CN106700730A - Solvent type ink-jet thermal sublimation printing ink - Google Patents
Solvent type ink-jet thermal sublimation printing ink Download PDFInfo
- Publication number
- CN106700730A CN106700730A CN201611158902.3A CN201611158902A CN106700730A CN 106700730 A CN106700730 A CN 106700730A CN 201611158902 A CN201611158902 A CN 201611158902A CN 106700730 A CN106700730 A CN 106700730A
- Authority
- CN
- China
- Prior art keywords
- parts
- ink
- resin
- solvent
- sublimation printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses solvent type ink-jet thermal sublimation printing ink. The solvent type ink-jet thermal sublimation printing ink is prepared from 5-30 parts of disperse dye sizing agent, 2-20 parts of resin, 2-15 parts of hydroxymethyl cellulose, 1-10 parts of bactericide, 2-15 parts of organic solvent, 2-15 parts of surfactant, 1-10 parts of electrodeless oxide, 1-15 parts of thickener, 1-10 parts of neutralizing agent, 2-15 parts of tall oil fatty acid, 1-15 parts of polyacrylamide, 1-10 parts of polysaccharide derivative, 1-15 parts of corrosion inhibitor, 1-10 parts of ink medium adsorbent, 1-12 parts of starch, 2-10 parts of preservative, 1-10 parts of morpholine, 1-10 parts of defoaming agent, 1-15 parts of cellulose, 1-15 parts of kaolin, 1-15 parts of calcium carbonate, 4-10 parts of nano titanium dioxide powder, 1-15 parts of superfine antimony oxide powder, 2-20 parts of sodium alginate, 2-8 parts of phenolic resin, 1-20 parts of ionized water, 4-8 parts of diimidazoline ammonium salt corrosion inhibitor and 1-20 parts of thiophene water dispersion solution. The solvent type ink-jet thermal sublimation printing ink is simple in preparation process, the prepared ink has good corrosion resistance, abrasion resistance, oxidation resistance, water resistance and adhesion ability.
Description
Technical field
The present invention relates to technical field of ink, specially a kind of solvent-based inkjet heat sublimation printing inks.
Background technology
Thermal dye sublimation transfer printing is a kind of water-free dyeing technique, with environmental protection effect higher, the high energy advocated current country
Consumption industry energy-saving emission reduction improvement project has important value, and study hotspot has been turned at present.The principle of thermal dye sublimation transfer printing is in height
Under temperature (usually more than 220 DEG C), the disperse dyes on thermal dye sublimation transfer printing medium are sublimed up on chemical fiber plus material and directly by fabric
Fiber is fixed, and the chemical fiber plus material printed and dyed can be with Non-water washing.It is believed that thermal dye sublimation transfer printing technique, especially digital heat sublimation
Transfer printing process, is a kind of high in environmental protection and practical reliable technique, is hopeful to substitute traditional dyeing and finishing technique.
Because distillation trans-printing process requires heat to temperature higher, therefore certain limit is generated to cloth selection
The synthetic fabrics binding strengths such as system, disperse dyes and terylene are good, and thermal-sublimation water-based intaglio printing ink is suitable for terylene, Buddhist nun
The stamp of dragon, triacetate and blend fabric, is not suitable for natural fabric;Thermal-sublimation water-based intaglio printing ink need to be
150~250 DEG C are heated, and distillation is transferred on textile cloth, and the binder of ink must possess certain heat-resisting when high temperature is shifted
Property, to avoid transfer paper and cloth from being sticked together in transfer process phenomenon.At present both at home and abroad for heat sublimation transfer printing and dyeing oil
Ink and preparation method thereof is less.
The content of the invention
It is an object of the invention to provide a kind of solvent-based inkjet heat sublimation printing inks, with solving above-mentioned background technology
The problem of proposition.
