CN106700998A - High-performance epoxy anchor adhesive, as well as preparation method and application thereof - Google Patents
High-performance epoxy anchor adhesive, as well as preparation method and application thereof Download PDFInfo
- Publication number
- CN106700998A CN106700998A CN201510790974.9A CN201510790974A CN106700998A CN 106700998 A CN106700998 A CN 106700998A CN 201510790974 A CN201510790974 A CN 201510790974A CN 106700998 A CN106700998 A CN 106700998A
- Authority
- CN
- China
- Prior art keywords
- component
- parts
- epoxy
- epoxy resin
- anchor adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of anchor adhesives, and discloses a high-performance epoxy anchor adhesive, as well as a preparation method and application thereof. The high-performance epoxy anchor adhesive is prepared from components A and B, wherein the component A is prepared from the following components in parts by mass: 35 to 65 parts of an epoxy resin, 5 to 10 parts of a reactive diluent, 3 to 8 parts of a toughening agent, 25 to 40 parts of an inorganic filler, 0.5 to 1 part of a coupling agent and 5 to 15 parts of a thixotropic agent; the component B is prepared from the following components in parts by mass: 5 to 10 parts of an accelerator, 40 to 80 parts of a curing agent, 20 to 35 parts of the inorganic filler, 0.3 to 0.6 parts of the coupling agent and 5 to 10 parts of the thixotropic agent. The epoxy anchor adhesive prepared by the synergistic effects of each raw material is strong in strength, high in water resistance, acid and alkali corrosion resistance and heat resistance, environment-friendly and pollution-free, and can be applied to steel bar embedding of a building in moisture, hot and acid and alkali corrosion environments and the like, and moreover, a preparation process is simple and easy for industrialization.
Description
Technical field
The invention belongs to anchor adhesive field, anchor member is chemically fixed on drilling by more particularly to one kind
Among high-performance epoxy anchor adhesive and preparation method and application.
Background technology
Anchor adhesive is generally made up of two components, is well mixed two components using preceding, then by hardware anchor
It is scheduled in base material, base material is typically the building being made up of concrete, the material of brick, natural stone etc..
Anchorage technology slowly grows up on the basis of expansion bolt.Expansion bolt can be produced around anchorage zone
Life stress very high, thus when by load action, during in particular by dynamic load function, expanding screw
Bolt is easy to loosen.In order to overcome the shortcoming of expansion bolt, early in nineteen fifty-nine, Germany begins one's study resin glue
Capsule is used to anchor mine anchor pole, and hereafter embedding re-bar technique is greatly developed, and gradually forms a kind of new antidetonation
Anchorage technology.And reinforced concrete structure China industry with civil buildings in occupy extremely important status and
Considerable quantity, with the development and the adjustment of the industrial structure of China's economic construction, generally requires to some
Engineering undergoes technological transformation or concrete structure is reinforced, therefore chemically-planted steel bar glue has obtained rapid hair
Open up and be widely applied.
The most frequently used polymer includes epoxy resin, unsaturated polyester resin, epoxide modified in chemical anchors solid glue
Acrylic resin, ethylene polyacrylates resin, polyurethane resin etc., the curing mechanism of every kind of polymer with
Curing system it is different and different, the characteristic of anchor adhesive is also not quite similar after solidification.Unsaturated polyester resin type,
Main chain is unsaturated polyester (UP), and reactant is styrene, because containing styrene reactant, its alkali resistant acts on energy
Power is low, and at architectural engineering scene, resin can at leisure absorb moisture, cause resin hydrolyzing, so as to interrupt tree
The strand of fat.Vinyl ester resin advantage is high chemical stability/durability, high temperature resistant, but it contains
Carcinogenic styrene, price is higher, and burning-point is low;Acrylic resin can typically accomplish 30min as anchor adhesive
Gel, reaches maximum intensity for 1~2 hour, but its anti-drawing strength is relatively low, it is impossible to meet anchoring resistance to plucking bar
Part.The anchor adhesive humidity resistance of polyurethane type resin is preferable, but the gel time that cold curing needs is more long,
It is 2~3 hours, and anti-drawing strength is poor.
