CN106700604A - Black corn stalk dye and production method thereof - Google Patents
Black corn stalk dye and production method thereof Download PDFInfo
- Publication number
- CN106700604A CN106700604A CN201510482666.XA CN201510482666A CN106700604A CN 106700604 A CN106700604 A CN 106700604A CN 201510482666 A CN201510482666 A CN 201510482666A CN 106700604 A CN106700604 A CN 106700604A
- Authority
- CN
- China
- Prior art keywords
- parts
- maize straw
- black
- bark
- lily
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a black corn stalk dye and a production method thereof. The black corn stalk dye is prepared by taking corn stalks, Dongkeshu bark, folium ilicis purpureae, fructus mori, bulbus lilii, alum, an iron ion compound solution and mineral water as main raw materials; the production method comprises the following main processes: selecting materials, cutting, soaking, hot-cooking, dyeing and fixing color. The black corn stalk dye provided by the invention is prepared from pure plants, has fragrance emitted from the plants, is not added with any chemical substance in the production process, has no harms to human bodies, and is wide in source of raw materials, short in processing routing, and easy to be processed and produced.
Description
Technical field:
The present invention relates to a kind of vegetable colour, more particularly to a kind of
Black
Maize straw dyestuff and its production method.
Background technology:
Industrial art refer to daily living article after art up treatment, be allowed to the product with strong aesthetic value.Industrial art is typically divided into the industrial art that the practical art fine arts and furnishings are appreciated by we.The practical art fine arts are main body and the basis of whole industrial art, including clothing, food, change, row, arts and crafts, practical value is the chief value of this kind of handicraft, and aesthetic value is present as auxiliary value.This kind of handicraft is including the tea tableware by decorative processing, light fixture, wood furniture, embroidered article, careless plaited bamboo articles etc..It refers to those to furnish, view and admire the handicraft based on function that furnishings appreciate handicraft, this kind of handicraft with it is aesthetic be its primary value, manual skill is very strong, such as jadeware, jewel, ivory carving, cloisonne enamel, lacquerware, wall hanging, pottery art.
Chinese industrial art it is with a long history, be China culture treasure-house in a bright jewel, it is plain well-known in the world.Industrial art originates from the epoch that the mankind start manufacture instrument.Industrial art is mostly that working people directly creates, and the material life and cultural life with people are closely related.Its generation, often because of period of history, geographical environment, economic condition, cultural technical merit, show different style characteristics national prevailing custom is different with aesthetic standard.
In the prior art, the primary raw material maize straw for making stalk picture is dyed
Black
Method have a many kinds, but most dyestuffs are chemical dye, dye
Black
It is impure, easily fade, not only not environmentally, some dyes even can produce toxic gas, the health of harmful to human during system is contaminated.
The content of the invention:
It is an object of the invention to provide a kind of pure natural, pollution-free, environmental protection, being configured to pure plant of being had no toxic side effect to the person
Black
Maize straw dyestuff and its production method.
The object of the present invention is achieved like this.It is that the raw material matched somebody with somebody by following weight is made,
Maize straw
25-50
Part, the winter can bark
15-30
Part, leaf of Chinese ilex
10-22
Part, mulberry fruit
7-18
Part, lily
5-15
Part, alum
5-15
Part, ferric ion compounds solution
5-15
Part, mineral water
30-80
Part
。
Prepare the present invention
Black
Maize straw dyestuff preferred weight ratio range is, wherein the weight proportion of various raw materials is,
Maize straw
25-40
Part, the winter can bark
15-25
Part, leaf of Chinese ilex
10-16
Part, mulberry fruit
7-13
Part, lily
5-10
Part, alum
5-10
Part, ferric ion compounds solution
5-10
Part, mineral water
30-70
Part
。
Prepare the present invention
Black
The best weight ratio scope of maize straw dyestuff is, wherein the weight proportion of various raw materials is, it is beautiful
Rice stalk
33
Part, the winter can bark
20
Part, leaf of Chinese ilex
13
Part, mulberry fruit
10
Part, lily
8
Part, alum
7
Part, ferric ion compounds solution
7
Part, mineral water
60
Part
。
Above-mentioned each component is made the present invention
Black
The production method of maize straw dyestuff, technical process is:Sorting, blank, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively:A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Winter can bark, leaf of Chinese ilex, mulberry fruit, lily
, alum, ferric ion compounds solution, mineral water it is standby;B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby;
The raw material that will be selected
Winter can bark, leaf of Chinese ilex, mulberry fruit, lily
, be cut into bulk respectively
It is standby
;C, immersion, selected raw material is placed in the storage tank equipped with mineral water and is soaked, temperature is 20 DEG C -25 DEG C, time 2-4 hours of room;D, heat are boiled, incited somebody to action
Salt and water are placed in iron pan and heat, and water temperature heating is arrived
40
°, alum is put into, it is persistently overheating to be to water temperature
70
°, it is put into
Leaching
After bubble
Winter can bark, leaf of Chinese ilex, mulberry fruit, lily, and be stirred continuously, be put into
Ferric ion compounds solution,
Boiling 2-3 hours, cook
Black
Pigment solution;The pigment solution that E, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and fully absorbs maize straw
Black
Pigment, level dyeing;
F
, fixation, the maize straw after dyeing is pulled out, stand