To achieve the above object, the present invention provides following technical scheme:A kind of solvent-based inkjet heat sublimation printing inks, bag
Include 5-30 parts of disperse dyes slurry, resin 2-20 parts, hydroxymethyl cellulose 2-15 parts, bactericide 1-10 parts, organic solvent 2-15
Part, surfactant 2-15 parts, electrodeless oxide 1-10 parts, thickener 1-15 parts, nertralizer 1-10 parts, tall oil fatty acid 2-
15 parts, polyacrylamide 1-15 parts, polysaccharide derivates 1-10 parts, corrosion inhibiter 1-15 parts, 1-10 parts of ink medium adsorbent, starch
1-12 parts, preservative 2-10 parts, morpholine 1-10 parts, defoamer 1-10 parts, cellulose 1-15 parts, kaolin 1-15 parts, calcium carbonate
1-15 parts, nano titanium dioxide powder 4-10 parts, 1-15 parts of superfine tin oxide antimony powder end, sodium alginate 2-20 parts, phenolic resin
1-20 parts of 2-8 parts, deionized water 1-20 parts, 4-8 parts of bi-imidazoline quaternary ammonium salt corrosion inhibitor and thiophene aqueous dispersions.
Preferably, the polysaccharide derivates include:Polydextrose, glucan, Arabic gum, agar, glycogen, hyalomitome
Acid.
Preferably, the resin is solvent type resin 1652, polyester resin ES-100, polyester resin ES-VB-220A or poly-
Ester resin W312.
Preferably, preferred composition proportion is:20 parts of disperse dyes slurry, 5 parts of resin, 4 parts of hydroxymethyl cellulose, sterilization
2 parts of agent, 8 parts of organic solvent, 2 parts of surfactant, 1 part of electrodeless oxide, 2 parts of thickener, 2 parts of nertralizer, tall oil fat
2 parts of acid, 2 parts of polyacrylamide, 5 parts of polysaccharide derivates, 3 parts of corrosion inhibiter, 2 parts of ink medium adsorbent, 5 parts of starch, preservative 4
Part, 3 parts of morpholine, 2 parts of defoamer, 4 parts of cellulose, 1 part of kaolin, 2 parts of calcium carbonate, 4 parts of nano titanium dioxide powder, ultra-fine oxygen
Change 2 parts of tin antimony powder end, 3 parts of sodium alginate, 3 parts of phenolic resin, 5 parts of deionized water, 4 parts of bi-imidazoline quaternary ammonium salt corrosion inhibitor and
2 parts of thiophene aqueous dispersions.
Described solvent-based inkjet heat sublimation printing inks are realized, its preparation method is comprised the following steps:
A, by disperse dyes slurry, resin, hydroxymethyl cellulose, bactericide, organic solvent, surfactant, electrodeless oxygen
Compound, thickener, nertralizer, tall oil fatty acid, polysaccharide derivates, corrosion inhibiter, ink medium adsorbent, starch, preservative,
Morpholine, defoamer, cellulose, kaolin, calcium carbonate, nano titanium dioxide powder, superfine tin oxide antimony powder end and deionized water
It is ground in addition grinder, obtains mixture A;
B, in mixture A add polyacrylamide, sodium alginate, phenolic resin, bi-imidazoline quaternary ammonium salt corrosion inhibitor with
And thiophene aqueous dispersions, stirring in mechanical stirring kettle is added after mixing, mechanical stirring kettle rotating speed is 3000 revs/min, mixing time
It is 15min, obtains mixture B;
C, mixture B is put into constant temperature 10min in baking oven, oven temperature is 40 DEG C, ink is obtained after taking out cooling.
Compared with prior art, the beneficial effects of the invention are as follows:
(1) preparation process is simple of the present invention, prepared ink has good wearability, inoxidizability, water resistance and attachment
Ability;
(2) increasing in the present invention has anticorrosive, and ink can be made to have good anticorrosive property;
(3) a certain proportion of nano titanium dioxide powder and superfine tin oxide antimony powder end are added with the present invention, can be made
Ink is more uniform, further increases transfer quality;
(4) the bi-imidazoline quaternary ammonium salt corrosion inhibitor and thiophene aqueous dispersions of present invention addition, can adjust the PH of ink,
Can also prevent simultaneously in print procedure, coating stopped nozzles influence transferring effect.