Chinese invention patent CN103339082B discloses a kind of double component mortar and application thereof, describes
A kind of bi-component mortar that chemically anchor member is fixed among drilling, it has curable tree
Fat component and curing agent component, resin contain resin, filler, the promotion of at least one free redical polymerization
Agent, stabilizer and other optional common mortar compositions, described curing agent at least contain a kind of peroxidating
Thing.The hardening time of the bi-component sizing material of the invention is short, can be with rapid curing, but reaction diluent contains cause
Cancer substances styrene and its derivative, it is larger to environment and workmen's harm.
Chinese invention patent CN102190458B is disclosed and is suitable to building purpose, is especially suitable for chemical anchoring
Resin mortar, it comprises the resin Composition of available aliphatic amine and peroxide cure and comprising at least
The hardener component of a kind of peroxide and at least one amine, it is characterised in that the resin Composition includes energy
Carry out the compound of radical polymerization, can with amine react compound, selected from Cu, Mn and Fe compound
Transistion metal compound, at least one inhibitor adjust gel time and with least two reactivity
The bridge joint compound of functional group.The intensity of the anchor adhesive of the invention is big, stability is high, but the receipts of solidfied material
Shrinkage is larger, poor heat resistance, and temperature is too high to increase creep, deformation, causes building steel-bar-planting unstability.
Chinese disclosure CN101619188A discloses a kind of underwater high-strength epoxy anchor adhesive and its preparation
Method.The anchor adhesive is made up of the component of A, B two, component A by epoxy resin, diluent, toughener,
Coupling agent, thixotropic agent, filler, defoamer composition, B component are made up of QS-H205 curing agent.Use
When press 5~8:1 mixed preparing obtains final product underwater epoxy anchor adhesive.The performance test results show that compression strength is 75.1
MPa, tensile strength is 11.3MPa, and bending strength is 59.4MPa, and pull-out test result is
290.6~295.5kN.The water-tolerant of anchor adhesive of the invention, but insufficient strength is big, resistance to elevated temperatures
It is bad.
Chinese disclosure CN1608092A discloses a kind of patent of invention adhesive composition, described
Adhesive can be used in concrete or masonry or to fixing material, including epoxide on concrete or masonry
And curing agent, the curing agent includes at least one aliphatic amine and at least one tertiary amine.The adhesive of this invention
Hardening time it is short, but fatty amine excitant is larger, and the solidfied material for obtaining is firmly crisp, and anti-drawing strength is small, and
And pollution environment.
Chinese invention patent CN103320074B disclose under a kind of low temperature environment rapid curing anchor adhesive and
Its preparation method.The anchor adhesive is made up of A, B, and component A raw material includes that vinylite, vinyl are dilute
Release agent, peroxide initiator, stabilizer, acid anhydrides, filler, B component raw material include vinylite,
Vinyl diluent, accelerator, stabilizer, alkaline earth oxide, filler.Ring of the invention in low temperature
Can solidify under border and reach certain intensity, can be used in winter, but diluent is carcinogen styrene
And its derivative, and not acid-alkali-corrosive-resisting, for a long time facile hydrolysis in wet condition.In addition, the solidfied material
Also non-refractory, at high temperature can creep so that the security reduction of building.
Invention advantage and disadvantage described above are obvious, in order to solve above-mentioned mentioned non-refractory, not humidity
Property, anti acid alkali performance is poor, intensity is poor, pollution environment, the shortcomings of fatty amines corrosivity is strong.The present invention is logical
Cross test of many times and obtained that a kind of acid and alkali-resistance, high temperature resistant, environment friendly and pollution-free, mechanical strength be high, combination property
Epoxy anchor adhesive high.
The content of the invention
In order to overcome the shortcomings and deficiencies of the prior art described above, primary and foremost purpose of the invention is to provide a kind of high
Performance epoxy anchor adhesive.
Another object of the present invention is the preparation method for providing above-mentioned high-performance epoxy anchor adhesive.
Still a further object of the present invention is the application for providing above-mentioned high-performance epoxy anchor adhesive in building steel-bar-planting field.
The purpose of the present invention is realized by following proposal:
A kind of high-performance epoxy anchor adhesive, is made up of the component of A, B two, wherein, in parts by mass, A groups
Part composition be:
The composition of B component is:
Described epoxy resin can be E-51 epoxy resin, bisphenol-s epoxy resin and F-51 epoxy novolac trees
Two or more compounding in fat.
Preferably, described epoxy resin is E-51 epoxy resin, bisphenol-s epoxy resin and F-51 phenolic aldehyde
The compounding of epoxy resin three.
