CN106700354A - Mind-tranquilizing and heart-nourishing plasticine - Google Patents
Mind-tranquilizing and heart-nourishing plasticine Download PDFInfo
- Publication number
- CN106700354A CN106700354A CN201611129129.8A CN201611129129A CN106700354A CN 106700354 A CN106700354 A CN 106700354A CN 201611129129 A CN201611129129 A CN 201611129129A CN 106700354 A CN106700354 A CN 106700354A
- Authority
- CN
- China
- Prior art keywords
- parts
- plasticine
- tranquilization
- mental
- silane
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses mind-tranquilizing and heart-nourishing plasticine which is prepared from the following substances in parts by weight: 25 to 34 parts of polytetrafluoroethylene fine powder, 2 to 5 parts of jasmine essential oil, 2 to 4 parts of vervain essential oil, 8 to 12 parts of sorghum flour, 3 to 6 parts of aluminum oxide, 1 to 4 parts of semen boitae, 2 to 4 parts of a silane coupling agent, 1 to 3 parts of sodium alginate, 2 to 4 parts of pectin, 1 to 2 parts of sodium carboxymethylcellulose, 2 to 5 parts of potassium oxide, 1 to 2 parts of talcum powder, 2 to 4 parts of sorbitol, 1 to 2 parts of carrageenin, 2 to 3 parts of microcrystalline cellulose and 3 to 5 parts of an antibacterial agent. When a plasticine handicraft is prepared, the mind-tranquilizing and heart-nourishing plasticine is excellent in plasticity, is not sticky to hand, and can be reused even if the mind-tranquilizing and heart-nourishing plasticine is stewed for a long time; meanwhile, by the adding of a few of mind-tranquilizing and heart-nourishing substances and the antibacterial agent, growth of germs is prevented.
Description
Technical field
The present invention relates to plasticine field, especially a kind of plasticine of mental-tranquilization.
Background technology
Develop into today, the material and technique of plasticine all there occurs very big change, unlike former, it is impossible to colour mixture, it is impossible to
Reuse, and it is relatively rough harden, present plasticine is also referred to as color mud, then high-end is exactly Ou Keni.Traditional rubber
Mud is long placed in and is easily air-dried using the raw material commonly used in kitchen, and is also easy to produce crack.Rubber clay plasticine is easy to children to play
Play, be divided into oiliness plasticine or aqueous plasticine.Oiliness plasticine can intactly keep the shape of its model, but hard
Hard plasticine causes children to be difficult with the plasticine to make model.Aqueous plasticine the characteristics of easily kneading because facilitating
For playing for children, but its moisture is more, therefore sticky phenomenon is serious when making, and shrinks after the drying and become
The phenomenon of shape, therefore, it is difficult to take care of for a long time.If additionally, put for a long time using above-mentioned oiliness plasticine and aqueous plasticine
Put, can be hardened because of moisture evaporation, influence is reused.
The content of the invention
To solve the above problems, the invention discloses a kind of plasticine of mental-tranquilization.
In order to reach object above, the present invention provides following technical scheme：
A kind of plasticine of mental-tranquilization, the material comprising following weight portion：Ptfe micropowder 25-34 parts, refined jasmine oil
2-5 parts, 2-4 parts of Verbena officinalis essential oil, sorghum flour 8-12 parts, aluminum oxide 3-6 parts, seed of Oriental arborvitae 1-4 parts, silane coupler 2-4 parts, sea
Mosanom 1-3 parts, pectin 2-4 parts, sodium carboxymethylcellulose 1-2 parts, potassium oxide 2-5 parts, talcum powder 1-2 parts, D-sorbite 2-4
Part, carrageenan 1-2 parts, microcrystalline cellulose 2-3 parts, antiseptic 3-5 parts.