Specific embodiment
The technical scheme in the embodiment of the present invention is clearly and completely described below, it is clear that described embodiment
Only it is a part of embodiment of the invention, rather than whole embodiments.Based on the embodiment in the present invention, ordinary skill
The every other embodiment that personnel are obtained under the premise of creative work is not made, belongs to the scope of protection of the invention.
The present invention provides a kind of technical scheme:A kind of solvent-based inkjet heat sublimation printing inks, including disperse dyes slurry
5-30 parts, resin 2-20 parts, hydroxymethyl cellulose 2-15 parts, bactericide 1-10 parts, organic solvent 2-15 parts, surfactant 2-
15 parts, electrodeless oxide 1-10 parts, thickener 1-15 parts, nertralizer 1-10 parts, tall oil fatty acid 2-15 parts, polyacrylamide
1-15 parts, polysaccharide derivates 1-10 parts, corrosion inhibiter 1-15 parts, 1-10 parts of ink medium adsorbent, starch 1-12 parts, preservative 2-
10 parts, morpholine 1-10 parts, defoamer 1-10 parts, cellulose 1-15 parts, kaolin 1-15 parts, calcium carbonate 1-15 parts, nano-silica
Change 4-10 parts of titanium powder, 1-15 parts of superfine tin oxide antimony powder end, sodium alginate 2-20 parts, phenolic resin 2-8 parts, deionized water 1-
1-20 parts of 20 parts, 4-8 parts of bi-imidazoline quaternary ammonium salt corrosion inhibitor and thiophene aqueous dispersions.
Embodiment one:
In the present embodiment, the composition proportion for using for:20 parts of disperse dyes slurry, 5 parts of resin, hydroxymethyl cellulose 4
Part, 2 parts of bactericide, 8 parts of organic solvent, 2 parts of surfactant, 1 part of electrodeless oxide, 2 parts of thickener, 2 parts of nertralizer, pine slurry
2 parts of fatty acid oil, 2 parts of polyacrylamide, 5 parts of polysaccharide derivates, 3 parts of corrosion inhibiter, 2 parts of ink medium adsorbent, 5 parts of starch,
4 parts of preservative, 3 parts of morpholine, 2 parts of defoamer, 4 parts of cellulose, 1 part of kaolin, 2 parts of calcium carbonate, nano titanium dioxide powder 4
Part, 2 parts of superfine tin oxide antimony powder end, 3 parts of sodium alginate, 3 parts of phenolic resin, 5 parts of deionized water, bi-imidazoline quaternary ammonium salt inhibition
2 parts of 4 parts of agent and thiophene aqueous dispersions.
In the present embodiment, the polysaccharide derivates include:Polydextrose, glucan, Arabic gum, agar, glycogen, thoroughly
Bright matter acid.
In the present embodiment, the resin is solvent type resin 1652, polyester resin ES-100, polyester resin ES-VB-
220A or polyester resin W312.
Described solvent-based inkjet heat sublimation printing inks are realized, its preparation method is comprised the following steps:
A, by disperse dyes slurry, resin, hydroxymethyl cellulose, bactericide, organic solvent, surfactant, electrodeless oxygen
Compound, thickener, nertralizer, tall oil fatty acid, polysaccharide derivates, corrosion inhibiter, ink medium adsorbent, starch, preservative,
Morpholine, defoamer, cellulose, kaolin, calcium carbonate, nano titanium dioxide powder, superfine tin oxide antimony powder end and deionized water
It is ground in addition grinder, obtains mixture A;
B, in mixture A add polyacrylamide, sodium alginate, phenolic resin, bi-imidazoline quaternary ammonium salt corrosion inhibitor with
And thiophene aqueous dispersions, stirring in mechanical stirring kettle is added after mixing, mechanical stirring kettle rotating speed is 3000 revs/min, mixing time
It is 15min, obtains mixture B;
C, mixture B is put into constant temperature 10min in baking oven, oven temperature is 40 DEG C, ink is obtained after taking out cooling.