Novolac epoxy resin is because, containing the epoxy radicals of more than 2, reactivity is big, with bis-phenol in its molecule
A epoxy resin is compared, and its solidfied material crosslink density is high, close structure, have good heat resistance and preferably
Mechanical strength.Bisphenol-s epoxy resin has thermal deformation temperature higher than bisphenol f type epoxy resin solidfied material
Degree and more preferable heat resistance.Three kinds of epoxy resin are used cooperatively, advantage and disadvantage are complementary, the epoxy anchor of preparation
Solid glue combination property is more excellent.
It is furthermore preferred that E-51 epoxy resin used, bisphenol-s epoxy resin and F-51 novolac epoxy resins
Mass ratio be (15~25):(10~20):(10~20).
Described reactive diluent can be the low molecule epoxide with reaction terminal epoxy groups group.
Because epoxy resin viscosity is larger, the viscosity that different epoxy product needs is different, reactive diluent by
Can be reacted with amine curing agent in containing epoxide group, using diluent come influence liquidity, so as to increase
The mechanical property of anchor adhesive.
Preferably, described reactive diluent be butanediol diglycidyl ether, diglycidylaniline and
At least one in phenyl glycidyl ether.
Described toughener can be polyurethane elastomer.
Because the soft segment of polyurethane can be continuous through in resin phase, " IPN ", " Semi-IPN " are formed
Special networks structure, produces positive coopertive effect, with polyurethane elastomer flexibilizing epoxy tree with epoxy networks
Fat, can be improved epoxy resin cure material mechanical performance.
The inorganic filler in inorganic filler and B component in described component A can be talcum powder, quartz
At least one in sand, portland cement, molten silicon stone flour, the wherein particle diameter of inorganic filler are 300~2000
Mesh.The inorganic filler in inorganic filler and B component in component A can be the same or different.
The main purpose for adding filler is to improve mechanical property, improves heat conductivity, improves the resistance to of solidfied material
Hot, hygroscopicity.The improvement effect of filler depends on property, the size of particle and the consumption of filler itself
How much.
Preferably, the inorganic filler in described component A be talcum powder, quartz sand, portland cement,
Two or more compounding in molten silicon stone flour, the wherein particle diameter of inorganic filler are 300~2000 mesh.
The coupling agent in coupling agent and B component in described component A can be gamma-aminopropyl-triethoxy
In silane (KH-550) and γ-glycidyl ether oxygen propyl trimethoxy silicane (KH-560) at least one
Kind, the coupling agent in coupling agent and B component in component A can be the same or different.
Contain Inorganic functional groups and organo-functional group in silane coupler, the former reacts with inorganic filler, the latter
There is bonding reaction with epoxy resin, coupling agent plays intermediate layer, filler surface is processed, from
And improve the enhancing modified effect of filler.
The thixotropic agent in thixotropic agent and B component in described component A is aerosil.
Thixotropic agent is a kind of insoluble additives with very high surface area.The surface of aerosil and thing
There is the possibility for forming hydrogen bond between material parent.Tridimensional network can be mutually piled between particle.It is quiet
During state, viscosity is larger, once can significantly be declined by shearing force material viscosity.
Described accelerator is tertiary amines accelerator.
Preferably, described accelerator is 2,4,6- tri- (dimethylamino methyl) phenol (DMP-30).
Described curing agent can be at least one in polyamide polyamine curing agent and pnenolic aldehyde amine hardener.
Described polyamide polyamine curing agent can be in polyamide 6 50, polyamide 6 51 and kymene 00
At least one.
Low molecular polyamides polyamine is long with epoxy resin component working life, volatility is small, almost non-toxic
Property, to skin irritation very little.And the polyamide of liquid in the molecule thereof containing the big alkyl of hydrophobicity and
Some hydrophilic amidos, with very strong hygroscopicity.
Described pnenolic aldehyde amine hardener can be at least one in the pnenolic aldehyde amine hardener of T31, TZ series,
The pnenolic aldehyde amine hardener of wherein TZ series includes TZ 50, TZ 500, TZ 550 and TZ 600.Phenolic aldehyde amine
Curing agent, small toxicity pollutes small, can be with cold curing, and solidfied material intensity is high, good mechanical performance.
