CN106700755A - Coating for building external wall - Google Patents
Coating for building external wall Download PDFInfo
- Publication number
- CN106700755A CN106700755A CN201611239208.4A CN201611239208A CN106700755A CN 106700755 A CN106700755 A CN 106700755A CN 201611239208 A CN201611239208 A CN 201611239208A CN 106700755 A CN106700755 A CN 106700755A
- Authority
- CN
- China
- Prior art keywords
- percent
- coating
- emulsion
- exterior wall
- building exterior
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a coating for a building external wall. The coating is prepared from the following raw materials in percentage by weight: 15 to 20 percent of fluorocarbon emulsion, 6 to 10 percent of organic silicon modified crylic acid emulsion, 6 to 10 percent of organic fluorine modified crylic acid emulsion, 6 to 12 percent of cellular quartz powder, 25 to 36 percent of anatase nano TiO2, 5 to 10 percent of nano zinc oxide. 1 to 3 percent of a compatilizer, 1 to 3 percent of a defoaming agent, 1 to 4 percent of a dispersing agent, 2 to 6 percent of hydroxyethyl cellulose, 1 to 3 percent of a thickener, 1 to 3 percent of a PH regulator, 1 to 2 percent of an antifreezing agent and 3 to 9 percent of water. The coating is plump and fine in paint film, has a bright color, is high in leveling property, high in adhesive force, nontoxic, long-acting, antibacterial, environmentally friendly, and high in weather resistance, stain resistance and chemical stability, and can achieve long-term effective cleaning.
Description
Technical field
The present invention relates to building decoration field, and in particular to a kind of coating used for building exterior wall.
Background technology
Existing coating used for building exterior wall is mainly fluorocarbon coating, and fluorocarbon coating refers to fluororesin as main film forming substance
Coating, also known as F-C paint, fluoro coatings, fluorine resin coating etc..Among various coating, fluorine resin coating is due to the fluorine unit for introducing
Plain electronegativity is big, and carbon-fluorine bond can be strong, with especially advantageous properties：Weatherability, heat resistance, lower temperature resistance, chemically-resistant medicine
Moral character, and with unique non-stick and low abrasiveness.Fluorocarbon coating as the multifunctional coating with super weather resisteant, in light
Damp conservation rate, fade resistant, Corrosion Protection aspect, fully meet the use requirement of client, but in the long-term dicoration side of coating
Face, conventional fluorocarbon coating kind could not also reach a high level, fluorocarbon coating after some time of use, meeting
Produce rainprint pollution.In actual application process, fluorocarbon coating has relatively low surface relative to other coating varieties in fact
For, pollution is not easily susceptible to, even if pollutant is also bonded loosely in coating surface, it is easy to be easily removed.But make for a long time
The low-surface-energy of film can not well prevent the generation of rainprint under the conditions of.Conversely with the continuous accumulation of spot, film
Original decorative effect can be deteriorated, and lose original gay colours, and blackening is graying, form black, the yellow spot of various strips,
If do not cleaned manually, dicoration can be gradually lost.Therefore, fluorocarbon coating has property easy to clean, rather than self-cleaning property.In order to reach
To self-cleaning property, the building coating for having stain resistance in current China market is added by hydrophobic of modified organic silicone resin
The coating of agent.This modified organic silicone resin addition low-surface-energy small molecule is put forward the stain resistant ability of organosilicon coating
Height, but this coating stain resistance over time, reduced rapidly due to the loss of low-surface-energy small molecule, or even
Lose, still reach to less than effectively self-cleaning.
The content of the invention
It is an object of the present invention to provide a kind of coating used for building exterior wall, paint film is plentiful, exquisiteness, and beautiful in colour, good leveling property is attached
Put forth effort strong, nontoxic, long acting antibiotic, environmental protection, high-weatherability, high dirt resistance, chemical stability is good, and reaches permanently effective
Automatically cleaning.
In order to realize the above object the technical solution adopted by the present invention is：A kind of coating used for building exterior wall, according to weight hundred
Dividing the raw material of ratio includes：
Fluorine carbon emulsion 15 ~ 20%,
Organosilicon-modified acrylic emulsion 6 ~ 10%,
Organic fluoride modified acrylic acid emulsion 6 ~ 10%,
Porous konilite 6 ~ 12%,
Dichloride in anatase type TiO225 ~ 36%,
Nano zine oxide 5 ~ 10%,
Compatilizer 1 ~ 3%,
Defoamer 1 ~ 3%,
Dispersant 1 ~ 4%,
Hydroxyethyl cellulose 2 ~ 6%,
Thickener 1 ~ 3%,
PH conditioning agents 1 ~ 3%,
Antifreezing agent 1 ~ 2%,
Water 3 ~ 9%.