Preferably, material of the plasticine of mental-tranquilization comprising following weight portion：30 parts of ptfe micropowder, jasmine essence
Oil 3 parts, 3 parts of Verbena officinalis essential oil, 10 parts of sorghum flour, 4 parts of aluminum oxide, 2 parts of the seed of Oriental arborvitae, 3 parts of silane coupler, 2 parts of sodium alginate,
3 parts of pectin, 1 part of sodium carboxymethylcellulose, 3 parts of potassium oxide, 1 part of talcum powder, 2 parts of D-sorbite, 2 parts of carrageenan, crystallite are fine
Dimension plain 2 parts, 4 parts of antiseptic.
Preferably, the silane coupler is isobutyl triethoxy silane, aminopropyltriethoxy diethoxy silane, 16
Alkyl trimethoxysilane, mercaptopropyl trimethoxysilane, MTMS, MTES, vinyl
Triethoxysilane, vinyltrimethoxy silane, one or more of allyl glycidyl ether.
Preferably, the antiseptic be zinc oxide, cupric oxide, ammonium dihydrogen phosphate, one or more of lithium carbonate.
Preferably, the plasticine of described mental-tranquilization, comprising following preparation process and step：
S1：Aluminum oxide, potassium oxide, talcum powder are added into ethanol solution, ultrasonic disperse 10-15 minutes, silane coupler is added,
80 mesh sieves are crossed in the stirring in water bath 30-40min at 60-70 DEG C, drying, grinding；
S2：By ptfe micropowder, sorghum flour, the seed of Oriental arborvitae, sodium alginate, pectin, sodium carboxymethylcellulose, D-sorbite,
Carrageenan, microcrystalline cellulose and S1 gains are added in banbury, and 10-12min is kneaded with 20r/min；
S3：Rubbed after S2 gains are taken out, and rubbed into refined jasmine oil, Verbena officinalis essential oil and antiseptic, used preservative film
Or egg shell wrap it is standby.
Beneficial effects of the present invention：It is not sticky tack-free with excellent plasticity, shelved for a long time after manufacturing products of craftsmanship
Can reuse.Meanwhile, the material of mental-tranquilization is with the addition of, children is played too crazy, can play more absorbedly.Addition
There is a small amount of antiseptic, prevent the growth of bacterium.
Specific embodiment
With reference to specific embodiment, the present invention is furture elucidated, it should be understood that following specific embodiments are only used for
The bright present invention rather than limitation the scope of the present invention.
Embodiment 1：
S1：Ethanol solution, ultrasonic disperse 12 minutes is added to add 3 parts of silicon 4 parts of aluminum oxide, 3 parts of potassium oxides, 1 part of talcum powder
Alkane coupling agent is modified to it, the stirring in water bath 35min at 65 DEG C, drying removal ethanol, ground 80 mesh sieve；
S2：By 30 parts of ptfe micropowders, 10 parts of sorghum flours, 2 parts of seed of Oriental arborvitaes, 2 parts of sodium alginates, 3 parts of pectin, 1 part of carboxylic first
Base sodium cellulosate, 2 parts of D-sorbites, 2 parts of carrageenans, 2 parts of microcrystalline celluloses and S1 gains are added in banbury, with 20r/
Min kneads 11min, is well mixed it；
S3：Rubbed after S2 gains are taken out, and rubbed into 3 parts of refined jasmine oils, 3 parts of Verbena officinalis essential oils and 4 parts of antiseptics,
The plasticine of mental-tranquilization is can be prepared by, is wrapped with preservative film or egg shell standby.
Embodiment 2：
S1：Ethanol solution, ultrasonic disperse 10 minutes is added to add 2 parts of silicon 3 parts of aluminum oxide, 2 parts of potassium oxides, 1 part of talcum powder
Alkane coupling agent is modified to it, the stirring in water bath 30min at 60 DEG C, drying removal ethanol, ground 80 mesh sieve；
S2：By 25 parts of ptfe micropowders, 8 parts of sorghum flours, 1 part of seed of Oriental arborvitae, 1 part of sodium alginate, 2 parts of pectin, 1 part of carboxymethyl
Sodium cellulosate, 2 parts of D-sorbites, 1 part of carrageenan, 2 parts of microcrystalline celluloses and S1 gains are added in banbury, with 20r/
Min kneads 10min, is well mixed it；
S3：Rubbed after S2 gains are taken out, and rubbed into 2 parts of refined jasmine oils, 2 parts of Verbena officinalis essential oils and 3 parts of antiseptics,
The plasticine of mental-tranquilization is can be prepared by, is wrapped with preservative film or egg shell standby.
