CN106700601A - Yellow-green corn stalk dye and production method thereof - Google Patents
Yellow-green corn stalk dye and production method thereof Download PDFInfo
- Publication number
- CN106700601A CN106700601A CN201510482551.0A CN201510482551A CN106700601A CN 106700601 A CN106700601 A CN 106700601A CN 201510482551 A CN201510482551 A CN 201510482551A CN 106700601 A CN106700601 A CN 106700601A
- Authority
- CN
- China
- Prior art keywords
- parts
- yellow
- maize straw
- gladiolus
- mango
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a yellow-green corn stalk dye and a production method thereof. The yellow-green corn stalk dye uses core stalk, white mulberry bark, redwood needle, mango, yellow gladiolus flower, alum, an iron ion compound solution and mineral water as main raw materials. The production method comprises the following steps: material selection, material cutting, soaking, hot boiling, dyeing and dye fixation. The dye provided by the invention is prepared from pure plants and has delicate fragrance given out by the plants; no chemical substance is added in the process of production, so the dye is free of harm to human beings; the raw materials are widely available; the production method is simple in process route; and the dye is easy to process and make.
Description
Technical field:
The present invention relates to a kind of vegetable colour, more particularly to a kind of
Yellow green
Maize straw dyestuff and its production method.
Background technology:
Industrial art refer to daily living article after art up treatment, be allowed to the product with strong aesthetic value.Industrial art is typically divided into the industrial art that the practical art fine arts and furnishings are appreciated by we.The practical art fine arts are main body and the basis of whole industrial art, including clothing, food, change, row, arts and crafts, practical value is the chief value of this kind of handicraft, and aesthetic value is present as auxiliary value.This kind of handicraft is including the tea tableware by decorative processing, light fixture, wood furniture, embroidered article, careless plaited bamboo articles etc..It refers to those to furnish, view and admire the handicraft based on function that furnishings appreciate handicraft, this kind of handicraft with it is aesthetic be its primary value, manual skill is very strong, such as jadeware, jewel, ivory carving, cloisonne enamel, lacquerware, wall hanging, pottery art.
Chinese industrial art it is with a long history, be China culture treasure-house in a bright jewel, it is plain well-known in the world.Industrial art originates from the epoch that the mankind start manufacture instrument.Industrial art is mostly that working people directly creates, and the material life and cultural life with people are closely related.Its generation, often because of period of history, geographical environment, economic condition, cultural technical merit, show different style characteristics national prevailing custom is different with aesthetic standard.
In the prior art, the primary raw material maize straw for making stalk picture is dyed
Yellow green
Method have a many kinds, but most dyestuffs are chemical dye, dye
Yellow green
It is impure, easily fade, not only not environmentally, some dyes even can produce toxic gas, the health of harmful to human during system is contaminated.
The content of the invention:
It is an object of the invention to provide a kind of pure natural, pollution-free, environmental protection, being configured to pure plant of being had no toxic side effect to the person
Yellow green
Maize straw dyestuff and its production method.
