
Ground prepared nanometer sepiolite composite powder.
Embodiment 2
(1) to 4 parts of polyethylene glycol oxides and 2 parts of aromatic modified terpene resins are added in 6 parts of PLAs, with the liter of 5 DEG C/min
Warm speed be warming up to 130-135 DEG C insulation mixing 25min, add 2 parts of nanometer sepiolite composite powders, 1 part of HPO and
0.1 part of maleic anhydride is grafted compatilizer, is continuously maintained at 130-135 DEG C of insulation mixing 15min, then naturally cools to room temperature,
Obtain final product material I;
(2) acyl is carried out to 3 parts of polyvinyl alcohol resins of addition and 2 parts of diphenyl-methane spans in 5 parts of modified waste tire rubber powders
Imines, 125-130 DEG C of insulation mixing 20min is warming up to the programming rate of 5 DEG C/min, adds 2 parts of microwaxes and 0.5 part of N-
NMA, is continuously maintained at 125-130 DEG C of insulation mixing 15min, is then lowered the temperature with the cooling rate of 10 DEG C/min
To room temperature, material II is obtained final product;
(3) to addition material II, 25 parts of pulp powders, 5 parts of atlapulgites, 0.5 part of Firebrake ZB and 0.5 part poly- two in material I
Allyl dimethyl ammonium chloride, sends into extruder after being sufficiently mixed, and sets 125-130 DEG C of cross-head temperature, machine barrel temperature
One section 90-95 DEG C, two sections 105-110 DEG C, three sections 125-130 DEG C of degree, extruded, cooling and shaping obtains the ultra-thin of thickness 2-3mm
Base material, last drawn method is made alveolate texture, obtains final product paper honeycomb filtrate.
The preparation of modified waste tire rubber powder:To 2 parts of turpentine oil of addition in 50 parts of rubber powder of waste tire and 1 part of hydrogenation
Pentalyn, is sufficiently mixed after microwave treatment 10min under microwave frequency 2450MHz, power output 700W, and be transferred to
30min is stood in 0-5 DEG C of environment, 0.5 part of allyl glycidyl ether, 0.5 part of HPMA and 0.2 part of sulphur is added
Change lard, microwave treatment 10min is continued after being well mixed, being then cooled to 50-55 DEG C of sealing with the cooling rate of 5 DEG C/min protects
Temperature stands 30min, ground to be made micro mist of the fineness less than 20 μm in gained mixture feeding ball mill.
The preparation of nanometer sepiolite composite powder:To 3 parts of ceramics, 1 part of poly- Alpha-Methyl of addition in 10 parts of sepiolite fibres
Styrene resin and 1 part of chliorinated polyvinyl chloride, are sufficiently mixed at microwave under microwave frequency 2450MHz, power output 700W
Reason 10min, adds 0.5 part of hexamethylolmelamine pregnancy ether and 0.1 part of nano zine oxide, and microwave is continued after being well mixed
Treatment 5min, then adds 3 parts of flake asbestos and 0.3 part of portland cement while hot, in gained mixture feeding nano-level grinder, warp
Grinding is obtained nanometer sepiolite composite powder.
Reference examples 1
(1) to 3 parts of polyethylene glycol oxides and 3 parts of aromatic modified terpene resins are added in 5 parts of PLAs, with the liter of 5 DEG C/min
Warm speed be warming up to 130-135 DEG C insulation mixing 25min, add 2 parts of nanometer sepiolite composite powders, 1 part of HPO and
0.1 part of maleic anhydride is grafted compatilizer, is continuously maintained at 130-135 DEG C of insulation mixing 15min, then naturally cools to room temperature,
Obtain final product material I;
(2) to addition 3 parts of polyvinyl alcohol resins and 2 parts of diphenyl methane dimaleimides in 4 parts of rubber powder of waste tire,
125-130 DEG C of insulation mixing 20min is warming up to the programming rate of 5 DEG C/min, 1 part of microwax and 0.5 part of N- hydroxyl first is added
Base acrylamide, is continuously maintained at 125-130 DEG C of insulation mixing 15min, is then cooled to room with the cooling rate of 10 DEG C/min
Temperature, obtains final product material II;
(3) to addition material II, 25 parts of pulp powders, 5 parts of atlapulgites, 0.5 part of Firebrake ZB and 0.5 part poly- two in material I
Allyl dimethyl ammonium chloride, sends into extruder after being sufficiently mixed, and sets 125-130 DEG C of cross-head temperature, machine barrel temperature
One section 90-95 DEG C, two sections 105-110 DEG C, three sections 125-130 DEG C of degree, extruded, cooling and shaping obtains the ultra-thin of thickness 2-3mm
Base material, last drawn method is made alveolate texture, obtains final product paper honeycomb filtrate.