Preferably, described curing agent is the compounding of polyamide polyamine curing agent and pnenolic aldehyde amine hardener.It is poly-
Amide hardener water resistance is strong, pnenolic aldehyde amine hardener mechanical strength is high, and two kinds of curing agent compounding use advantages are mutual
Mend, the epoxy anchor adhesive of high comprehensive performance can be obtained.
A kind of preparation method of above-mentioned high-performance epoxy anchor adhesive, comprises the following steps:
(1) preparation of component A:Epoxy resin, reactive diluent, coupling agent, toughener are mixed,
Stir;Inorganic filler is added, is well mixed;Thixotropic agent mixing is added, is stirred, obtain A groups
Part;
(2) preparation of B component:Accelerator, curing agent, coupling agent are mixed, is stirred;Add
Inorganic filler, is well mixed;Thixotropic agent mixing is added, is stirred, obtain B component;
(3) component of A, B two that will be obtained encapsulate respectively it is standby, when using, the component A that will obtain and
B component presses certain mass than well mixed, obtains underwater curing high-performance epoxy anchor adhesive.
The mass ratio of component A and B component described in step (3) can be (2~4):1.
Application of the described high-performance epoxy anchor adhesive in terms of building steel-bar-planting.
Mechanism of the invention is:
Epoxy anchor adhesive of the invention, using the bisphenol-s epoxy resin of weatherability, novolac epoxy resin F-51
And the compounding of epoxy resin E-51, the compounding of these three epoxy resin can cooperate with and improve the resistance to of solidfied material
Hot, anti-drawing strength;Using polyurethane elastomer as toughener, solidfied material can be effectively formed mutually
Network structure is worn, increases its toughness and bending strength;The talcum powder of use, quartz sand, cement, melting
The inorganic fillers such as Cab-O-sil can effectively improve humidity, acid-alkali-corrosive-resisting and mechanical property.Use
Polyamide polyamine and pnenolic aldehyde amine hardener can improve water resistance and corrosion resistance, to increase its antifatigue strong
Degree.The cooperative effect of each raw material more than, the epoxy anchor adhesive prepared have high intensity, water resistance,
It is acid-alkali-corrosive-resisting, heat resistance, environment friendly and pollution-free.Can be applied under the environment such as moist sweltering heat, acid and alkali corrosion
Building steel-bar-planting.
The present invention has the following advantages and beneficial effect relative to prior art:
Epoxy anchor adhesive obtained by the present invention has mechanical strength higher, stronger humidity, acid and alkali-resistance rotten
The characteristic such as erosion, high temperature resistant, ageing-resistant, mechanical strength is high, excellent combination property, can be used for building steel-bar-planting.
And environmentally safe, preparation process is simple, is suitable for industrialized production.
Specific embodiment
With reference to embodiment, the present invention is described in further detail, but embodiments of the present invention are not limited
In this.
Agents useful for same is commercially available in embodiment.
Embodiment 1
(1) preparation of component A:By mass parts by 15 parts of epoxy resin E-51 (Guangzhou Wei Linaization
Work Co., Ltd), 18 parts of novolac epoxy resin F-51 (Guangzhou Wei Lina Chemical Co., Ltd.s), 18 parts
Bisphenol-s epoxy resin (Guangzhou Wei Lina Chemical Co., Ltd.s), 5 parts of butanediol 2-glycidyl
Ether (the husband's chemical industry goods and materials Co., Ltd of Guangzhou one), 0.5 part of KH-550 (the Guangzhou limited public affairs of Jing Gang chemical industry
Department), 5 parts of polyurethane elastomer (Anhui An great Hua Tai new materials Science and Technology Ltd.) mix it is equal
It is even;Add 10 parts of inorganic filler talcum powder (2000 mesh) (Guangzhou Rong Yue industrial chemicals Co., Ltd)
Quartz sand (300 mesh) (Guangzhou Rong Yue industrial chemicals Co., Ltd) with 20 parts is well mixed;Then again
8.5 parts of aerosil (opening up hundred million Co., Ltds in Guangzhou) is added, mixing and stirring obtains final product A groups
Part;
(2) preparation of B component:It is (wide 5 parts of 2,4,6- tri- (dimethylamino methyl) phenol by mass fraction
Zhou Jing ridges Chemical Co., Ltd.), 30 parts of polyamide 6s 50 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 30 parts
Phenolic aldehyde amine curing agent T 31 (Guangzhou Qi Hua Chemical Co., Ltd.s), 0.3 part of KH-550 (Guang Zhoujing
Ridge Chemical Co., Ltd.) mixing and stirring;Add 25 parts portland cement (300 mesh) (Hainan
Hai Yuda Industrial Co., Ltd.s) it is well mixed, the aerosil for then adding 9.7 parts (is opened up in Guangzhou
Hundred million Co., Ltds), mixing and stirring obtains B component;
(3) A, B component are encapsulated respectively it is standby, when using by A, B component in mass ratio be 2:1
Extrude respectively, be well mixed, be placed in the hole of anchoring, then Ribbed Bar to be anchored is rotatably inserted into hole,
Stand solidification and obtain final product high-performance epoxy anchor adhesive.