Embodiment two:
In the present embodiment, the composition proportion for using for:15 parts of disperse dyes slurry, 6 parts of resin, hydroxymethyl cellulose 5
Part, 2 parts of bactericide, 8 parts of organic solvent, 2 parts of surfactant, 1 part of electrodeless oxide, 2 parts of thickener, 2 parts of nertralizer, pine slurry
2 parts of fatty acid oil, 2 parts of polyacrylamide, 5 parts of polysaccharide derivates, 3 parts of corrosion inhibiter, 2 parts of ink medium adsorbent, 5 parts of starch,
4 parts of preservative, 3 parts of morpholine, 2 parts of defoamer, 4 parts of cellulose, 1 part of kaolin, 2 parts of calcium carbonate, nano titanium dioxide powder 4
Part, 5 parts of superfine tin oxide antimony powder end, 3 parts of sodium alginate, 3 parts of phenolic resin, 5 parts of deionized water, bi-imidazoline quaternary ammonium salt inhibition
2 parts of 4 parts of agent and thiophene aqueous dispersions.
In the present embodiment, the polysaccharide derivates include:Polydextrose, glucan, Arabic gum, agar, glycogen, thoroughly
Bright matter acid.
In the present embodiment, the resin is solvent type resin 1652, polyester resin ES-100, polyester resin ES-VB-
220A or polyester resin W312.
Described solvent-based inkjet heat sublimation printing inks are realized, its preparation method is comprised the following steps:
A, by disperse dyes slurry, resin, hydroxymethyl cellulose, bactericide, organic solvent, surfactant, electrodeless oxygen
Compound, thickener, nertralizer, tall oil fatty acid, polysaccharide derivates, corrosion inhibiter, ink medium adsorbent, starch, preservative,
Morpholine, defoamer, cellulose, kaolin, calcium carbonate, nano titanium dioxide powder, superfine tin oxide antimony powder end and deionized water
It is ground in addition grinder, obtains mixture A;
B, in mixture A add polyacrylamide, sodium alginate, phenolic resin, bi-imidazoline quaternary ammonium salt corrosion inhibitor with
And thiophene aqueous dispersions, stirring in mechanical stirring kettle is added after mixing, mechanical stirring kettle rotating speed is 3000 revs/min, mixing time
It is 15min, obtains mixture B;
C, mixture B is put into constant temperature 10min in baking oven, oven temperature is 40 DEG C, ink is obtained after taking out cooling.
Embodiment three:
In the present embodiment, the composition proportion for using for:18 parts of disperse dyes slurry, 9 parts of resin, hydroxymethyl cellulose 7
Part, 3 parts of bactericide, 8 parts of organic solvent, 2 parts of surfactant, 1 part of electrodeless oxide, 2 parts of thickener, 2 parts of nertralizer, pine slurry
2 parts of fatty acid oil, 2 parts of polyacrylamide, 5 parts of polysaccharide derivates, 3 parts of corrosion inhibiter, 2 parts of ink medium adsorbent, 8 parts of starch,
4 parts of preservative, 3 parts of morpholine, 2 parts of defoamer, 4 parts of cellulose, 1 part of kaolin, 2 parts of calcium carbonate, nano titanium dioxide powder 4
Part, 2 parts of superfine tin oxide antimony powder end, 3 parts of sodium alginate, 3 parts of phenolic resin, 5 parts of deionized water, bi-imidazoline quaternary ammonium salt inhibition
2 parts of 4 parts of agent and thiophene aqueous dispersions.
In the present embodiment, the polysaccharide derivates include:Polydextrose, glucan, Arabic gum, agar, glycogen, thoroughly
Bright matter acid.
In the present embodiment, the resin is solvent type resin 1652, polyester resin ES-100, polyester resin ES-VB-
220A or polyester resin W312.