The preparation of nanometer sepiolite composite powder:To 3 parts of ceramics, 1 part of poly- Alpha-Methyl of addition in 10 parts of sepiolite fibres
Styrene resin and 1 part of chliorinated polyvinyl chloride, are sufficiently mixed at microwave under microwave frequency 2450MHz, power output 700W
Reason 10min, adds 0.5 part of hexamethylolmelamine pregnancy ether and 0.1 part of nano zine oxide, and microwave is continued after being well mixed
Treatment 5min, then adds 3 parts of flake asbestos and 0.3 part of portland cement while hot, in gained mixture feeding nano-level grinder, warp
Grinding is obtained nanometer sepiolite composite powder.
Reference examples 2
(1) to 4 parts of polyethylene glycol oxides and 2 parts of aromatic modified terpene resins are added in 6 parts of PLAs, with the liter of 5 DEG C/min
Warm speed be warming up to 130-135 DEG C insulation mixing 25min, add 2 parts of nanometer sepiolite fibre powder, 1 part of HPO and
0.1 part of maleic anhydride is grafted compatilizer, is continuously maintained at 130-135 DEG C of insulation mixing 15min, then naturally cools to room temperature,
Obtain final product material I;
(2) acyl is carried out to 3 parts of polyvinyl alcohol resins of addition and 2 parts of diphenyl-methane spans in 5 parts of modified waste tire rubber powders
Imines, 125-130 DEG C of insulation mixing 20min is warming up to the programming rate of 5 DEG C/min, adds 2 parts of microwaxes and 0.5 part of N-
NMA, is continuously maintained at 125-130 DEG C of insulation mixing 15min, is then lowered the temperature with the cooling rate of 10 DEG C/min
To room temperature, material II is obtained final product;
(3) to addition material II, 25 parts of pulp powders, 5 parts of atlapulgites, 0.5 part of Firebrake ZB and 0.5 part poly- two in material I
Allyl dimethyl ammonium chloride, sends into extruder after being sufficiently mixed, and sets 125-130 DEG C of cross-head temperature, machine barrel temperature
One section 90-95 DEG C, two sections 105-110 DEG C, three sections 125-130 DEG C of degree, extruded, cooling and shaping obtains the ultra-thin of thickness 2-3mm
Base material, last drawn method is made alveolate texture, obtains final product paper honeycomb filtrate.
The preparation of modified waste tire rubber powder:To 2 parts of turpentine oil of addition in 50 parts of rubber powder of waste tire and 1 part of hydrogenation
Pentalyn, is sufficiently mixed after microwave treatment 10min under microwave frequency 2450MHz, power output 700W, and be transferred to
30min is stood in 0-5 DEG C of environment, 0.5 part of allyl glycidyl ether, 0.5 part of HPMA and 0.2 part of sulphur is added
Change lard, microwave treatment 10min is continued after being well mixed, being then cooled to 50-55 DEG C of sealing with the cooling rate of 5 DEG C/min protects
Temperature stands 30min, ground to be made micro mist of the fineness less than 20 μm in gained mixture feeding ball mill.
Embodiment 3
Tower biological filter is built using embodiment 1, embodiment 2, reference examples 1 and the made paper honeycomb filtrate of reference examples 2, and
To being processed with batch sanitary sewage, treatment effect is as shown in table 1.
The present invention of table 1 builds the wastewater treatment efficiency of tower biological filter
Project | Embodiment 1 | Embodiment 2 | Reference examples 1 | Reference examples 2 |
COD reduced rates/% | 93.5 | 94.4 | 82.1 | 81.3 |
BOD reduced rates/% | 94.2 | 93.8 | 83.4 | 81.9 |
Ammonia nitrogen reduced rate/% | 95.6 | 94.9 | 79.8 | 80.5 |
Organophosphor reduced rate/% | 92.8 | 93.3 | 80.9 | 81.7 |
Colourity | Basic clarification | Basic clarification | Still show muddiness | Still show muddiness |
Peculiar smell | Substantially tasteless | Substantially tasteless | Slight peculiar smell | Slight peculiar smell |
General principle of the invention and principal character and advantages of the present invention has been shown and described above.The technology of the industry
Personnel it should be appreciated that the present invention is not limited to the above embodiments, simply explanation described in above-described embodiment and specification this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and modifications of the present invention are possible, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appending claims and its
Equivalent thereof.