Embodiment 3：
S1：Ethanol solution, ultrasonic disperse 15 minutes is added to add 4 parts of silicon 6 parts of aluminum oxide, 5 parts of potassium oxides, 2 parts of talcum powder
Alkane coupling agent is modified to it, the stirring in water bath 40min at 70 DEG C, drying removal ethanol, ground 80 mesh sieve；
S2：By 34 parts of ptfe micropowders, 12 parts of sorghum flours, 4 parts of seed of Oriental arborvitaes, 3 parts of sodium alginates, 4 parts of pectin, 2 parts of carboxylic first
Base sodium cellulosate, 4 parts of D-sorbites, 2 parts of carrageenans, 3 parts of microcrystalline celluloses and S1 gains are added in banbury, with 20r/
Min kneads 12min, is well mixed it；
S3：Rubbed after S2 gains are taken out, and rubbed into 5 parts of refined jasmine oils, 4 parts of Verbena officinalis essential oils and 5 parts of antiseptics,
The plasticine of mental-tranquilization is can be prepared by, is wrapped with preservative film or egg shell standby.
Embodiment 4：
S1：Ethanol solution, ultrasonic disperse 11 minutes is added to add 3 parts of silicon 4 parts of aluminum oxide, 3 parts of potassium oxides, 1 part of talcum powder
Alkane coupling agent is modified to it, the stirring in water bath 33min at 62 DEG C, drying removal ethanol, ground 80 mesh sieve；
S2：By 27 parts of ptfe micropowders, 9 parts of sorghum flours, 2 parts of seed of Oriental arborvitaes, 2 parts of sodium alginates, 2 parts of pectin, 1 part of carboxymethyl
Sodium cellulosate, 2 parts of D-sorbites, 1 part of carrageenan, 2 parts of microcrystalline celluloses and S1 gains are added in banbury, with 20r/
Min kneads 11min, is well mixed it；
S3：Rubbed after S2 gains are taken out, and rubbed into 3 parts of refined jasmine oils, 3 parts of Verbena officinalis essential oils and 4 parts of antiseptics,
The plasticine of mental-tranquilization is can be prepared by, is wrapped with preservative film or egg shell standby.
Embodiment 5：
S1：Ethanol solution, ultrasonic disperse 14 minutes is added to add 4 parts of silicon 5 parts of aluminum oxide, 4 parts of potassium oxides, 2 parts of talcum powder
Alkane coupling agent is modified to it, the stirring in water bath 37min at 68 DEG C, drying removal ethanol, ground 80 mesh sieve；
S2：By 32 parts of ptfe micropowders, 11 parts of sorghum flours, 3 parts of seed of Oriental arborvitaes, 3 parts of sodium alginates, 3 parts of pectin, 2 parts of carboxylic first
Base sodium cellulosate, 4 parts of D-sorbites, 2 parts of carrageenans, 3 parts of microcrystalline celluloses and S1 gains are added in banbury, with 20r/
Min kneads 12min, is well mixed it；
S3：Rubbed after S2 gains are taken out, and rubbed into 4 parts of refined jasmine oils, 4 parts of Verbena officinalis essential oils and 5 parts of antiseptics,
The plasticine of mental-tranquilization is can be prepared by, is wrapped with preservative film or egg shell standby.
Different commercially available plasticine samples and the plasticine sample of the embodiment of the present invention 1 are carried out into durability experiment, constant temperature is put into
In constant humidity cabinet, temperature is 25 DEG C, and humidity is 45%RH, the results are shown in Table 1：
The durability test result of table 1
By the data display of table 1, the plasticine of the embodiment of the present invention 1 best performance in durability test.