Preferably, described coating used for building exterior wall, includes according to the raw material of percentage by weight：
Fluorine carbon emulsion 18%,
Organosilicon-modified acrylic emulsion 8%,
Organic fluoride modified acrylic acid emulsion 8%,
Porous konilite 8%,
Dichloride in anatase type TiO230%,
Nano zine oxide 7%,
Compatilizer 2%,
Defoamer 2%,
Dispersant 3%,
Hydroxyethyl cellulose 4%,
Thickener 2%,
PH conditioning agents 1%,
Antifreezing agent 1%,
Water 6%.
Further, described compatilizer is perfluor silicone resin.
Further, described thickener polyvinyl alcohol.
Further, described dispersant is polyvinylpyrrolidone.
Further, described defoamer is CF-246 defoamers.
Further, described antifreezing agent is propane diols.
Further, 5% pure acrylic latex is contained in described fluorine carbon emulsion.
The technical effects of the invention are that：The present invention is using dichloride in anatase type TiO2Material, the main machine of its polluting proofing property
Reason shows two aspects：One is dichloride in anatase type TiO2The photocatalytic Degradation of itself, under light illumination nano titanium oxide
Constantly decompose and be gathered in the organic matter of coating surface, the spot of absorption is lost adhesive effect with coating；Two is nano-silica
Change the addition of titanium, hydrophilic surface can be produced, completely cut off oiliness pollutant, mitigate rainprint pollution.Use porous konilite be
Volcanic ash sedimentary rock, its natural particle diameter is thin（0.5 μm or so）, even particle distribution, specific surface area is big, with electronic microscope image
See, its surface is entirely nano level mesoporous.Periporate quartz surfaces contain a number of hydroxyl（-OH）- silanol.As polarity
Functional group, is favorably improved the adhesive force and caking property of coating.On the other hand, due to the presence of hydroxyl, it is easier to by coupling
Agent be surface-treated, increase its crosslinking, the effect of reinforcement, that is, increase product physical and mechanical property improve again film stretching it is strong
Degree and the attachment to collective, caking property.The nano zine oxide of use has high-specific surface area, high activity, specific physical property, cause
Make its environment to external world（Such as temperature, light, moisture）Very sensitive, the change of external environment can rapidly cause the notable of its resistance
Change, it has the characteristic of semiconductor, with electric conductivity higher, thus can play electrostatic screen, and anti-static effect is fine,
This is that it is used for an advantage of the present invention.Additionally, such nano zine oxide can make coating have shielding ultraviolet rays, absorb it is red
Outside line and fungus and mildew resistance are acted on.Using hydroxyethyl cellulose as a kind of surfactant of nonionic, with thickening, hang
Floating, bonding, floatingization, film forming, dispersion, water conservation and offer protective coating colloid action.The coating obtained according to said ratio, paint film
Plentiful, exquisiteness, beautiful in colour, good leveling property, adhesive force is strong, nontoxic, long acting antibiotic, environmental protection, high-weatherability, high dirt resistance
Property, chemical stability is good.Can be under long-term conditions, it is not necessary to artificial cleaning and oneself can maintain good clean conditions requirement from
Cleaning.
Specific embodiment
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the invention, rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under the premise of creative work is not made, all
Belong to the scope of protection of the invention.
Embodiment 1：A kind of coating used for building exterior wall, includes according to the raw material of percentage by weight：
Fluorine carbon emulsion 18%,
Organosilicon-modified acrylic emulsion 8%,
Organic fluoride modified acrylic acid emulsion 8%,
Porous konilite 8%,
Dichloride in anatase type TiO230%,
Nano zine oxide 7%,
Compatilizer 2%,
Defoamer 2%,
Dispersant 3%,
Hydroxyethyl cellulose 4%,
Thickener 2%,
PH conditioning agents 1%,
Antifreezing agent 1%,
Water 6%.
Further, described compatilizer is perfluor silicone resin.
Further, described thickener polyvinyl alcohol.
Further, described dispersant is polyvinylpyrrolidone.
Further, described defoamer is CF-246 defoamers.
Further, described antifreezing agent is propane diols.
Further, 5% pure acrylic latex is contained in described fluorine carbon emulsion.
The defoamer of above-mentioned score, dispersant, thickener, defoamer, antifreezing agent etc. are dispersed in water and are obtained processing and is helped
Agent, then adds porous konilite, dichloride in anatase type TiO according to the above ratio2, other slurries such as fluorine carbon emulsion, in dispersion machine
High-speed stirred is disperseed, and is added above-mentioned processing aid and is sufficiently stirred for, and finally adds PH conditioning agents to adjust the pH value of coating.According to
The coating that said ratio is obtained, paint film is plentiful, exquisiteness, beautiful in colour, good leveling property, and adhesive force is strong, and nontoxic, long acting antibiotic is green
Colour circle is protected, and high-weatherability, high dirt resistance, chemical stability is good.Can be under the long-term conditions of at least 5 years, it is not necessary to artificial clear
Wash and the automatically cleaning of energy oneself the good clean conditions requirement of maintenance.