Described solvent-based inkjet heat sublimation printing inks are realized, its preparation method is comprised the following steps:
A, by disperse dyes slurry, resin, hydroxymethyl cellulose, bactericide, organic solvent, surfactant, electrodeless oxygen
Compound, thickener, nertralizer, tall oil fatty acid, polysaccharide derivates, corrosion inhibiter, ink medium adsorbent, starch, preservative,
Morpholine, defoamer, cellulose, kaolin, calcium carbonate, nano titanium dioxide powder, superfine tin oxide antimony powder end and deionized water
It is ground in addition grinder, obtains mixture A;
B, in mixture A add polyacrylamide, sodium alginate, phenolic resin, bi-imidazoline quaternary ammonium salt corrosion inhibitor with
And thiophene aqueous dispersions, stirring in mechanical stirring kettle is added after mixing, mechanical stirring kettle rotating speed is 3000 revs/min, mixing time
It is 15min, obtains mixture B;
C, mixture B is put into constant temperature 10min in baking oven, oven temperature is 40 DEG C, ink is obtained after taking out cooling.
Example IV:
In the present embodiment, the composition proportion for using for:20 parts of disperse dyes slurry, 10 parts of resin, hydroxymethyl cellulose 7
Part, 2 parts of bactericide, 10 parts of organic solvent, 2 parts of surfactant, 1 part of electrodeless oxide, 2 parts of thickener, 2 parts of nertralizer, pine
2 parts of fatty acid oil of slurry, 2 parts of polyacrylamide, 5 parts of polysaccharide derivates, 3 parts of corrosion inhibiter, 2 parts of ink medium adsorbent, starch 5
Part, 5 parts of preservative, 3 parts of morpholine, 5 parts of defoamer, 4 parts of cellulose, 1 part of kaolin, 2 parts of calcium carbonate, nano titanium dioxide powder
4 parts, superfine tin oxide antimony powder end 2 parts, 3 parts of sodium alginate, 3 parts of phenolic resin, 5 parts of deionized water, bi-imidazoline quaternary ammonium salt delay
Erosion 2 parts of 8 parts of agent and thiophene aqueous dispersions.
In the present embodiment, the polysaccharide derivates include:Polydextrose, glucan, Arabic gum, agar, glycogen, thoroughly
Bright matter acid.
In the present embodiment, the resin is solvent type resin 1652, polyester resin ES-100, polyester resin ES-VB-
220A or polyester resin W312.
Described solvent-based inkjet heat sublimation printing inks are realized, its preparation method is comprised the following steps:
A, by disperse dyes slurry, resin, hydroxymethyl cellulose, bactericide, organic solvent, surfactant, electrodeless oxygen
Compound, thickener, nertralizer, tall oil fatty acid, polysaccharide derivates, corrosion inhibiter, ink medium adsorbent, starch, preservative,
Morpholine, defoamer, cellulose, kaolin, calcium carbonate, nano titanium dioxide powder, superfine tin oxide antimony powder end and deionized water
It is ground in addition grinder, obtains mixture A;
B, in mixture A add polyacrylamide, sodium alginate, phenolic resin, bi-imidazoline quaternary ammonium salt corrosion inhibitor with
And thiophene aqueous dispersions, stirring in mechanical stirring kettle is added after mixing, mechanical stirring kettle rotating speed is 3000 revs/min, mixing time
It is 15min, obtains mixture B;
C, mixture B is put into constant temperature 10min in baking oven, oven temperature is 40 DEG C, ink is obtained after taking out cooling.
Preparation process is simple of the present invention, prepared ink have good anti-corrosive properties, wearability, inoxidizability, water resistance and
Adhesive ability;Anticorrosive is added in the present invention, can make ink that there is good anticorrosive property, additionally, being added with the present invention
A certain proportion of nano titanium dioxide powder and superfine tin oxide antimony powder end, can make coating more uniform, moreover it is possible to improve ink
Antistatic effect, improve transfer quality;The bi-imidazoline quaternary ammonium salt corrosion inhibitor and thiophene aqueous dispersions of present invention addition,
The PH of ink can be adjusted, while in can also preventing print procedure, clogged with ink nozzle influences transferring effect.