Claims (5)
1. a kind of tower biological filter builds and uses paper honeycomb filtrate, it is characterised in that be made up of the raw material of following parts by weight:
Pulp powder 20-25 parts, atlapulgite 5-10 parts, PLA 5-10 parts, 3-6 parts of modified waste tire rubber powder, polyethylene
Alcohol resin 3-6 parts, polyethylene glycol oxide 3-6 parts, aromatic modified terpene resin 2-4 parts, diphenyl methane dimaleimide 2-4 parts,
2-4 parts of sepiolite composite powder of nanometer, microwax 1-2 parts, HPO 1-2 parts, Firebrake ZB 0.5-1 parts, N- methylol propylene
Acid amides 0.5-1 parts, diallyl dimethyl ammoniumchloride 0.3-0.5 parts, maleic anhydride 0.05-0.1 parts of compatilizer of grafting.
2. tower biological filter according to claim 1 builds and uses paper honeycomb filtrate, it is characterised in that its preparation method bag
Include following steps:
(1) to polyethylene glycol oxide and aromatic modified terpene resin is added in PLA, it is warming up to the programming rate of 5 DEG C/min
130-135 DEG C of insulation mixing 25min, adds a nanometer sepiolite composite powder, HPO and maleic anhydride grafting compatilizer,
130-135 DEG C of insulation mixing 15min is continuously maintained at, room temperature is then naturally cooled to, material I is obtained final product;
(2) to polyvinyl alcohol resin and diphenyl methane dimaleimide is added in modified waste tire rubber powder, with 5 DEG C/min
Programming rate be warming up to 125-130 DEG C of insulation mixing 20min, add microwax and N hydroxymethyl acrylamide, continue to tie up
Hold in 125-130 DEG C of insulation mixing 15min, room temperature is then cooled to the cooling rate of 10 DEG C/min, obtain final product material II;
(3) to material II, pulp powder, atlapulgite, Firebrake ZB and diallyl dimethyl ammoniumchloride is added in material I, fill
Divide after mixing in feeding extruder, 125-130 DEG C of setting cross-head temperature, one section 90-95 DEG C, two sections 105- of barrel zone temperature
110 DEG C, three sections 125-130 DEG C, extruded, cooling and shaping obtains the Ultrathin substrate of thickness 2-3mm, and last drawn method is made honeybee
Nest shape structure, obtains final product paper honeycomb filtrate.
3. tower biological filter according to claim 1 and 2 builds and uses paper honeycomb filtrate, it is characterised in that:It is described modified
Rubber powder of waste tire is formed by the modified treatment of rubber powder of waste tire, and specific preparation method is:To rubber powder of waste tire
It is middle to add turpentine oil and hydrogenated rosin pentaerythritol ester, it is sufficiently mixed after micro- under microwave frequency 2450MHz, power output 700W
Ripple processes 10min, and is transferred in 0-5 DEG C of environment and stands 30min, adds allyl glycidyl ether, HPMA
And sulfurized lard, be well mixed after continue microwave treatment 10min, then with the cooling rate of 5 DEG C/min be cooled to 50-55 DEG C it is close
Envelope insulation stands 30min, ground to be made micro mist of the fineness less than 20 μm in gained mixture feeding ball mill.
4. tower biological filter according to claim 3 builds and uses paper honeycomb filtrate, it is characterised in that:The junked tire
Rubber powder, turpentine oil, hydrogenated rosin pentaerythritol ester, allyl glycidyl ether, HPMA and sulfurized lard
Amount ratio is 45-50:1-2:0.5-1:0.5-1:0.3-0.5:0.1-0.2.
5. tower biological filter according to claim 1 and 2 builds and uses paper honeycomb filtrate, it is characterised in that the nanometer
Sepiolite composite powder is made up of the raw material of following parts by weight:Sepiolite fibre 5-10 parts, flake asbestos 2-3 parts, ceramic 2-3
Part, 1-2 parts of poly alpha methylstyrene resin, chliorinated polyvinyl chloride 0.5-1 parts, 0.5-1 parts of hexamethylolmelamine pregnancy ether,
Portland cement 0.3-0.5 parts, nano zine oxide 0.1-0.3 parts, its preparation method is:To being added in sepiolite fibre, ceramics are micro-
Powder, poly alpha methylstyrene resin and chliorinated polyvinyl chloride, are sufficiently mixed after microwave frequency 2450MHz, power output 700W
Lower microwave treatment 10min, adds hexamethylolmelamine pregnancy ether and nano zine oxide, continues at microwave after being well mixed
Reason 5min, then adds flake asbestos and portland cement while hot, and in gained mixture feeding nano-level grinder, ground being obtained is received
Rice sepiolite composite powder.