Embodiment 2
(1) preparation of component A:By mass parts by 15 parts of epoxy resin E-51 (Guangzhou Wei Linaization
Work Co., Ltd), 10 parts of novolac epoxy resin F-51 (Guangzhou Wei Lina Chemical Co., Ltd.s), 10 parts
Bisphenol-s epoxy resin (Guangzhou Wei Lina Chemical Co., Ltd.s), 10 parts of butanediol 2-glycidyl
Ether, 0.5 part of KH-550,4 parts of polyurethane elastomer (big Thailand of the China new material limited public affairs of science and technology of Anhui peace
Department) mixing and stirring;Add 15 parts inorganic filler talcum powder (2000 mesh) and 10 parts molten
Melt Cab-O-sil (300 mesh) to be well mixed;Then the aerosil for adding 15 parts (opens up hundred million in Guangzhou
Co., Ltd), mixing and stirring obtains final product component A;
(2) preparation of B component:It is (wide 6 parts of 2,4,6- tri- (dimethylamino methyl) phenol by mass fraction
Zhou Jing ridges Chemical Co., Ltd.), 10 parts of polyamide 6s 50 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 30 parts
Phenolic aldehyde amine curing agent TZ 550 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 0.5 part of KH-550 mixing are stirred
Mix uniform;Again to the portland cement (300 mesh) and 15 parts of fused silicas that 20 parts are added in resulting material
Powder (300 mesh) is well mixed;Then 5 parts of aerosil (opening up hundred million Co., Ltds in Guangzhou) is added,
Mixing and stirring, obtains B component;
(3) A, B component are encapsulated respectively it is standby, when using, by A, B component in mass ratio be 3:1
Extrude respectively, be well mixed, be placed in the hole of anchoring, then Ribbed Bar to be anchored is rotatably inserted into hole,
Stand solidification and obtain final product high-performance epoxy anchor adhesive.
Embodiment 3
(1) preparation of component A:By mass parts by 25 parts of epoxy resin E-51 (Guangzhou Wei Linaization
Work Co., Ltd), 20 parts of novolac epoxy resin F-51 (Guangzhou Wei Lina Chemical Co., Ltd.s), 20 parts
Bisphenol-s epoxy resin (Guangzhou Wei Lina Chemical Co., Ltd.s), 8 parts of diglycidylaniline,
0.7 part of KH-560,7 parts of polyurethane elastomer (Anhui An great Hua Tai new materials Science and Technology Ltd.)
Mixing and stirring;Add 20 parts of inorganic filler talcum powder (2000 mesh) and 20 parts of molten silicon
Stone flour (300 mesh) is well mixed;Then (Guangzhou opens up hundred million to be had to add 9.3 parts of aerosil agent
Limit company), mixing and stirring obtains final product component A;
(2) preparation of B component:It is 10 parts of 2,4,6- tri- (dimethylamino methyl) phenol by mass fraction
(Guangzhou Jing Gang Chemical Co., Ltd.s), 20 parts of polyamide 6s 51 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 30
Part phenolic aldehyde amine curing agent TZ 600 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 0.3 part of KH-560 mixing
Stir;Add 11 parts portland cement (300 mesh) and 10 parts of molten silicon stone flours (300 mesh)
It is well mixed;Then 8.7 parts of aerosil (opening up hundred million Co., Ltds in Guangzhou) is added, mixing is stirred
Mix uniform, obtain B component;
(3) A, B component are encapsulated respectively it is standby, when using by A, B component in mass ratio be 2:1
Extrude respectively, be well mixed, be placed in the hole of anchoring, then Ribbed Bar to be anchored is rotatably inserted into hole,
Stand solidification and obtain final product high-performance epoxy anchor adhesive.
