CN106731859A - 陶瓷膜的清洗方法 - Google Patents
陶瓷膜的清洗方法 Download PDFInfo
- Publication number
- CN106731859A CN106731859A CN201611243526.8A CN201611243526A CN106731859A CN 106731859 A CN106731859 A CN 106731859A CN 201611243526 A CN201611243526 A CN 201611243526A CN 106731859 A CN106731859 A CN 106731859A
- Authority
- CN
- China
- Prior art keywords
- ceramic membrane
- recoiled
- water
- cleaning
- clear liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及清洗剂技术领域,具体是涉及一种陶瓷膜的清洗方法。步骤如下:1)酸洗:常温条件下,以稀盐酸溶液为酸洗剂对陶瓷膜进行酸洗,在酸洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;2)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲;3)清洗剂清洗:以陶瓷膜清洗剂对陶瓷膜进行清洗,在清洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;4)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲。本发明的陶瓷膜的清洗剂方法比较简单,清洗效率高,清洗较为彻底,且不会污染陶瓷膜。
Description
技术领域
本发明涉及清洗剂技术领域,具体是涉及一种陶瓷膜的清洗方法。
背景技术
陶瓷膜(ceramic membrane)又称无机陶瓷膜,是以无机陶瓷材料经特殊工艺制备而形成的非对称膜。陶瓷膜分为管式陶瓷膜和平板陶瓷膜两种。管式陶瓷膜管壁密布微孔,在压力作用下,原料液在膜管内或膜外侧流动,小分子物质(或液体)透过膜,大分子物质(或固体)被膜截留,从而达到分离、浓缩、纯化和环保等目的。平板陶瓷膜板面密布微孔,根据在一定的膜孔径范围内,渗透的物质分子直径不同则渗透率不同,以膜两侧的压力差为驱动力,膜为过滤介质,在一定压力作用下,当料液流过膜表面时,只允许水、无机盐、小分子物质透过膜,而阻止水中的悬浮物、胶和微生物等大分子物质通过。
陶瓷膜具有分离效率高、效果稳定、化学稳定性好、耐酸碱、耐有机溶剂、耐菌、耐高温、抗污染、机械强度高、再生性能好、分离过程简单、能耗低、操作维护简便、使用寿命长等众多优势,已经成功应用于食品、饮料、植(药)物深加工、生物医药、发酵、精细化工等众多领域,可用于工艺过程中的分离、澄清、纯化、浓缩、除菌、除盐等。
但是,现有的用于陶瓷膜清洗的清洗剂以及清洗方法,主要存在清洗不彻底,易污染陶瓷膜等缺陷。
发明内容
本发明的目的在于提供一种陶瓷膜清洗剂及其制备方法、陶瓷膜的清洗方法,为实现上述目的,本发明采用了以下技术方案:
一种陶瓷膜清洗剂,由以下重量份的组分制成:
30份去离子水、15.5份氢氧化钾、5份碳酸氢钠、6份十二烷基苯磺酸钠、11.5份次磷酸钙、3份正溴丙烷、15份醋酸丁酯和2.5份3-乙酰氨基-5-甲基异噁唑。
一种陶瓷膜清洗剂的制备方法,步骤如下:
在配制设备中首先加入20份去离子水,接着逐步加入15.5份氢氧化钾、5份碳酸氢钠、6份十二烷基苯磺酸钠、11.5份次磷酸钙、3份正溴丙烷、15份醋酸丁酯和2.5份3-乙酰氨基-5-甲基异噁唑,每添加一种物料后均间隔20分钟,并且保持搅拌状态;最后加入10份去离子水后升温至50℃混合1小时即可得到陶瓷膜清洗剂。
一种陶瓷膜的清洗方法,步骤如下:
1)酸洗:常温条件下,以稀盐酸溶液为酸洗剂对陶瓷膜进行酸洗,在酸洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;
2)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲;
3)清洗剂清洗:以陶瓷膜清洗剂对陶瓷膜进行清洗,在清洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;
4)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲。
本发明的有益效果表现在:
本发明通过加入合理设计的组分,特别是加入2.5份3-乙酰氨基-5-甲基异噁唑,可以提升陶瓷膜清洗剂的整体品质,进一步使陶瓷膜清洗剂的清洗性能提升80%以上。这种制备工艺参数设计合理,加工成本低。另外,这种陶瓷膜的清洗剂方法比较简单,清洗效率高,清洗较为彻底,且不会污染陶瓷膜。
具体实施方式
以下将结合实施例,对本发明进行较为详细的说明。但是,实施例内容仅是对本发明所作的举例和说明,所属本技术领域的技术人员对所描述的具体实施例做各种各样的修改或补充或采用类似的方式替代,只要不偏离发明的构思或者超越本权利要求书所定义的范围,均应属于本发明的保护范围。
实施例1
一种陶瓷膜清洗剂,由以下重量份的组分制成:
30份去离子水、15.5份氢氧化钾、5份碳酸氢钠、6份十二烷基苯磺酸钠、11.5份次磷酸钙、3份正溴丙烷、15份醋酸丁酯和2.5份3-乙酰氨基-5-甲基异噁唑。
一种陶瓷膜清洗剂的制备方法,步骤如下:
在配制设备中首先加入20份去离子水,接着逐步加入15.5份氢氧化钾、5份碳酸氢钠、6份十二烷基苯磺酸钠、11.5份次磷酸钙、3份正溴丙烷、15份醋酸丁酯和2.5份3-乙酰氨基-5-甲基异噁唑,每添加一种物料后均间隔20分钟,并且保持搅拌状态;最后加入10份去离子水后升温至50℃混合1小时即可得到陶瓷膜清洗剂。
实施例2
一种陶瓷膜的清洗方法,步骤如下:
1)酸洗:常温条件下,以稀盐酸溶液为酸洗剂对陶瓷膜进行酸洗,在酸洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;
2)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲;
3)清洗剂清洗:以陶瓷膜清洗剂(实施例1制备)对陶瓷膜进行清洗,在清洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;
4)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲。
Claims (1)
1.一种陶瓷膜的清洗方法,其特征在于:步骤如下:
1)酸洗:常温条件下,以稀盐酸溶液为酸洗剂对陶瓷膜进行酸洗,在酸洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;
2)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲;
3)清洗剂清洗:以陶瓷膜清洗剂对陶瓷膜进行清洗,在清洗的过程中以陶瓷膜过滤的清液为反冲溶液,对陶瓷膜进行反冲;
4)水洗:用水对陶瓷膜进行水洗,在水洗过程中以陶瓷膜过滤的清液为反冲溶液,对该组陶瓷膜进行反冲。