30
Minute, it is put into clear water
5-10
Minute, taken out after drifting out loose colour, it is put at shady and cool ventilation and dries, obtain a kind of maize straw dyestuff of black
。
The advantage of the invention is that:1st, raw material is selected, scientific formulation, color is pure;2nd, product is made by pure plant,
With the delicate fragrance that plant distributes in itself, without any chemical substance in manufacturing process, to human body without any injury
;3rd, raw material sources are extensive, plus process line is short, the manufacture of product easy processing.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated:
Embodiment 1:
Prepare the present invention
Black
Maize straw dyestuff weight proportion scope is:
Maize straw
25-50
Part, the winter can bark
15-30
Part, leaf of Chinese ilex
10-22
Part, mulberry fruit
7-18
Part, lily
5-15
Part, alum
5-15
Part, ferric ion compounds solution
5-15
Part, mineral water
30-80
Part
。
Embodiment 2:
Prepare the present invention
Black
Maize straw dyestuff preferred weight ratio range is:
Maize straw
25-40
Part, the winter can bark
15-25
Part, leaf of Chinese ilex
10-16
Part, mulberry fruit
7-13
Part, lily
5-10
Part, alum
5-10
Part, ferric ion compounds solution
5-10
Part, mineral water
30-70
Part
。
Embodiment 3:
Prepare the present invention
Black
Maize straw dyestuff best weight ratio scope is:It is beautiful
Rice stalk
33
Part, the winter can bark
20
Part, leaf of Chinese ilex
13
Part, mulberry fruit
10
Part, lily
8
Part, alum
7
Part, ferric ion compounds solution
7
Part, mineral water
60
Part
。
Above-mentioned each component is made the present invention
Black
The production method of maize straw dyestuff, technical process is:Sorting, blank, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively:A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Winter can bark, leaf of Chinese ilex, mulberry fruit, lily
, alum, ferric ion compounds solution, mineral water it is standby;B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby;
The raw material that will be selected
Winter can bark, leaf of Chinese ilex, mulberry fruit, lily
, be cut into bulk respectively
It is standby
;C, immersion, selected raw material is placed in the storage tank equipped with mineral water and is soaked, temperature is 20 DEG C -25 DEG C, time 2-4 hours of room;D, heat are boiled, incited somebody to action
Salt and water are placed in iron pan and heat, and water temperature heating is arrived
40
°, alum is put into, it is persistently overheating to be to water temperature
70
°, it is put into
Leaching
After bubble
Winter can bark, leaf of Chinese ilex, mulberry fruit, lily, and be stirred continuously, be put into
Ferric ion compounds solution,
Boiling 2-3 hours, cook
Black
Pigment solution;The pigment solution that E, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and fully absorbs maize straw
Black
Pigment, level dyeing;
F
, fixation, the maize straw after dyeing is pulled out, stand
30
Minute, it is put into clear water
5-10
Minute, taken out after drifting out loose colour, it is put at shady and cool ventilation and dries, obtain a kind of maize straw dyestuff of black
。
Claims (4)
1. a kind of black maize straw dyestuff, it is characterised in that:It is that the raw material matched by following weight is made, maize straw 25-50 parts, the winter can bark 15-30 parts, leaf of Chinese ilex 10-22 parts, mulberry fruit 7-18 parts, lily 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 30-80 parts of ferric ion compounds solution.
2. a kind of black maize straw dyestuff, it is characterised in that:The weight proportion of wherein various raw materials is, maize straw 25-40 parts, the winter can bark 15-25 parts, leaf of Chinese ilex 10-16 parts, mulberry fruit 7-13 parts, lily 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 30-70 parts of ferric ion compounds solution.
3. a kind of black maize straw dyestuff, it is characterised in that:The weight proportion of wherein various raw materials is that 33 parts of maize straw, winter can 20 parts of bark, 13 parts of leaf of Chinese ilex, 10 parts of mulberry fruit, 8 parts of lily, 7 parts of alum, 7 parts of ferric ion compounds solution, 60 parts of mineral waters.
4. a kind of production method for preparing black maize straw dyestuff according to claim 3, it is characterised in that:Technical process is:Sorting, blank, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively:A, sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried, removes other branch, removes Section 1 and last 1 section, leave and take center section, select meet national health and quality standard winter can bark, leaf of Chinese ilex, mulberry fruit, lily, alum, ferric ion compounds solution, mineral water it is standby;B, blank, maize straw knife is longitudinally cut open, the interior flesh part inside removal, retain outside stalk part it is standby;The raw material winter that will be selected can bark, leaf of Chinese ilex, mulberry fruit, lily, be cut into respectively it is block standby;C, immersion, selected raw material is placed in the storage tank equipped with mineral water and is soaked, temperature is 20 DEG C -25 DEG C, time 2-4 hours of room;D, heat boil, salt and water are placed in iron pan and are heated, and water temperature heating is put into alum to 40 °, persistently overheating is 70 ° to water temperature, be put into the winter after immersion can bark, leaf of Chinese ilex, mulberry fruit, lily, and be stirred continuously, ferric ion compounds solution is put into, boiling 2-3 hours, black pigment solution is cooked;The pigment solution that E, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and maize straw is fully absorbed black pigment, level dyeing;F, fixation, the maize straw after dyeing is pulled out, stand 30 minutes, be put into 5-10 minute in clear water, taken out after drifting out loose colour, be put into drying at shady and cool ventilation, obtain a kind of maize straw dyestuff of black.