Different commercially available plasticine samples and plasticine sample of the present invention are done into Mechanics Performance Testing, 2~3g samples are weighed,
Be made the sample of 2cm*0.5cm*0.5cm, two ends gently clamped with test clamp, carried out with general-purpose mechanics tester tensile strength and
The test of elongation at break, the results are shown in Table 2：
The tensile strength of table 2 and elongation at break test result
According to the data display of table 2, the plasticine of the embodiment of the present invention 1 performance in the test of tensile strength and elongation at break
More excellent, the plasticine tensile strength of the embodiment of the present invention 1 is of a relatively high, and durability is preferable.
The above, is only presently preferred embodiments of the present invention, and not the present invention is imposed any restrictions, every according to the present invention
Any simple modification, change and equivalent structure change that technical spirit is made to above example, still fall within skill of the present invention
In the protection domain of art scheme.
Claims (5)
1. a kind of plasticine of mental-tranquilization, it is characterised in that the material comprising following weight portion：Ptfe micropowder 25-
34 parts, refined jasmine oil 2-5 parts, 2-4 parts of Verbena officinalis essential oil, sorghum flour 8-12 parts, aluminum oxide 3-6 parts, seed of Oriental arborvitae 1-4 parts, silane
Coupling agent 2-4 parts, sodium alginate 1-3 parts, pectin 2-4 parts, sodium carboxymethylcellulose 1-2 parts, potassium oxide 2-5 parts, talcum powder 1-2
Part, D-sorbite 2-4 parts, carrageenan 1-2 parts, microcrystalline cellulose 2-3 parts, antiseptic 3-5 parts.
2. the plasticine of mental-tranquilization as claimed in claim 1, it is characterised in that the material comprising following weight portion：Poly- four
30 parts of PVF micro mist, 3 parts of refined jasmine oil, 3 parts of Verbena officinalis essential oil, 10 parts of sorghum flour, 4 parts of aluminum oxide, 2 parts of the seed of Oriental arborvitae, silane
3 parts of coupling agent, 2 parts of sodium alginate, 3 parts of pectin, 1 part of sodium carboxymethylcellulose, 3 parts of potassium oxide, 1 part of talcum powder, D-sorbite 2
Part, 2 parts of carrageenan, 2 parts of microcrystalline cellulose, 4 parts of antiseptic.
3. the plasticine of mental-tranquilization as claimed in claim 1, it is characterised in that the silane coupler is the second of isobutyl group three
TMOS, aminopropyltriethoxy diethoxy silane, hexadecyl trimethoxy silane, mercaptopropyl trimethoxysilane, methyl
Trimethoxy silane, MTES, VTES, vinyltrimethoxy silane, pi-allyl contracting
One or more of water glycerin ether.
4. the plasticine of mental-tranquilization as claimed in claim 1, it is characterised in that the antiseptic be zinc oxide, cupric oxide,
One or more of ammonium dihydrogen phosphate, lithium carbonate.
5. the plasticine of mental-tranquilization as claimed in claim 1, it is characterised in that comprising following preparation process and step：
S1：Aluminum oxide, potassium oxide, talcum powder are added into ethanol solution, ultrasonic disperse 10-15 minutes, silane coupler is added,
80 mesh sieves are crossed in the stirring in water bath 30-40min at 60-70 DEG C, drying, grinding；
S2：By ptfe micropowder, sorghum flour, the seed of Oriental arborvitae, sodium alginate, pectin, sodium carboxymethylcellulose, D-sorbite,
Carrageenan, microcrystalline cellulose and S1 gains are added in banbury, and 10-12min is kneaded with 20r/min；
S3：Rubbed after S2 gains are taken out, and rubbed into refined jasmine oil, Verbena officinalis essential oil and antiseptic, used preservative film
Or egg shell wrap it is standby.