CN102690451A - Non-toxic plasticine and production method thereof - Google Patents
Non-toxic plasticine and production method thereof Download PDFInfo
- Publication number
- CN102690451A CN102690451A CN2012102020937A CN201210202093A CN102690451A CN 102690451 A CN102690451 A CN 102690451A CN 2012102020937 A CN2012102020937 A CN 2012102020937A CN 201210202093 A CN201210202093 A CN 201210202093A CN 102690451 A CN102690451 A CN 102690451A
- Authority
- CN
- China
- Prior art keywords
- parts
- plasticine
- atoxic
- banburying
- cis
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a non-toxic plasticine and a production method thereof. The non-toxic plasticine comprises the following materials in parts by weight: 40-60 parts of butyl rubber, 50-70 parts of cis-1,4-polybutadiene rubber, 230-360 parts of filler, 230-300 parts of softening agent and 5-10 parts of pigment. The method provided by the invention is simple and easy to implement; and the plasticine provided by the invention has the advantages of no toxicity, no smell and high safety and reliability, can not crack or harden after long time storage, can be used repeatedly, and is applicable to children.
Description
Technical field
The present invention relates to a kind of Atoxic plasticine and working method thereof.
Background technology
Along with people's is to the attention of health, particularly children population, the children educational product more next with the extensive attention that receives people more, be safety to the toy that children contacted and the requirement of apparatus, nontoxic, tasteless, can not be to children's healthy generation harm.But make a general survey of the present plasticine product in market; Though what select for use on the material is flour and water; But in order to prevent to go mouldy, a large amount of sanitass, mould inhibitor, mask agent, spices have been added, peculiar smell easy-clear not on the contact defensive position; Children eat the back by mistake and can damage health, and very easily exsiccation, hardening, can't use repeatedly.
Summary of the invention
Problems and shortcomings to present market plasticine product the objective of the invention is to propose a kind of Atoxic plasticine, and this plasticine is nontoxic, tasteless, it is not dry and cracked to put for a long time, not hardening, can use repeatedly.
Another object of the present invention is to provide the method for manufacture of above-mentioned Atoxic plasticine, this method is simple.
For realizing above-mentioned purpose, the scheme that the present invention solves is:
A kind of Atoxic plasticine, this Atoxic plasticine comprises following materials in weight portion:
40 parts-60 parts of butyl rubbers; 50 parts-70 parts of cis-1,4-polybutadiene rubbers;
230 parts-360 parts of fillers; 230 parts-300 parts of tenderizers;
5 parts-10 parts of pigment.
Further, said rubber is medical grade material.
Further, said filler comprises 10 parts of-30 parts of polybutene, 200 parts of-300 parts of lime carbonate, 5 parts of-30 parts of paraffin, and said filler is food grade materials.
Further, said tenderizer comprises 150 parts of-200 parts of white oils and 80 parts of-100 parts of epoxy soybean oils, and said tenderizer is the material of food grade.
Further, said pigment is food grade materials.
A kind of method of manufacture of above-mentioned Atoxic plasticine may further comprise the steps:
1) get 40 parts of-60 parts of butyl rubbers, 50 parts of-70 parts of cis-1,4-polybutadiene rubbers are placed in the Banbury mixer mixing;
2) again 230 parts-360 fillers, 5 parts of-10 parts of pigment and 230 parts of-300 parts of tenderizers are added successively, treat various material banburying mixings after, take out to place;
The said mixture that 3) will be mixed is put into forcing machine, extrudes, moulding, packing.
Further, the butyl rubber in the said step (1), cis-1,4-polybutadiene rubber are under the 50-70 degree banburying 10-15 minute.
Further, the banburying condition of said step (2) is under the 50-70 degree banburying 10-15 minute.
The present invention compared with prior art has the following advantages:
1, all raw materials of the present invention or employing medical grade or employing food grade materials reach nontoxic effect, guarantee the quality safety of articles for children.
2, the present invention is heat-resisting, ageing-resistant, and electrical insulating property is good, good springiness.
Embodiment
Below in conjunction with embodiment the present invention is further specified:
Embodiment 1
A kind of method of manufacture of Atoxic plasticine may further comprise the steps:
(1) 50 parts of 50 parts of butyl rubbers, cis-1,4-polybutadiene rubber is put into Banbury mixer banburying mixing 10-15 minute under the 50-70 degree;
(2) gained mixture in the step (1) is added 10 parts of polybutene, 250 parts in lime carbonate, 5 parts in paraffin, 150 parts of white oils, 80 parts of epoxy soybean oils, 7 parts of bright red HO-02-02 of pigment under the 50-70 degree banburying mixing 10-15 minute once more;
(3) gained mixture in the step (2) was put into clean material disc cooling after 2 hours, puts into forcing machine and extrude, the packing of segment simultaneously finished product.