Embodiment 2：A kind of coating used for building exterior wall, includes according to the raw material of percentage by weight：
Fluorine carbon emulsion 15%,
Organosilicon-modified acrylic emulsion 7%,
Organic fluoride modified acrylic acid emulsion 8%,
Porous konilite 10%,
Dichloride in anatase type TiO235%,
Nano zine oxide 8%,
Compatilizer 1%,
Defoamer 1%,
Dispersant 2%,
Hydroxyethyl cellulose 5%,
Thickener 1%,
PH conditioning agents 1%,
Antifreezing agent 1%,
Water 5%.
Further, described compatilizer is perfluor silicone resin.
Further, described thickener polyvinyl alcohol.
Further, described dispersant is polyvinylpyrrolidone.
Further, described defoamer is CF-246 defoamers.
Further, described antifreezing agent is propane diols.
Further, 5% pure acrylic latex is contained in described fluorine carbon emulsion.
The coating obtained according to said ratio, paint film is plentiful, exquisiteness, beautiful in colour, good leveling property, and adhesive force is strong, nontoxic,
Long acting antibiotic, environmental protection, high-weatherability, high dirt resistance, chemical stability is good.Can be under the long-term conditions of at least 5 years, no
Need the automatically cleaning of artificial cleaning and the good clean conditions requirement of energy oneself maintenance.
Embodiment 3：A kind of coating used for building exterior wall, includes according to the raw material of percentage by weight：
Fluorine carbon emulsion 16%,
Organosilicon-modified acrylic emulsion 8%,
Organic fluoride modified acrylic acid emulsion 7%,
Porous konilite 10%,
Dichloride in anatase type TiO235%,
Nano zine oxide 8%,
Compatilizer 1%,
Defoamer 1%,
Dispersant 2%,
Hydroxyethyl cellulose 5%,
Thickener 1%,
PH conditioning agents 1%,
Antifreezing agent 1%,
Water 4%.
Further, described compatilizer is perfluor silicone resin.
Further, described thickener polyvinyl alcohol.
Further, described dispersant is polyvinylpyrrolidone.
Further, described defoamer is CF-246 defoamers.
Further, described antifreezing agent is propane diols.
Further, 5% pure acrylic latex is contained in described fluorine carbon emulsion.
The coating obtained according to said ratio, paint film is plentiful, exquisiteness, beautiful in colour, good leveling property, and adhesive force is strong, nontoxic,
Long acting antibiotic, environmental protection, high-weatherability, high dirt resistance, chemical stability is good.Can be under the long-term conditions of at least 5 years, no
Need the automatically cleaning of artificial cleaning and the good clean conditions requirement of energy oneself maintenance.
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of without departing substantially from spirit or essential attributes of the invention, the present invention can be in other specific forms realized.
Claims (8)
1. a kind of coating used for building exterior wall, it is characterised in that the raw material according to percentage by weight includes：
Fluorine carbon emulsion 15 ~ 20%,
Organosilicon-modified acrylic emulsion 6 ~ 10%,
Organic fluoride modified acrylic acid emulsion 6 ~ 10%,
Porous konilite 6 ~ 12%,
Dichloride in anatase type TiO225 ~ 36%,
Nano zine oxide 5 ~ 10%,
Compatilizer 1 ~ 3%,
Defoamer 1 ~ 3%,
Dispersant 1 ~ 4%,
Hydroxyethyl cellulose 2 ~ 6%,
Thickener 1 ~ 3%,
PH conditioning agents 1 ~ 3%,
Antifreezing agent 1 ~ 2%,
Water 3 ~ 9%.
2. coating used for building exterior wall according to claim 1, it is characterised in that the raw material according to percentage by weight includes：
Fluorine carbon emulsion 18%,
Organosilicon-modified acrylic emulsion 8%,
Organic fluoride modified acrylic acid emulsion 8%,
Porous konilite 8%,
Dichloride in anatase type TiO230%,
Nano zine oxide 7%,
Compatilizer 2%,
Defoamer 2%,
Dispersant 3%,
Hydroxyethyl cellulose 4%,
Thickener 2%,
PH conditioning agents 1%,
Antifreezing agent 1%,
Water 6%.
3. coating used for building exterior wall according to claim 1 and 2, it is characterised in that described compatilizer is perfluor silica
Alkane resin.
4. coating used for building exterior wall according to claim 1 and 2, it is characterised in that described thickener polyvinyl alcohol.
5. coating used for building exterior wall according to claim 1 and 2, it is characterised in that described dispersant is polyethylene pyrrole
Pyrrolidone.
6. coating used for building exterior wall according to claim 1 and 2, it is characterised in that described defoamer disappears for CF-246
Infusion.
7. coating used for building exterior wall according to claim 1 and 2, it is characterised in that described antifreezing agent is propane diols.
8. coating used for building exterior wall according to claim 1 and 2, it is characterised in that pure containing 5% in described fluorine carbon emulsion
Acrylic emulsion.