Embodiment 4
(1) preparation of component A:By mass parts by 17 parts of epoxy resin E-51 (Guangzhou Wei Linaization
Work Co., Ltd), 15 parts of novolac epoxy resin F-51 (Guangzhou Wei Lina Chemical Co., Ltd.s), 10 parts
Bisphenol-s epoxy resin (Guangzhou Wei Lina Chemical Co., Ltd.s), 6 parts of phenyl glycidyl ether,
0.7 part of KH-560,5 parts of polyurethane elastomer (Anhui An great Hua Tai new materials Science and Technology Ltd.)
Mixing and stirring;Add 10 parts of inorganic filler talcum powder (2000 mesh) and 25 parts of molten silicon
Stone flour (300 mesh) is well mixed;Then (Guangzhou opens up hundred million to be had to add 11.3 parts of aerosil agent
Limit company), mixing and stirring obtains final product component A;
(2) preparation of B component:It is by mass parts that 6 parts of 2,4,6- tri- (dimethylamino methyl) phenol are (wide
Zhou Jing ridges Chemical Co., Ltd.), 28 parts of polyamide 6s 50 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 30 parts
Phenolic aldehyde amine curing agent TZ 50 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 0.6 part of KH-560 mixing are stirred
Mix uniform;Add 15 parts portland cement (300 mesh) and 10 parts of molten silicon stone flours (300 mesh)
It is well mixed;Then 8.4 parts of aerosil (opening up hundred million Co., Ltds in Guangzhou) is added, mixing is stirred
Mix uniform, obtain B component;
(3) A, B component are encapsulated respectively it is standby, when using by A, B component in mass ratio be 4:1
Extrude respectively, be well mixed, be placed in the hole of anchoring, then Ribbed Bar to be anchored is rotatably inserted into hole,
Stand solidification and obtain final product high-performance epoxy anchor adhesive.
Embodiment 5
(1) preparation of component A:By mass parts by 16 parts of epoxy resin E-51 (Guangzhou Wei Linaization
Work Co., Ltd), 13 parts of novolac epoxy resin F-51 (Guangzhou Wei Lina Chemical Co., Ltd.s), 15 parts
Bisphenol-s epoxy resin (Guangzhou Wei Lina Chemical Co., Ltd.s), 7 parts of phenyl glycidyl ether,
0.7 part of KH-560,7 parts of polyurethane elastomer (Anhui An great Hua Tai new materials Science and Technology Ltd.)
Mixing and stirring;Add 15 parts of inorganic filler talcum powder (2000 mesh) and 20 parts of molten silicon
Stone flour (300 mesh) is well mixed;Then (Guangzhou opens up hundred million to be had to add 6.3 parts of aerosil agent
Limit company), mixing and stirring obtains final product component A;
(2) preparation of B component:It is by mass parts that 8 parts of 2,4,6- tri- (dimethylamino methyl) phenol are (wide
Zhou Jing ridges Chemical Co., Ltd.), 25 parts of polyamide 6s 51 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 35 parts
Phenolic aldehyde amine curing agent TZ 500 (Guangzhou first month of the lunar year Chemical Co., Ltd.), 0.6 part of KH-560 mixing are stirred
Mix uniform;Add 15 parts portland cement (300 mesh) and 10 parts of molten silicon stone flours (300 mesh)
It is well mixed, 8.4 parts of aerosil (opening up hundred million Co., Ltds in Guangzhou) is then added, mixing is stirred
Mix uniform, obtain B component;
(3) A, B component are encapsulated respectively it is standby, when using by A, B component in mass ratio be 3.5:1,
Extrude respectively, be well mixed, be placed in the hole of anchoring, then Ribbed Bar to be anchored is rotatably inserted into hole,
Stand solidification and obtain final product high-performance epoxy anchor adhesive.
After the high-performance epoxy anchor adhesive of gained in embodiment 1~5 is fully cured into 48h, to its progressive
Can test, test result is as shown in table 1 below, and wherein bending strength test refers to GB/T2567-2008;It is anti-
Compressive Strength test reference GB/T2567-2008;Tensile strength test refers to GB/T2567-2008;C30 is mixed
Solidifying soil pull-out test refers to GB/T50367-2006.