The object of the present invention is achieved like this.It is that the raw material matched somebody with somebody by following weight is made,
Maize straw
25-50
Part, white mulberry tree bark
15-30
Part, fire works of sequoia tree pin
10-22
Part, mango
7-18
Part, yellow gladiolus flower
5-15
Part, alum
5-15
Part, ferric ion compounds solution
5-15
Part, mineral water
30-80
Part
。
Prepare the present invention
Yellow green
Maize straw dyestuff preferred weight ratio range is, wherein the weight proportion of various raw materials is,
Maize straw
25-40
Part, white mulberry tree bark
15-25
Part, fire works of sequoia tree pin
10-16
Part, mango
7-13
Part, yellow gladiolus flower
5-10
Part, alum
5-10
Part, ferric ion compounds solution
5-10
Part, mineral water
30-70
Part
。
Prepare the present invention
Yellow green
The best weight ratio scope of maize straw dyestuff is, wherein the weight proportion of various raw materials is, it is beautiful
Rice stalk
33
Part, white mulberry tree bark
20
Part, fire works of sequoia tree pin
13
Part, mango
10
Part, yellow gladiolus flower
8
Part, alum
7
Part, ferric ion compounds solution
7
Part, mineral water
60
Part
。
Above-mentioned each component is made the present invention
Yellow green
The production method of maize straw dyestuff, technical process is:Sorting, blank, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively:A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Bai Sangshu barks, fire works of sequoia tree pin, mango, yellow gladiolus flower
, alum, ferric ion compounds solution, mineral water it is standby;B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby;
The raw material that will be selected
Bai Sangshu barks, fire works of sequoia tree pin, mango, yellow gladiolus flower
, be cut into bulk respectively
It is standby
;C, immersion, selected raw material is placed in the storage tank equipped with mineral water and is soaked, temperature is 20 DEG C -25 DEG C, time 2-4 hours of room;D, heat are boiled, incited somebody to action
Salt and water are placed in iron pan and heat, and water temperature heating is arrived
40
°, alum is put into, it is persistently overheating to be to water temperature
70
°, it is put into
Leaching
After bubble
Bai Sangshu barks, fire works of sequoia tree pin, mango, yellow gladiolus flower, and be stirred continuously, it is put into
Ferric ion compounds solution,
Boiling 2-3 hours, cook
Yellow green
Pigment solution;The pigment solution that E, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and fully absorbs maize straw
Yellow green
Pigment, level dyeing;
F
, fixation, the maize straw after dyeing is pulled out, stand
30
Minute, it is put into clear water
5-10
Minute, taken out after drifting out loose colour, it is put at shady and cool ventilation and dries, obtain a kind of maize straw dyestuff of yellow green
。
The advantage of the invention is that:1st, raw material is selected, scientific formulation, color is pure;2nd, product is made by pure plant,
With the delicate fragrance that plant distributes in itself, without any chemical substance in manufacturing process, to human body without any injury
;3rd, raw material sources are extensive, plus process line is short, the manufacture of product easy processing.
Specific embodiment
With reference to specific embodiment, the present invention is further illustrated:
Embodiment 1:
Prepare the present invention
Yellow green
Maize straw dyestuff weight proportion scope is:
Maize straw
25-50
Part, white mulberry tree bark
15-30
Part, fire works of sequoia tree pin
10-22
Part, mango
7-18
Part, yellow gladiolus flower
5-15
Part, alum
5-15
Part, ferric ion compounds solution
5-15
Part, mineral water
30-80
Part
。
Embodiment 2:
Prepare the present invention
Yellow green
Maize straw dyestuff preferred weight ratio range is:
Maize straw
25-40
Part, white mulberry tree bark
15-25
Part, fire works of sequoia tree pin
10-16
Part, mango
7-13
Part, yellow gladiolus flower
5-10
Part, alum
5-10
Part, ferric ion compounds solution
5-10
Part, mineral water
30-70
Part
。
Embodiment 3:
Prepare the present invention
Yellow green
Maize straw dyestuff best weight ratio scope is:It is beautiful
Rice stalk
33
Part, white mulberry tree bark
20
Part, fire works of sequoia tree pin
13
Part, mango
10
Part, yellow gladiolus flower
8
Part, alum
7
Part, ferric ion compounds solution
7
Part, mineral water
60
Part
。
Above-mentioned each component is made the present invention
Yellow green
The production method of maize straw dyestuff, technical process is:Sorting, blank, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively:A
、
Sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried removes other branch, removes Section 1 and last 1 section, leaves and takes center section, selects and meets national health and quality standard