Embodiment 2:
(1) 60 parts of butyl rubbers, cis-1,4-polybutadiene rubber are put into the banburying machine for 40 parts and carry out banburying mixing, banburying temperature 50-70 degree;
(2) gained mixture in the step (1) is added 20 parts of polybutene, 270 parts in lime carbonate, paraffin
10 parts, 180 parts of white oils, 90 parts of epoxy soybean oils, 5 parts of phthalocyanine blue LA-61-02 of pigment carry out banburying once more, banburying temperature 50-70 degree;
(3) gained mixture in the step (2) is put into clean material disc cooling after, put into forcing machine and extrude, the packing of segment simultaneously finished product.
Embodiment 3:
(1) 35 parts of butyl rubbers, cis-1,4-polybutadiene rubber are put into the banburying machine for 65 parts and carry out banburying mixing, banburying temperature 50-70 degree;
(2) gained mixture in the step (1) is added the yellow HU-02-02 of junket in 10 parts of 15 parts of the polybutene, 200 parts in lime carbonate, 20 parts in paraffin, 160 parts of white oils, 85 parts of epoxy soybean oils, pigment, carry out banburying once more, banburying temperature 50-70 degree;
(3) gained mixture in the step (2) is put into clean material disc cooling after, put into forcing machine and extrude, the packing of segment simultaneously finished product.
Embodiment 4:
(1) 40 parts of butyl rubbers, cis-1,4-polybutadiene rubber are put into the banburying machine for 70 parts and carry out banburying mixing, banburying temperature 50-70 degree;
(2) gained mixture in the step (1) is added 30 parts of polybutene, 300 parts in lime carbonate, 30 parts in paraffin, 200 parts of white oils, 100 parts of epoxy soybean oils, the blue LA-61-02 of monastral blue; Bright red HO-02-02; Each 5 parts are carried out banburying once more, banburying temperature 50-70 degree;
(3) gained mixture in the step (2) is put into clean material disc cooling after, put into forcing machine and extrude, the packing of segment simultaneously finished product.
Obviously, the above embodiment of the present invention only be for clearly the present invention is described and is done for example, and be not to be qualification to embodiment of the present invention.For the those of ordinary skill in affiliated field, on the basis of above-mentioned explanation, can also make other multi-form variation or change.Here can't give exhaustive to all embodiments.Everyly belong to the row that conspicuous variation that technical scheme of the present invention extends out or change still are in protection scope of the present invention.
Claims (8)
1. an Atoxic plasticine is characterized in that, this Atoxic plasticine comprises following materials in weight portion:
40 parts-60 parts of butyl rubbers; 50 parts-70 parts of cis-1,4-polybutadiene rubbers;
230 parts-360 parts of fillers; 230 parts-300 parts of tenderizers;
5 parts-10 parts of pigment.
2. Atoxic plasticine according to claim 1 is characterized in that: said butyl rubber, cis-1,4-polybutadiene rubber are medical grade material.
3. Atoxic plasticine according to claim 1 is characterized in that: said filler comprises 10 parts of-30 parts of polybutene, 200 parts of-300 parts of lime carbonate, 5 parts of-30 parts of paraffin.
4. Atoxic plasticine according to claim 1 is characterized in that: said tenderizer comprises 150 parts of-200 parts of white oils and 80 parts of-100 parts of epoxy soybean oils.
5. according to claim 1,3 or 4 described Atoxic plasticines, it is characterized in that: said filler, tenderizer, pigment are food grade materials.
6. method of manufacture like the described arbitrary Atoxic plasticine of claim 1-4 is characterized in that: may further comprise the steps:
1) get 40 parts of-60 parts of butyl rubbers, 50 parts of-70 parts of cis-1,4-polybutadiene rubbers are placed in the Banbury mixer mixing;
2) again 230 parts-360 fillers, 5 parts of-10 parts of pigment and 230 parts of-300 parts of tenderizers are added successively, treat various material banburying mixings after, take out to place;
The said mixture that 3) will be mixed is put into forcing machine, extrudes, moulding, packing.
7. the method for manufacture of Atoxic plasticine according to claim 6 is characterized in that: the butyl rubber in the said step (1), cis-1,4-polybutadiene rubber under the 50-70 degree banburying 10-15 minute.
8. the method for manufacture of Atoxic plasticine according to claim 6 is characterized in that: the banburying condition of said step (2) is under the 50-70 degree banburying 10-15 minute.