Performance test data in the embodiment 1~5 of table 1 after the high-performance epoxy anchor adhesive curing 48h of gained
From table 1 it follows that the present invention is by the compounding of various epoxy resin, polyamide curing agent and phenol
The compounding of aldehyde amine hardener, the inorganic filler of addition multiple efficacies have obtained high-performance epoxy anchor adhesive, by it
Compared with the anchor adhesive mentioned in commercially available and background technology, anchor adhesive mechanical property of the invention is excellent
Good, shear strength is high, ambient temperature curable, short hardening time, acid-alkali-corrosive-resisting, humidity, environmental protection without dirt
Dye, excellent combination property.
Above-described embodiment is the present invention preferably implementation method, but embodiments of the present invention do not receive above-mentioned reality
Apply the limitation of example, it is other it is any without departing from the change made under Spirit Essence of the invention and principle, modification,
Substitute, combine, simplify, should be equivalent substitute mode, be included within protection scope of the present invention.
Claims (8)
1. a kind of high-performance epoxy anchor adhesive, is made up of the component of A, B two, it is characterised in that:By quality
Part is counted, and the composition of component A is:
The composition of B component is:
2. high-performance epoxy anchor adhesive according to claim 1, it is characterised in that:
Described epoxy resin is E-51 epoxy resin, bisphenol-s epoxy resin and F-51 novolac epoxy resins
In two or more compounding;
Described reactive diluent is the low molecule epoxide with reaction terminal epoxy groups group;
Described toughener is polyurethane elastomer;
The inorganic filler in inorganic filler and B component in described component A be talcum powder, quartz sand,
At least one in portland cement, molten silicon stone flour, the mesh of particle diameter 300~2000 of wherein inorganic filler;
The coupling agent in coupling agent and B component in described component A is in KH-550 and KH-560
At least one;
The thixotropic agent in thixotropic agent and B component in described component A is aerosil;
Described accelerator is tertiary amines accelerator;
Described curing agent is at least one in polyamide polyamine curing agent and pnenolic aldehyde amine hardener.
3. high-performance epoxy anchor adhesive according to claim 1, it is characterised in that:
Described epoxy resin is E-51 epoxy resin, bisphenol-s epoxy resin and F-51 novolac epoxy resins
The compounding of three;
Described reactive diluent is butanediol diglycidyl ether, diglycidylaniline and phenyl glycidyl
At least one of glycerin ether;
Inorganic filler in described component A is talcum powder, quartz sand, portland cement, fused silica
Two or more compounding in powder, the wherein particle diameter of inorganic filler are 300~2000 mesh;
Described accelerator is 2,4,6- tri- (dimethylamino methyl) phenol;
Described curing agent is the compounding of polyamide polyamine curing agent and pnenolic aldehyde amine hardener.
4. a kind of high-performance epoxy anchor adhesive according to Claims 2 or 3, it is characterised in that:
The mass ratio of E-51 epoxy resin, bisphenol-s epoxy resin and F-51 novolac epoxy resins used is
(15~25):(10~20):(10~20).
5. the high-performance epoxy anchor adhesive according to Claims 2 or 3, it is characterised in that:
Described polyamide polyamine curing agent is in polyamide 6 50, polyamide 6 51 and kymene 00
It is at least one;
Described pnenolic aldehyde amine hardener is at least one in the pnenolic aldehyde amine hardener of T31, TZ series, its
The pnenolic aldehyde amine hardener of middle TZ series includes TZ 50, TZ 500, TZ 550 and TZ 600.
6. the preparation method of high-performance epoxy anchor adhesive according to claim 1, it is characterised in that bag
Include following steps:
(1) preparation of component A:Epoxy resin, reactive diluent, coupling agent, toughener are mixed,
Stir;Inorganic filler is added, is well mixed;Thixotropic agent mixing is added, is stirred, obtain A groups
Part;
(2) preparation of B component:Accelerator, curing agent, coupling agent are mixed, is stirred;Add
Inorganic filler, is well mixed;Thixotropic agent mixing is added, is stirred, obtain B component;
(3) component A and B component that will be obtained encapsulate respectively it is standby, when using, by component A and B
Component presses certain mass than well mixed, obtains high-performance epoxy anchor adhesive.
7. the preparation method of high-performance epoxy anchor adhesive according to claim 6, it is characterised in that:
The mass ratio of component A and B component described in step (3) is (2~4):1.
8. application of the high-performance epoxy anchor adhesive according to claim 1 in terms of building steel-bar-planting.