CN106700542A - 一种基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物及制造方法 - Google Patents
一种基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物及制造方法 Download PDFInfo
- Publication number
- CN106700542A CN106700542A CN201610108489.3A CN201610108489A CN106700542A CN 106700542 A CN106700542 A CN 106700542A CN 201610108489 A CN201610108489 A CN 201610108489A CN 106700542 A CN106700542 A CN 106700542A
- Authority
- CN
- China
- Prior art keywords
- aromatic polyamide
- parts
- artificial leather
- aluminium
- hypophosphorous acid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物,主要包括如下质量份数的组分:全芳香族聚酰胺60~80份,三(二乙基次磷酸)铝10~15份,锌粉0.2~0.5份,无机填料5~25份。阻燃组合物的制造方法是将上述原料熔融混合,由行星挤出机挤出,冷却后得到。本发明中的全芳香族聚酰胺人造革具有成分简单,对设备无腐蚀,环境友好等优点。
Description
技术领域
本发明属于聚酰胺人造革技术领域,具体涉及聚酰胺人造革的阻燃组合物及制造方法。
背景技术
聚酰胺树脂具有柔软性、结合力强,耐磨,耐油,抗酶菌等优良的性能,从而广泛应用于机械、电子/ 电气等领域。随着近年来人们对于阻燃剂毒性及安全等方面的日益关注,无卤阻燃剂越来越广泛地应用。聚酰胺在制备过程中,部分添加物质在加工温度下趋于分解或降解,这些分解或降解产物可腐蚀挤压机筒体、模塑机表面、螺杆及其他熔融加工设备。
发明内容
本发明所要解决的技术问题是针对上述现有技术提供一种基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物及相应的制造方法,成分简单,减少生产污染,保护加工设备。
本发明解决上述问题所采用的技术方案为:一种基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物,主要包括如下质量份数的组分
全芳香族聚酰胺 60~80份,
三(二乙基次磷酸)铝 10~15份,
锌粉 0.2~0.5份,
无机填料5~25份。
优选地,所述无机填料为:玻璃纤维、玻璃薄片、高岭土、粘土、滑石、钙硅石、碳酸钙、二氧化硅、碳纤维或钛酸钾中的一种或两种以上的混合物。
较合理的是,所述组合物中还包括稳定剂、抗氧剂、润滑剂、颜料、脱模机、成核剂、增塑剂。
上述基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物的制造方法,是将全芳香族聚酰胺 60~80份,三(二乙基次磷酸)铝 10~15份,锌粉 0.2~0.5份,无机填料5~25份熔融共混,由行星挤出机挤出,冷却后得到。
与现有技术相比,本发明的优点在于:采用三(二乙基次磷酸)铝作为阻燃剂,代替传统的含卤阻燃剂,减少了工业污染,其对加工设备无腐蚀,环境友好。
具体实施方式
以下对本发明作进一步详细描述。
本实施例中的基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物按质量份计包括:全芳香族聚酰胺 60~80份,三(二乙基次磷酸)铝 10~15份,锌粉 0.2~0.5份,无机填料5~25份和相应比例的稳定剂、抗氧剂、润滑剂、颜料、脱模机、成核剂、增塑剂。
其中无机填料可以是玻璃纤维、玻璃薄片、高岭土、粘土、滑石、钙硅石、碳酸钙、二氧化硅、碳纤维或钛酸钾中的一种或两种以上的混合物。
阻燃组合物的制造方法是将上述原料熔融混合,由行星挤出机挤出,冷却后得到。
本实施例中的全芳香族聚酰胺人造革具有成分简单,对设备无腐蚀,环境友好等优点。
Claims (4)
1.一种基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物,其特征在于:主要包括如下质量份数的组分:
全芳香族聚酰胺 60~80份,
三(二乙基次磷酸)铝 10~15份,
锌粉 0.2~0.5份,
无机填料5~25份。
2.根据权利要求1所述的基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物,其特征在于:所述无机填料为:玻璃纤维、玻璃薄片、高岭土、粘土、滑石、钙硅石、碳酸钙、二氧化硅、碳纤维或钛酸钾。
3.根据权利要求1所述的基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物,其特征在于:还包括稳定剂、抗氧剂、润滑剂、颜料、脱模机、成核剂、增塑剂。
4.一种制造权利要求1所述的基于三(二乙基次磷酸)铝的全芳香族聚酰胺人造革阻燃组合物的方法,其特征在于:是将全芳香族聚酰胺 60~80份,锌粉 0.2~0.5份,三(二乙基次磷酸)铝 10~15份,无机填料5~25份熔融共混,由行星挤出机挤出,冷却后得到。