Although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
Understanding can carry out various changes, modification, replacement to these embodiments without departing from the principles and spirit of the present invention
And modification, the scope of the present invention be defined by the appended.
Claims (5)
1. a kind of solvent-based inkjet heat sublimation printing inks, it is characterised in that:Including 5-30 parts of disperse dyes slurry, resin 2-20
Part, hydroxymethyl cellulose 2-15 parts, bactericide 1-10 parts, organic solvent 2-15 parts, surfactant 2-15 parts, electrodeless oxide
1-10 parts, thickener 1-15 parts, nertralizer 1-10 parts, tall oil fatty acid 2-15 parts, polyacrylamide 1-15 parts, polysaccharide derivative
Thing 1-10 parts, corrosion inhibiter 1-15 parts, 1-10 parts of ink medium adsorbent, starch 1-12 parts, preservative 2-10 parts, morpholine 1-10
Part, defoamer 1-10 parts, cellulose 1-15 parts, kaolin 1-15 parts, calcium carbonate 1-15 parts, nano titanium dioxide powder 4-10
Part, 1-15 parts of superfine tin oxide antimony powder end, sodium alginate 2-20 parts, phenolic resin 2-8 parts, deionized water 1-20 parts, double imidazoles
1-20 parts of 4-8 parts of hyamine corrosion inhibiter and thiophene aqueous dispersions.
2. solvent-based inkjet heat sublimation printing inks according to claim 1, it is characterised in that:The polysaccharide derivates bag
Include:Polydextrose, glucan, Arabic gum, agar, glycogen, hyaluronic acid.
3. solvent-based inkjet heat sublimation printing inks according to claim 1, it is characterised in that:The resin is solvent-borne type
Resin 1652, polyester resin ES-100, polyester resin ES-VB-220A or polyester resin W312.
4. solvent-based inkjet heat sublimation printing inks according to claim 1, it is characterised in that:Preferred composition proportion
For:20 parts of disperse dyes slurry, 5 parts of resin, 4 parts of hydroxymethyl cellulose, 2 parts of bactericide, 8 parts of organic solvent, surfactant 2
Part, 1 part of electrodeless oxide, 2 parts of thickener, 2 parts of nertralizer, 2 parts of tall oil fatty acid, 2 parts of polyacrylamide, polysaccharide derivates
5 parts, 3 parts of corrosion inhibiter, 2 parts of ink medium adsorbent, 5 parts of starch, 4 parts of preservative, 3 parts of morpholine, 2 parts of defoamer, cellulose 4
Part, 2 parts of 1 part of kaolin, 2 parts of calcium carbonate, 4 parts of nano titanium dioxide powder, superfine tin oxide antimony powder end, 3 parts of sodium alginate, phenol
2 parts of 3 parts of urea formaldehyde, 5 parts of deionized water, 4 parts of bi-imidazoline quaternary ammonium salt corrosion inhibitor and thiophene aqueous dispersions.
5. the solvent-based inkjet heat sublimation printing inks described in claim 1 are realized, it is characterised in that:Its preparation method include with
Lower step:
A, by disperse dyes slurry, resin, hydroxymethyl cellulose, bactericide, organic solvent, surfactant, electrodeless oxide,
Thickener, nertralizer, tall oil fatty acid, polysaccharide derivates, corrosion inhibiter, ink medium adsorbent, starch, preservative, morpholine,
Defoamer, cellulose, kaolin, calcium carbonate, nano titanium dioxide powder, superfine tin oxide antimony powder end and deionized water are added and ground
It is ground in grinding machine, obtains mixture A;
B, addition polyacrylamide, sodium alginate, phenolic resin, bi-imidazoline quaternary ammonium salt corrosion inhibitor and thiophene in mixture A
Fen aqueous dispersions, add stirring in mechanical stirring kettle after mixing, mechanical stirring kettle rotating speed is 3000 revs/min, and mixing time is
15min, obtains mixture B;
C, mixture B is put into constant temperature 10min in baking oven, oven temperature is 40 DEG C, ink is obtained after taking out cooling.