Bai Sangshu barks, fire works of sequoia tree pin, mango, yellow gladiolus flower
, alum, ferric ion compounds solution, mineral water it is standby;B
, blank, maize straw knife is longitudinally cut open, it is interior inside removal
Flesh part, the stalk part outside reservation is standby;
The raw material that will be selected
Bai Sangshu barks, fire works of sequoia tree pin, mango, yellow gladiolus flower
, be cut into bulk respectively
It is standby
;C, immersion, selected raw material is placed in the storage tank equipped with mineral water and is soaked, temperature is 20 DEG C -25 DEG C, time 2-4 hours of room;D, heat are boiled, incited somebody to action
Salt and water are placed in iron pan and heat, and water temperature heating is arrived
40
°, alum is put into, it is persistently overheating to be to water temperature
70
°, it is put into
Leaching
After bubble
Bai Sangshu barks, fire works of sequoia tree pin, mango, yellow gladiolus flower, and be stirred continuously, it is put into
Ferric ion compounds solution,
Boiling 2-3 hours, cook
Yellow green
Pigment solution;The pigment solution that E, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and fully absorbs maize straw
Yellow green
Pigment, level dyeing;
F
, fixation, the maize straw after dyeing is pulled out, stand
30
Minute, it is put into clear water
5-10
Minute, taken out after drifting out loose colour, it is put at shady and cool ventilation and dries, obtain a kind of maize straw dyestuff of yellow green
。
Claims (4)
1. a kind of yellow green maize straw dyestuff, it is characterised in that:It is by following weight match raw material be made, maize straw 25-50 part, 15-30 parts of white mulberry tree bark, 10-22 parts of fire works of sequoia tree pin, mango 7-18 parts, yellow gladiolus flower 5-15 parts, alum 5-15 parts, 5-15 parts, mineral water 30-80 parts of ferric ion compounds solution.
2. a kind of yellow green maize straw dyestuff, it is characterised in that:The weight proportion of wherein various raw materials is, maize straw 25-40 parts, 15-25 parts of white mulberry tree bark, 10-16 parts of fire works of sequoia tree pin, mango 7-13 parts, yellow gladiolus spend 5-10 parts, alum 5-10 parts, 5-10 parts, mineral water 30-70 parts of ferric ion compounds solution.
3. a kind of yellow green maize straw dyestuff, it is characterised in that:The weight proportion of wherein various raw materials is, 33 parts of maize straw, 20 parts of white mulberry tree bark, 13 parts of fire works of sequoia tree pin, 10 parts of mango, yellow gladiolus spend 8 parts, 7 parts of alum, 7 parts of ferric ion compounds solution, 60 parts of mineral water.
4. a kind of production method for preparing yellow green maize straw dyestuff according to claim 3, it is characterised in that:Technical process is:Sorting, blank, immersion, heat are boiled, dyeed, fixation, and concrete operation method follow these steps to successively:A, sorting, by raw material weight proportioning of soup processed, the maize straw that selection is completely dried, remove other branch, remove Section 1 and last 1 section, center section is left and taken, selects that to meet the white mulberry tree bark of national health and quality standard, fire works of sequoia tree pin, mango, yellow gladiolus flower, alum, ferric ion compounds solution, mineral water standby;B, blank, maize straw knife is longitudinally cut open, the interior flesh part inside removal, retain outside stalk part it is standby;The white mulberry tree bark of raw material that to select, fire works of sequoia tree pin, mango, yellow gladiolus flower, be cut into respectively it is block standby;C, immersion, selected raw material is placed in the storage tank equipped with mineral water and is soaked, temperature is 20 DEG C -25 DEG C, time 2-4 hours of room;D, heat boil, salt and water are placed in iron pan and are heated, water temperature heating is to 40 °, it is put into alum, it is persistently overheating to water temperature be 70 °, the white mulberry tree bark after immersion, fire works of sequoia tree pin, mango, yellow gladiolus flower are put into, and are stirred continuously, be put into ferric ion compounds solution, boiling 2-3 hours, cook yellow green pigment solution;The pigment solution that E, dyeing, extraction boiling go out, puts into pottery, is put into the maize straw after immersion, and boiling 1-2 hours, and period is stirred continuously, and maize straw is fully absorbed yellow green pigment, level dyeing;F, fixation, the maize straw after dyeing is pulled out, stand 30 minutes, be put into 5-10 minute in clear water, taken out after drifting out loose colour, be put into drying at shady and cool ventilation, obtain a kind of maize straw dyestuff of yellow green.